Process conditions and precursors for atomic layer deposition (ALD) of AL2O3
Assignee: Applied Materials Inc
•
Filing: 2002-01-18
•
Granted: 2003-09-16
•
Expires: 2022-01-18
Abstract
Abstract A semiconductor processing chamber has been utilized to perform sequential deposition of high-K Al 2 O 3 thin films on a substrate disposed in the chamber employing low viscosity precursors. The method commences with introduction of an aluminum precursor into the processing chamber. In this manner, a monolayer of aluminum precursor is chemisorbed onto the substrate surface. Thereafter, non-chemisorbed aluminum precursor is purged from the processing chamber, followed by introduction of an oxygen precursor. The oxygen precursor reacts with the chemisorbed layer, resulting in a monolayer of Al 2 O 3 . Finally, excess oxygen precursor and by-products of the reaction are purged completing the sequential deposition cycle. The sequential deposition cycle can be repeated to grow the Al 2 O 3 film to a desired thickness.
Inventors
- 👤 Kevin Song
- 👤 Jallepally Ravi
- 👤 Shih-Hung Li
- 👤 Liang-Yuh Chen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:49
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6938; H10P14/6939; H10P14/69391; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/403; C23C16/44; C23C16/448; C23C16/452; C23C16/455; C23C16/45523; C23C16/45525; C23C16/45553; H10P14/66; H10P14/668; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6339
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
98 words
A method for depositing an aluminum-containing layer on a substrate disposed in a processing chamber, said method comprising: forming an aluminum-containing monolayer upon said substrate by flowing an aluminum-containing compound and a liquid solvent into a vaporizer and then delivering the aluminum-containing process gas onto said substrate; reacting oxygen with said aluminum-containing monolayer by exposing said aluminum-containing monolayer to an oxygen-containing precursor to produce a layer of Al 2 O 3 ; and repeating forming said aluminum-containing layer and reacting oxygen with said aluminum-containing monolayer to form said layer of Al 2 O 3 with a desired thickness.
Claim 2
Independent Claim
98 words
A method for depositing an aluminum-containing layer on a substrate disposed in a processing chamber, said method comprising: forming an aluminum-containing monolayer upon said substrate by flowing an aluminum-containing compound and a liquid solvent into a vaporizer and then delivering the aluminum-containing process gas onto said substrate; reacting oxygen with said aluminum-containing monolayer by exposing said aluminum-containing monolayer to an oxygen-containing precursor to produce a layer of Al 2 O 3 ; and repeating forming said aluminum-containing layer and reacting oxygen with said aluminum-containing monolayer to form said layer of Al 2 O 3 with a desired thickness.
Claim 3
Dependent Claim
45 words
The method as recited in claim 1 wherein forming said aluminum-containing monolayer further includes vaporizing a liquid aluminum-containing precursor selected from the set of precursors consisting essentially of Triisopropoxyaluminum-Tetrahydrofuran, Aluminumtrichloride, Dimethylaluminumhydride:Dimethylethylamine and Ethylpiperidine:Dimethylaluminumhydride and reacting oxygen further includes vaporizing water to produce said oxygen-containing precursor.
Claim 4
Dependent Claim
42 words
The method as recited in claim 1 wherein forming said aluminum-containing monolayer further includes vaporizing a liquid aluminum-containing precursor selected from the set of precursors consisting essentially of Triisopropoxyaluminum-Hexane, Triisopropoxyaluminum-Tetrahydrofuran, Dimethylaluminumhydride:Dimethylethylamine and Ethylpiperidine:Dimethylaluminumhydride, by flowing said liquid aluminum-containing precursor into a vaporizer.
Claim 5
Dependent Claim
37 words
The method as recited in claim 1 wherein reacting oxygen further includes flowing an oxygen-containing compound, selected from a set of compounds consisting essentially of ozone, water vapor, oxygen radical and oxygen ions into said processing chamber.
Claim 6
Dependent Claim
49 words
The method as recited in claim 1 wherein forming said aluminum-containing monolayer further includes heating said substrate to a temperature in a range of 100° C. to 500° C., inclusive and establishing a pressure within said processing chamber to be in a range of 0.1 Torr to 500 Torr.
