Method and apparatus for forming silicon oxide film by chemical vapor deposition
Assignee: NEC Electronics Corp
•
Filing: 1995-06-28
•
Granted: 1997-01-14
•
Expires: 2015-06-28
Abstract
Abstract The subject is a plasma-enhanced CVD process for depositing a silicon oxide film on a substrate by using an organosilicon compound such as tetraethoxysilane and oxygen or ozone as the essential reactants. The disclosed CVD method uses a plasma containing oxygen ions, and the density of oxygen ions impinging on the substrate surface is cyclically decreased and increased with a short period such as, e.g., 1 sec. In extreme cases which are rather preferable, the effect of the oxygen plasma is cyclically nullified and returned to a maximum to thereby alternate plasma CVD and plain thermal CVD. The obtained film is comparable in film properties to silicon oxide films deposited by known plasma CVD methods and, when the substrate has steps such as aluminum wiring lines, is better in step coverage and gap filling capability. The film exhibits a still better profile when hydrogen peroxide gas or an alternative hydrogen containing gas is added to the reactant gas mixture.
Inventors
- 👤 Yasuo Ikeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:06
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/402; C23C16/44; C23C16/52; H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6339; H10P14/66; H10P14/668; H10P14/6681; H10P14/6687; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6927; H10P14/6336; H10P14/6684; H10P14/6686; H10P14/69215
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
236 words
A method of forming a silicon oxide film on a heated substrate by chemical vapor deposition (CVD) using an organosilicon compound gas and oxygen gas as essential reactants in the presence of a plasma containing oxygen ions, said plasma having an intensity represented by the density of said oxygen ions impinging on a surface of said substrate, the method comprising the steps of: (a) depositing a first plasma CVD silicon oxide film on the substrate while the intensity of said plasma is at a first level; (b) lowering the intensity of said plasma from said first level to a second level and depositing an intermediate CVD silicon oxide film on said first plasma CVD silicon oxide film, said intermediate CVD silicon oxide film having a step coverage and a gap filling capability that are superior to that of said first plasma CVD silicon oxide film and having a film quality that is inferior to that of said first plasma CVD silicon oxide film, wherein said film quality is measured by criteria comprising moisture content; and (c) raising the intensity of said plasma from said second level to said first level and depositing a second plasma CVD silicon oxide film on said intermediate CVD silicon oxide film, thereby converting said intermediate CVD silicon oxide film into a silicon oxide film which is substantially equivalent in film quality to said first and second plasma CVD silicon oxide films.
Claim 2
Independent Claim
236 words
A method of forming a silicon oxide film on a heated substrate by chemical vapor deposition (CVD) using an organosilicon compound gas and oxygen gas as essential reactants in the presence of a plasma containing oxygen ions, said plasma having an intensity represented by the density of said oxygen ions impinging on a surface of said substrate, the method comprising the steps of: (a) depositing a first plasma CVD silicon oxide film on the substrate while the intensity of said plasma is at a first level; (b) lowering the intensity of said plasma from said first level to a second level and depositing an intermediate CVD silicon oxide film on said first plasma CVD silicon oxide film, said intermediate CVD silicon oxide film having a step coverage and a gap filling capability that are superior to that of said first plasma CVD silicon oxide film and having a film quality that is inferior to that of said first plasma CVD silicon oxide film, wherein said film quality is measured by criteria comprising moisture content; and (c) raising the intensity of said plasma from said second level to said first level and depositing a second plasma CVD silicon oxide film on said intermediate CVD silicon oxide film, thereby converting said intermediate CVD silicon oxide film into a silicon oxide film which is substantially equivalent in film quality to said first and second plasma CVD silicon oxide films.
Claim 3
Dependent Claim
19 words
A method according to claim 1, wherein said second level of the intensity of said plasma is nearly zero.
Claim 4
Dependent Claim
58 words
A method according to claim 1, wherein said plasma is produced by applying RF power to a reactant gas mixture containing said organosilicon compound gas and oxygen gas in a reaction chamber in which the substrate is placed, the level of the intensity of said plasma being lowered and raised by varying the magnitude of the RF power.
Claim 5
Dependent Claim
38 words
A method according to claim 3, wherein the RF power is switched off for a first predetermined time to lower the intensity of said plasma and switched on for a second predetermined time to again raise said intensity.
Claim 6
Dependent Claim
48 words
A method according to claim 1, wherein a duty ratio of the applied RF power is in the range from 40 to 60% wherein said duty ratio equals the ratio of said first predetermined time to the sum of said first predetermined time and said second predetermined time.
Claim 7
Dependent Claim
76 words
A method according to claim 1, wherein said plasma is produced in an ion source chamber and introduced into a reaction chamber in which the substrate is placed while a reactant gas mixture containing said organosilicon compound gas and oxygen gas is supplied into the reaction chamber, the intensity of said plasma in the reaction chamber being lowered and raised by controlling the flow of the plasma from the ion source chamber into the reaction chamber.
Claim 8
Dependent Claim
28 words
A method according to claim 6, wherein the step (b) is performed by blocking the flow of said plasma form the ion source chamber into the reaction chamber.
Claim 9
Dependent Claim
12 words
A method according to claim 1, wherein said oxygen gas contains ozone.
Claim 10
Dependent Claim
25 words
A method according to claim 8, wherein the concentration of ozone in the oxygen gas is in the range from 1% to 10% by volume.
