Assignee: Applied Materials Inc
•
Filing: 1996-04-29
•
Granted: 1998-12-01
•
Expires: 2016-04-29
Abstract
Abstract A method of etching a dielectric layer on a substrate with high etching selectivity, low etch rate microloading, and high etch rates is described. In the method, the substrate is placed in a process zone, and a plasma is formed from process gas introduced into the process zone. The process gas comprises (i) fluorocarbon gas for etching the dielectric layer and for forming passivating deposits on the substrate, (ii) carbon-oxygen gas for enhancing formation of the passivating deposits, and (iii) nitrogen-containing gas for etching the passivating deposits on the substrate. The volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is selected to provide a dielectric to resist etching selectivity ratio of at least about 10:1, an etch rate microloading of <10%, and a dielectric etch rate of at least about 100 nm/min. Preferably, the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is selected so that the rate of formation of passivating deposits on the sidewalls of the freshly etched features is approximately equal to the rate of removal of the passivating deposits.
Inventors
- 👤 Bryan Pu
- 👤 Hongching Shan
- 👤 Michael Welch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 14:17
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283
Claims Analysis
Total Claims: 57
Claim 1
Independent Claim
130 words
A method of selectively etching a substrate having a dielectric layer with a resist material thereon, the method comprising the steps of: (a) placing the substrate in a process zone; (b) forming a plasma from a process gas introduced into the process zone, the process gas comprising (i) fluorocarbon gas for etching the dielectric layer and for forming passivating deposits on the substrate, (ii) carbon-oxygen gas to enhance formation of the passivating deposits, and (iii) nitrogen-containing gas for etching the passivating deposits formed on the substrate, wherein the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is selected to provide a dielectric to resist etching selectivity ratio of at least about 10:1, an etch rate microloading of less than about 10%, and a dielectric etch rate of at least about 100 nm/min.
Claim 2
Independent Claim
130 words
A method of selectively etching a substrate having a dielectric layer with a resist material thereon, the method comprising the steps of: (a) placing the substrate in a process zone; (b) forming a plasma from a process gas introduced into the process zone, the process gas comprising (i) fluorocarbon gas for etching the dielectric layer and for forming passivating deposits on the substrate, (ii) carbon-oxygen gas to enhance formation of the passivating deposits, and (iii) nitrogen-containing gas for etching the passivating deposits formed on the substrate, wherein the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is selected to provide a dielectric to resist etching selectivity ratio of at least about 10:1, an etch rate microloading of less than about 10%, and a dielectric etch rate of at least about 100 nm/min.
Claim 3
Dependent Claim
36 words
The method of claim 1, wherein the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is selected so that the rate of formation of passivating deposits is approximately equal to the rate of removal of the passivating deposits.
Claim 4
Dependent Claim
61 words
The method of claim 1, wherein the substrate further comprises an underlayer below the dielectric layer, the underlayer is selected from the group consisting of a polysilicon, monocrystalline silicon, titanium silicide, diffusion barrier, or anti-reflective layer, and wherein the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is selected to provide a dielectric to underlayer etching selectivity ratio of at least about 20:1.
Claim 5
Dependent Claim
50 words
The method of claim 1, wherein the process gas etches features having sidewalls in the dielectric layer, and wherein the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is selected so that the sidewalls of the etched features form angles of at least about 85° with a surface of the dielectric layer.
Claim 6
Dependent Claim
20 words
The method of claim 1, wherein the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is from about 7:8:4 to about 3:4:4.
Claim 7
Dependent Claim
20 words
The method of claim 4, wherein the volumetric flow ratio of fluorocarbon:carbon-oxygen:nitrogen-containing gas is from about 6:7:4 to about 4:5:4.
Claim 8
Dependent Claim
23 words
The method of claim 1, wherein the fluorocarbon gas comprises (i) first fluorocarbon gas containing hydrogen, and (ii) second fluorocarbon gas absent hydrogen.
Claim 9
Dependent Claim
43 words
The method of claim 7, wherein the first fluorocarbon gas is selected from the group consisting of CHF 3 , CH 3 F, C 2 HF 5 , CH 2 F 2 , C 2 H 4 F 2 , and mixtures thereof.
Claim 10
Dependent Claim
42 words
The method of claim 7, wherein the second fluorocarbon gas selected from the group consisting of CF 4 , C 2 F 6 , C 3 F 8 , C 4 F 8 , C 4 F 10 , and mixtures thereof.
Claim 11
Dependent Claim
40 words
The method of claim 1, wherein nitrogen-containing gas is absent fluorine, and is selected from the group consisting of N 2 , N 2 O, NO x in which x is from about 1 to about 2, and mixtures thereof.
