Assignee: Semiconductor Energy Laboratory Co Ltd
•
Filing: 1995-03-01
•
Granted: 1998-05-19
•
Expires: 2015-03-01
Abstract
Abstract A semiconductor material and a method for forming the same, said semiconductor material having produced by a process comprising melting a noncrystal semiconductor film containing therein carbon, nitrogen, and oxygen each at a concentration of 5×10 19 atoms.cm -3 or lower, preferably 1×10 19 atoms.cm -3 or lower, by irradiating a laser beam or a high intensity light equivalent to a laser beam to said noncrystal semiconductor film, and then recrystallizing the thus molten amorphous silicon film. The present invention provides thin film semiconductors having high mobility at an excellent reproducibility, said semiconductor materials being useful for fabricating thin film semiconductor devices such as thin film transistors improved in device characteristics.
Inventors
- 👤 Shunpei Yamazaki
- 👤 Hongyong Zhang
- 👤 Naoto Kusumoto
- 👤 Yasuhiko Takemura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:24
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/10; H10P; H10P14/00; H10P14/20; H10P14/22; H10P14/29; H10P14/2901; H10P14/2921; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3451; H10P14/3452; H10P14/3454; H10P14/38; H10P14/3802; H10P14/3808; H10P14/3816; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
156 words
A method of manufacturing a semiconductor device comprising the steps of: depositing a non-single crystal semiconductor film comprising silicon, germanium or silicon-germanium alloy on a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon, and nitrogen contained in said non-single crystal semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said non-single crystal semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air, and irradiating said semiconductor film with a light to melt and crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon, and nitrogen contained in said semiconductor film after the crystallization by said light remains not higher than 1×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 2
Independent Claim
156 words
A method of manufacturing a semiconductor device comprising the steps of: depositing a non-single crystal semiconductor film comprising silicon, germanium or silicon-germanium alloy on a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon, and nitrogen contained in said non-single crystal semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said non-single crystal semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air, and irradiating said semiconductor film with a light to melt and crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon, and nitrogen contained in said semiconductor film after the crystallization by said light remains not higher than 1×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 3
Independent Claim
141 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a film formation chamber wherein each concentration of oxygen, carbon, or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with a light to crystallize said semiconductor film in said light annealing chamber, wherein each concentration of oxygen, carbon, or nitrogen in said semiconductor film after the crystallization by said light remains not higher than 1 ×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 4
Independent Claim
141 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a film formation chamber wherein each concentration of oxygen, carbon, or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with a light to crystallize said semiconductor film in said light annealing chamber, wherein each concentration of oxygen, carbon, or nitrogen in said semiconductor film after the crystallization by said light remains not higher than 1 ×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 5
Dependent Claim
12 words
The method of claim 2 wherein said light is a laser light.
Claim 6
Independent Claim
166 words
A method of manufacturing a semiconductor device comprising the following sequential steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a first chamber wherein each concentration of oxygen, carbon or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said first chamber to a second chamber; forming an insulating film on said semiconductor film in said second chamber; transferring said substrate from said second chamber to a third chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with laser light through said insulating film to crystallize said semiconductor film in said third chamber, wherein each concentration of oxygen, carbon or nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 7
Independent Claim
166 words
A method of manufacturing a semiconductor device comprising the following sequential steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a first chamber wherein each concentration of oxygen, carbon or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said first chamber to a second chamber; forming an insulating film on said semiconductor film in said second chamber; transferring said substrate from said second chamber to a third chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with laser light through said insulating film to crystallize said semiconductor film in said third chamber, wherein each concentration of oxygen, carbon or nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 8
Dependent Claim
12 words
The method of claim 4 wherein said laser is an excimer laser.
Claim 9
Independent Claim
170 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon, germanium or silicon-germanium alloy on a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon and nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with laser light to crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon and nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 , and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3.
Claim 10
Independent Claim
170 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon, germanium or silicon-germanium alloy on a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon and nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with laser light to crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon and nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 , and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3.
Claim 11
Independent Claim
178 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a film formation chamber wherein each concentration of oxygen, carbon or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with laser light to crystallize said semiconductor film in said light annealing chamber, wherein said substrate is maintained under a pressure smaller than 10 -6 Torr during said transferring step and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3, and wherein each concentration of oxygen, carbon or nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 .
Claim 12
Independent Claim
178 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a film formation chamber wherein each concentration of oxygen, carbon or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with laser light to crystallize said semiconductor film in said light annealing chamber, wherein said substrate is maintained under a pressure smaller than 10 -6 Torr during said transferring step and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3, and wherein each concentration of oxygen, carbon or nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 .
Claim 13
Independent Claim
178 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a film formation chamber wherein each concentration of oxygen, carbon or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; irradiating said semiconductor film with laser light to crystallize said semiconductor film in said light annealing chamber, forming a gate insulating film on said semiconductor film; and forming a gate electrode on said gate insulating film, wherein each concentration of oxygen, carbon or nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 , and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3.
Claim 14
Independent Claim
178 words
A method of manufacturing a semiconductor device comprising the steps of: depositing an amorphous semiconductor film comprising silicon on a substrate in a film formation chamber wherein each concentration of oxygen, carbon or nitrogen contained in said amorphous semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said amorphous semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; irradiating said semiconductor film with laser light to crystallize said semiconductor film in said light annealing chamber, forming a gate insulating film on said semiconductor film; and forming a gate electrode on said gate insulating film, wherein each concentration of oxygen, carbon or nitrogen in said semiconductor film after the crystallization by said laser light remains not higher than 1×10 19 atoms/cm 3 , and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3.
