Method for forming an aluminum contact through an insulating layer
Assignee: STMicroelectronics lnc USA
•
Filing: 1993-11-30
•
Granted: 1997-08-19
•
Expires: 2013-11-30
Abstract
Abstract A method for forming an aluminum contact through an insulating layer includes the formation of an opening. A barrier layer is formed, if necessary, over the insulating layer and in the opening. A thin refractory metal layer is then formed over the barrier layer, and aluminum deposited over the refractory metal layer. Proper selection of the refractory metal layer and aluminum deposition conditions allows the aluminum to flow into the contact and completely fill it. Preferably, the aluminum is deposited over the refractory metal layer without breaking vacuum.
Inventors
- 👤 Yih-Shung Lin
- 👤 Fu-Tai Liou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:29
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/047; H10W20/049; C; C23; C23C; C23C16/00; C23C16/02; C23C16/0272; C23C16/0281; C23C16/06; C23C16/18; C23C16/20; H10W20/033; H10W20/035; H10W20/048; H10W20/056; H10W20/40; H10W20/41; H10W20/425
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
208 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer to expose a conducting structure; forming a barrier layer over the insulating layer and extending into the opening to cover the conducting structure; forming an upper layer of refractory metal over the barrier layer to a thickness of between approximately 50 Å and 600 Å; and depositing aluminum over the upper refractory metal layer at a temperature and rate which maximizes surface mobility of the aluminum, allowing it to completely fill the opening, the depositing aluminum step including the steps of: forming a first aluminum layer in a first chamber of a multi-chamber sputtering machine at a temperature of less than approximately 300° C.; moving the device from the first chamber to a second chamber of the multi-chamber sputtering machine without exposing the device to air, wherein the second chamber is maintained at a temperature between approximately 400° C. and 500° C., wherein the temperature of the device is increased to a temperature between approximately 400° C. and 500° C.; and during the temperature increasing step, continuing to deposit aluminum over the first aluminum layer at a rate between approximately 30 and 50 Å/sec.
Claim 2
Independent Claim
208 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer to expose a conducting structure; forming a barrier layer over the insulating layer and extending into the opening to cover the conducting structure; forming an upper layer of refractory metal over the barrier layer to a thickness of between approximately 50 Å and 600 Å; and depositing aluminum over the upper refractory metal layer at a temperature and rate which maximizes surface mobility of the aluminum, allowing it to completely fill the opening, the depositing aluminum step including the steps of: forming a first aluminum layer in a first chamber of a multi-chamber sputtering machine at a temperature of less than approximately 300° C.; moving the device from the first chamber to a second chamber of the multi-chamber sputtering machine without exposing the device to air, wherein the second chamber is maintained at a temperature between approximately 400° C. and 500° C., wherein the temperature of the device is increased to a temperature between approximately 400° C. and 500° C.; and during the temperature increasing step, continuing to deposit aluminum over the first aluminum layer at a rate between approximately 30 and 50 Å/sec.
Claim 3
Independent Claim
146 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer to expose a conducting structure; forming a first refractory metal layer over the insulating layer and over sidewalls and a bottom of the opening; forming a refractory metal nitride layer over the first refractory metal layer; forming a second refractory metal layer over the refractory metal nitride layer; heating the device in a nitrogen atmosphere to convert the second refractory metal layer to a refractory metal nitride to form a barrier layer; forming an upper layer of refractory metal over the barrier layer to a thickness of between approximately 50 Å and 600 Å; and depositing aluminum over the upper refractory metal layer at a temperature and rate which maximizes surface mobility of the aluminum, allowing it to completely fill the opening.
Claim 4
Independent Claim
146 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer to expose a conducting structure; forming a first refractory metal layer over the insulating layer and over sidewalls and a bottom of the opening; forming a refractory metal nitride layer over the first refractory metal layer; forming a second refractory metal layer over the refractory metal nitride layer; heating the device in a nitrogen atmosphere to convert the second refractory metal layer to a refractory metal nitride to form a barrier layer; forming an upper layer of refractory metal over the barrier layer to a thickness of between approximately 50 Å and 600 Å; and depositing aluminum over the upper refractory metal layer at a temperature and rate which maximizes surface mobility of the aluminum, allowing it to completely fill the opening.
