HDP-CVD dep/etch/dep process for improved deposition into high aspect ratio features
Assignee: Applied Materials Inc
•
Filing: 2002-05-03
•
Granted: 2005-06-21
•
Expires: 2022-05-03
Abstract
Abstract A method of depositing a film on a substrate disposed in a substrate processing chamber. The method includes depositing a first portion of the film by forming a high density plasma from a first gaseous mixture flown into the process chamber. The deposition processes is then stopped and part of the deposited first portion of the film is etched by flowing a halogen etchant into the processing chamber. Next, the surface of the etched film is passivated by flowing a passivation gas into the processing chamber, and then a second portion of the film is deposited over the first portion by forming a high density plasma from a second gaseous mixture flown into the process chamber. In one embodiment the passivation gas consists of an oxygen source with our without an inert gas.
Inventors
- 👤 Dongqing Li
- 👤 Xiaolin C. Chen
- 👤 Lin Zhang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 03:46
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; C; C23; C23C; C23C16/00; C23C16/04; C23C16/045; C23C16/44; C23C16/455; C23C16/45523; C23C16/56; H10P14/66; H10P14/668; H10P14/6681; H10P14/6682; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/6922; H10P14/6923; H10P14/6924; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; Y; Y10; Y10S; Y10S438/00; Y10S438/978
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
106 words
A method of depositing a film on a substrate disposed in a substrate processing chamber, the method comprising: depositing a first portion of the film by forming a high density plasma from a first gaseous mixture flown into the process chamber; thereafter, etching part of the deposited first portion of the film by flowing a halogen etchant into the processing chamber; thereafter, passivating the surface of the etched film by flowing a passivation gas into the processing chamber; thereafter, depositing a second portion of the film over the first portion by forming a high density plasma from a second gaseous mixture flown into the process chamber.
Claim 2
Independent Claim
106 words
A method of depositing a film on a substrate disposed in a substrate processing chamber, the method comprising: depositing a first portion of the film by forming a high density plasma from a first gaseous mixture flown into the process chamber; thereafter, etching part of the deposited first portion of the film by flowing a halogen etchant into the processing chamber; thereafter, passivating the surface of the etched film by flowing a passivation gas into the processing chamber; thereafter, depositing a second portion of the film over the first portion by forming a high density plasma from a second gaseous mixture flown into the process chamber.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein the halogen etchant is a fluorine-containing gas.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the first and second gaseous mixtures are silica glass deposition gases.
Claim 5
Dependent Claim
17 words
The method of claim 3 wherein the first and second gaseous mixtures each comprise silane and oxygen.
Claim 6
Dependent Claim
29 words
The method of claim 1 wherein bias power is applied while the first gaseous mixture is flowed into the chamber during deposition of the first portion of the film.
Claim 7
Dependent Claim
21 words
The method of claim 5 wherein the bias power is switched off prior to flowing the halogen etchant into the chamber.
Claim 8
Dependent Claim
11 words
The method of claim 1 wherein the passivation gas comprises oxygen.
Claim 9
Dependent Claim
33 words
The method of claim 1 wherein the passivating step comprises exposing the surface of the etched film to a high density plasma consisting of an oxygen source with or without an inert gas.
Claim 10
Dependent Claim
17 words
The method of claim 1 wherein bias power is applied to the chamber during the passivating step.
Claim 11
Independent Claim
139 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the method comprising, in order: flowing a first process gas comprising silane and oxygen into the processing chamber and forming a high density plasma from the first process gas to deposit a first portion of the silica glass film over the substrate; stopping deposition of the silica glass film and flowing a fluorine etchant into the process chamber to etch part of the first portion of the silica glass film; flowing a passivation gas comprising oxygen into the processing chamber; and flowing a second process gas comprising silane and oxygen into the processing chamber to deposit a second portion of the silica glass film over the first portion; wherein the high density plasma is continuously maintained during each of the above steps.
Claim 12
Independent Claim
139 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the method comprising, in order: flowing a first process gas comprising silane and oxygen into the processing chamber and forming a high density plasma from the first process gas to deposit a first portion of the silica glass film over the substrate; stopping deposition of the silica glass film and flowing a fluorine etchant into the process chamber to etch part of the first portion of the silica glass film; flowing a passivation gas comprising oxygen into the processing chamber; and flowing a second process gas comprising silane and oxygen into the processing chamber to deposit a second portion of the silica glass film over the first portion; wherein the high density plasma is continuously maintained during each of the above steps.