Claim 15
Independent Claim
194 words
A method of manufacturing a semiconductor device comprising the steps of: depositing a non-single crystal semiconductor film comprising silicon germanium or silicon-germanium alloy on a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon and nitrogen contained in said non-single crystal semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said non-single crystal semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with a light to melt and crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon and nitrogen in said semiconductor film after the crystallization by said light remains not higher than 1×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3.
Claim 16
Independent Claim
194 words
A method of manufacturing a semiconductor device comprising the steps of: depositing a non-single crystal semiconductor film comprising silicon germanium or silicon-germanium alloy on a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon and nitrogen contained in said non-single crystal semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said non-single crystal semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with a light to melt and crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon and nitrogen in said semiconductor film after the crystallization by said light remains not higher than 1×10 19 atoms/cm 3 , and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher and a ratio of a full band width at half maximum (FWHM) of a Raman peak of said semiconductor film after the crystallization to a FWHM of a Raman peak of a single crystalline silicon is less than 3.
Claim 17
Independent Claim
177 words
A method of manufacturing an insulated gate field effect transistor having source, drain and channel regions, said method comprising the steps of: depositing a non-single crystal semiconductor film comprising silicon germanium or silicon-germanium alloy including at least said channel region over a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon and nitrogen contained in said non-single crystal semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said non-single crystal semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with a light to melt and crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon and nitrogen in at least said channel region of the semiconductor film remains not higher than 1×10 19 atoms/cm 3 after the crystallization by said light, and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 18
Independent Claim
177 words
A method of manufacturing an insulated gate field effect transistor having source, drain and channel regions, said method comprising the steps of: depositing a non-single crystal semiconductor film comprising silicon germanium or silicon-germanium alloy including at least said channel region over a substrate in a film formation chamber wherein concentration of at least one of oxygen, carbon and nitrogen contained in said non-single crystal semiconductor film is not higher than 1×10 19 atoms/cm 3 ; transferring said substrate having said non-single crystal semiconductor film thereon from said film formation chamber to a light annealing chamber without exposing said semiconductor film to air; and irradiating said semiconductor film with a light to melt and crystallize said semiconductor film in said light annealing chamber, wherein concentration of at least one of oxygen, carbon and nitrogen in at least said channel region of the semiconductor film remains not higher than 1×10 19 atoms/cm 3 after the crystallization by said light, and said semiconductor film after the crystallization shows a Raman shift at a wavenumber of 515 cm -1 or higher.
Claim 19
Dependent Claim
31 words
The method of claim 1, 2, 4, 6, 7, 8, 9, or 10 wherein said semiconductor film after the crystallization has an electron mobility as high as 1000 cm 2 /Vs.
Claim 20
Dependent Claim
31 words
The method of claim 1, 2, 4, 6, 7, 8, 9, or 10 wherein said semiconductor film after the crystallization has a hole mobility from 300 to 500 cm 2 /Vs.
Claim 21
Independent Claim
29 words
The method of claims 1, 2, 4, 6, 7, 8, 9, or 10 wherein each concentration of oxygen, carbon and nitrogen is measured by secondary ion mass spectroscopy (SIMS).
References Cited (Backward Citations)
US4151058A
Cited
US4226898A
Cited
US4343081A
Cited
US4567061A
Cited
US4609407A
Cited
GB2065973A
Cited
US4482395A
Cited
US5091334A
Cited
US4322253A
Cited
US4313783A
Cited
JPS5710267A
Cited
US4803528A
Cited
US4405435A
Cited
JPS5745921A
Cited
US4335161A
Cited
US4498416A
Cited
US4402762A
Cited
US4576851A
Cited
US4589951A
Cited
JPS5893223A
Cited
JPS58112324A
Cited
US4557036A
Cited
US4766477A
Cited
US4843022A
Cited
JPS58212178A
Cited
US4582720A
Cited
US4575466A
Cited
US4592799A
Cited
US4552595A
Cited
US4503807A
Cited
JPS6042817A
Cited
JPS60110164A
Cited
US4592306A
Cited
US4523370A
Cited
US4698486A
Cited
US4963503A
Cited
US4959700A
Cited
US4727044A
Cited
US4595601A
Cited
US4640223A
Cited
US4624737A
Cited
JPS6158278A
Cited
US4699863A
Cited
US4590091A
Cited
US4694143A
Cited
JPS6216509A
Cited
US5171710A
Cited
US5296405A
Cited
EP0211634A2
Cited
US4888305A
Cited
US4719123A
Cited
US4663829A
Cited
US4772927A
Cited
US4808554A
Cited
US4714684A
Cited
US5009689A
Cited
US4800174A
Cited
US4814292A
Cited
JPS6354773A
Cited
JPS6360519A
Cited
JPS63300509A
Cited
JPS6425515A
Cited
US4937205A
Cited
JPH01184928A
Cited
JPH01187814A
Cited
US5174881A
Cited
JPH01286463A
Cited
JPH02148831A
Cited
US5108843A
Cited
US5200017A
Cited
US5186718A
Cited
US5036373A
Cited
US5194398A
Cited
JPH0388323A
Cited
JPH03220529A
Cited
US5310410A
Cited
US5306651A
Cited
US5120667A
Cited
US5141058A
Cited
US5145808A
Cited
US5112764A
Cited
US5314839A
Cited
US5313076A
Cited
US5266116A
Cited
US5314538A
Cited
US5324360A
Cited
US5288658A
Cited
US5352291A
Cited
US5352291B1
Cited
US5264383A
Cited
US5292675A
Cited
US5338388A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-05-18 | 2001-11-17 | 2002-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-05-18 | 2005-11-17 | 2006-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-05-18 | 2009-11-17 | 2010-05-19 | $7700.00 | Window Closed / Lapsed |