High deposition rate recipe for low dielectric constant films
Assignee: Applied Materials Inc
•
Filing: 1997-06-03
•
Granted: 2000-10-24
•
Expires: 2017-06-03
Abstract
Abstract An insulating film with a low dielectric constant is more quickly formed on a substrate by reducing the co-etch rate as the film is deposited. The process gas is formed into a plasma from silicon-containing and fluorine-containing gases. The plasma is biased with an RF field to enhance deposition of the film. Deposition and etching occur simultaneously. The relative rate of deposition to etching is increased in the latter portion of the deposition process by decreasing the bias RF power, which decreases the surface temperature of the substrate and decreases sputtering and etching activities. Processing time is reduced compared to processes with fixed RF power levels. Film stability, retention of water by the film, and corrosion of structures on the substrate are all improved. The film has a relatively uniform and low dielectric constant and may fill trenches with aspect ratios of at least 4:1 and gaps less than 0.5 mu m.
Inventors
- 👤 Pravin Narwankar
- 👤 Laxman Murugesh
- 👤 Turgut Sahin
- 👤 Maciek Orczyk
- 👤 Jianmin Qiao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 01:50
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6924; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/44; C23C16/50; C23C16/505; C23C16/52; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/66; H10P14/668; H10P14/6681; H10P14/6682; H10P14/69215
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
173 words
A method for forming a film on a substrate having a gap, the method comprising the steps of: (a) flowing a silicon-containing gas, a halogen-containing gas, and oxygen into a chamber at a first flow rate; (b) creating a plasma in said chamber with an RF source generator; (c) applying RF bias power at a first bias power level to said plasma with an RF bias generator; (d) depositing a first portion of the film on the substrate at a first deposition-to-etch ratio, said first portion of the film partially filling the gap in the substrate; (e) increasing said first flow rate of said silicon-containing gas and said halogen-containing gas and said oxygen to a second flow rate; (f) reducing said RF bias power to a second bias power level; and (g) depositing a second portion of the film on the substrate at a second deposition-to-etch ratio wherein said second deposition-to-etch ratio is greater than said first deposition-to-etch ratio, said first and second portions of the film filling the gap in the substrate.
Claim 2
Independent Claim
173 words
A method for forming a film on a substrate having a gap, the method comprising the steps of: (a) flowing a silicon-containing gas, a halogen-containing gas, and oxygen into a chamber at a first flow rate; (b) creating a plasma in said chamber with an RF source generator; (c) applying RF bias power at a first bias power level to said plasma with an RF bias generator; (d) depositing a first portion of the film on the substrate at a first deposition-to-etch ratio, said first portion of the film partially filling the gap in the substrate; (e) increasing said first flow rate of said silicon-containing gas and said halogen-containing gas and said oxygen to a second flow rate; (f) reducing said RF bias power to a second bias power level; and (g) depositing a second portion of the film on the substrate at a second deposition-to-etch ratio wherein said second deposition-to-etch ratio is greater than said first deposition-to-etch ratio, said first and second portions of the film filling the gap in the substrate.
Claim 3
Dependent Claim
56 words
The method of claim 1 wherein said RF source generator operates at a source frequency of about 2 MHz and a source power level of between about 12-16 W/cm 2 , and said RF bias generator operates at a frequency of about 13.56 MHz and a bias power level of between about 7-13 W/cm 2 .
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said silicon-containing gas is SiH 4 and said halogen-containing gas is SiF 4 .
Claim 5
Dependent Claim
31 words
The method of claim 1 wherein the step (f) of reducing said RF bias power to the second bias power level is performed while maintaining the RF source power substantially constant.
Claim 6
Dependent Claim
23 words
The method of claim 1 wherein the RF source generator is operated at a frequency of nominally 2 MHz to create the plasma.
Claim 7
Dependent Claim
24 words
The method of claim 1 wherein the RF bias generator is operated at a frequency of 13.56 MHz to apply the RF bias power.
Claim 8
Dependent Claim
55 words
The method of claim 1 wherein the RF bias power is reduced to the second bias power level to decrease an etch rate of the film by decreasing activity of etchant species produced from the gases in the chamber and to increase a deposition rate of the film by reducing surface temperature of the substrate.
