High density plasma CVD process for gapfill into high aspect ratio features
Assignee: Applied Materials Inc
•
Filing: 2002-10-23
•
Granted: 2004-10-12
•
Expires: 2022-10-23
Abstract
Abstract A method of depositing a film on a substrate. In one embodiment, the method includes depositing a first portion of the film using a high density plasma to partially fill a gap formed between adjacent features formed on the substrate. The film deposition process is then stopped before or shortly after the entry of the gap pinches off and the film is etched to widen entry to the gap using a two step etching process that includes a first physical etch step that forms a plasma from a sputtering agent introduced into the processing chamber and biases the plasma towards the substrate and a subsequent chemical etch step that forms a plasma from a reactive etchant gas introduced into the processing chamber. After the etching sequence is complete, a second portion of the film is deposited over the first portion using a high density plasma to further fill the gap.
Inventors
- 👤 Farhan Ahmad
- 👤 Michael Awdshiew
- 👤 Alok Jain
- 👤 Bikram Kapoor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 01:22
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6923; C; C23; C23C; C23C16/00; C23C16/04; C23C16/045; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/44; C23C16/50; C23C16/505; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/098; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/69215; H10P14/6924
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
131 words
A method of depositing a film on a substrate disposed in a substrate processing chamber, the method comprising: depositing a first portion of the film over the substrate by forming a high density plasma from a first gaseous mixture flown into the process chamber; thereafter, sputter etching part of the deposited first portion of the film by forming a plasma from a sputtering agent introduced into the processing chamber and biasing the plasma towards the substrate; thereafter, chemically etching part of the deposited first portion of the film by forming a plasma from a reactive etchant gas introduced into the processing chamber; and thereafter, depositing a second portion of the film over the first portion by forming a high density plasma from a second gaseous mixture flown into the process chamber.
Claim 2
Independent Claim
131 words
A method of depositing a film on a substrate disposed in a substrate processing chamber, the method comprising: depositing a first portion of the film over the substrate by forming a high density plasma from a first gaseous mixture flown into the process chamber; thereafter, sputter etching part of the deposited first portion of the film by forming a plasma from a sputtering agent introduced into the processing chamber and biasing the plasma towards the substrate; thereafter, chemically etching part of the deposited first portion of the film by forming a plasma from a reactive etchant gas introduced into the processing chamber; and thereafter, depositing a second portion of the film over the first portion by forming a high density plasma from a second gaseous mixture flown into the process chamber.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein the bias power is switched OFF during the chemical etching step.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the first and second gaseous mixtures are silica glass deposition gases.
Claim 5
Dependent Claim
17 words
The method of claim 3 wherein the first and second gaseous mixtures each comprise silane and oxygen.
Claim 6
Dependent Claim
32 words
The method of claim 1 wherein the sputter etching includes a flow of a reactive etchant gas that is less than a flow of the reactive etchant gas in the chemical etch.
Claim 7
Dependent Claim
48 words
The method of claim 5 wherein the reactive etchant flowed into the chamber in the sputter etch and chemical etch is the same gas and wherein the flow rate of the reactive etchant is at least 300 percent higher in the chemical etch than in the sputter etch.
Claim 8
Dependent Claim
28 words
The method of claim 6 wherein the flow rate of the reactive etchant is at least 500 percent higher in the chemical etch than in the sputter etch.
Claim 9
Dependent Claim
13 words
The method of claim 6 wherein the reactive etchant is a fluorine-containing gas.
Claim 10
Dependent Claim
20 words
The method of claim 6 wherein the sputter etch and chemical etch each include a flow of an oxygen-containing gas.
Claim 11
Independent Claim
172 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the substrate having a trench formed between adjacent raised surfaces, the method comprising, in order: depositing a first portion of the silica glass film over the substrate and within the trench by forming a high density plasma process that has simultaneous deposition and sputtering components from a first deposition gas comprising a silicon source and an oxygen source; stopping deposition of the silica glass film and sputter etching the first portion of the film by biasing a high density plasma formed from a sputtering agent introduced into the processing chamber towards the substrate; thereafter, chemically etching the first portion of the film with reactive species formed from an etchant gas; and thereafter, depositing a second portion of the silica glass film over the substrate and within the trench by forming a high density plasma process that has simultaneous deposition and sputtering components from a second deposition gas comprising a silicon source and an oxygen source.
