US5432015A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electroluminescent laminate with thick film dielectric
Assignee: 749110 ALBERTA Ltd
•
Filing: 1993-04-30
•
Granted: 1995-07-11
•
Expires: 2013-04-30
Abstract
Abstract An improved dielectric layer of an electroluminescent laminate, and method of preparation are provided. The dielectric layer is formed as a thick layer from a ceramic material to provide: a dielectric strength greater than about 1.0×10 6 V/m; a dielectric constant such that the ratio of the dielectric constant of the dielectric material to that of the phosphor layer is greater than about 50:1; a thickness such that the ratio of the thickness of the dielectric layer to that of the phosphor layer is in the range of about 20:1 to 500:1; and a surface adjacent the phosphor layer which is compatible with the phosphor layer and sufficiently smooth that the phosphor layer illuminates generally uniformly at a given excitation voltage. The invention also provides for electrical connection of an electroluminescent laminate to voltage driving circuity with through hole technology. The invention also extends to laser scribing the transparent conductor lines of an electroluminescent laminate.
Inventors
- 👤 Xingwei Wu
- 👤 James A. R. Stiles
- 👤 Ken K. Foo
- 👤 Phillip Bailey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 03:51
CPC Classifications
H; H05; H05B; H05B33/00; H05B33/12; H05B33/26; H05B33/28; H05B33/10; H05B33/22; Y; Y10; Y10S; Y10S117/00; Y10S117/903; Y10S117/904; Y10S428/00; Y10S428/917; Y10S438/00; Y10S438/94
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
165 words
An electroluminescent laminate comprising: a planar phosphor layer: a front and a rear planar electrode on either side of the phosphor layer; a rear substrate on which the rear electrode is formed, the substrate having sufficient rigidity to support the laminate; and a planar dielectric layer between the rear electrode and the phosphor layer, the dielectric layer being formed from a sintered ceramic material such that the dielectric layer provides a dielectric strength greater than about 1.0×10 6 V/m and a dielectric constant such that the ratio of the dielectric constant of the dielectric layer to that of the phosphor layer is greater than about 50:1, the dielectric layer having a thickness such that the ratio of the thickness of the dielectric layer to that of the phosphor layer is in the range of about 20:1 to 500:1, and the dielectric layer having a surface adjacent the phosphor layer which is sufficiently smooth that the phosphor layer illuminates generally uniformly at a given excitation voltage.
Claim 2
Dependent Claim
165 words
An electroluminescent laminate comprising: a planar phosphor layer: a front and a rear planar electrode on either side of the phosphor layer; a rear substrate on which the rear electrode is formed, the substrate having sufficient rigidity to support the laminate; and a planar dielectric layer between the rear electrode and the phosphor layer, the dielectric layer being formed from a sintered ceramic material such that the dielectric layer provides a dielectric strength greater than about 1.0×10 6 V/m and a dielectric constant such that the ratio of the dielectric constant of the dielectric layer to that of the phosphor layer is greater than about 50:1, the dielectric layer having a thickness such that the ratio of the thickness of the dielectric layer to that of the phosphor layer is in the range of about 20:1 to 500:1, and the dielectric layer having a surface adjacent the phosphor layer which is sufficiently smooth that the phosphor layer illuminates generally uniformly at a given excitation voltage.
Claim 3
Dependent Claim
64 words
The laminate as set forth in claim 1, wherein the ratio of the dielectric constant of the dielectric layer to that of the phosphor layer is greater than about 100:1, and wherein the dielectric layer has a thickness such that the ratio of the thickness of the dielectric layer to that of the phosphor layer is in the range of about 40:1 to 300:1.
Claim 4
Dependent Claim
45 words
The laminate as set forth in claim 1 wherein the phosphor layer is a thin film layer sandwiched between the front electrode and the rear electrode, the front electrode being transparent, and the phosphor layer being separated from the rear electrode by the dielectric layer.
