Integrated low K dielectrics and etch stops
Assignee: Applied Materials Inc
•
Filing: 1999-06-09
•
Granted: 2002-01-22
•
Expires: 2019-06-09
Abstract
Abstract A method of depositing and etching dielectric layers having low dielectric constants and etch rates that vary by at least 3:1 for formation of horizontal interconnects. The amount of carbon or hydrogen in the dielectric layer is varied by changes in deposition conditions to provide low k dielectric layers that can replace etch stop layers or conventional dielectric layers in damascene applications. A dual damascene structure having two or more dielectric layers with dielectric constants lower than about 4 can be deposited in a single reactor and then etched to form vertical and horizontal interconnects by varying the concentration of a carbon:oxygen gas such as carbon monoxide. The etch gases for forming vertical interconnects preferably comprises CO and a fluorocarbon, and CO is preferably excluded from etch gases for forming horizontal interconnects.
Inventors
- 👤 Claes H. Bjorkman
- 👤 Min Melissa Yu
- 👤 Hongquing Shan
- 👤 David W. Cheung
- 👤 Wai-Fan Yau
- 👤 Kuowei Liu
- 👤 Nasreen Gazala Chapra
- 👤 Gerald Yin
- 👤 Farhad K. Moghadam
- 👤 Judy H. Huang
- 👤 Dennis Yost
- 👤 Betty Tang
- 👤 Yunsang Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 12:19
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10P; H10P50/00; H10P50/20; H10P50/28; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/401; H10P14/00; H10P14/60; H10P14/66; H10P14/668; H10P14/6681; H10P50/282; H10P50/283; H10P50/286; H10P50/287; H10W20/074; H10W20/081; H10W20/084; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/65; H10P14/6502; H10P14/6506; H10P14/662; H10P14/6682; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
75 words
A process for depositing and etching intermetal dielectric layers, comprising: depositing a first dielectric layer having a dielectric constant less than about 4.0; depositing a second dielectric layer having a dielectric constant less than about 4.0 on the first dielectric layer; and etching the second dielectric layer under conditions wherein the second dielectric layer has an etch rate that is at least about three times greater than an etch rate for the first dielectric layer.
Claim 2
Dependent Claim
75 words
A process for depositing and etching intermetal dielectric layers, comprising: depositing a first dielectric layer having a dielectric constant less than about 4.0; depositing a second dielectric layer having a dielectric constant less than about 4.0 on the first dielectric layer; and etching the second dielectric layer under conditions wherein the second dielectric layer has an etch rate that is at least about three times greater than an etch rate for the first dielectric layer.
Claim 3
Dependent Claim
45 words
The process of claim 1 , wherein the first dielectric layer comprises silicon, oxygen, and at least about 5% carbon by atomic weight, and the second dielectric layer comprises silicon, oxygen, and less than about two-thirds of the carbon contained in the first dielectric layer.
Claim 4
Dependent Claim
61 words
The process of claim 2 , wherein the first dielectric layer is etched to form vertical interconnects with a first gas mixture comprising one or more fluorocarbon compounds and one or more carbon:oxygen compounds, and the second dielectric layer is etched to form horizontal interconnects with a second gas mixture comprising one or more fluorocarbon compounds and essentially no carbon:oxygen compounds.
Claim 5
Dependent Claim
13 words
The process of claim 3 , wherein the carbon:oxygen compound is carbon monoxide.
Claim 6
Dependent Claim
45 words
The process of claim 1 , wherein the first dielectric layer comprises silicon, oxygen, carbon, and at least 1% hydrogen by atomic weight, and the second dielectric layer comprises silicon, oxygen, carbon, and less than one-fifth of the hydrogen contained in the first dielectric layer.
Claim 7
Dependent Claim
61 words
The process of claim 5 , wherein the first dielectric layer is etched to form vertical interconnects with a first gas mixture comprising one or more fluorocarbon compounds and one or more carbon:oxygen compounds, and the second dielectric layer is etched to form horizontal interconnects with a second gas mixture comprising one or more fluorocarbon compounds and essentially no carbon:oxygen compounds.
Claim 8
Dependent Claim
13 words
The process of claim 6 , wherein the carbon:oxygen compound is carbon monoxide.
Claim 9
Dependent Claim
20 words
The process of claim 1 , wherein the first and second dielectric layers are deposited by oxidizing an organosilicon compound.
Claim 10
Dependent Claim
14 words
The process of claim 8 , wherein the organosilicon compound is methylsilane or trimethylsiloxane.
Claim 11
Dependent Claim
26 words
The process of claim 1 , wherein the first dielectric layer is deposited on a third dielectric layer having a dielectric constant less than about 4.0.
Claim 12
Dependent Claim
75 words
A process for depositing low dielectric constant layers, comprising: varying one or more process conditions for depositing an organosilicon compound to obtain first and second dielectric layers having varying silicon, oxygen, carbon, and hydrogen contents and dielectric constants less than about 4; and etching the second dielectric layer using conditions wherein the second dielectric layer has an etch rate that is at least 3 times greater than an etch rate for the first dielectric layer.
Claim 13
Dependent Claim
75 words
A process for depositing low dielectric constant layers, comprising: varying one or more process conditions for depositing an organosilicon compound to obtain first and second dielectric layers having varying silicon, oxygen, carbon, and hydrogen contents and dielectric constants less than about 4; and etching the second dielectric layer using conditions wherein the second dielectric layer has an etch rate that is at least 3 times greater than an etch rate for the first dielectric layer.
Claim 14
Dependent Claim
59 words
The process of claim 11 , wherein the first dielectric layer contains at least 5% carbon by atomic weight or at least 1% hydrogen by atomic weight, and wherein the second dielectric layer contains less than two-thirds of the carbon in the first silicon oxide layer or less than one-fifth of the hydrogen in the first silicon oxide layer.
Claim 15
Dependent Claim
31 words
The process of claim 12 wherein the second dielectric layer is etched to form horizontal interconnects with a first gas mixture comprising one or more fluorocarbons and essentially no carbon:oxygen compounds.
Claim 16
Dependent Claim
31 words
The process of claim 11 , wherein the first dielectric layer is deposited on a third dielectric layer having silicon, oxygen, carbon, and hydrogen contents similar to the second dielectric layer.
References Cited (Backward Citations)
US4900591A
Cited
US5356515A
Cited
US5302236A
Cited
US5262279A
Cited
EP0519079A1
Cited
EP0519079B1
Cited
US5204141A
Cited
WO1994001885A1
Cited
US5360646A
Cited
US5593741A
Cited
US5486493A
Cited
US5591677A
Cited
US5660738A
Cited
US5488015A
Cited
US5789319A
Cited
US5492736A
Cited
US5559055A
Cited
US5679608A
Cited
US5700720A
Cited
JPH098031A
Cited
JPH09237785A
Cited
DE19654737A1
Cited
US5843847A
Cited
US5807785A
Cited
WO1998008249A1
Cited
EP0840365A2
Cited
EP0849789A2
Cited
DE19804375A1
Cited
US6124641A
Cited
US6140226A
Cited
WO1999041423A2
Cited
US6287990B1
Cited
US6159871A
Cited
US6054206A
Cited
US6147009A
Cited
US6169021B1
Cited
WO2000022671A1
Cited
EP1063692A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2005-01-21 | 2005-07-23 | 2006-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2009-01-21 | 2009-07-23 | 2010-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2013-01-21 | 2013-07-23 | 2014-01-22 | $7700.00 | Window Closed / Lapsed |