US4898834A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Open-tube, benign-environment annealing method for compound semiconductors
Assignee: Amber Engineering Inc
•
Filing: 1988-06-27
•
Granted: 1990-02-06
•
Expires: 2008-06-27
Abstract
Abstract An improved system and method for annealing indium antimonide ion implanted junctions employing an open-tube benign annealing environment. A furnace having a hollow chamber therein is maintained continuously at a predetermined annealing temperature and wafers of indium antimonide to be annealed are inserted into the chamber through a resealable airlock at one end of the chamber. A source of molten indium saturated with antimony is provided within the chamber to maintain desired partial pressures of indium and antimony within the chamber. Hydrogen gas is continuously flushed through the chamber to purge contaminants and maintain the chamber at a desired slight overpressure over atmospheric. At the conclusion of annealing, the indium antimonide wafer is removed from the chamber into the airlock which is flushed with hydrogen gas. The wafer is allowed to cool to room temperature and removed from the airlock for subsequent processing steps.
Inventors
- 👤 Arthur H. Lockwood
- 👤 Adela Gonzales
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:28
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/90; H10P95/904; H10F; H10F30/00; H10F30/20; H10F30/21; H10F30/22; H10F30/221; H10F30/2215; H10F71/00; H10F71/128; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y10; Y10S; Y10S148/00; Y10S148/003; Y10S148/005; Y10S148/022; Y10S148/084
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
117 words
A method for annealing ion implanted junctions in indium antimonide wafers, employing a furnace having resealable means for accessing said furnace, comprising the steps of: maintaining said furnace at a predetermined annealing temperature; providing an indium-antimony atmosphere within said furnace, said indium and antimony being provided at their equilibrium vapor pressure at said annealing temperature; inserting said wafer into said furnace and into contact with said atmosphere through said resealable means for accessing said furnace; maintain said wafer in said furnace for a predetermined annealing time; and removing said wafer from said furnace and said atmosphere through said resealable means for accessing at the end of said predetermined time while maintaining said indium-antimony atmosphere within said furnace.
Claim 2
Independent Claim
117 words
A method for annealing ion implanted junctions in indium antimonide wafers, employing a furnace having resealable means for accessing said furnace, comprising the steps of: maintaining said furnace at a predetermined annealing temperature; providing an indium-antimony atmosphere within said furnace, said indium and antimony being provided at their equilibrium vapor pressure at said annealing temperature; inserting said wafer into said furnace and into contact with said atmosphere through said resealable means for accessing said furnace; maintain said wafer in said furnace for a predetermined annealing time; and removing said wafer from said furnace and said atmosphere through said resealable means for accessing at the end of said predetermined time while maintaining said indium-antimony atmosphere within said furnace.
Claim 3
Dependent Claim
23 words
A method for annealing as set out in claim 1, wherein said annealing temperature is in the range 315° C. to 475° C.
Claim 4
Dependent Claim
26 words
An annealing method as set out in claim 1, wherein said predetermined annealing temperature is 400° C. and said predetermined annealing time is one half hour.
Claim 5
Dependent Claim
22 words
A method for annealing as set out in claim 1, further comprising the step of continuously flushing said furnace with hydrogen gas.
Claim 6
Dependent Claim
27 words
A method for annealing as set out in claim 1, further comprising providing hydrogen gas within said furnace at approximately 1/3 pounds per square inch over atmospheric.
Claim 7
Dependent Claim
25 words
A method for annealing as set out in claim 1, wherein said indium antimony atmosphere is provided by a molten solution of indium and antimony.
Claim 8
Dependent Claim
32 words
A method for annealing as set out in claim 6, wherein said wafer is positioned within said furnace at a position adjacent to, and above, said molten solution of indium and antimony.
Claim 9
Dependent Claim
33 words
A method for annealing as set out in claim 6, wherein said wafer is maintained at substantially the same temperature as said molten solution of indium and antimony during said predetermined annealing time.
Claim 10
Independent Claim
128 words
A method for annealing ion implanted junctions of compound semiconductor material wafers employing a furnace having resealable means for accessing said furnace, comprising the steps of: maintaining said furnace at a predetermined annealing temperature; providing a molten solution of said compound semiconductor material within said furnace, said solution providing a source of an atmosphere of the compound semiconductor constituents at their equilibrium vapor pressure at said annealing temperature; inserting said wafer into said furnace and into contact with said atmosphere through said resealable means for accessing said furnace; maintaining said wafer in said furnace for a predetermined annealing time at substantially the same temperature as the molten source; and removing said wafer from said furnace through said resealable means for accessing at the end of said predetermined time.
Claim 11
Independent Claim
128 words
A method for annealing ion implanted junctions of compound semiconductor material wafers employing a furnace having resealable means for accessing said furnace, comprising the steps of: maintaining said furnace at a predetermined annealing temperature; providing a molten solution of said compound semiconductor material within said furnace, said solution providing a source of an atmosphere of the compound semiconductor constituents at their equilibrium vapor pressure at said annealing temperature; inserting said wafer into said furnace and into contact with said atmosphere through said resealable means for accessing said furnace; maintaining said wafer in said furnace for a predetermined annealing time at substantially the same temperature as the molten source; and removing said wafer from said furnace through said resealable means for accessing at the end of said predetermined time.
Claim 12
Dependent Claim
35 words
A method for annealing as set out in claim 9, wherein said wafer is inserted into said furnace through said resealable means for accessing said furnace to a position adjacent to and above said source.
Claim 13
Dependent Claim
29 words
A method for annealing as set out in claim 1, wherein said furnace is maintained at said annealing temperature during said step of removing said wafer from said furnace.
Claim 14
Dependent Claim
29 words
A method for annealing as set out in claim 9, wherein said furnace is maintained at said annealing temperature during said step of removing said wafer from said furnace.
Claim 15
Dependent Claim
117 words
A method for annealing as set out in claim 1, wherein said resealable means for accessing said furnace includes a chamber having a gas inlet port, and a gas outlet port and resealable means connecting said chamber to the interior of said furnace and means for accessing said chamber from outside, wherein said step of removing said wafer from said furnace comprises the steps of removing said wafer from said furnace into said chamber and further comprising the step of removing any residual indium-antimony vapor from said chamber by providing flow of a neutral gas into said chamber through said gas inlet port and exhausting said neutral gas and said residual indium-antimony vapor through said outlet port.
References Cited (Backward Citations)
US3945110A
Cited
US4080721A
Cited
US4128681A
Cited
US4174982A
Cited
US4312681A
Cited
US4401487A
Cited
US4482423A
Cited
US4544417A
Cited
US4795717A
Cited
US4696094A
Cited
US4576652A
Cited
US4713354A
Cited
US4772489A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-05 | 1993-08-07 | 1994-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-05 | 1997-08-07 | 1998-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-05 | 2001-08-07 | 2002-02-06 | $7700.00 | Window Closed / Lapsed |