Method of growing nitride semiconductors, nitride semiconductor substrate and nitride semiconductor device
Assignee: Nichia Corp
•
Filing: 1998-04-09
•
Granted: 2000-11-28
•
Expires: 2018-04-09
Abstract
Abstract A method of growing a nitride semiconductor crystal which has very few crystal defects and can be used as a substrate is disclosed. This invention includes the step of forming a first selective growth mask on a support member including a dissimilar substrate having a major surface and made of a material different from a nitride semiconductor, the first selective growth mask having a plurality of first windows for selectively exposing the upper surface of the support member, and the step of growing nitride semiconductor portions from the upper surface, of the support member, which is exposed from the windows, by using a gaseous Group 3 element source and a gaseous nitrogen source, until the nitride semiconductor portions grown in the adjacent windows combine with each other on the upper surface of the selective growth mask.
Inventors
- 👤 Hiroyuki Kiyoku
- 👤 Shuji Nakamura
- 👤 Tokuya Kozaki
- 👤 Naruhito Iwasa
- 👤 Kazuyuki Chocho
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:12
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/02; B; B82; B82Y; B82Y20/00; C23; C23C; C23C16/00; C23C16/04; C23C16/042; C23C16/22; C23C16/30; C23C16/301; C23C16/303; C30B29/00; C30B29/10; C30B29/40; C30B29/403; C30B29/406; H; H01; H01S; H01S5/00; H01S5/30; H01S5/32; H01S5/3202; H01S5/32025; H10; H10H; H10H20/00; H10H20/01; H10H20/011; H10H20/013; H10H20/0133; H10H20/01335; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/27; H10P14/271; H10P14/272; H10P14/276; H10P14/29; H10P14/2901; H10P14/2921; H10P14/2926; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3216; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3416; H10P14/3438; H10P14/3441; H10P14/3442; H01S2301/00; H01S2301/17; H01S2301/173; H01S2304/00; H01S2304/12; H01S5/02; H01S5/0206; H01S5/0213; H01S5/04; H01S5/042; H01S5/0421; H01S5/0422; H01S5/20; H01S5/22; H01S5/2201; H01S5/3211; H01S5/3216; H01S5/34; H01S5/343; H01S5/34333; H10H20/80; H10H20/81; H10H20/817; H10P14/3242; H10P14/3244; H10P14/3248
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
121 words
A nitride semiconductor growth method comprising the steps of: (a) forming a nitride semiconductor layer on a support member including a dissimilar substrate made of a material different from a nitride semiconductor and having a major surface; (b) forming a plurality of recess portions having bottom surfaces substantially parallel to an upper surface of the support member in said nitride semiconductor layer; (c) selectively forming a first growth control mask on a top surface of the nitride semiconductor layer to selectively expose the nitride semiconductor layer from side surfaces of the recess portions; and (d) growing a nitride semiconductor from an exposed surface of the nitride semiconductor layer by using a gaseous Group 3 element source and a gaseous nitrogen source.
Claim 2
Dependent Claim
121 words
A nitride semiconductor growth method comprising the steps of: (a) forming a nitride semiconductor layer on a support member including a dissimilar substrate made of a material different from a nitride semiconductor and having a major surface; (b) forming a plurality of recess portions having bottom surfaces substantially parallel to an upper surface of the support member in said nitride semiconductor layer; (c) selectively forming a first growth control mask on a top surface of the nitride semiconductor layer to selectively expose the nitride semiconductor layer from side surfaces of the recess portions; and (d) growing a nitride semiconductor from an exposed surface of the nitride semiconductor layer by using a gaseous Group 3 element source and a gaseous nitrogen source.
Claim 3
Dependent Claim
26 words
A method according to claim 1, wherein the recess portions are formed by a plurality of individual grooves spaced apart from each other and extending parallel.
Claim 4
Dependent Claim
41 words
A method according to claim 2, wherein the plurality of individual grooves have a plurality of individual walls formed therebetween, and said first growth control mask is made up of individual stripes formed on top surfaces of the respective individual walls.
Claim 5
Dependent Claim
27 words
A method according to claim 3, wherein a total surface area of said first growth control mask is larger than that of bottom surfaces of the grooves.
Claim 6
Dependent Claim
35 words
A method according to claim 4, wherein a ratio of a width of each of the individual stripes to a width of each of the grooves is more than 1 and not more than 20.
Claim 7
Dependent Claim
20 words
A method according to claim 5, wherein each of the grooves has a depth of 500 angstroms to 5 μm.
Claim 8
Dependent Claim
38 words
A method according to claim 3, wherein the dissimilar substrate is a sapphire substrate having a major surface forming a (0001) plane, and the respective individual stripes extend in a direction perpendicular to a (1120) plane of sapphire.
Claim 9
Dependent Claim
38 words
A method according to claim 3, wherein the dissimilar substrate is a sapphire substrate having a major surface forming a (1120) plane, and the respective individual stripes extend in a direction perpendicular to the (1120) plane of sapphire.
Claim 10
Dependent Claim
37 words
A method according to claim 3, wherein the dissimilar substrate is a spinnel substrate having a major surface forming a (111) plane, and the respective stripes extend in a direction perpendicular to the (110) plane of spinnel.
Claim 11
Dependent Claim
29 words
A method according to claim 1, wherein the step (d) further comprises doping the nitride semiconductor portion with an n-type impurity during growth of the first nitride semiconductor portion.
