Method of fabricating a buried-ridge II-VI laser diode
Assignee: 3M Co
•
Filing: 1994-12-23
•
Granted: 1996-07-23
•
Expires: 2014-12-23
Abstract
Abstract A buried-ridge or buried-heterostructure II-VI laser diode. Polycrystalline II-VI semiconductor such as ZnS, ZnSSe, ZnSe or CdS deposited by vacuum evaporation buries the etched ridge.
Inventors
- 👤 Michael A. Haase
- 👤 Jun Qiu
- 👤 Hwa Cheng
- 👤 James M. DePuydt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:55
CPC Classifications
H; H01; H01S; H01S5/00; H01S5/30; H01S5/32; H01S5/323; H10; H10H; H10H20/00; H10H20/80; H10H20/83; H10H20/832; B; B82; B82Y; B82Y20/00; H01S5/04; H01S5/042; H01S5/0421; H01S5/34; H01S5/347; H10D; H10D64/00; H10D64/60; H10D64/62; H10H20/01; H10H20/011; H10H20/012; H10H20/0125; H10H20/81; H10H20/822; H10H20/823; H10H20/8232; H10H20/831; H01S5/20; H01S5/22; H01S5/2205; H01S5/2211; H01S5/223; H01S5/2231; H01S5/305; H01S5/3054; H01S5/3059; H01S5/3068; H01S5/327; H01S5/3403; H10H20/032; H10H20/816; H10H20/8162
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
138 words
A method for fabricating a II-VI compound semiconductor laser diode with a self-aligned buried-ridge waveguide, including: providing a semiconductor substrate of a first conductivity type; growing epitaxial layers of II-VI semiconductor above one another on the substrate, including: growing a first guiding layer of the first conductivity type; growing a second guiding layer of a second conductivity type over the first guiding layer to form a pn junction with the first guiding layer; and growing a quantum well active layer adjacent the pn junction; etching portions of at least one of the layers of semiconductor to form a ridge; forming a II-VI semiconductor burying layer to bury the ridge; etching the burying layer to expose an upper surface of the ridge; and depositing electrodes on opposite sides of the ridge to couple electrical energy to the pn junction.
Claim 2
Independent Claim
138 words
A method for fabricating a II-VI compound semiconductor laser diode with a self-aligned buried-ridge waveguide, including: providing a semiconductor substrate of a first conductivity type; growing epitaxial layers of II-VI semiconductor above one another on the substrate, including: growing a first guiding layer of the first conductivity type; growing a second guiding layer of a second conductivity type over the first guiding layer to form a pn junction with the first guiding layer; and growing a quantum well active layer adjacent the pn junction; etching portions of at least one of the layers of semiconductor to form a ridge; forming a II-VI semiconductor burying layer to bury the ridge; etching the burying layer to expose an upper surface of the ridge; and depositing electrodes on opposite sides of the ridge to couple electrical energy to the pn junction.
Claim 3
Dependent Claim
24 words
The laser diode fabrication method of claim 1 wherein forming the burying layer includes depositing a polycrystalline II-VI semiconductor burying layer over the ridge.
Claim 4
Dependent Claim
24 words
The laser diode fabrication method of claim 2 wherein forming the burying layer includes depositing the polycrystalline II-VI semiconductor burying layer by vacuum evaporation.
Claim 5
Dependent Claim
23 words
The laser diode fabrication method of claim 1 wherein etching the layers to form the ridge includes ion etching with Xe + .
Claim 6
Dependent Claim
50 words
The laser diode fabrication method of claim 1 wherein etching to expose the upper surface of the ridge includes: applying a photoresist mask above the burying layer over portions of the burying layer adjacent the ridge; and ion beam etching to remove portions of the burying layer over the ridge.
Claim 7
Dependent Claim
40 words
The laser diode fabrication method of claim 5 wherein ion beam etching to remove portions of the burying layer includes directing the ion beam toward the laser diode at an angle between about 45° and 90° with respect to normal.
Claim 8
Dependent Claim
41 words
The laser diode fabrication method of claim 5 wherein the ion beam etching to remove portions of the burying layer includes directing the ion beam toward the laser diode at an angle between about 80° and 90° with respect to normal.
Claim 9
Dependent Claim
34 words
The laser diode fabrication method of claim 5 and further including lifting off any remaining burying layer semiconductor and photoresist on the ridge following ion beam etching to remove portions of the burying layer.
Claim 10
Dependent Claim
26 words
The laser diode fabrication method of claim 1 wherein etching portions of the semiconductor layers includes etching through at least portions of the second guiding layer.
Claim 11
Dependent Claim
56 words
The laser diode fabrication method of claim 1 wherein: growing epitaxial layers of II-VI semiconductor further includes: growing a first cladding layer of the first conductivity type between the substrate and the first guiding layer; and growing a second cladding layer of the second conductivity type opposite the second guiding layer from the first guiding layer.
Claim 12
Dependent Claim
24 words
The laser diode fabrication method of claim 10 wherein etching portions of the semiconductor layers includes etching through portions of the second cladding layer.
Claim 13
Dependent Claim
28 words
The laser diode fabrication method of claim 10 wherein etching portions of the semiconductor layers includes etching portions of the second cladding layer and the second guiding layer.
Claim 14
Dependent Claim
29 words
The laser diode fabrication method of claim 10 wherein etching portions of the semiconductor layers includes etching through portions of the second cladding layer and the second guiding layer.
References Cited (Backward Citations)
US4534033A
Cited
US4607369A
Cited
JPS60178684A
Cited
US4575919A
Cited
US4727557A
Cited
JPS637692A
Cited
US4868615A
Cited
US4856013A
Cited
US4735662A
Cited
US4963507A
Cited
US4959106A
Cited
US4926433A
Cited
US4957337A
Cited
US5037709A
Cited
US4894833A
Cited
GB2226698A
Cited
US4995687A
Cited
EP0380106A2
Cited
US5081632A
Cited
US5219785A
Cited
US5140149A
Cited
US5008891A
Cited
US5032879A
Cited
JPH0378279A
Cited
US4995047A
Cited
US5155738A
Cited
US4989214A
Cited
EP0475606A2
Cited
US5157467A
Cited
US5356832A
Cited
US5213998A
Cited
US5291507A
Cited
US5395791A
Cited
WO1994015369A1
Cited
US5363395A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-07-23 | 2000-01-22 | 2000-07-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-07-23 | 2004-01-22 | 2004-07-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-07-23 | 2008-01-22 | 2008-07-23 | $7700.00 | Window Closed / Lapsed |