Claim 11
Dependent Claim
26 words
A method according to claim 1, wherein said organosilicon compound is selected from the group consisting of tetraethylorthosilicate, tetramethylsilane, triethyoxysilane, tetramethylcyclotetrasiloxane, octamethylcyclotetrasiloxane, hexamethyldislazane, tris(dimethylamino)silane and tris(diethylamino)silane.
Claim 12
Dependent Claim
43 words
A method according to claim 1, wherein another gaseous reactant which provides water vapor is added to said reactant gas mixture, said another gaseous reactant being selected from the group consisting of hydrogen peroxide, hydrogen, water, hydrocarbons, alcohols, carbonyl compounds and carboxylic acids.
Claim 13
Dependent Claim
54 words
A method according to claim 1, wherein the steps (a) and (b) are successively performed within a time period in the range from about 0.1 seconds to about 30 seconds and steps (b) and (c) are successively performed within a time period in the range of from about 0.1 seconds to about 30 seconds.
Claim 14
Dependent Claim
56 words
A method according to claim 12, wherein with the steps (a) and (b) are successively performed within a time period in the range from about 0.1 sec to about 30 sec and the steps (b) and (c) are also successively performed within a time period in the range from about 0.1 sec to about 30 sec.
Claim 15
Independent Claim
181 words
A method of forming a silicon oxide film on a heated substrate by chemical vapor deposition (CVD) using an organosilicon compound gas and oxygen gas as essential reactants, the method comprising the steps of: (a) applying a plasma containing oxygen ions to the substrate and depositing a first plasma CVD silicon oxide film on said substrate; (b) interrupting the application of said plasma and depositing an intermediate CVD silicon oxide film on said first plasma CVD silicon oxide film, said intermediate CVD silicon oxide film is superior to said first plasma CVD silicon oxide film in step coverage and gap filling capability and inferior to said first plasma CVD silicon oxide film in film quality, wherein said film quality is measured by criteria comprising moisture content; and (c) again applying said plasma to the substrate and depositing a second plasma CVD silicon oxide film on said intermediate CVD silicon oxide film thereby converting said intermediate CVD silicon oxide film into a silicon oxide film which is substantially equivalent in film quality to said first and second plasma CVD silicon oxide films.
Claim 16
Independent Claim
181 words
A method of forming a silicon oxide film on a heated substrate by chemical vapor deposition (CVD) using an organosilicon compound gas and oxygen gas as essential reactants, the method comprising the steps of: (a) applying a plasma containing oxygen ions to the substrate and depositing a first plasma CVD silicon oxide film on said substrate; (b) interrupting the application of said plasma and depositing an intermediate CVD silicon oxide film on said first plasma CVD silicon oxide film, said intermediate CVD silicon oxide film is superior to said first plasma CVD silicon oxide film in step coverage and gap filling capability and inferior to said first plasma CVD silicon oxide film in film quality, wherein said film quality is measured by criteria comprising moisture content; and (c) again applying said plasma to the substrate and depositing a second plasma CVD silicon oxide film on said intermediate CVD silicon oxide film thereby converting said intermediate CVD silicon oxide film into a silicon oxide film which is substantially equivalent in film quality to said first and second plasma CVD silicon oxide films.
Claim 17
Dependent Claim
66 words
A method according to claim 14, wherein said plasma is produced by applying RF power to a reactant gas mixture containing said organosilicon compound gas and oxygen gas in a reaction chamber in which the substrate is placed, the RF power being cyclically switched on for a first predetermined time and off for a second predetermined time to thereby perform the steps (a), (b) and (c).
Claim 18
Dependent Claim
48 words
A method according to claim 15, wherein a duty ratio of the applied RF power is in the range from 40 to 60%, wherein said duty ratio equals the ratio of said first predetermined time to the sum of said first predetermined time and said second predetermined time.
Claim 19
Dependent Claim
83 words
A method according to claim 14, wherein said plasma is produced in an ion source chamber and introduced into a reaction chamber and introduced into a reaction chamber in which the substrate is placed while a reactant gas mixture containing said organosilicon compound gas and oxygen gas is supplied into the reaction chamber, the application of said plasma to the substrate being interrupted in the step (b) by blocking the flow of the plasma from the ion source chamber into the reaction chamber.
Claim 20
Dependent Claim
12 words
A method according to claim 14, wherein said oxygen gas contains ozone.
Claim 21
Dependent Claim
25 words
A method according to claim 18, wherein the concentration of ozone in the oxygen gas is in the range from 1% to 10% by volume.
Claim 22
Dependent Claim
25 words
A method according to claim 14 wherein organosilicon compound is selected from the group consisting of tetraethylorthosilicate, tetramethylsilane, triethyoxysilane, tetramethylcyclotetrasiloxane, octamethylcyclotetrasiloxane, hexamethyldislazane, tris(dimethylamino)silane and tris(diethylamino)silane.
Claim 23
Dependent Claim
43 words
A method according to claim 14 wherein another gaseous reactant which provides water vapor is added to said reactant gas mixture, said another gaseous reactant being selected form the group consisting of hydrogen peroxide, hydrogen, water, hydrocarbons, alcohols, carboxyl compounds and carboxylic acids.
References Cited (Backward Citations)
US4987005A
Cited
JPH0372077A
Cited
US5124014A
Cited
US5314724A
Cited
US5124180A
Cited
US5279865A
Cited
US5356722A
Cited
US5271972A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-01-14 | 2000-07-15 | 2001-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-01-14 | 2004-07-15 | 2005-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-01-14 | 2008-07-15 | 2009-01-14 | $7700.00 | Window Closed / Lapsed |