Method for producing an amorphous silicon semiconductor device using a multichamber PECVD apparatus
Assignee: Panasonic Holdings Corp
•
Filing: 1987-05-18
•
Granted: 1989-01-24
•
Expires: 2007-05-18
Abstract
Abstract A method of producing an amorphous silicon semiconductor device makes use of a capacitance-coupled high-frequency glow-discharge semiconductor production apparatus which is equipped with a plurality of glow-discharge chambers each having a high-frequency electrode and a substrate holder opposing each other and means for supplying material gases to the glow-discharge chambers. A reaction of a material gas is effected in a first glow-discharge chamber, so as to form a semiconductor layer having a first conductivity type on a substrate introduced into the first glow-discharge chamber, and, after moving the substrate into a second glow-discharge chamber, a reaction of a material gas different from the material gas used in the first glow-discharge chamber is effected, thereby forming a semiconductor layer having a second conductivity type on the semiconductor layer of the first conductivity type. The substrate with the semiconductor layer of the first conductivity formed thereon is moved from the first glow-discharge chamber to the second glow-discharge chamber after a predetermined gas atmosphere is formed in the first glow-discharge chamber. The distance between the electrode and the substrate holder is made smaller in one of the first and second glow-discharge chambers which is designed for forming the thicker one of the semiconductor layers of the first and second conductivity types than in the other of the first and second glow-discharge chambers. The temperature of the substrate is set higher in one of the first and second glow-discharge chambers which is designed for forming the thicker one of the semiconductor layers of the first and second conductivity types than in the other of the first and second glow-discharge chambers.
Inventors
- 👤 Shinichiro Ishihara
- 👤 Masatoshi Kitagawa
- 👤 Takashi Hirao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:31
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/54; C23C16/22; C23C16/24; Y; Y10; Y10S; Y10S148/00; Y10S148/025; Y10S148/045; Y10S148/072; Y10S438/00; Y10S438/907; Y10S438/908
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
318 words
In a method of producing an amorphous silicon semiconductor device having the steps of: preparing a capacitance-coupled high-frequency glow-discharge semiconductor production apparatus which is equipped with a plurality of glow-discharge chambers each having a high-frequency electrode and a substrate holder opposing each other and means for supplying material gases to said glow-discharge chambers; effecting, in a first one of said glow-discharge chambers, plasma reaction so as to deposit, on a substrate introduced into the first glow-discharge chamber, a first amorphous silicon layer or a first amorphous layer consisting mainly of silicon having a first conductivity type, and effecting, after moving said substrate into a second one of said glow-discharge chambers, a plasma reaction of a material gas different from said material gas used in the first glow-discharge chamber, thereby forming a second amorphous silicon layer of a second conductivity type on said first layer; the improvement comprising: that said substrate with said first amorphous silicon layer or said first amorphous layer mainly consisting of silicon of said first conductivity formed thereon is moved from said first glow-discharge chamber to said second glow-discharge chamber after a predetermined gas atmosphere is formed in said first glow-discharge chamber; that the distance between said electrode and said substrate holder is made smaller in that one of said first and second glow-discharge chambers which is designed for forming the thicker one of said first and second layers than in the other of said first and second glow-discharge chambers; that the temperature of said substrate is set higher in that one of said first and second glow-discharge chambers which is designed for forming the thicker one of said first and second layers; and that the pressure is set higher in that one of said first and second glow-discharge chambers which is designed for forming the thicker one of said first and second layers than in the other of said first and second glow-discharge chambers.