Claim 5
Dependent Claim
15 words
The method of claim 2, wherein the first and second refractory metal layers comprise titanium.
Claim 6
Dependent Claim
19 words
The method of claim 3, wherein the upper layer of refractory metal formed over the barrier layer comprises titanium.
Claim 7
Dependent Claim
36 words
The method of claim 4, wherein the step of depositing aluminum causes the upper layer of titanium to alloy with the aluminum, forming a layer of aluminum/titanium alloy between the aluminum layer and the barrier layer.
Claim 8
Independent Claim
199 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer to expose a conducting structure; forming an upper layer of refractory metal, over the insulating layer and extending into the opening to cover the conducting structure, to a thickness of between approximately 50 Å and 600 Å; and depositing aluminum over the upper refractory metal layer at a temperature and rate which maximizes surface mobility of the aluminum, allowing it to completely fill the opening, the depositing aluminum step including the steps of: forming a first aluminum layer in a first chamber of a multi-chamber sputtering machine at a temperature of less than approximately300° C.; moving the device from the first chamber to a second chamber of the multi-chamber sputtering machine without exposing the device to air, wherein the second chamber is maintained at a temperature between approximately 400° C. and 500° C., wherein the temperature of the device is increased to a temperature between approximately 400° C. and 500° C.; and during the temperature increasing step, continuing to deposit aluminum over the first aluminum layer at a rate between approximately 30 and 50 Å/sec.
Claim 9
Independent Claim
199 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer to expose a conducting structure; forming an upper layer of refractory metal, over the insulating layer and extending into the opening to cover the conducting structure, to a thickness of between approximately 50 Å and 600 Å; and depositing aluminum over the upper refractory metal layer at a temperature and rate which maximizes surface mobility of the aluminum, allowing it to completely fill the opening, the depositing aluminum step including the steps of: forming a first aluminum layer in a first chamber of a multi-chamber sputtering machine at a temperature of less than approximately300° C.; moving the device from the first chamber to a second chamber of the multi-chamber sputtering machine without exposing the device to air, wherein the second chamber is maintained at a temperature between approximately 400° C. and 500° C., wherein the temperature of the device is increased to a temperature between approximately 400° C. and 500° C.; and during the temperature increasing step, continuing to deposit aluminum over the first aluminum layer at a rate between approximately 30 and 50 Å/sec.
Claim 10
Independent Claim
157 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer; depositing a first titanium layer over the insulating layer and in the opening; depositing a titanium nitride layer over the first titanium layer; depositing a second titanium layer over the titanium nitride layer; heating the device in a nitrogen atmosphere, wherein the second titanium layer is converted to titanium nitride; depositing an upper titanium layer over the converted titanium nitride to a thickness of between approximately 50 Å and 600 Å; depositing aluminum over the upper titanium layer; during the aluminum depositing step, heating the device to a temperature in the range of approximately 400° C. and 500° C., wherein the aluminum fills the opening and forms a planar upper surface over the opening, and wherein the upper titanium layer alloys with the aluminum during deposition to form a layer of aluminum/titanium alloy.
Claim 11
Independent Claim
157 words
A method for forming an interlevel aluminum contact for an integrated circuit device, comprising the steps of: forming an opening through an insulating layer; depositing a first titanium layer over the insulating layer and in the opening; depositing a titanium nitride layer over the first titanium layer; depositing a second titanium layer over the titanium nitride layer; heating the device in a nitrogen atmosphere, wherein the second titanium layer is converted to titanium nitride; depositing an upper titanium layer over the converted titanium nitride to a thickness of between approximately 50 Å and 600 Å; depositing aluminum over the upper titanium layer; during the aluminum depositing step, heating the device to a temperature in the range of approximately 400° C. and 500° C., wherein the aluminum fills the opening and forms a planar upper surface over the opening, and wherein the upper titanium layer alloys with the aluminum during deposition to form a layer of aluminum/titanium alloy.
Claim 12
Dependent Claim
67 words
The method of claim 7, wherein the steps of depositing aluminum and heating the device comprise the steps of: depositing a first portion of the aluminum over the upper titanium layer at a temperature below approximately 300° C.; increasing the temperature of the device to within the range of approximately 400° C. to 500° C.; and continuing to deposit aluminum during the step of increasing the temperature.
