US5972105A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of fabricating semiconductor device
Assignee: Semiconductor Energy Laboratory Co Ltd
•
Filing: 1995-09-14
•
Granted: 1999-10-26
•
Expires: 2015-09-14
Abstract
Abstract Thin-film transistors (TFTs) having characteristics comparable to those of a single-crystal silicon wafer are provided. A buffer film made from silicon oxide is formed on a first amorphous silicon film. A nickel acetate solution containing a metal element such as nickel for promoting crystallization of silicon is applied to the first amorphous silicon film. The laminate is heat-treated to form a nickel silicide layer. The nickel silicide layer is then patterned. A second amorphous silicon film is formed and heat-treated to grow crystals. Thus, monodomain regions which can be regarded as single crystals are formed. Active layers of TFTs are formed from these monodomain regions.
Inventors
- 👤 Shunpei Yamazaki
- 👤 Naoto Kusumoto
- 👤 Satoshi Teramoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:57
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2922; H10D; H10D30/00; H10D30/60; H10D30/67; C; C30; C30B; C30B1/00; C30B1/02; C30B1/023; C30B29/00; C30B29/02; C30B29/06; H10D86/00; H10D86/01; H10D86/021; H10D86/0221; H10D86/0223; H10D86/0225; H10D86/40; H10D86/421; H10D86/60; H10P14/27; H10P14/271; H10P14/274; H10P14/32; H10P14/3202; H10P14/3238; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3451; H10P14/3452; H10P14/3458; H10P14/38; H10P14/3802; H10P14/3806; H10P14/3808; H10D30/01; H10D30/021; H10D30/031; H10D30/0312; H10D30/0314; H10D30/0321
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
142 words
A method of fabricating a semiconductor device, comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; maintaining a metal containing layer for promoting crystallization of silicon in contact with said first film; heat-treating said first film to crystallize same with the aid of said metal containing layer; patterning the crystallized film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate with a portion of said second film being in contact with said at least one crystal nucleus; and crystallizing said second film based on said at least one nucleus, and patterning the crystallized second film into at least one active layer for said semiconductor device; wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 2
Independent Claim
142 words
A method of fabricating a semiconductor device, comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; maintaining a metal containing layer for promoting crystallization of silicon in contact with said first film; heat-treating said first film to crystallize same with the aid of said metal containing layer; patterning the crystallized film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate with a portion of said second film being in contact with said at least one crystal nucleus; and crystallizing said second film based on said at least one nucleus, and patterning the crystallized second film into at least one active layer for said semiconductor device; wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 3
Independent Claim
157 words
A method of fabricating a semiconductor device, comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; maintaining a metal containing layer for promoting crystallization of silicon in contact with said first film; heat-treating said first film to crystallize [it] same with the aid of said metal containing layer; patterning the crystallized film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate with a portion of said second film being in contact with said at least one crystal nucleus; and crystallizing said second film based on said at least one nucleus to form a substantially single crystal region in said second film by light irradiation patterning the crystallized second film into at least one active layer for said semiconductor device; and wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 4
Independent Claim
157 words
A method of fabricating a semiconductor device, comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; maintaining a metal containing layer for promoting crystallization of silicon in contact with said first film; heat-treating said first film to crystallize [it] same with the aid of said metal containing layer; patterning the crystallized film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate with a portion of said second film being in contact with said at least one crystal nucleus; and crystallizing said second film based on said at least one nucleus to form a substantially single crystal region in said second film by light irradiation patterning the crystallized second film into at least one active layer for said semiconductor device; and wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 5
Independent Claim
133 words
A method of fabricating a semiconductor device, comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; maintaining a metal containing layer for promoting crystallization of silicon in contact with said first film; heat-treating said first film to crystallize same with the aid of said metal containing layer; patterning the crystallized film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate with a portion of said second film being in contact with said at least one crystal nucleus; and crystallizing said second film based on said at least one nucleus by light while heating said second film, wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 6
Independent Claim
133 words
A method of fabricating a semiconductor device, comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; maintaining a metal containing layer for promoting crystallization of silicon in contact with said first film; heat-treating said first film to crystallize same with the aid of said metal containing layer; patterning the crystallized film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate with a portion of said second film being in contact with said at least one crystal nucleus; and crystallizing said second film based on said at least one nucleus by light while heating said second film, wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 7
Independent Claim
38 words
A method of fabricating a semiconductor device as set forth in any one of claims 1-3, wherein said metal is selected from the group consisting of Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, Cu, and Au.
Claim 8
Independent Claim
60 words
A method of fabricating a semiconductor device as set forth in any one of claims 1-3, wherein said metal is selected from the group consisting of Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, Cu, and Au, and wherein a concentration of said metal in said active layer is from 1×10 14 to 1×10 19 atoms cm 3 .
Claim 9
Independent Claim
30 words
A method of fabricating a semiconductor device as set forth in any one of claims 1-3, wherein said active layer contains 0.001 to 5 atomic % hydrogen or halogen element.
Claim 10
Dependent Claim
33 words
A method of fabricating a semiconductor device according to claim 1 wherein said active layer is substantially single crystal which has no grain boundary therein and contains hydrogen to neutralize point defects therein.
Claim 11
Dependent Claim
22 words
A method of fabricating a semiconductor device according to claim 7 wherein said grain boundary is a line-defect or a two-dimensional defect.