Claim 13
Dependent Claim
20 words
The method of claim 10 wherein the passivation gas consists of an oxygen source with our without an inert gas.
Claim 14
Dependent Claim
21 words
The method of claim 11 wherein bias power is applied to the chamber while the passivating is flown into the chamber.
Claim 15
Dependent Claim
58 words
The method of claim 10 wherein bias power is (i) applied while the first process gas is flowed into the chamber during deposition of the first portion of the silica glass film and (ii) switched off prior to flowing the fluorine etchant gas into the chamber to etch part of the first portion of the silica glass film.
Claim 16
Dependent Claim
32 words
The method of claim 13 wherein bias power is again applied while the second process gas is flowed into the chamber during deposition of the second portion of the silica glass film.
Claim 17
Dependent Claim
30 words
The method of claim 14 wherein an oxygen-containing source is flowed into the chamber along with the fluorine etchant when the first portion of the silica glass film is etched.
Claim 18
Independent Claim
196 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the method comprising: forming a high density plasma within the substrate processing chamber to heat the substrate to a temperature of at least 400° C. prior to depositing the silica glass film on the substrate; maintaining the high density plasma while (i) flowing a first process gas comprising a silicon source and an oxygen source into the processing chamber to deposit a first portion of the silica glass film over the substrate, (ii) flowing a fluorine-containing etchant gas into the process chamber to etch part of the first portion of the silica glass film; (iii) flowing a passivation gas comprising oxygen into the processing chamber and (iv) flowing a second process gas comprising silane and oxygen into the processing chamber to deposit a second portion of the silica glass film over the first portion; wherein RF bias power is applied to the chamber during deposition of the first portion of the film, stopped prior to etching the part of the first portion of the film and then again applied prior to deposition of the second portion of the film.
Claim 19
Independent Claim
196 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the method comprising: forming a high density plasma within the substrate processing chamber to heat the substrate to a temperature of at least 400° C. prior to depositing the silica glass film on the substrate; maintaining the high density plasma while (i) flowing a first process gas comprising a silicon source and an oxygen source into the processing chamber to deposit a first portion of the silica glass film over the substrate, (ii) flowing a fluorine-containing etchant gas into the process chamber to etch part of the first portion of the silica glass film; (iii) flowing a passivation gas comprising oxygen into the processing chamber and (iv) flowing a second process gas comprising silane and oxygen into the processing chamber to deposit a second portion of the silica glass film over the first portion; wherein RF bias power is applied to the chamber during deposition of the first portion of the film, stopped prior to etching the part of the first portion of the film and then again applied prior to deposition of the second portion of the film.
Claim 20
Dependent Claim
47 words
The method of claim 16 wherein the passivation gas consists of an oxygen source with our without an inert gas and a second step, after the first step, in which the flow of the oxygen source is maintained while the flow of the fluorine source is stopped.
Claim 21
Dependent Claim
17 words
The method of claim 17 wherein bias power is applied to the chamber during the passivating step.
Claim 22
Independent Claim
231 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the method comprising: flowing an inert gas into the substrate processing chamber; forming a high density plasma within the substrate processing chamber from the inert gas; adding a flow of oxygen to the plasma and heating the substrate to a temperature of at least 400° C. prior to depositing the silica glass film on the substrate; adding a flow of silane to the plasma to deposit a first portion of the silica glass film over the substrate, wherein RE bias power is applied to the chamber during deposition of the first portion of the film; stopping the flow of silane and adding a flow of a fluorine-containing etchant to the plasma to etch part of the first portion of the silica glass film, wherein RF bias power is stopped prior to etching the part of the first portion of the film; stopping the flow of the fluorine-containing etchant and exposing the surface of the substrate to a oxygen plasma for between 5 and 20 seconds, wherein RE bias power is applied during passivation of the upper surface; adding a flow of silane to the plasma to deposit a second portion of the silica glass film over the first portion, wherein RE bias power is applied during deposition of the second portion of the film.