Claim 12
Dependent Claim
26 words
The method of claim 1, wherein the flow rate of the carbon-oxygen gas is less than or equal to the flow rate of the fluorocarbon gas.
Claim 13
Dependent Claim
34 words
The method of claim 1, wherein inert gas is added to the process gas, the inert gas capable of being activated by the plasma to form sputtering ions that sputter material from the substrate.
Claim 14
Dependent Claim
24 words
The method of claim 12, wherein the volumetric flow ratio of the process gas to inert gas is from about 3:1 to about 1:2.
Claim 15
Dependent Claim
22 words
The method of claim 12, wherein the inert gas is selected from the group consisting of argon, xenon, neon, krypton, and helium.
Claim 16
Dependent Claim
28 words
The method of claim 1, wherein the dielectric layer is selected from the group consisting of silicon dioxide, undoped silicate glass, phophosilicate glass, borophosphosilicate glass, or mixtures thereof.
Claim 17
Dependent Claim
35 words
The method of claim 1, wherein the plasma is formed by applying an RF voltage at a power level of from about 100 Watts to about 2000 Watts to process electrodes in the process zone.
Claim 18
Independent Claim
160 words
A method of selectively etching a substrate having (i) a dielectric layer, (ii) an underlayer below the dielectric layer, and (iii) a resist material on the dielectric layer, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) fluorocarbon gas for etching the dielectric layer and for forming passivating deposits on the substrate, (ii) carbon-oxygen gas for enhancing formation of the passivating deposits, (iii) nitrogen for etching the passivating deposits formed on the substrate, and (iv) inert gas capable of sputtering material from the substrate; and (c) forming a plasma from the process gas introduced into the process zone to etch the dielectric layer on the substrate at an etch rate of at least about 100 nm/min, with a dielectric to resist etching selectivity ratio of at least about 10:1, and a dielectric to underlayer etching selectivity ratio of at least about 20:1.
Claim 19
Independent Claim
160 words
A method of selectively etching a substrate having (i) a dielectric layer, (ii) an underlayer below the dielectric layer, and (iii) a resist material on the dielectric layer, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) fluorocarbon gas for etching the dielectric layer and for forming passivating deposits on the substrate, (ii) carbon-oxygen gas for enhancing formation of the passivating deposits, (iii) nitrogen for etching the passivating deposits formed on the substrate, and (iv) inert gas capable of sputtering material from the substrate; and (c) forming a plasma from the process gas introduced into the process zone to etch the dielectric layer on the substrate at an etch rate of at least about 100 nm/min, with a dielectric to resist etching selectivity ratio of at least about 10:1, and a dielectric to underlayer etching selectivity ratio of at least about 20:1.
Claim 20
Dependent Claim
22 words
The method of claim 17, wherein the volumetric flow of flurocarbon gas to nitrogen gas is from about 5:1 to about 1:5.
Claim 21
Dependent Claim
22 words
The method of claim 17, wherein the volumetric flow of flurocarbon gas to nitrogen gas is from about 3:1 to about 1:3.
Claim 22
Dependent Claim
47 words
The method of claim 17, wherein the volumetric flow rates of the fluorocarbon, carbon-oxygen, nitrogen, and inert gas are selected so that the process gas deposits passivating deposits on the substrate at a rate that is approximately equal to the rate of removal of the passivating deposits.
Claim 23
Dependent Claim
27 words
The method of claim 17, wherein the underlayer comprising at least one material selected from the group consisting of polysilicon, monocrystalline silicon, titanium silicide, and silicon nitride.
Claim 24
Dependent Claim
23 words
The method of claim 17, wherein the fluorocarbon gas comprises (i) first fluorocarbon gas containing hydrogen, and (ii) second fluorocarbon gas absent hydrogen.
Claim 25
Dependent Claim
43 words
The method of claim 22, wherein the first fluorocarbon gas is selected from the group consisting of CH 3 F, CHF 3 , C 2 HF 5 , CH 2 F 2 , C 2 H 4 F 2 , and mixtures thereof.
Claim 26
Dependent Claim
42 words
The method of claim 22, wherein the second fluorocarbon gas is selected from the group consisting of CF 4 , C 2 F 6 , C 3 F 8 , C 4 F 8 , C 4 F 10 and mixtures thereof.
Claim 27
Dependent Claim
22 words
The method of claim 17, wherein the inert gas is selected from the group consisting of argon, xenon, neon, krypton, and helium.
