Method and apparatus for thermal processing of semiconductor substrates
Assignee: National Technology and Engineering Solutions of Sandia LLC
•
Filing: 2000-08-18
•
Granted: 2002-03-12
•
Expires: 2020-08-18
Abstract
Abstract An improved apparatus and method for thermal processing of semiconductor wafers. The apparatus and method provide the temperature stability and uniformity of a conventional batch furnace as well as the processing speed and reduced time-at-temperature of a lamp-heated rapid thermal processor (RTP). Individual wafers are rapidly inserted into and withdrawn from a furnace cavity held at a nearly constant and isothermal temperature. The speeds of insertion and withdrawal are sufficiently large to limit thermal stresses and thereby reduce or prevent plastic deformation of the wafer as it enters and leaves the furnace. By processing the semiconductor wafer in a substantially isothermal cavity, the wafer temperature and spatial uniformity of the wafer temperature can be ensured by measuring and controlling only temperatures of the cavity walls. Further, peak power requirements are very small compared to lamp-heated RTPs because the cavity temperature is not cycled and the thermal mass of the cavity is relatively large. Increased speeds of insertion and/or removal may also be used with non-isothermal furnaces.
Inventors
- 👤 Stewart K. Griffiths
- 👤 Robert H. Nilson
- 👤 Brad S. Mattson
- 👤 Stephen E. Savas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:32
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90; H10P72/00; H10P72/06; H10P72/0602; C; C23; C23C; C23C16/00; C23C16/44; C23C16/46; C23C16/54; C30; C30B; C30B25/00; C30B25/02; C30B25/10; C30B31/00; C30B31/06; C30B31/12; H10P72/04; H10P72/0431; H10P72/0434
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
113 words
An apparatus for rapid thermal processing of a semiconductor wafer, comprising: a process chamber; a wafer transport configured to insert the wafer horizontally into the process chamber for processing and to withdraw the wafer from the chamber horizontally after processing into a substantially cooler thermal environment, wherein the speed of withdrawal is at least 0.3 meters per second; a first heater configured to provide substantially uniform heat to the bottom of the wafer during processing; and a second heater configured to provide substantially uniform heat to the top of the wafer during processing, wherein the first heater and the second heater are configured to heat the wafer to at least 800 degrees Celsius.
Claim 2
Independent Claim
113 words
An apparatus for rapid thermal processing of a semiconductor wafer, comprising: a process chamber; a wafer transport configured to insert the wafer horizontally into the process chamber for processing and to withdraw the wafer from the chamber horizontally after processing into a substantially cooler thermal environment, wherein the speed of withdrawal is at least 0.3 meters per second; a first heater configured to provide substantially uniform heat to the bottom of the wafer during processing; and a second heater configured to provide substantially uniform heat to the top of the wafer during processing, wherein the first heater and the second heater are configured to heat the wafer to at least 800 degrees Celsius.
Claim 3
Dependent Claim
25 words
The apparatus of claim 1 , wherein the first heater and the second heater are planar resistance heaters positioned parallel to the wafer during processing.
Claim 4
Dependent Claim
19 words
The apparatus of claim 1 , wherein the semiconductor wafer has a diameter of at least about 300 mm.
Claim 5
Dependent Claim
19 words
The apparatus of claim 1 , wherein the speed of withdrawal is greater than about 0.5 meters per second.
Claim 6
Dependent Claim
19 words
The apparatus of claim 1 , wherein the speed of withdrawal is greater than about 0.75 meters per second.
Claim 7
Dependent Claim
19 words
The apparatus of claim 1 , wherein the speed of withdrawal is greater than about 1 meter per second.
Claim 8
Dependent Claim
29 words
The apparatus of claim 1 , wherein the processing temperature is greater than about 1000 degrees Celsius and the semiconductor wafer has a diameter of at least 300 mm.
Claim 9
Dependent Claim
29 words
The apparatus of claim 1 , wherein the processing temperature is greater than about 1100 degrees Celsius and the semiconductor wafer has a diameter of at least 300 mm.
