Deposition and planarizing methods and apparatus
Assignee: Machine Technology Inc
•
Filing: 1986-12-04
•
Granted: 1988-07-12
•
Expires: 2006-12-04
Abstract
Abstract A layer of a substance such as an aluminum alloy is deposited, preferably by sputtering, onto a surface of a substrate such as a semiconductor wafer. The deposited substance is redistributed by bombarding the layer with ions. The ion bombardment may be induced by applying low frequency RF excitation at about 5 KHz -1 MHz to the substrate.
Inventors
- 👤 Lawrence T. Lamont, Jr.
- 👤 Roderick C. Mosely
- 👤 Timothy M. McEntee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:05
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/3435; C23C14/345; C23C14/225; C23C14/35; H; H01; H01J; H01J37/00; H01J37/32; H01J37/32009; H01J37/32082; H01J37/34; H01J37/3402; H01J37/3405; H01J37/3408; H01J2237/00; H01J2237/32; H01J2237/33; H01J2237/332; H01J2237/3322; H01J2237/3327
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
103 words
A method of depositing and planarizing a layer of a substance on a surface of a substrate comprising the steps of: (a) depositing said substance on said surface from a gaseous phase to thereby form said layer; (b) exposing said layer to a plasma during said depositing step; and (c) applying an RF excitation at between about 5 KHz to about 1 MHz to said substrate so that said RF excitation induces a bias voltage on said substrate with respect to said plasma whereby ions from said plasma will bombard said layer and mobilize said substance on said layer during said depositing step.
Claim 2
Independent Claim
103 words
A method of depositing and planarizing a layer of a substance on a surface of a substrate comprising the steps of: (a) depositing said substance on said surface from a gaseous phase to thereby form said layer; (b) exposing said layer to a plasma during said depositing step; and (c) applying an RF excitation at between about 5 KHz to about 1 MHz to said substrate so that said RF excitation induces a bias voltage on said substrate with respect to said plasma whereby ions from said plasma will bombard said layer and mobilize said substance on said layer during said depositing step.
Claim 3
Dependent Claim
43 words
A method as claimed in claim 1 wherein said substance is not resputtered from said layer by said bombarding ions at a rate greater than about 10% of the rate at which said substance is deposited on said surface in said depositing step.
Claim 4
Dependent Claim
23 words
A method as claimed in claim 1 wherein said bias induced by said RF excitation is between about 100 and about 500 volts.
Claim 5
Dependent Claim
31 words
A method as claimed in claim 3 wherein the frequency of said RF excitation is selected so that the capacitive voltage drop through said substrate is less than about 10 volts.
Claim 6
Dependent Claim
23 words
A method as claimed in claim 4 wherein said frequency of said RF excitation is between about 50 kHz and about 450 kHz.
Claim 7
Dependent Claim
16 words
A method as claimed in claim 1 wherein said substance is a metal or metal alloy.
Claim 8
Dependent Claim
36 words
A method as claimed in claim 6 wherein said metal or metal alloy includes at least about 50% aluminum and said layer is maintained at a bulk temperature below about 525° C. during said depositing step.
Claim 9
Dependent Claim
26 words
A method as claimed in claim 7 wherein said bulk temperature of said layer is maintained at at least about 150° C. during said bombarding step.
Claim 10
Dependent Claim
29 words
A method as claimed in claim 8 further comprising the step of preheating said substrate to between about 150° C. and about 400° C. prior to said depositing step.
Claim 11
Dependent Claim
30 words
A method as claimed in claim 1 further comprising the step of maintaining said layer at a bulk temperature below the solidus temperature of said substance during said depositing step.
Claim 12
Dependent Claim
31 words
A method as claimed in claim 10 wherein said step of maintaining said layer at said bulk temperature includes the step of abstracting heat from said substrate during said depositing step.
Claim 13
Dependent Claim
32 words
A method as claimed in claim 1 further comprising the step of interrupting said depositing step, abstracting heat from said substrate during said interruption and resuming said depositing step after said interruption.
Claim 14
Dependent Claim
33 words
A method as claimed in claim 1 wherein said depositing step includes the step of directing adatoms of said substance towards said surface at angles oblique to the vector normal to said surface.
Claim 15
Dependent Claim
28 words
A method as claimed in claim 1 wherein said depositing step includes the step of sputtering adatoms of said substance from an eroding surface of a sputter source.
Claim 16
Dependent Claim
54 words
A method as claimed in claim 14 wherein said eroding surface and said surface of said substrate are both generally planar, said method further comprising the step of maintaining said eroding surface at an angle of between about 10° and about 45° with respect to said surface of said substrate during said depositing step.
Claim 17
Dependent Claim
29 words
A method as claimed in claim 15 further comprising the step of maintaining both said eroding surface and said surface of said substrate substantially vertical during and depositing step.
Claim 18
Dependent Claim
25 words
A method as claimed in claim 15 further comprising the step of rotating said substrate about an axis normal to said surface of said substrate.
Claim 19
Dependent Claim
49 words
A method as claimed in claim 1 wherein said depositing, exposing and applying steps are conducted so that said substance substantially fills a tubular via hole in said surface less than about two micrometers in diameter and having an aspect ratio more than about 0.5 during said depositing step.
Claim 20
Dependent Claim
25 words
A method as claimed in claim 1 wherein said depositing step includes the step of depositing said substance on a surface of a semiconductor wafer.