Claim 2
Dependent Claim
318 words
In a method of producing an amorphous silicon semiconductor device having the steps of: preparing a capacitance-coupled high-frequency glow-discharge semiconductor production apparatus which is equipped with a plurality of glow-discharge chambers each having a high-frequency electrode and a substrate holder opposing each other and means for supplying material gases to said glow-discharge chambers; effecting, in a first one of said glow-discharge chambers, plasma reaction so as to deposit, on a substrate introduced into the first glow-discharge chamber, a first amorphous silicon layer or a first amorphous layer consisting mainly of silicon having a first conductivity type, and effecting, after moving said substrate into a second one of said glow-discharge chambers, a plasma reaction of a material gas different from said material gas used in the first glow-discharge chamber, thereby forming a second amorphous silicon layer of a second conductivity type on said first layer; the improvement comprising: that said substrate with said first amorphous silicon layer or said first amorphous layer mainly consisting of silicon of said first conductivity formed thereon is moved from said first glow-discharge chamber to said second glow-discharge chamber after a predetermined gas atmosphere is formed in said first glow-discharge chamber; that the distance between said electrode and said substrate holder is made smaller in that one of said first and second glow-discharge chambers which is designed for forming the thicker one of said first and second layers than in the other of said first and second glow-discharge chambers; that the temperature of said substrate is set higher in that one of said first and second glow-discharge chambers which is designed for forming the thicker one of said first and second layers; and that the pressure is set higher in that one of said first and second glow-discharge chambers which is designed for forming the thicker one of said first and second layers than in the other of said first and second glow-discharge chambers.
Claim 3
Dependent Claim
74 words
A method of producing an amorphous silicon semiconductor device according to claim 1, wherein said material gas used in said first glow-discharge chamber contains a gas which delivers an impurity for determining the conductivity type of said first amorphous silicon layer or for varying the optical band gap of said first amorphous silicon layer, whle said material gas used in said second glow-discharge chamber does not contain any gas which delivers such an impurity.
Claim 4
Dependent Claim
301 words
In a method of producing an amorphous silicon semiconductor device having the steps of: preparing a capacitance-coupled high-frequency glow-discharge semiconductor production apparatus which is equipped with a plurality of glow-discharge chambers each having a high-frequency electrode and a substrate holder opposing each other and means for supplying material gases to said glow-discharge chambers; effecting, in a first one of said glow-discharge chambers, a plasma reaction of a material gas so as to deposit, on a substrate introduced into the first glow-discharge chamber, an amorphous silicon layer having a first conductivity type; and effecting, after moving said substrate into a second one of said glow-discharge chambers, a plasma reaction of a material gas different from said material gas used in the first glow-discharge chamber, thereby forming an amorphous silicon layer or an amorphous layer consisting mainly of silicon having a second conductivity type on said layer of said first conductivity type; the improvement comprising: that said substrate with said amorphous silicon layer of said first conductivity formed thereon is moved from said first glow-discharge chamber to said second glow-discharge chamber after the gas atmosphere of the same kind and pressure as in said first glow-discharge chamber is established in said second glow-discharge chamber; that the distance between said electrode and said substrate holder is made smaller in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said layers of said first and second conductivity types than in the other of said first and second glow-discharge chambers; and that the temperature of said substrate is set higher in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said layers of said first and second conductivity types than in the other of said first and second glow-discharge chambers.
Claim 5
Dependent Claim
301 words
In a method of producing an amorphous silicon semiconductor device having the steps of: preparing a capacitance-coupled high-frequency glow-discharge semiconductor production apparatus which is equipped with a plurality of glow-discharge chambers each having a high-frequency electrode and a substrate holder opposing each other and means for supplying material gases to said glow-discharge chambers; effecting, in a first one of said glow-discharge chambers, a plasma reaction of a material gas so as to deposit, on a substrate introduced into the first glow-discharge chamber, an amorphous silicon layer having a first conductivity type; and effecting, after moving said substrate into a second one of said glow-discharge chambers, a plasma reaction of a material gas different from said material gas used in the first glow-discharge chamber, thereby forming an amorphous silicon layer or an amorphous layer consisting mainly of silicon having a second conductivity type on said layer of said first conductivity type; the improvement comprising: that said substrate with said amorphous silicon layer of said first conductivity formed thereon is moved from said first glow-discharge chamber to said second glow-discharge chamber after the gas atmosphere of the same kind and pressure as in said first glow-discharge chamber is established in said second glow-discharge chamber; that the distance between said electrode and said substrate holder is made smaller in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said layers of said first and second conductivity types than in the other of said first and second glow-discharge chambers; and that the temperature of said substrate is set higher in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said layers of said first and second conductivity types than in the other of said first and second glow-discharge chambers.