Claim 10
Dependent Claim
32 words
The apparatus of claim 1 , further comprising a heat shield for the edge of the semiconductor wafer which decreases the rate of cooling at the edge of the wafer after withdrawal.
Claim 11
Independent Claim
58 words
A method for processing a semiconductor wafer comprising: providing two parallel heaters for heating the wafer; inserting the wafer horizontally between the two parallel heaters for processing; heating the wafer to at least 800 degrees Celsius; and withdrawing the wafer horizontally into a substantially cooler thermal environment at a withdrawal speed of at least 0.3 meters per second.
Claim 12
Independent Claim
58 words
A method for processing a semiconductor wafer comprising: providing two parallel heaters for heating the wafer; inserting the wafer horizontally between the two parallel heaters for processing; heating the wafer to at least 800 degrees Celsius; and withdrawing the wafer horizontally into a substantially cooler thermal environment at a withdrawal speed of at least 0.3 meters per second.
Claim 13
Dependent Claim
21 words
The method of claim 10 , wherein the first heater and the second heater are each heated to the same temperature.
Claim 14
Dependent Claim
18 words
The method of claim 10 , wherein the semiconductor wafer has a diameter of at least 300 mm.
Claim 15
Dependent Claim
31 words
The method of claim 10 , wherein the speed of withdrawal is sufficient to prevent plastic deformation of the semiconductor wafer due to the withdrawal into the substantially cooler thermal environment.
Claim 16
Dependent Claim
42 words
The method of claim 10 , wherein the speed of withdrawal is sufficient to substantially reduce plastic deformation of the wafer relative to the level of plastic deformation that would result at a speed of withdrawal of about 0.2 meters per second.
Claim 17
Dependent Claim
19 words
The method of claim 10 , wherein the speed of withdrawal is greater than about 0.5 meters per second.
Claim 18
Dependent Claim
19 words
The method of claim 10 , wherein the speed of withdrawal is greater than about 0.75 meters per second.
Claim 19
Dependent Claim
19 words
The method of claim 10 , wherein the speed of withdrawal is greater than about 1 meter per second.
Claim 20
Dependent Claim
43 words
The method of claim 10 , wherein the speed of withdrawal is between about 0.3 to 1.2 meters per second and is selected such that plastic deformation defects are formed which are limited to point-like defects with lengths less than about 100 microns.
Claim 21
Dependent Claim
17 words
The method of claim 10 , wherein the processing temperature is greater than about 1000 degrees Celsius.
Claim 22
Dependent Claim
29 words
The method of claim 10 , wherein the processing temperature is greater than about 1100 degrees Celsius and the wafer has a diameter of at last about 300 mm.
References Cited (Backward Citations)
US4496609A
Cited
US3737282A
Cited
US3723053A
Cited
US4081313A
Cited
US4194276A
Cited
US4909314A
Cited
US4417347A
Cited
US4468195A
Cited
US4481406A
Cited
US4540876A
Cited
US4507078A
Cited
EP0134716A1
Cited
US4518349A
Cited
US4555273A
Cited
US4698486A
Cited
US4777022A
Cited
US4649361A
Cited
JPS61180438A
Cited
US4794217A
Cited
JPS62120475A
Cited
US4770630A
Cited
US4891335A
Cited
JPS63260016A
Cited
US5040484A
Cited
JPS6412524A
Cited
US4818327A
Cited
US5001327A
Cited
US4943234A
Cited
US4857689A
Cited
US4898834A
Cited
US5048800A
Cited
JPH02238616A
Cited
US5011794A
Cited
US5059770A
Cited
US5219798A
Cited
US5043300A
Cited
US5430271A
Cited
US5060354A
Cited
US5252807A
Cited
US5207573A
Cited
US5536918A
Cited
US5387557A
Cited
US5445676A
Cited
US5429498A
Cited
US5343012A
Cited
US5520742A
Cited
US5498292A
Cited
US5680502A
Cited
US6002109A
Cited
US5695654A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2005-03-11 | 2005-09-10 | 2006-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2009-03-11 | 2009-09-10 | 2010-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2013-03-11 | 2013-09-10 | 2014-03-12 | $7700.00 | Window Closed / Lapsed |