Claim 5
Dependent Claim
29 words
The laminate as set forth in claim 3, wherein the dielectric layer has a dielectric constant greater than about 500 and a thickness in the range of 10-300 microns.
Claim 6
Dependent Claim
92 words
The laminate as set forth in claim 4, wherein the dielectric layer includes at least two layers, a first dielectric layer formed on the rear electrode and having the dielectric strength and dielectric constant values as set forth in claim 4, and a second dielectric layer formed on the first dielectric layer and having the surface adjacent the phosphor layer which is sufficiently smooth that the phosphor layer illuminates generally uniformly at a given excitation voltage, the first and second dielectric layers having a combined thickness as set forth in claim 4.
Claim 7
Dependent Claim
21 words
The laminate as set forth in claim 5, wherein the first and second dielectric layers are formed from ferroelectric ceramic materials.
Claim 8
Dependent Claim
30 words
The laminate as set forth in claim 5, wherein the second dielectric layer provides a dielectric constant of at least 20 and a thickness of at least about 2 microns.
Claim 9
Dependent Claim
34 words
The laminate as set forth in claim 7, wherein the first dielectric layer provides a dielectric constant of at least 1000 and the second dielectric layer provides a dielectric constant of at least 100.
Claim 10
Dependent Claim
38 words
The laminate as set forth in claim 8, wherein the first dielectric layer has a thickness in the range of about 20-150 microns and the second dielectric layer has a thickness in the range of about 2-10 microns.
Claim 11
Dependent Claim
25 words
The laminate as set forth in claim 9, wherein the first and second dielectric layers are formed from ferroelectric ceramic materials having perovskite crystal structures.
Claim 12
Dependent Claim
59 words
The laminate as set forth in claim 5, 6 or 10, wherein the substrate and rear electrode are formed from materials which can withstand temperatures of about 850° C., and wherein the first dielectric layer is formed by thick film techniques followed by sintering at a temperature less than the melting point of the rear electrode and the substrate.
Claim 13
Dependent Claim
18 words
The laminate as set forth in claim 11, wherein the first dielectric layer is formed by screen printing.
Claim 14
Dependent Claim
37 words
The laminate as set forth in claim 11, wherein the second dielectric layer is formed by sol gel techniques followed by sintering at a temperature less than the melting point of the rear electrode and the substrate.
Claim 15
Dependent Claim
42 words
The laminate as set forth in claim 12, wherein the second dielectric layer is formed by sol gel techniques, including spin deposition or dipping followed by sintering at a temperature less than the melting point of the rear electrode and the substrate.
Claim 16
Dependent Claim
38 words
The laminate as set forth in claim 5, 6, or 10, wherein the first dielectric layer is formed from lead niobate and wherein the second dielectric layer is formed from lead zirconate titanate or lead lanthanum zirconate titanate.
Claim 17
Dependent Claim
35 words
The laminate as set forth in claim 11, wherein the first dielectric layer is formed from lead niobate and wherein the second dielectric layer is formed from lead zirconate titanate or lead lanthanum zirconate titanate.
Claim 18
Dependent Claim
35 words
The laminate as set forth in claim 14, wherein the first dielectric layer is formed from lead niobate and wherein the second dielectric layer is formed from lead zirconate titanate or lead lanthanum zirconate titanate.
Claim 19
Dependent Claim
13 words
The laminate as set forth in claim 14, wherein the substrate is alumina.
Claim 20
Dependent Claim
36 words
The laminate as set forth in claim 14, wherein the surface of the dielectric layer adjacent the phosphor layer has a surface relief which does not vary more than about 0.5 microns over about 1000 microns.
Claim 21
Dependent Claim
35 words
The laminate as set forth in claim 17, wherein the rear electrode is formed of fired silver/platinum address lines on an alumina substrate and the front electrode is formed of indium tin oxide address lines.
Claim 22
Dependent Claim
17 words
The laminate as set forth in claim 20, further comprising a sealing layer above the front electrode.
Claim 23
Dependent Claim
22 words
The laminate as set forth in claim 1, wherein the dielectric layer is in contact with, and compatible with, the phosphor layer.