Claim 21
Dependent Claim
85 words
Apparatus for depositing and planarizing a layer of a substance on a surface of a substrate comprising: (a) means for holding said substrate; (b) means for depositing said substance on said surface from a gaseous phase to thereby form a layer of said substance; (c) means for providing a plasma in proximity to said surface during operation of said depositing means; and (d) substrate RF power means for applying RF excitation to said substrate at a frequency of about 5 kHz to about 1 MHz.
Claim 22
Dependent Claim
85 words
Apparatus for depositing and planarizing a layer of a substance on a surface of a substrate comprising: (a) means for holding said substrate; (b) means for depositing said substance on said surface from a gaseous phase to thereby form a layer of said substance; (c) means for providing a plasma in proximity to said surface during operation of said depositing means; and (d) substrate RF power means for applying RF excitation to said substrate at a frequency of about 5 kHz to about 1 MHz.
Claim 23
Dependent Claim
32 words
Apparatus as claimed in claim 20, further comprising temperature control means for maintaining said layer at a bulk temperature below the solidus temperature of said substance during operation of said depositing means.
Claim 24
Dependent Claim
62 words
Apparatus as claimed in claim 21 wherein said depositing means includes means for retaining a sputter source having an erodable surface in proximity to said substrate so that said erodable surface faces generally towards said substrate and said plasma, and source power means for applying a bias to said sputter source to thereby cause sputtering of said substance from said erodable surface.
Claim 25
Dependent Claim
68 words
Apparatus as claimed in claim 22 wherein said means for retaining a sputter source is operative to retain a sputter source having a generally planar erodable surface and said means for holding said substrate includes means for retaining a substrate having a generally planar front surface so that said front surface is disposed at an angle of about 10° to about 45° with respect to said erodable surface.
Claim 26
Dependent Claim
41 words
Apparatus as claimed in claim 21 wherein said temperature control means includes means for controlling the operation of said depositing means to thereby limit addition of heat to said layer by said substance as said substance is deposited in said layer.
Claim 27
Dependent Claim
25 words
Apparatus as claimed in claim 21 wherein said temperature control means includes means for abstracting heat from said substrate during operation of said depositing means.
Claim 28
Dependent Claim
41 words
Apparatus as claimed in claim 21 wherein said temperature control means is operative to maintain said bulk temperature of said layer at an elevated temperature at least about 150° C., but below said solidus temperature during operation of said depositing means.
Claim 29
Independent Claim
141 words
A method of depositing and planarizing a layer of a substance on a surface of a substrate comprising the steps of: (a) depositing a substance selected from the group consisting of metals and metal alloys on said surface of said substrate by sputtering to thereby form said layer; (b) exposing said layer to a plasma during said depositing step; and (c) applying an RF excitation at between about 50 KHz and about 450 KHz to said substrate so that said RF excitation induces a bias voltage between about 100 and about 500 volts on said substrate with respect to said plasma whereby ions from said plasma will bombard said layer and mobilize said substance on said layer during said depositing step; and (d) maintaining said layer at a bulk temperature below the solidus temperature of said substance during said depositing step.
Claim 30
Independent Claim
141 words
A method of depositing and planarizing a layer of a substance on a surface of a substrate comprising the steps of: (a) depositing a substance selected from the group consisting of metals and metal alloys on said surface of said substrate by sputtering to thereby form said layer; (b) exposing said layer to a plasma during said depositing step; and (c) applying an RF excitation at between about 50 KHz and about 450 KHz to said substrate so that said RF excitation induces a bias voltage between about 100 and about 500 volts on said substrate with respect to said plasma whereby ions from said plasma will bombard said layer and mobilize said substance on said layer during said depositing step; and (d) maintaining said layer at a bulk temperature below the solidus temperature of said substance during said depositing step.
Claim 31
Dependent Claim
43 words
A method as claimed in claim 27 wherein said substance is not resputtered from said layer by said bombarding ions at a rate greater than about 10% of the rate at which said substance is deposited on said surface in said depositing step.
Claim 32
Dependent Claim
36 words
A method as claimed in claim 28 wherein said metal or metal alloy includes at least about 50% aluminum and said layer is maintained at a bulk temperature below about 525° C. during said depositing step.
Claim 33
Dependent Claim
26 words
A method as claimed in claim 29 wherein said bulk temperature of said layer is maintained at at least about 150° C. during said bombarding step.
Claim 34
Dependent Claim
56 words
A method as claimed in claim 30 wherein said depositing step includes the step of directing adatoms of said substance towards said surface of said substrate at angles oblique to the vector normal to said surface, the method further comprising the step of rotating said substrate about an axis normal to said surface of said substrate.
Claim 35
Dependent Claim
49 words
A method as claimed in claim 31 wherein said depositing, exposing and applying steps are conducted so that said substance substantially fills a tubular via hole in said surface less than about two micrometers in diameter and having an aspect ratio more than about 0.5 during said depositing step.
References Cited (Backward Citations)
US3451912A
Cited
US3528906A
Cited
US3661761A
Cited
US3983022A
Cited
US3775285A
Cited
US3804738A
Cited
US3868723A
Cited
US4036723A
Cited
US4007103A
Cited
US4468437A
Cited
US4410407A
Cited
US4664935A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-12 | 1992-01-11 | 1992-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-12 | 1996-01-11 | 1996-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-12 | 2000-01-11 | 2000-07-12 | $7700.00 | Window Closed / Lapsed |