Claim 12
Dependent Claim
27 words
A method according to claim 10, wherein the n-type impurity is added such that a doping concentration decreases with an increase in distance from the dissimilar substrate.
Claim 13
Dependent Claim
28 words
A method according to claim 1, wherein the gaseous nitrogen source and the gaseous Group 3 element source are supplied at a molar ratio not more than 2,000.
Claim 14
Dependent Claim
29 words
A method according to claim 12, wherein the gaseous nitrogen source and the gaseous Group 3 element source are supplied at a molar ratio of not less than 10.
Claim 15
Dependent Claim
26 words
A method according to claim 12, wherein growth of the nitride semiconductor portion in the step (d) is performed by a metal organic vapor-phase epitaxial method.
Claim 16
Dependent Claim
24 words
A method according to claim 14, wherein growth of the nitride semiconductor portion is performed under a reduced pressure of 50 to 400 Torr.
Claim 17
Dependent Claim
40 words
A method according to claim 1, wherein the step (c) further comprises forming a second growth control mask on the bottom surfaces of the recess portions to selectively expose the nitride semiconductor layer from side surfaces of the recess portions.
Claim 18
Dependent Claim
26 words
A method according to claim 16, wherein the recess portions are formed by a plurality of individual grooves spaced apart from each other and extending parallel.
Claim 19
Dependent Claim
41 words
A method according to claim 17, wherein the plurality of individual grooves have a plurality of individual walls formed therebetween, and said first growth control mask is made up of individual stripes formed on top surfaces of the respective individual walls.
Claim 20
Dependent Claim
34 words
A method according to claim 18, wherein a portion of the nitride semiconductor layer that is exposed from a side surface of the recess portion has a thickness of not less than 100 angstroms.
Claim 21
Dependent Claim
33 words
A method according to claim 18, wherein a portion of the nitride semiconductor layer that is exposed from a side surface of the recess portion has a thickness of 1 to 10 μm.
Claim 22
Dependent Claim
38 words
A method according to claim 18, wherein the dissimilar substrate is a sapphire substrate having a major surface forming a (0001) plane, and the respective individual stripes extend in a direction perpendicular to a (1120) plane of sapphire.
Claim 23
Dependent Claim
38 words
A method according to claim 18, wherein the dissimilar substrate is a sapphire substrate having a major surface forming a (1120) plane, and the respective individual stripes extend in a direction perpendicular to the (1120) plane of sapphire.
Claim 24
Dependent Claim
37 words
A method according to claim 18, wherein the dissimilar substrate is a spinnel substrate having a major surface forming a (111) plane, and the respective stripes extend in a direction perpendicular to the (110) plane of spinnel.
Claim 25
Dependent Claim
29 words
A method according to claim 16, wherein the step (d) further comprises doping the nitride semiconductor portion with an n-type impurity during growth of the first nitride semiconductor portion.
Claim 26
Dependent Claim
27 words
A method according to claim 24, wherein the n-type impurity is added such that a doping concentration decreases with an increase in distance from the dissimilar substrate.
Claim 27
Dependent Claim
29 words
A method according to claim 16, wherein the gaseous nitrogen source and the gaseous Group 3 element source are supplied at a molar ratio of not more than 2,000.
Claim 28
Dependent Claim
29 words
A method according to claim 26, wherein the gaseous nitrogen source and the gaseous Group 3 element source are supplied at a molar ratio of not less than 10.
Claim 29
Dependent Claim
24 words
A method according to claim 27, wherein growth of the nitride semiconductor portion is performed under a reduced pressure of 50 to 400 Torr.
Claim 30
Dependent Claim
26 words
A method according to claim 26, wherein growth of the nitride semiconductor portion in the step (d) is performed by a metal organic vapor-phase epitaxial method.
Claim 31
Dependent Claim
84 words
A nitride semiconductor growth method characterized by comprising the steps of forming a nitride semiconductor on a support member including a dissimilar substrate, using said nitride semiconductor as a seed crystal to grow a new nitride semiconductor in substantially only a lateral direction while suppressing growth of the nitride semiconductor in a vertical direction, and then growing the nitride semiconductor in both the vertical and lateral directions, thereby obtaining an integral nitride semiconductor crystal on a substantially entire upper surface of the support member.
Claim 32
Dependent Claim
84 words
A nitride semiconductor growth method characterized by comprising the steps of forming a nitride semiconductor on a support member including a dissimilar substrate, using said nitride semiconductor as a seed crystal to grow a new nitride semiconductor in substantially only a lateral direction while suppressing growth of the nitride semiconductor in a vertical direction, and then growing the nitride semiconductor in both the vertical and lateral directions, thereby obtaining an integral nitride semiconductor crystal on a substantially entire upper surface of the support member.
References Cited (Backward Citations)
US4482422A
Cited
US4578142A
Cited
US4908074A
Cited
US5364815A
Cited
US5247533A
Cited
US5290393A
Cited
JPH0555631A
Cited
US5239188A
Cited
JPH05343741A
Cited
US5709745A
Cited
JPH07201745A
Cited
US5679152A
Cited
JPH07273367A
Cited
JPH0864791A
Cited
US5727008A
Cited
US5789265A
Cited
US5764673A
Cited
US5773369A
Cited
US5766695A
Cited
US5880485A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-11-28 | 2004-05-29 | 2004-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-11-28 | 2008-05-29 | 2008-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-11-28 | 2012-05-29 | 2012-11-28 | $7700.00 | Window Closed / Lapsed |