Claim 12
Dependent Claim
33 words
A method of fabricating a semiconductor device according to claim 2 wherein said active layer is substantially single crystal which has no grain boundary therein and contains hydrogen to neutralize point defects therein.
Claim 13
Dependent Claim
22 words
A method of fabricating a semiconductor device according to claim 9 wherein said grain boundary is a line-defect or a two-dimensional defect.
Claim 14
Dependent Claim
14 words
A method according to claim 2 wherein said light irradiation is a laser irradiation.
Claim 15
Dependent Claim
33 words
A method of fabricating a semiconductor device according to claim 3 wherein said active layer is substantially single crystal which has no grain boundary therein and contains hydrogen to neutralize point defects therein.
Claim 16
Dependent Claim
22 words
A method of fabricating a semiconductor device according to claim 12 wherein said grain boundary is a line-defect or a two-dimensional defect.
Claim 17
Dependent Claim
14 words
A method according to claim 3 wherein said light irradiation is a laser irradiation.
Claim 18
Dependent Claim
22 words
A method of fabricating a semiconductor device according to claim 1 wherein said semiconductor device is an active matrix liquid crystal display.
Claim 19
Dependent Claim
33 words
A method of fabricating a semiconductor device according to claim 1 further comprising a step of adding impurities to portions of said active layer to form a source region and a drain region.
Claim 20
Dependent Claim
22 words
A method of fabricating a semiconductor device according to claim 2 wherein said semiconductor device is an active matrix liquid crystal display.
Claim 21
Dependent Claim
33 words
A method of fabricating a semiconductor device according to claim 2 further comprising a step of adding impurities to portions of said active layer to form a source region and a drain region.
Claim 22
Dependent Claim
22 words
A method of fabricating a semiconductor device according to claim 3 wherein said semiconductor device is an active matrix liquid crystal display.
Claim 23
Dependent Claim
32 words
A method of fabricating a semiconductor device according to claim 3 further comprising a step of adding impurities to portions of said active layer to forma source region and a drain region.
Claim 24
Independent Claim
144 words
A method of manufacturing a semiconductor device comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; providing an entirely region of said first film with a catalyst material for promoting crystallization of said first film; crystallizing said first film with an aid of said catalyst material; patterning the crystallized first film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate and said at least one crystal nucleus wherein a portion of the second film contacts said at least one crystal nucleus; crystallizing said second film from said at least one crystal nucleus; patterning the crystallized second film into at least one active layer for said semiconductor device; wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 25
Independent Claim
144 words
A method of manufacturing a semiconductor device comprising the steps of: forming a first film comprising amorphous silicon over a substrate having an insulating surface; providing an entirely region of said first film with a catalyst material for promoting crystallization of said first film; crystallizing said first film with an aid of said catalyst material; patterning the crystallized first film into at least one crystal nucleus; forming a second film comprising amorphous silicon over said substrate and said at least one crystal nucleus wherein a portion of the second film contacts said at least one crystal nucleus; crystallizing said second film from said at least one crystal nucleus; patterning the crystallized second film into at least one active layer for said semiconductor device; wherein said crystallized second film is so patterned that said portion of the second film is excluded from said active layer.
Claim 26
Dependent Claim
21 words
A method according to claim 21 wherein said catalyst material is formed on an entire upper surface of the first film.
Claim 27
Dependent Claim
13 words
A method according to claim 21 wherein said catalyst material comprises a metal.
Claim 28
Dependent Claim
28 words
A method according to claim 23 wherein said metal is selected from the group consisting of Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, Cu and Au.
Claim 29
Dependent Claim
16 words
A method to claim 21 wherein the crystallization ofthe second film is conducted by light irradiation.
Claim 30
Dependent Claim
28 words
A method according to claim 21 wherein said active layer is substantially single crystal which has no grain boundary therein and contains hydrogen to neutralize point defects therein.
References Cited (Backward Citations)
JPS5958821A
Cited
JPS59148322A
Cited
JPS6281017A
Cited
US4992839A
Cited
JPH02222546A
Cited
US5290712A
Cited
US5147826A
Cited
US5294811A
Cited
US5373803A
Cited
US5563426A
Cited
US5403772A
Cited
US5604360A
Cited
US5696386A
Cited
US5639698A
Cited
US5608232A
Cited
US5275851A
Cited
US5624851A
Cited
US5595944A
Cited
US5426064A
Cited
US5677549A
Cited
US5646424A
Cited
US5569610A
Cited
US5569936A
Cited
US5580792A
Cited
US5614733A
Cited
US5595923A
Cited
US5589694A
Cited
US5501989A
Cited
US5481121A
Cited
US5488000A
Cited
US5663077A
Cited
US5529937A
Cited
US5492843A
Cited
US5696388A
Cited
US5614426A
Cited
US5637515A
Cited
US5508533A
Cited
US5534716A
Cited
US5616506A
Cited
US5643826A
Cited
US5612250A
Cited
US5543352A
Cited
US5585291A
Cited
US5654203A
Cited
US5705829A
Cited
US5605846A
Cited
US5656825A
Cited
US5620910A
Cited
US5712191A
Cited
US5621224A
Cited
US5606179A
Cited
US5700333A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-25 | 2003-04-26 | 2003-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-25 | 2007-04-26 | 2007-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-25 | 2011-04-26 | 2011-10-26 | $7700.00 | Window Closed / Lapsed |