Process for forming silicon oxide film
Assignee: Fujitsu VLSI Ltd
•
Filing: 1991-12-19
•
Granted: 1994-05-24
•
Expires: 2011-12-19
Abstract
Abstract PCT No. PCT/JP91/01739 Sec. 371 Date Aug. 27, 1992 Sec. 102(e) Date Aug. 27, 1992 PCT Filed Dec. 19, 1991 PCT Pub. No. WO92/12535 PCT Pub. Date Jul. 23, 1992.A process for the formation of a silicon oxide film, comprising the steps of exciting a gas comprising an organosilane or organosiloxane gas and a gas containing H and OH above a substrate in a reaction chamber to react them with each other in a gaseous phase or on the substrate, thereby depositing a thin film of an organic-group-containing silanol, silanol polymer, or siloxane-bonded polymer on the substrate, and removing the organic groups from the thin film to form a silicon oxide film. Preferably, the formation of a film is conducted while repeating the step of deposition and the step of removing the organic groups through a plasma treatment within an identical chamber, and the film is further heat-treated at a temperature of 450 DEG C. or below. Thus, a good insulating film having a flatness comparable to that of an SOG film can be obtained.
Inventors
- 👤 Atuhiro Tsukune
- 👤 Yuji Furumura
- 👤 Hatanaka Masanobu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:59
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6339; H10P14/65; H10P14/6516; H10P14/6529; H10P14/6532; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/092; H10P14/6336; H10P14/66; H10P14/668; H10P14/6681; H10P14/6684; H10P14/6686; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; H10P14/6922
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
92 words
A process for the formation of a silicon oxide film, comprising the steps of: exciting a gas, comprising an organosilane or organosiloxane gas constituent and a gas constituent containing H and OH, above a substrate in a reaction chamber thereby to cause the gas constituents to react with each other in a gaseous phase or on the substrate and thereby to deposit a thin film of an organic-group-containing silanol, silanol polymer, or siloxane-bonded polymer on the substrate; and removing the organic groups from the thin film to obtain a silicon oxide film.
Claim 2
Dependent Claim
92 words
A process for the formation of a silicon oxide film, comprising the steps of: exciting a gas, comprising an organosilane or organosiloxane gas constituent and a gas constituent containing H and OH, above a substrate in a reaction chamber thereby to cause the gas constituents to react with each other in a gaseous phase or on the substrate and thereby to deposit a thin film of an organic-group-containing silanol, silanol polymer, or siloxane-bonded polymer on the substrate; and removing the organic groups from the thin film to obtain a silicon oxide film.
Claim 3
Dependent Claim
33 words
A process according to claim 1, wherein said organosilane or organosiloxane comprises at least one member selected from the group consisting of tetraethoxysilane, tetramethoxysilane, tetramethylsilane, tetramethylcyclotetrasiloxane, octomethylcyclotetrasiloxane, diacetoxy-di-tertbutoxysilane, hexamethyldisiloxane, and their substituted compounds.
Claim 4
Dependent Claim
19 words
A process according to claim 1, wherein said gas containing H and OH is water vapor or hydrogen peroxide.
Claim 5
Dependent Claim
39 words
A process according to claim 1, wherein said thin film contains 90% by weight or less of the organic groups prior to said step of removing the organic groups from the thin film to obtain a silicon oxide film.
Claim 6
Dependent Claim
39 words
A process according to claim 4, wherein said thin film contains 20 to 60% by weight of the organic groups prior to said step of removing the organic groups from the thin film to obtain a silicon oxide film.
Claim 7
Dependent Claim
39 words
A process according to claim 4, wherein said thin film contains 30% by weight or less of the organic groups prior to said step of removing the organic groups from the thin film to obtain a silicon oxide film.
Claim 8
Dependent Claim
34 words
A process according to claim 6, wherein said excitation time is sufficiently short such that the organosilane or organosiloxane gas or its reaction product still contains the organic group when it reaches the substrate.
Claim 9
Dependent Claim
15 words
A process according to claim 1, wherein said excitation is conducted in a pulsing manner.
Claim 10
Dependent Claim
25 words
A process according to claim 1, wherein said step of deposition is performed at a temperature in the range of from -50° to 450° C.