Claim 12
Independent Claim
172 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the substrate having a trench formed between adjacent raised surfaces, the method comprising, in order: depositing a first portion of the silica glass film over the substrate and within the trench by forming a high density plasma process that has simultaneous deposition and sputtering components from a first deposition gas comprising a silicon source and an oxygen source; stopping deposition of the silica glass film and sputter etching the first portion of the film by biasing a high density plasma formed from a sputtering agent introduced into the processing chamber towards the substrate; thereafter, chemically etching the first portion of the film with reactive species formed from an etchant gas; and thereafter, depositing a second portion of the silica glass film over the substrate and within the trench by forming a high density plasma process that has simultaneous deposition and sputtering components from a second deposition gas comprising a silicon source and an oxygen source.
Claim 13
Dependent Claim
27 words
The method of claim 10 wherein the high density plasma is continuously maintained between depositing a first position of the silica glass film and the sputter etching.
Claim 14
Dependent Claim
32 words
The method of claim 11 wherein the reactive species in the chemically etching the first portion of the film are dissociated remotely from a fluorine etchant gas and transported into the chamber.
Claim 15
Dependent Claim
29 words
The method of claim 11 wherein the reactive species in the chemically etching the first portion of the film are generated within the chamber by a high density plasma.
Claim 16
Dependent Claim
33 words
The method of claim 13 wherein the high density plasma is continuously maintained between depositing a first portion of the silica glass film and depositing a second portion of the silica glass film.
Claim 17
Dependent Claim
48 words
The method of claim 14 wherein the reactive etchant flowed into the chamber in the sputter etch and chemical etch is the same gas and wherein the flow rate of the reactive etchant is at least 300 percent higher in the chemical etch than in the sputter etch.
Claim 18
Dependent Claim
20 words
The method of claim 15 wherein the sputter etch and chemical etch each include a flow of an oxygen-containing gas.
Claim 19
Dependent Claim
38 words
The method of claim 16 further comprising, after chemically etching the first portion of the film, exposing the first portion of the film to a passivation gas consisting of an oxygen source with or without an inert gas.
Claim 20
Dependent Claim
21 words
The method of claim 16 wherein the trench is part of a shallow trench isolation structure formed on a silicon substrate.
Claim 21
Dependent Claim
21 words
The method of claim 16 wherein the silicon source in the first and second deposition gases comprises monosilane (SiH 4 ).
Claim 22
Dependent Claim
22 words
The method of claim 19 wherein the oxygen source in the first and second deposition gases comprises molecular oxygen (O 2 ).
Claim 23
Dependent Claim
22 words
The method of claim 20 wherein the first and second deposition gases each further comprise an inert gas as a sputtering component.
Claim 24
Dependent Claim
23 words
The method of claim 16 wherein the plasma is not biased towards the substrate while chemically etching the first portion of the film.
Claim 25
Dependent Claim
34 words
The method of claim 10 wherein the sputter etching etches at least two and a half times more of the silica glass film over the raised surfaces than at a bottom of the trench.
Claim 26
Dependent Claim
31 words
The method of claim 10 wherein the sputter etching etches at least five times more of the silica glass film over the raised surfaces than at a bottom of the trench.
Claim 27
Dependent Claim
31 words
The method of claim 10 wherein the sputter etching etches at least ten times more of the silica glass film over the raised surfaces than at a bottom of the trench.