Claim 24
Dependent Claim
22 words
The laminate as set forth in claim 5, wherein the dielectric layer is in contact with, and compatible with, the phosphor layer.
Claim 25
Dependent Claim
38 words
The laminate as set forth in claim 4 or 5, wherein the surface of the dielectric layer adjacent the phosphor layer has a surface relief which does not vary more than about 0.5 microns over about 1000 microns.
Claim 26
Dependent Claim
179 words
In an electroluminescent laminate having a phosphor layer sandwiched between a front and a rear electrode, the rear electrode being formed on a substrate and the phosphor layer being separated from the rear electrode by a dielectric layer, the improvement comprising: the dielectric layer being formed from at least two layers, a first dielectric layer formed on the rear electrode, and a second dielectric layer formed on the first dielectric layer, the second layer having a surface which is sufficiently smooth that the phosphor layer illuminates generally uniformly at a given excitation voltage, the first and second dielectric layers being formed from sintered ceramic materials to provide a dielectric strength greater than about 1.0×10 6 V/m and a dielectric constant such that the ratio of the dielectric constant of the dielectric layer to that of the phosphor layer is greater than about 50:1, the combined thickness of the first and second layers being such that the ratio of the thickness of the dielectric layer to that of the phosphor layer is in the range of about 20:1 to 500:1.
Claim 27
Dependent Claim
179 words
In an electroluminescent laminate having a phosphor layer sandwiched between a front and a rear electrode, the rear electrode being formed on a substrate and the phosphor layer being separated from the rear electrode by a dielectric layer, the improvement comprising: the dielectric layer being formed from at least two layers, a first dielectric layer formed on the rear electrode, and a second dielectric layer formed on the first dielectric layer, the second layer having a surface which is sufficiently smooth that the phosphor layer illuminates generally uniformly at a given excitation voltage, the first and second dielectric layers being formed from sintered ceramic materials to provide a dielectric strength greater than about 1.0×10 6 V/m and a dielectric constant such that the ratio of the dielectric constant of the dielectric layer to that of the phosphor layer is greater than about 50:1, the combined thickness of the first and second layers being such that the ratio of the thickness of the dielectric layer to that of the phosphor layer is in the range of about 20:1 to 500:1.
Claim 28
Dependent Claim
65 words
The improvement as set forth in claim 25, wherein the ratio of the dielectric constant of the dielectric layer to that of the phosphor layer is greater than about 100:1, and wherein the dielectric layer has a combined thickness such that the ratio of the thickness of the dielectric layer to that of the phosphor layer is in the range of about 40:1 to 300:1.
Claim 29
Dependent Claim
55 words
The improvement as set forth in claim 26, wherein the first dielectric layer has a dielectric constant greater than about 500 and a thickness in the range of about 10 to 300 microns, and wherein the second dielectric layer has a dielectric constant of at least 20 and a thickness of at least 2 microns.
Claim 30
Dependent Claim
21 words
The improvement as set forth in claim 27, wherein the first and second dielectric layers are formed from ferroelectric ceramic materials.
Claim 31
Dependent Claim
34 words
The improvement as set forth in claim 28, wherein the first dielectric layer provides a dielectric constant of at least 1000 and the second dielectric layer provides a dielectric constant of at least 100.
Claim 32
Dependent Claim
42 words
The improvement as set forth in claim 29, wherein the first dielectric layer has a thickness in the range of about 20 to 150 microns and the second dielectric layer has a thickness in the range of about 2 to 10 microns.
Claim 33
Dependent Claim
25 words
The improvement as set forth in claim 30, wherein the first and second dielectric layers are formed from ferroelectric ceramic materials having perovskite crystal structures.
Claim 34
Dependent Claim
41 words
The improvement as set forth in claim 30, wherein the first dielectric layer is formed on the rear electrode by thick film techniques followed by sintering at a temperature less than the melting point of the rear electrode or the substrate.