Claim 23
Independent Claim
231 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the method comprising: flowing an inert gas into the substrate processing chamber; forming a high density plasma within the substrate processing chamber from the inert gas; adding a flow of oxygen to the plasma and heating the substrate to a temperature of at least 400° C. prior to depositing the silica glass film on the substrate; adding a flow of silane to the plasma to deposit a first portion of the silica glass film over the substrate, wherein RE bias power is applied to the chamber during deposition of the first portion of the film; stopping the flow of silane and adding a flow of a fluorine-containing etchant to the plasma to etch part of the first portion of the silica glass film, wherein RF bias power is stopped prior to etching the part of the first portion of the film; stopping the flow of the fluorine-containing etchant and exposing the surface of the substrate to a oxygen plasma for between 5 and 20 seconds, wherein RE bias power is applied during passivation of the upper surface; adding a flow of silane to the plasma to deposit a second portion of the silica glass film over the first portion, wherein RE bias power is applied during deposition of the second portion of the film.
Claim 24
Independent Claim
179 words
A method of filling a gap formed between adjacent raised surfaces on a substrate with a silica glass film, the method comprising: transferring the substrate into a high density plasma CVD substrate processing chamber; partially filling the gap by depositing a first portion of the silica glass film over the substrate by flowing a first process gas comprising silicon and oxygen into the processing chamber and forming a high density plasma from the first process gas; etching the first portion of the silica glass film by flowing an etchant gas comprising a fluorine etchant into the process chamber and forming a high density plasma from the etchant gas; thereafter, exposing the first portion of the silica glass film to a high density plasma formed from a passivation gas comprising oxygen introduced into the processing chamber; and thereafter, filling the gap by depositing a second portion of the silica glass film over the first portion by flowing a second process gas comprising silicon and oxygen into the processing chamber and forming a high density plasma from the second process gas.
Claim 25
Independent Claim
179 words
A method of filling a gap formed between adjacent raised surfaces on a substrate with a silica glass film, the method comprising: transferring the substrate into a high density plasma CVD substrate processing chamber; partially filling the gap by depositing a first portion of the silica glass film over the substrate by flowing a first process gas comprising silicon and oxygen into the processing chamber and forming a high density plasma from the first process gas; etching the first portion of the silica glass film by flowing an etchant gas comprising a fluorine etchant into the process chamber and forming a high density plasma from the etchant gas; thereafter, exposing the first portion of the silica glass film to a high density plasma formed from a passivation gas comprising oxygen introduced into the processing chamber; and thereafter, filling the gap by depositing a second portion of the silica glass film over the first portion by flowing a second process gas comprising silicon and oxygen into the processing chamber and forming a high density plasma from the second process gas.
Claim 26
Dependent Claim
18 words
The method of claim 20 wherein the passivation gas consists of oxygen with or without an inert gas.
Claim 27
Dependent Claim
18 words
The method of claim 21 wherein the first and second process gases each comprise silane and molecular oxygen.
Claim 28
Dependent Claim
12 words
The method of claim 22 wherein the etchant gas comprises nitrogen trifluoride.
References Cited (Backward Citations)
US4690746A
Cited
US5362526A
Cited
US4872947A
Cited
US4892753A
Cited
US4960488A
Cited
US5000113A
Cited
US6167834B1
Cited
US5156881A
Cited
JPH0258836A
Cited
US5275977A
Cited
US5089442A
Cited
US5319247A
Cited
US5279865A
Cited
US5271972A
Cited
US5624582A
Cited
US5302233A
Cited
US5416048A
Cited
JPH07161703A
Cited
US5468342A
Cited
US5571576A
Cited
US6039851A
Cited
US5719085A
Cited
US5599740A
Cited
US5915190A
Cited
US5679606A
Cited
US6191026B1
Cited
US5872052A
Cited
US5858876A
Cited
US6182602B1
Cited
US6170428B1
Cited
US5953635A
Cited
US5913140A
Cited
US5990000A
Cited
US6059643A
Cited
US5850105A
Cited
US5968610A
Cited
US6189483B1
Cited
US5937323A
Cited
US6136685A
Cited
US5872058A
Cited
US6194038B1
Cited
US6602434B1
Cited
US6395150B1
Cited
US6030881A
Cited
US6087278A
Cited
US6037018A
Cited
US6203863B1
Cited
US6197705B1
Cited
US6335288B1
Cited
US6596654B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2008-06-20 | 2008-12-20 | 2009-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2012-06-20 | 2012-12-20 | 2013-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2016-06-20 | 2016-12-20 | 2017-06-21 | $7700.00 | Window Closed / Lapsed |