Claim 7
Dependent Claim
41 words
The method as recited in claim 1 wherein forming said aluminum-containing monolayer further includes vaporizing a liquid Triisopropoxyaluminum-Hexane having a weight ratio of Triisopropoxyaluminum to Hexane in a range of 10:90 to 60:40, by flowing said liquid Triisopropoxyaluminum-Hexane into a vaporizer.
Claim 8
Dependent Claim
41 words
The method as recited in claim 1 wherein forming said aluminum-containing monolayer further includes vaporizing a liquid Triisopropoxyaluminum-Tetrahydrofuran having a weight ratio of Triisopropoxyaluminum to Tetrahydrofuran in a range of 10:90 to 60:40, by flowing said liquid Triisopropoxyaluminum-Tetrahydrofuran into a vaporizer.
Claim 9
Dependent Claim
39 words
The method as recited in claim 1 wherein forming an aluminum-containing monolayer upon said substrate further includes flowing said aluminum-containing process gas into said processing chamber at a rate in a range of 1 mg/minute to 200 mg/minute, inclusive.
Claim 10
Dependent Claim
63 words
The method as recited in claim 1 wherein forming said aluminum-containing monolayer further includes vaporizing a liquid aluminum-containing precursor by heating liquid Aluminumtrhichloride to a temperature above a sublimation temperature that is associated with said liquid Aluminumtrichloride to produce Aluminumtrichloride gas and introducing said Aluminumtrichloride gas into said processing chamber at a rate in a range of 20 sccm to 1000 sccm, inclusive.
Claim 11
Dependent Claim
45 words
The method as recited in claim 1 wherein reacting oxygen further includes dissociating an oxygen-containing gas to form reactive species by impinging microwave frequencies on said oxygen-containing gas in a range of 100 Watts to 3000 Watts, and flowing said reactive species over said substrate.
Claim 12
Dependent Claim
49 words
The method as recited in claim 1 further including purging, after forming said aluminum-containing layer, said processing chamber of said aluminum-containing process gas before reacting oxygen with said aluminum-containing monolayer, and removing, after reacting oxygen and before repeating forming said aluminum-containing layer, said oxygen-containing precursor from said processing chamber.
Claim 13
Dependent Claim
29 words
The method of claim 1 , wherein the aluminum-containing compound and the liquid solvent are flowed into the vaporizer in a weight ratio between about 10:90 and about 60:40.
Claim 14
Independent Claim
131 words
A method for depositing an aluminum-containing layer onto a substrate disposed in a processing chamber, said method comprising: heating said substrate to a temperature in a range of 100° C. to 500° C., inclusive; establishing a pressure within said processing chamber in a range of 0.1 Torr to 500 Torr; forming an aluminum-containing monolayer upon said substrate by flowing an aluminum-containing compound and a liquid solvent into a vaporizer and then delivering the aluminum-containing process gas onto said substrate; reacting oxygen with said aluminum-containing monolayer by exposing said aluminum-containing monolayer to an oxygen-containing precursor to produce a layer of Al 2 O 3 and by-products; and repeating forming said aluminum-containing layer and reacting oxygen with said aluminum-containing monolayer to form said layer of Al 2 O 3 with a desired thickness.
Claim 15
Independent Claim
131 words
A method for depositing an aluminum-containing layer onto a substrate disposed in a processing chamber, said method comprising: heating said substrate to a temperature in a range of 100° C. to 500° C., inclusive; establishing a pressure within said processing chamber in a range of 0.1 Torr to 500 Torr; forming an aluminum-containing monolayer upon said substrate by flowing an aluminum-containing compound and a liquid solvent into a vaporizer and then delivering the aluminum-containing process gas onto said substrate; reacting oxygen with said aluminum-containing monolayer by exposing said aluminum-containing monolayer to an oxygen-containing precursor to produce a layer of Al 2 O 3 and by-products; and repeating forming said aluminum-containing layer and reacting oxygen with said aluminum-containing monolayer to form said layer of Al 2 O 3 with a desired thickness.