Claim 11
Dependent Claim
53 words
A process according to claim 9, wherein the step of deposition is conducted at a temperature n the range of from room temperature to 250° C. and the step of removing the organic groups is performed by a heat treatment step at a temperature in the range of from 250° to 450° C.
Claim 12
Dependent Claim
24 words
A process according to claim 10, wherein said thin film is irradiated with ultraviolet rays simultaneously with or subsequent to the heat treatment step.
Claim 13
Dependent Claim
33 words
A process according to claim 1, wherein the step of removing the organic groups is performed by a heat treatment step at a temperature in the range of from 250° to 850° C.
Claim 14
Dependent Claim
26 words
A process according to claim 1, wherein the step of deposition and the step of removing the organic groups are successively performed without breaking the vacuum.
Claim 15
Dependent Claim
50 words
A process according to claim 1, wherein the flow rate ratio of the gas containing H and OH to the organosilane or organosiloxane gas is 1/10 to 50 times the stoichiometric molar ratio necessary for completely hydrolyzing or oxidizing the organosilane or organosiloxane with the gas containing H and OH.
Claim 16
Dependent Claim
23 words
A process according to claim 1, wherein the step of removing the organic groups comprises subjecting the thin film to a plasma treatment.
Claim 17
Dependent Claim
25 words
A process according to claim 15, wherein said plasma treatment is conducted at a temperature in the range of from room temperature to 450° C.
Claim 18
Dependent Claim
38 words
A process according to claim 16, wherein a silicon oxide film having a desired film thickness is formed on the substrate by alternatively repeating the step of deposition and the step of plasma treatment in the same chamber.
Claim 19
Dependent Claim
34 words
A process according to claim 17, wherein the step of deposition and the step of plasma treatment are alternately conducted by intermittently stopping the supply of the organosilane or organosiloxane to the reaction chamber.
Claim 20
Dependent Claim
15 words
A process according to claim 17, wherein said excitation is performed in a pulsed manner.
Claim 21
Dependent Claim
30 words
A process according to claim 16, wherein said plasma treatment is performed by an oxygen, a hydrogen, or a water plasma and the substrate temperature is 100° to 250° C.
Claim 22
Dependent Claim
28 words
A process according to claim 20, wherein after the steps of deposition and plasma treatment, the heat treatment is performed at a temperature of 250° to 450° C.
Claim 23
Dependent Claim
54 words
A process according to claim 1, wherein at least one member selected from a phosphorus source, a boron source, and an arsenic source is introduced together with the organosilane or organosiloxane and the gas containing H and OH to incorporate at least one member selected from phosphorus, boron, and arsenic into the thin film.
Claim 24
Dependent Claim
33 words
A process according to claim 1, wherein a gas containing nitrogen is introduced together with the organosilane or organosiloxane and the gas containing H and OH to incorporate nitrogen into the thin film.
Claim 25
Dependent Claim
29 words
A process according to claim 1, wherein oxygen gas is, further, continuously or intermittently introduced into the organosilane gas or organosiloxane gas and the gas containing H and OH.
Claim 26
Dependent Claim
184 words
A process according to claim 1, wherein said deposition is performed through the use of a planar-type plasma CVD system under conditions of a pressure in a range of from 5 to 15 Torr, a temperature in a range of from room temperature to 250° C., a distance between electrodes in a range of from 6 to 25 mm, a gas flow rate in a range of from 100 to 18000 cm 3 /min, an RF (discharge) frequency of 13.56 MHz, a pulse period of 100 times the time required for the reaction gas to pass through between electrodes of the parallel plates, a discharge power of 100 to 500 W, a discharge "on" time satisfying a requirement represented by the formula ##EQU3## wherein D represents the length of a discharge "on" time in terms of % by assuming the time requirement for a gas to reach the substrate after the introduction thereof into the plasma region to be 100 with the upper limit of the discharge "on" time being 100%, P represents an RF power, and T represents the temperature of the substrate.
Claim 27
Dependent Claim
23 words
A process according to claim 1, wherein said silicon oxide film is a layer insulation film for multilayer interconnection of a semiconductor device.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-23 | 1997-11-22 | 1998-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-23 | 2001-11-22 | 2002-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-23 | 2005-11-22 | 2006-05-24 | $7700.00 | Window Closed / Lapsed |