Claim 9
Dependent Claim
14 words
The method of claim 1 wherein said process gas further comprises a sputtering gas.
Claim 10
Dependent Claim
11 words
The method of claim 8 wherein the sputtering gas comprises argon.
Claim 11
Independent Claim
126 words
A method for forming a film on a substrate having a gap, the method comprising the steps of: (a) flowing a process gas comprising silicon, a halogen, and oxygen into a chamber, wherein the halogen and the silicon are in a first ratio, the process gas deriving from a silicon source, a halogen source, and an oxygen source; (b) depositing a first portion of the film over the substrate, said first portion of the film partially filling the gap in the substrate; (c) reducing the first ratio of the halogen to the silicon to a second ratio of the halogen to the silicon; and (d) depositing a second portion of the film, said first and second portions of the film filling the gap in the substrate.
Claim 12
Independent Claim
126 words
A method for forming a film on a substrate having a gap, the method comprising the steps of: (a) flowing a process gas comprising silicon, a halogen, and oxygen into a chamber, wherein the halogen and the silicon are in a first ratio, the process gas deriving from a silicon source, a halogen source, and an oxygen source; (b) depositing a first portion of the film over the substrate, said first portion of the film partially filling the gap in the substrate; (c) reducing the first ratio of the halogen to the silicon to a second ratio of the halogen to the silicon; and (d) depositing a second portion of the film, said first and second portions of the film filling the gap in the substrate.
Claim 13
Dependent Claim
17 words
The method of claim 10 further comprising the step of forming a plasma from the process gas.
Claim 14
Dependent Claim
18 words
The method of claim 10 wherein said silicon source comprises SiH 4 and said halogen source comprises fluorine.
Claim 15
Dependent Claim
47 words
The method of claim 10 wherein said silicon source comprises SiH 4 , said halogen source comprises SiF 4 , said first ratio is between about 0.6-0.8 SiF 4 to SiH 4 , and said second ratio is between about 0.4-0.6 SiF 4 to SiH 4 .
Claim 16
Independent Claim
137 words
A method suitable for depositing material in high aspect ratio trenches on a substrate, the method comprising: (a) flowing a process gas into the process zone, wherein the process gas introduced into the process zone comprises a deposition component and an etchant component; (b) establishing a plasma with power from an RF source generator; (c) applying an RF bias power at a first power level to the plasma; (d) maintaining the process gas and plasma at process conditions suitable for depositing material on the substrate while simultaneously etching a first portion of the material to form a second portion of the material on the substrate to partially fill the trenches; and (e) reducing the RF bias power to a second power level to form a third portion of the material on the substrate to fill the trenches.
Claim 17
Independent Claim
137 words
A method suitable for depositing material in high aspect ratio trenches on a substrate, the method comprising: (a) flowing a process gas into the process zone, wherein the process gas introduced into the process zone comprises a deposition component and an etchant component; (b) establishing a plasma with power from an RF source generator; (c) applying an RF bias power at a first power level to the plasma; (d) maintaining the process gas and plasma at process conditions suitable for depositing material on the substrate while simultaneously etching a first portion of the material to form a second portion of the material on the substrate to partially fill the trenches; and (e) reducing the RF bias power to a second power level to form a third portion of the material on the substrate to fill the trenches.
References Cited (Backward Citations)
US4468413A
Cited
JPS61276977A
Cited
US4872947A
Cited
US5000113A
Cited
US5385763A
Cited
US5156881A
Cited
US4851370A
Cited
US4894352A
Cited
US5013691A
Cited
US5275977A
Cited
US5089442A
Cited
US5319247A
Cited
US5474589A
Cited
US5314724A
Cited
JPH04239750A
Cited
US5215787A
Cited
JPH04341568A
Cited
US5413967A
Cited
WO1992020833A1
Cited
US5288518A
Cited
US5334552A
Cited
US5420075A
Cited
US5399529A
Cited
US5429995A
Cited
US5271972A
Cited
US5563105A
Cited
US5571576A
Cited
US5648175A
Cited
US5661093A
Cited
US5937323A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-10-24 | 2004-04-24 | 2004-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-10-24 | 2008-04-24 | 2008-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-10-24 | 2012-04-24 | 2012-10-24 | $7700.00 | Window Closed / Lapsed |