Claim 16
Dependent Claim
86 words
The method as recited in claim 13 wherein heating said substrate further includes heating said substrate to a processing temperature no less than 150° C. and forming said aluminum-containing monolayer further includes vaporizing a liquid aluminum-containing precursor selected from the set of precursors consisting essentially of Triisopropoxyaluminum-Hexane and Triisopropoxyaluminum-Tetrahydrofuran, by flowing said liquid aluminum-containing precursor into a vaporizer and reacting oxygen further includes flowing an oxygen-containing compound, selected from a set of compounds consisting essentially of ozone, oxygen radical and oxygen, ions into said processing chamber.
Claim 17
Dependent Claim
83 words
The method as recited in claim 13 wherein heating said substrate furthering includes heating said substrate to a processing temperature having a range no greater than 300° C. and, forming said aluminum-containing monolayer further includes vaporizing a liquid aluminum-containing precursor selected from the set of precursors consisting essentially of Triisopropoxyaluminum-Tetrahydrofuran, Dimethylaluminumhydride:Dimethylethylamine and Ethylpiperidine:Dimethylaluminumhydride and reacting oxygen further Includes flowing an oxygen-containing compound, selected from a set of compounds consisting essentially of water vapor, ozone, oxygen radicals and oxygen ions into said processing chamber.
Claim 18
Dependent Claim
67 words
The method as recited in claim 13 wherein heating said substrate furthering includes heating said substrate to a processing temperature having a range of 100° C. to 300° C., inclusive and forming said aluminum-containing monolayer further includes vaporizing a liquid aluminum-containing precursor selected from the set of precursors consisting essentially of, Aluminumtrichloride, Dimethylaluminumhydride:Dimethylethylamine and Ethylpiperidine:Dimethylaluminumhydride and reacting oxygen further includes flowing water vapor into said processing chamber.
Claim 19
Dependent Claim
49 words
The method as recited in claim 13 further including purging, after forming said aluminum-containing layer, said processing chamber of said aluminum-containing process gas before reacting oxygen into said aluminum-containing monolayer, and removing, after reacting oxygen and before repeating forming said aluminum-containing layer, said oxygen-containing precursor from said processing chamber.
Claim 20
Dependent Claim
29 words
The method of claim 13 , wherein the aluminum-containing compound and the liquid solvent are flowed into the vaporizer in a weight ratio between about 10:90 and about 60:40.
Claim 21
Dependent Claim
252 words
A processing system for forming an aluminum-containing layer on a substrate, said system comprising: a body defining a processing chamber; a cover disposed over the body and adapted to deliver gases into the processing chamber; a holder disposed within said processing chamber to support said substrate; an oxygen-containing precursor source mounted on the cover; an aluminum-containing precursor in fluid communication with the cover; a temperature control system in thermal communication with said processing chamber; a pressure control system in fluid communication with said processing chamber; a controller in electrical communication with the cover, said temperature control system, and said pressure control system; and a memory in data communication with said controller, said memory comprising a computer-readable medium having a computer-readable program embodied therein, said computer-readable program including a first set of instructions for controlling the cover, said pressure control system and said temperature control system to form an aluminum-containing monolayer upon said substrate by chemisorption of said aluminum-containing precursor, and a second set of instructions to control said gas delivery system, said pressure control system and said temperature control system to chemisorb oxygen into said aluminum-containing monolayer by exposing said aluminum-containing monolayer to said oxygen-containing precursor to produce a layer of Al 2 O 3 and by-products, and a third set of instructions to control the cover, said pressure control system and said temperature control system to repeat forming said aluminum-containing layer and chemisorbing oxygen into said aluminum-containing monolayer to form said layer of Al 2 O 3 with a desired thickness.
