Patent US5795495A successfully refreshed from Google Patents.
US5795495A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of chemical mechanical polishing for dielectric layers
Assignee: Micron Technology Inc
•
Filing: 1995-09-08
•
Granted: 1998-08-18
•
Expires: 2015-09-08
Abstract
Abstract A method of forming a planarized dielectric layer includes depositing a dielectric material on a substrate with a dopant concentration that decreases with depth and then chemically mechanically polishing the doped dielectric material. During the chemical mechanical polishing process the polish rate will be relatively fast initially but will slow down as the lighter doped material is contacted. Global planarity and polish selectivity are improved because the dopant gradient will automatically slow down the polish rate in areas where the lighter doped material is contacted. The high points of the dielectric material will thus polish faster than the low points. In an alternate embodiment of the invention, an underlying layer is deposited below a dopant graded dielectric layer having a predetermined dopant concentration that decreases with depth. The underlying layer may be undoped or uniformly doped. During the chemical mechanical planarization process, the dielectric layer with the graded profile is substantially removed. This insures that subsequent process steps will not be affected by a planarized dielectric layer having a non-uniform dopant concentration.
Inventors
- 👤 Scott G. Meikle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 05:28
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/06; H10P95/062
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
133 words
A chemical mechanical polishing method for forming a planarized dielectric layer on a substrate, comprising the steps of: depositing an undoped dielectric layer of silicon nitride on the substrate; depositing a doped dielectric layer on the undoped silicon nitride layer; controlling a dopant concentration of the doped dielectric layer to produce a dopant concentration profile with the dopant concentration decreasing with increasing depth into the doped dielectric layer and then leveling to a substantially uniform concentration; polishing the doped dielectric layer using a chemical mechanical polishing process; controlling a polish rate of the chemical mechanical polishing process using the dopant concentration such that the polish rate decreases with increasing depth into the doped dielectric layer; and end pointing the polishing process at a planar endpoint located within the undoped layer of silicon nitride.
Claim 2
Dependent Claim
133 words
A chemical mechanical polishing method for forming a planarized dielectric layer on a substrate, comprising the steps of: depositing an undoped dielectric layer of silicon nitride on the substrate; depositing a doped dielectric layer on the undoped silicon nitride layer; controlling a dopant concentration of the doped dielectric layer to produce a dopant concentration profile with the dopant concentration decreasing with increasing depth into the doped dielectric layer and then leveling to a substantially uniform concentration; polishing the doped dielectric layer using a chemical mechanical polishing process; controlling a polish rate of the chemical mechanical polishing process using the dopant concentration such that the polish rate decreases with increasing depth into the doped dielectric layer; and end pointing the polishing process at a planar endpoint located within the undoped layer of silicon nitride.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein the depositing step of the undoped silicon nitride layer comprises forming the silicon nitride layer at a constant thickness across the substrate.
Claim 4
Dependent Claim
33 words
The method of claim 1 wherein the endpointing step comprises stopping the polishing process within the undoped layer of silicon nitride at a point near the original surface of the silicon nitride layer.
Claim 5
Dependent Claim
32 words
The method of claim 1, further comprising the step of removing a portion of the silicon nitride layer between conducting lines to form a gap between conducting lines extending to the substrate.
Claim 6
Dependent Claim
201 words
A chemical mechanical polishing method for forming a planarized dielectric layer over an array of spaced apart conducting lines on a substrate, comprising the steps of: depositing a first dielectric layer on the conducting lines and on the substrate, the first layer having a relatively low polishing rate and a substantially constant thickness across the conducting lines and the substrate, wherein the first layer forms indentations between top surfaces of adjacent conducting lines; forming gaps in the indentations of the first layer that extend through the first layer to an underlying surface; depositing a second dielectric layer on the first layer so that the second layer fills the gaps and the indentations, and so that the second layer extends above the first layer, the second layer having a higher polishing rate than the first layer and being selectively etchable from the first layer; polishing the second layer using a chemical mechanical polishing process; and endpointing the polishing process at a planar endpoint when the first layer is exposed across the top surfaces of the conducting lines to form a self-aligned pattern between the conducting lines from material of the second layer that extends from the planarized surface to the underlying surface.
Claim 7
Dependent Claim
201 words
A chemical mechanical polishing method for forming a planarized dielectric layer over an array of spaced apart conducting lines on a substrate, comprising the steps of: depositing a first dielectric layer on the conducting lines and on the substrate, the first layer having a relatively low polishing rate and a substantially constant thickness across the conducting lines and the substrate, wherein the first layer forms indentations between top surfaces of adjacent conducting lines; forming gaps in the indentations of the first layer that extend through the first layer to an underlying surface; depositing a second dielectric layer on the first layer so that the second layer fills the gaps and the indentations, and so that the second layer extends above the first layer, the second layer having a higher polishing rate than the first layer and being selectively etchable from the first layer; polishing the second layer using a chemical mechanical polishing process; and endpointing the polishing process at a planar endpoint when the first layer is exposed across the top surfaces of the conducting lines to form a self-aligned pattern between the conducting lines from material of the second layer that extends from the planarized surface to the underlying surface.