Claim 35
Dependent Claim
18 words
The improvement as set forth in claim 32, wherein the first dielectric layer is formed by screen printing.
Claim 36
Dependent Claim
37 words
The improvement as set forth in claim 32, wherein the second dielectric layer is formed by sol gel techniques followed by sintering at a temperature less than the melting point of the rear electrode or the substrate.
Claim 37
Dependent Claim
18 words
The improvement as set forth in claim 34, wherein the sol gel techniques include spin deposition or dipping.
Claim 38
Dependent Claim
35 words
The improvement as set forth in claim 35, wherein the first dielectric layer is formed from lead niobate and wherein the second dielectric layer is formed from lead zirconate titanate or lead lanthanum zirconate titanate.
Claim 39
Dependent Claim
35 words
The improvement as set forth in claim 25 or 35, wherein the surface of the second dielectric layer has a surface relief which does not vary more than about 0.5 microns over about 1000 microns.
Claim 40
Dependent Claim
41 words
The improvement as set forth in claim 25, wherein the first dielectric layer is formed on the rear electrode by thick film techniques followed by sintering at a temperature less than the melting point of the rear electrode or the substrate.
References Cited (Backward Citations)
US2497912A
Cited
US3475640A
Cited
GB1141420A
Cited
US3504214A
Cited
GB1161977A
Cited
GB1194304A
Cited
GB1259358A
Cited
US3641390A
Cited
US3828215A
Cited
GB1431889A
Cited
US3889151A
Cited
JPS5258494A
Cited
US4280107A
Cited
US4292092A
Cited
GB2084778A
Cited
US4468659A
Cited
US4416933A
Cited
US4418118A
Cited
US4490603A
Cited
US4686110A
Cited
US4482841A
Cited
EP0111568A1
Cited
US4508990A
Cited
US4568578A
Cited
US4849252A
Cited
US4568409A
Cited
EP0145470A2
Cited
JPS60133792A
Cited
US4617195A
Cited
US4866348A
Cited
EP0160227A1
Cited
US4593228A
Cited
GB2161306A
Cited
DE3518598A1
Cited
GB2161011A
Cited
US4713518A
Cited
US4970368A
Cited
US4874920A
Cited
US4970369A
Cited
US4614668A
Cited
US4665342A
Cited
GB2165078A
Cited
US4686426A
Cited
US4983885A
Cited
US4680855A
Cited
EP0184877A1
Cited
JPS61168895A
Cited
US4721631A
Cited
US4691078A
Cited
US4783421A
Cited
US4757235A
Cited
US4667058A
Cited
GB2177838A
Cited
US4915982A
Cited
US4804558A
Cited
US4879139A
Cited
US4693906A
Cited
US4880475A
Cited
US5006365A
Cited
US4710395A
Cited
US4749840A
Cited
US4975145A
Cited
US4786358A
Cited
US4927493A
Cited
US4792500A
Cited
US4857802A
Cited
US4861964A
Cited
US4865686A
Cited
USRE33947E
Cited
US4705698A
Cited
EP0278194A1
Cited
JPS63182892A
Cited
US4849674A
Cited
US4877994A
Cited
WO1988009268A1
Cited
US4877481A
Cited
EP0295477A2
Cited
US5043567A
Cited
US4854974A
Cited
US4965092A
Cited
US4937129A
Cited
JPH01236687A
Cited
US4970366A
Cited
JPH01272095A
Cited
US4927490A
Cited
US4981712A
Cited
US4897319A
Cited
JPH0233890A
Cited
JPH0244691A
Cited
US4885448A
Cited
EP0365445A2
Cited
WO1990009730A1
Cited
US4909895A
Cited
JPH03105894A
Cited
US5131877A
Cited
US5057664A
Cited
US5109149A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-07-10 | 1999-01-09 | 1999-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-07-10 | 2003-01-09 | 2003-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-07-10 | 2007-01-09 | 2007-07-11 | $7700.00 | Window Closed / Lapsed |