Claim 6
Dependent Claim
72 words
A method of producing an amorphous silicon semiconductor device according to claim 3, wherein the material gas used in said first glow-discharge chamber does not contain any gas which would deliver an impurity, while the material gas used in said second glow-discharge chamber contains a gas for delivering an impurity for determining the conductivity type of said amorphous silicon layer or for varying the optical band gap of said amorphous silicon layer.
Claim 7
Dependent Claim
280 words
In a method of producing an amorphous silicon semiconductor device having the steps of: preparing a capacitance-coupled high-frequency glow-discharge semiconductor production apparatus which is equipped with a plurality of glow-discharge chambers each having a high-frequency electrode and a substrate holder opposing each other and means for supplying material gases to said glow-discharge chambers; effecting, in a first one of said glow-discharge chambers, a reaction of a material gas so as to form, on a substrate introduced into the first glow-discharge chamber, a semiconductor layer having a first conductivity type, and effecting, after moving said substrate into a second one of said glow-discharge chambers, a reaction of a material gas different from said material gas used in the first glow-discharge chamber, thereby forming a semiconductor layer having a second conductivity type on said semiconductor layer of said first conductivity type; the improvement comprising: that said substrate with said semiconductor layer of said first conductivity formed thereon is moved from said first glow-discharge chamber to said second glow-discharge chamber after a predetermined gas atmosphere is formed in said first glow-discharge chamber; that the distance between said electrode and said substrate holder is made smaller in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said semiconductor layers of said first and second conductivity types than in the other of said first and second glow-discharge chambers; and that the temperature of said substrate is set higher in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said semiconductor layer of said first and second conductivity types than in the other of said first and second glow-discharge chambers.
Claim 8
Dependent Claim
280 words
In a method of producing an amorphous silicon semiconductor device having the steps of: preparing a capacitance-coupled high-frequency glow-discharge semiconductor production apparatus which is equipped with a plurality of glow-discharge chambers each having a high-frequency electrode and a substrate holder opposing each other and means for supplying material gases to said glow-discharge chambers; effecting, in a first one of said glow-discharge chambers, a reaction of a material gas so as to form, on a substrate introduced into the first glow-discharge chamber, a semiconductor layer having a first conductivity type, and effecting, after moving said substrate into a second one of said glow-discharge chambers, a reaction of a material gas different from said material gas used in the first glow-discharge chamber, thereby forming a semiconductor layer having a second conductivity type on said semiconductor layer of said first conductivity type; the improvement comprising: that said substrate with said semiconductor layer of said first conductivity formed thereon is moved from said first glow-discharge chamber to said second glow-discharge chamber after a predetermined gas atmosphere is formed in said first glow-discharge chamber; that the distance between said electrode and said substrate holder is made smaller in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said semiconductor layers of said first and second conductivity types than in the other of said first and second glow-discharge chambers; and that the temperature of said substrate is set higher in one of said first and second glow-discharge chambers which is designed for forming the thicker one of said semiconductor layer of said first and second conductivity types than in the other of said first and second glow-discharge chambers.
References Cited (Backward Citations)
US4519339A
Cited
US4438723A
Cited
US4525376A
Cited
US4485125A
Cited
US4690717A
Cited
US4636401A
Cited
US4634601A
Cited
US4646681A
Cited
US4576829A
Cited
US4664939A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-24 | 1992-07-25 | 1993-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-24 | 1996-07-25 | 1997-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-24 | 2000-07-25 | 2001-01-24 | $7700.00 | Window Closed / Lapsed |