Claim 28
Independent Claim
258 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the substrate having a trench formed between adjacent raised surfaces, the method comprising: forming a high density plasma within the substrate processing chamber to heat the substrate to a temperature of at least 400° C. prior to depositing the silica glass film on the substrate; maintaining the high density plasma while (i) flowing a first process gas comprising a silicon source and an oxygen source into the processing chamber to deposit a first portion of the silica glass film over the substrate and in the trench using a deposition process that has simultaneous deposition and sputtering components, (ii) flowing a sputtering gas comprising an inert gas, an oxygen source and a fluorine etchant into the process chamber while biasing the plasma towards the substrate to sputter etch the first portion of the silica glass film; (iii) switching off bias power that biases the plasma towards the substrate and flowing a fluorine etchant and oxygen source into the chamber in order to chemically etch the first portion of the silica glass film, wherein a flow rate of the fluorine etchant is at least 300 percent higher than a flow rate of the fluorine etchant in the sputter etch; and (iv) flowing a second process gas comprising a silicon source and an oxygen source into the processing chamber to deposit a second portion of the silica glass film over the first portion using a deposition process that has simultaneous deposition and sputtering components.
Claim 29
Independent Claim
258 words
A method of depositing a silica glass film on a substrate disposed in a substrate processing chamber, the substrate having a trench formed between adjacent raised surfaces, the method comprising: forming a high density plasma within the substrate processing chamber to heat the substrate to a temperature of at least 400° C. prior to depositing the silica glass film on the substrate; maintaining the high density plasma while (i) flowing a first process gas comprising a silicon source and an oxygen source into the processing chamber to deposit a first portion of the silica glass film over the substrate and in the trench using a deposition process that has simultaneous deposition and sputtering components, (ii) flowing a sputtering gas comprising an inert gas, an oxygen source and a fluorine etchant into the process chamber while biasing the plasma towards the substrate to sputter etch the first portion of the silica glass film; (iii) switching off bias power that biases the plasma towards the substrate and flowing a fluorine etchant and oxygen source into the chamber in order to chemically etch the first portion of the silica glass film, wherein a flow rate of the fluorine etchant is at least 300 percent higher than a flow rate of the fluorine etchant in the sputter etch; and (iv) flowing a second process gas comprising a silicon source and an oxygen source into the processing chamber to deposit a second portion of the silica glass film over the first portion using a deposition process that has simultaneous deposition and sputtering components.
Claim 30
Dependent Claim
20 words
The method of claim 26 wherein the sputter etch and chemical etch each include a flow of an oxygen-containing gas.
Claim 31
Dependent Claim
21 words
The method of claim 27 wherein the trench is part of a shallow trench isolation structure formed on a silicon substrate.
Claim 32
Dependent Claim
34 words
The method of claim 26 wherein the sputter etching etches at least two and a half times more of the silica glass film over the raised surfaces than at a bottom of the trench.
Claim 33
Dependent Claim
31 words
The method of claim 26 wherein the sputter etching etches at least five times more of the silica glass film over the raised surfaces than at a bottom of the trench.
Claim 34
Dependent Claim
31 words
The method of claim 26 wherein the sputter etching etches at least ten times more of the silica glass film over the raised surfaces than at a bottom of the trench.
References Cited (Backward Citations)
US4690746A
Cited
US6167834B1
Cited
US4872947A
Cited
US4892753A
Cited
US4960488A
Cited
US5000113A
Cited
US5362526A
Cited
US5156881A
Cited
US5275977A
Cited
US5089442A
Cited
US5319247A
Cited
US5279865A
Cited
US5271972A
Cited
US5624582A
Cited
US5302233A
Cited
US5416048A
Cited
US5468342A
Cited
US5571576A
Cited
US6039851A
Cited
US5719085A
Cited
US5599740A
Cited
US5915190A
Cited
US5679606A
Cited
US6191026B1
Cited
US5872052A
Cited
US5858876A
Cited
US6182602B1
Cited
US6170428B1
Cited
US5953635A
Cited
US5913140A
Cited
US5990000A
Cited
US6190233B1
Cited
US6059643A
Cited
US5850105A
Cited
US5968610A
Cited
US6189483B1
Cited
US6136685A
Cited
US5937323A
Cited
US5872058A
Cited
US6194038B1
Cited
US6395150B1
Cited
US6030881A
Cited
US6037018A
Cited
US6203863B1
Cited
US6197705B1
Cited
US6335288B1
Cited
US6596654B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2007-10-12 | 2008-04-12 | 2008-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2011-10-12 | 2012-04-12 | 2012-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2015-10-12 | 2016-04-12 | 2016-10-12 | $7700.00 | Window Closed / Lapsed |