Claim 28
Independent Claim
139 words
A method of selectively etching a dielectric layer on a substrate, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) first fluorocarbon gas selected from the group consisting of CHF 3 , CH 3 F, C 2 HF 5 , CH 2 F 2 , and C 2 H 4 F 2 , (ii) second fluorocarbon gas selected from the group consisting of CF 4 , C 2 F 6 , C 3 F 8 , C 4 F 8 and C 4 F 10 , (ii) carbon-oxygen gas, (iii) nitrogen, and (iv) inert gas; and (c) forming a plasma from the process gas introduced into the process zone to etch the dielectric layer on the substrate with high etching selectivity.
Claim 29
Independent Claim
139 words
A method of selectively etching a dielectric layer on a substrate, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) first fluorocarbon gas selected from the group consisting of CHF 3 , CH 3 F, C 2 HF 5 , CH 2 F 2 , and C 2 H 4 F 2 , (ii) second fluorocarbon gas selected from the group consisting of CF 4 , C 2 F 6 , C 3 F 8 , C 4 F 8 and C 4 F 10 , (ii) carbon-oxygen gas, (iii) nitrogen, and (iv) inert gas; and (c) forming a plasma from the process gas introduced into the process zone to etch the dielectric layer on the substrate with high etching selectivity.
Claim 30
Dependent Claim
19 words
The method of claim 26, wherein the volumetric flow ratio of fluorocarbon:nitrogen is from about 3:1 to about 1:3.
Claim 31
Dependent Claim
19 words
The method of claim 26, wherein the volumetric flow ratio of fluorocarbon:nitrogen is from about 2:1 to about 1:2.
Claim 32
Dependent Claim
27 words
The method of claim 26, wherein the volumetric flow ratio of the first fluorocarbon gas to the second flurocarbon gas is from about 1:1 to about 10:1.
Claim 33
Dependent Claim
27 words
The method of claim 26, wherein the volumetric flow ratio of the first fluorocarbon gas to the second flurocarbon gas is from about 1:1 to about 6:1.
Claim 34
Dependent Claim
30 words
The method of claim 26, wherein the flow rate of the carbon-oxygen gas is less than or equal to the combined flow rates of the first and second fluorocarbon gases.
Claim 35
Dependent Claim
22 words
The method of claim 26, wherein the inert gas is selected from the group consisting of argon, xenon, neon, krypton, and helium.
Claim 36
Dependent Claim
28 words
The method of claim 26, wherein the dielectric layer is selected from the group consisting of silicon dioxide, undoped silicate glass, phophosilicate glass, borophosphosilicate glass, or mixtures thereof.
Claim 37
Independent Claim
90 words
A method of etching a dielectric layer on a substrate, the dielectric layer comprising one or more of oxide and nitride layers, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) CHF 3 , (ii) C 4 F 8 , (iii) CO, (iv) N 2 , and (iv) inert gas; and (c) forming a plasma from the process gas introduced into the process zone to etch the dielectric layer on the substrate.
Claim 38
Independent Claim
90 words
A method of etching a dielectric layer on a substrate, the dielectric layer comprising one or more of oxide and nitride layers, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) CHF 3 , (ii) C 4 F 8 , (iii) CO, (iv) N 2 , and (iv) inert gas; and (c) forming a plasma from the process gas introduced into the process zone to etch the dielectric layer on the substrate.
Claim 39
Dependent Claim
25 words
The method of claim 34, wherein the volumetric flow ratio of CHF 3 to C 4 F 8 is from about 1:1 to about 10:1.
Claim 40
Dependent Claim
25 words
The method of claim 34, wherein the volumetric flow ratio of CHF 3 to C 4 F 8 is from about 1:1 to about 6:1.
Claim 41
Dependent Claim
33 words
The method of claim 34, wherein the ratio of the combined CHF 3 and C 4 F 8 flow rate to the N 2 flow rate is from about 5:1 to about 1:5.
Claim 42
Dependent Claim
33 words
The method of claim 34, wherein the ratio of the combined CHF 3 and C 4 F 8 flow rate to the N 2 flow rate is from about 3:1 to about 1:3.
Claim 43
Dependent Claim
33 words
The method of claim 34, wherein the flow rate of the carbon-oxygen gas is less than or equal to the combined flow rates of the CHF 3 and C 4 F 8 gases.
Claim 44
Independent Claim
106 words
A method of etching a dielectric layer on an underlayer on a substrate, the dielectric layer comprising one or more of oxide and nitride layers, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) fluorocarbon gas, (ii) CO gas, and (iii) nitrogen gas; and (c) forming a plasma from the process gas in the process zone to etch the dielectric layer with the formation of passivating deposits on the substrate while simultaneously etching the passivating deposits, for enhanced control of microloading and dielectric layer to underlayer etching selectivity.