Claim 8
Dependent Claim
24 words
The method of claim 5 wherein the first layer is made from silicon nitride and the second layer is made from undoped silicon dioxide.
Claim 9
Dependent Claim
24 words
The method of claim 5 wherein the first layer is made from silicon nitride and the second layer is made from doped silicon dioxide.
Claim 10
Dependent Claim
195 words
A chemical mechanical polishing method for forming a planarized dielectric layer over an array of spaced-apart conducting lines on a substrate, comprising the steps of: depositing a silicon nitride layer on the conducting lines and on the substrate, the silicon nitride layer having a substantially constant thickness across the conducting lines and the substrate, wherein the silicon nitride layer forms indentations between top surfaces of adjacent conducting lines; depositing a doped silicon dioxide layer on the silicon nitride layer so that the doped silicon oxide layer fills the indentations and extends above the silicon nitride layer, the doped silicon oxide layer having a higher polishing rate than the silicon nitride layer and being selectively etchable from the silicon nitride layer; controlling a dopant concentration of the second layer to produce a dopant concentration profile within the second layer that decreases with increasing depth into the second layer and then levels to a substantially uniform concentration; controlling a polish rate of the chemical mechanical polishing process using the dopant concentration of the second layer such that the polish rate decreases with increasing depth into the second layer; and endpointing the polishing process at a planar endpoint.
Claim 11
Dependent Claim
195 words
A chemical mechanical polishing method for forming a planarized dielectric layer over an array of spaced-apart conducting lines on a substrate, comprising the steps of: depositing a silicon nitride layer on the conducting lines and on the substrate, the silicon nitride layer having a substantially constant thickness across the conducting lines and the substrate, wherein the silicon nitride layer forms indentations between top surfaces of adjacent conducting lines; depositing a doped silicon dioxide layer on the silicon nitride layer so that the doped silicon oxide layer fills the indentations and extends above the silicon nitride layer, the doped silicon oxide layer having a higher polishing rate than the silicon nitride layer and being selectively etchable from the silicon nitride layer; controlling a dopant concentration of the second layer to produce a dopant concentration profile within the second layer that decreases with increasing depth into the second layer and then levels to a substantially uniform concentration; controlling a polish rate of the chemical mechanical polishing process using the dopant concentration of the second layer such that the polish rate decreases with increasing depth into the second layer; and endpointing the polishing process at a planar endpoint.
Claim 12
Dependent Claim
40 words
The method of claim 5 wherein the first layer is undoped silicon nitride and the endpointing step comprising stopping the polishing process when the undoped layer of silicon nitride is uniformly exposed across the top surfaces of the conducting lines.
Claim 13
Dependent Claim
43 words
The method of claim 5 wherein the second dielectric layer is made from a material that has a polishing rate that is from 200% to 1500% greater than that of a first layer of silicon nitride under similar pressure, temperature, and slurry conditions.
Claim 14
Dependent Claim
29 words
The method of claim 9 wherein the second layer is silicon oxide that is doped with a material selected from the group consisting of boron, phosphorus, arsenic, and germanium.
Claim 15
Dependent Claim
34 words
The method of claim 5, further comprising the step of removing a portion of the first dielectric layer between the conducting lines to form a gap between the conducting lines extending to the substrate.
References Cited (Backward Citations)
US3841031A
Cited
US4030943A
Cited
USRE34400E
Cited
US4509249A
Cited
US4545852A
Cited
US4680893A
Cited
JPS63266830A
Cited
US4980306A
Cited
US5104482A
Cited
US5200351A
Cited
US5142828A
Cited
US5036015A
Cited
US5064683A
Cited
US5137597A
Cited
US5230184A
Cited
US5169491A
Cited
US5399233A
Cited
US5300463A
Cited
US5314843A
Cited
US5312512A
Cited
US5272117A
Cited
EP0602607A1
Cited
US5302233A
Cited
US5424240A
Cited
US5356513A
Cited
US5502007A
Cited
US5332467A
Cited
US5387540A
Cited
US5629242A
Cited
US5492858A
Cited
US5516729A
Cited
US5494854A
Cited
US5560802A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-17 | 2002-02-16 | 2002-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-17 | 2006-02-16 | 2006-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-17 | 2010-02-16 | 2010-08-18 | $7700.00 | Window Closed / Lapsed |