Claim 22
Dependent Claim
252 words
A processing system for forming an aluminum-containing layer on a substrate, said system comprising: a body defining a processing chamber; a cover disposed over the body and adapted to deliver gases into the processing chamber; a holder disposed within said processing chamber to support said substrate; an oxygen-containing precursor source mounted on the cover; an aluminum-containing precursor in fluid communication with the cover; a temperature control system in thermal communication with said processing chamber; a pressure control system in fluid communication with said processing chamber; a controller in electrical communication with the cover, said temperature control system, and said pressure control system; and a memory in data communication with said controller, said memory comprising a computer-readable medium having a computer-readable program embodied therein, said computer-readable program including a first set of instructions for controlling the cover, said pressure control system and said temperature control system to form an aluminum-containing monolayer upon said substrate by chemisorption of said aluminum-containing precursor, and a second set of instructions to control said gas delivery system, said pressure control system and said temperature control system to chemisorb oxygen into said aluminum-containing monolayer by exposing said aluminum-containing monolayer to said oxygen-containing precursor to produce a layer of Al 2 O 3 and by-products, and a third set of instructions to control the cover, said pressure control system and said temperature control system to repeat forming said aluminum-containing layer and chemisorbing oxygen into said aluminum-containing monolayer to form said layer of Al 2 O 3 with a desired thickness.
Claim 23
Dependent Claim
71 words
The system as recited in claim 19 wherein said computer-readable program further includes a fourth set of instructions to control the cover to purge said aluminum-containing precursor and by-products from said processing chamber before introduction of said oxygen-containing precursor into said processing chamber and a fifth set of instructions to remove said oxygen-containing precursor after chemisorbing said oxygen into said aluminum-containing monolayer and before execution of said third set of instructions.
Claim 24
Dependent Claim
17 words
The processing system of claim 19 , wherein the oxygen-containing precursor source comprises a remote plasma source.
References Cited (Backward Citations)
US4486487A
Cited
JPS6065712A
Cited
US4975252A
Cited
JPS6291495A
Cited
US4829022A
Cited
US4917556A
Cited
US4838983A
Cited
US4960720A
Cited
US4834831A
Cited
US5246536A
Cited
US4859625A
Cited
US4838993A
Cited
US4951601A
Cited
US5882165A
Cited
US5000113A
Cited
US5923985A
Cited
US4813846A
Cited
US5441703A
Cited
US5348911A
Cited
FR2626110A1
Cited
EP0344352A1
Cited
US5439876A
Cited
US4927670A
Cited
US5234561A
Cited
US4931132A
Cited
US5013683A
Cited
US5186718A
Cited
US5527733A
Cited
US5028565A
Cited
EP0429270A2
Cited
US5925574A
Cited
US5296403A
Cited
EP0442490A1
Cited
US5316615A
Cited
US5173474A
Cited
US5091320A
Cited
US5205077A
Cited
US5085885A
Cited
US5277788A
Cited
US5286296A
Cited
US5259881A
Cited
WO1993002111A1
Cited
US6001669A
Cited
US5311055A
Cited
US5254207A
Cited
US5580380A
Cited
FR2692597A1
Cited
US5469806A
Cited
US5601651A
Cited
US5455072A
Cited
US5856219A
Cited
US5492606A
Cited
US5674786A
Cited
US5503875A
Cited
US5438952A
Cited
US5540783A
Cited
US5521126A
Cited
US5866213A
Cited
US5749974A
Cited
US5796116A
Cited
US5641984A
Cited
US5695564A
Cited
US5707880A
Cited
US5730801A
Cited
US5644128A
Cited
US6158446A
Cited
US5616181A
Cited
WO1996017107A1
Cited
WO1996018756A1
Cited
US5609689A
Cited
DE19627017A1
Cited
US5788447A
Cited
US5947710A
Cited
US6084302A
Cited
US5667592A
Cited
US5788799A
Cited
US6062798A
Cited
US5858102A
Cited
US5747113A
Cited
US5830270A
Cited
US5942040A
Cited
US5835677A
Cited
US5923056A
Cited
US5928389A
Cited
US5807792A
Cited
US6051286A
Cited
US6174377B1
Cited
US5855675A
Cited
US20010011526A1
Cited
US6207302B1
Cited
US5866795A
Cited
US6140237A
Cited
US5882413A
Cited
US5904565A
Cited
US6287965B1
Cited
US6144060A
Cited
US6140238A
Cited
US5801634A
Cited
US6110556A
Cited
US6143659A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2006-09-15 | 2007-03-17 | 2007-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2010-09-15 | 2011-03-17 | 2011-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2014-09-15 | 2015-03-17 | 2015-09-16 | $7700.00 | Window Closed / Lapsed |