Claim 45
Independent Claim
106 words
A method of etching a dielectric layer on an underlayer on a substrate, the dielectric layer comprising one or more of oxide and nitride layers, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) fluorocarbon gas, (ii) CO gas, and (iii) nitrogen gas; and (c) forming a plasma from the process gas in the process zone to etch the dielectric layer with the formation of passivating deposits on the substrate while simultaneously etching the passivating deposits, for enhanced control of microloading and dielectric layer to underlayer etching selectivity.
Claim 46
Dependent Claim
41 words
The method of claim 40 wherein the nitrogen gas is absent fluorine, and is selected from the group consisting of N 2 , N 2 O, NO x in which x is from about 1 to about 2, and mixtures thereof.
Claim 47
Dependent Claim
27 words
The method of claim 40 wherein the fluorocarbon gas is selected from the group consisting of C 2 F 6 , CHF 3 , and mixtures thereof.
Claim 48
Dependent Claim
12 words
The method of claim 40 wherein the process gas further comprises Ar.
Claim 49
Dependent Claim
40 words
The method of claim 40 wherein the volumetric flow ratio of fluorocarbon, CO and nitrogen gas is selected so that the rate of formation of the passivating deposits is approximately equal to the rate of removal of the passivating deposits.
Claim 50
Dependent Claim
76 words
The method of claim 40 wherein the fluorocarbon gas comprises at least two components, the first component selected from the group consisting of CH 3 F, CHF 3 , CH 2 F 2 , and C 2 H 4 F 2 ; and the second component selected from the group consisting of CF 4 , C 2 F 6 , C 3 F 8 , C 4 F 8 , and C 4 F 10 .
Claim 51
Independent Claim
106 words
A method of etching a dielectric layer on an underlayer on a substrate, the dielectric layer comprising one or more of oxide and nitride layers, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) fluorine-containing gas, (ii) CO gas, and (iii) nitrogen gas; and (c) forming a plasma from the process gas in the process zone to etch the dielectric layer with the formation of passivating deposits on the substrate while simultaneously etching the passivating deposits, for enhanced control of microloading and dielectric layer to underlayer etching selectivity.
Claim 52
Independent Claim
106 words
A method of etching a dielectric layer on an underlayer on a substrate, the dielectric layer comprising one or more of oxide and nitride layers, the method comprising the steps of: (a) placing the substrate in a process zone; (b) introducing process gas into the process zone, the process gas comprising (i) fluorine-containing gas, (ii) CO gas, and (iii) nitrogen gas; and (c) forming a plasma from the process gas in the process zone to etch the dielectric layer with the formation of passivating deposits on the substrate while simultaneously etching the passivating deposits, for enhanced control of microloading and dielectric layer to underlayer etching selectivity.
Claim 53
Dependent Claim
42 words
The method of claim 46 wherein the nitrogen gas is absent fluorine, and is selected from the group consisting of N 2 , N 2 O, NO x , in which x is from about 1 to about 2, and mixtures thereof.
Claim 54
Dependent Claim
27 words
The method of claim 46 wherein the fluorine-containing gas is selected from the group consisting of C 2 F 6 , CHF 3 , and mixtures thereof.
Claim 55
Dependent Claim
12 words
The method of claim 46 wherein the process gas further comprises Ar.
Claim 56
Dependent Claim
42 words
The method of claim 46 wherein the volumetric flow ratio of fluorine-containing gas, CO gas, and nitrogen gas is selected so that the rate of formation of the passivating deposits is approximately equal to the rate of removal of the passivating deposits.
Claim 57
Dependent Claim
76 words
The method of claim 46 wherein the fluorine-containing gas comprises at least two components, the first component selected from the group consisting of CH 3 F, CHF 3 , CH 2 F 2 , and C 2 H 4 F 2 ; and the second component selected from the group consisting of CF 4 , C 2 F 6 , C 3 F 8 , C 4 F 8 , and C 4 F 10 .
References Cited (Backward Citations)
US4654112A
Cited
US5021121A
Cited
US5356515A
Cited
US5302236A
Cited
US5272115A
Cited
US5445710A
Cited
US5302240A
Cited
US5338399A
Cited
US5234537A
Cited
US5322590A
Cited
US5290383A
Cited
US5269879A
Cited
US5308742A
Cited
US5514247A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-30 | 2002-06-01 | 2002-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-30 | 2006-06-01 | 2006-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-30 | 2010-06-01 | 2010-12-01 | $7700.00 | Window Closed / Lapsed |