Claim 13
Dependent Claim
36 words
The method of claim 8, wherein the device remains in a vacuum between the step of depositing the upper titanium layer and the step of depositing a first portion of aluminum over the upper titanium layer.
Claim 14
Dependent Claim
113 words
The method of claim 8, wherein the step of depositing a first portion of the aluminum is performed in a first chamber of a multi-chamber sputtering machine, wherein the steps of increasing the temperature and continuing to deposit aluminum are performed in a second chamber of the multi-chamber sputtering machine, and wherein the first chamber is maintained at a temperature below approximately 375° C. and the second chamber is maintained at a temperature between approximately 400° C. and 550° C., and further comprising the step of: after the step of depositing a first portion of aluminum, moving the device from the first chamber to the second chamber without exposing the device to air.
Claim 15
Dependent Claim
54 words
The method of claim 10, wherein the step of depositing the upper titanium layer is performed in a third chamber of the multi-chamber sputtering machine, and further comprising the step of: after the upper titanium layer is deposited, moving the device from the first chamber to the second chamber without exposing it to air.
Claim 16
Dependent Claim
40 words
The method of claim 10, further comprising the step of: after the continuing to deposit aluminum step has deposited aluminum to a thickness greater than approximately 2500 Å, increasing the rate of deposition to a rate greater than 50 Å/sec.
Claim 17
Dependent Claim
69 words
The method of claim 2, wherein the step of depositing aluminum comprises the steps of: forming a first aluminum layer at a temperature of less than approximately 300° C.; increasing the temperature of the device to a temperature between approximately 400° C. and 500° C.; and during the temperature increasing step, continuing to deposit aluminum over the first aluminum layer at a rate between approximately 30 and 50 Å/sec.
Claim 18
Dependent Claim
24 words
The method of claim 13, further comprising; after the continuing to deposit step has deposited approximately 2000 Å of aluminum, increasing the deposition rate.
Claim 19
Dependent Claim
13 words
The method of claim 2, wherein the upper refractory metal layer comprises titanium.
Claim 20
Dependent Claim
24 words
The method of claim 1, further comprising; after the continuing to deposit step has deposited approximately 2000 Å of aluminum, increasing the deposition rate.
Claim 21
Dependent Claim
13 words
The method of claim 1, wherein the upper refractory metal layer comprises titanium.
Claim 22
Dependent Claim
24 words
The method of claim 6, further comprising; after the continuing to deposit step has deposited approximately 2000 Å of aluminum, increasing the deposition rate.
References Cited (Backward Citations)
US3158504A
Cited
US3900598A
Cited
US4107726A
Cited
JPS5471564A
Cited
US4436582A
Cited
JPS57139939A
Cited
JPS5846641A
Cited
GB2112566A
Cited
GB2128636A
Cited
EP0107259A2
Cited
EP0132720A1
Cited
EP0137701A1
Cited
US4502209A
Cited
US4592802A
Cited
JPS60227446A
Cited
US4566177A
Cited
US4661228A
Cited
EP0168828A2
Cited
US4772571A
Cited
JPS61142739A
Cited
US4892844A
Cited
EP0257277A2
Cited
JPS63124447A
Cited
EP0269019A2
Cited
JPS63136547A
Cited
US4756810A
Cited
US4951601A
Cited
EP0273715A2
Cited
EP0276087A2
Cited
US4988423A
Cited
JPS6477122A
Cited
US4758533A
Cited
EP0310108A2
Cited
JPH01160036A
Cited
EP0329227A1
Cited
US4837183A
Cited
EP0351001A1
Cited
US5106781A
Cited
US4976839A
Cited
US4944961A
Cited
JPH02137230A
Cited
US4970176A
Cited
US4994162A
Cited
US4975389A
Cited
EP0430403A2
Cited
EP0451571A2
Cited
US5108570A
Cited
US5108951A
Cited
EP0488628A2
Cited
EP0488264A2
Cited
EP0499241A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-08-18 | 2001-02-17 | 2001-08-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-08-18 | 2005-02-17 | 2005-08-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-08-18 | 2009-02-17 | 2009-08-19 | $7700.00 | Window Closed / Lapsed |