Plasma curing process for porous silica thin film
Assignee: Axcelis Technologies Inc
•
Filing: 2001-03-19
•
Granted: 2003-05-06
•
Expires: 2021-03-19
Abstract
Abstract Low dielectric constant films with improved elastic modulus. The method of making such coatings involves providing a porous network coating produced from a resin containing at least 2 Si-H groups and plasma curing the coating to convert the coating into porous silica. Plasma curing of the network coating yields a coating with improved modulus, but with a higher dielectric constant. The costing is plasma cured for between about 15 and about 120 seconds at a temperature less than or about 350° C. The plasma cured coating can optionally be annealed. Rapid thermal processing (RTP) of the plasma cured coating reduces the dielectric constant of the coating while maintaining an improved elastic modulus as compared to the plasma cured porous network coating. The annealing temperature is typically loss than or about 475° C., and the annealing time is typically no more than or about 180 seconds. The annealed, plasma cured coating has a dielectric constant in the range of from about 1.1 to about 2.4 and an improved elastic modulus.
Inventors
- 👤 Ivan L. Berry, III
- 👤 Todd Bridgewater
- 👤 Wei Chen
- 👤 Qingyuan Han
- 👤 Eric S. Moyer
- 👤 Michael J. Spaulding
- 👤 Carlo Waldfried
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:01
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/113; C01B33/12; H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6925; C01B33/126; H10P14/65; H10P14/6516; H10P14/6529; H10P14/6532; H10P14/63; H10P14/6326; H10P14/6342; H10P14/66; H10P14/665
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
60 words
A method of making a plasma cured coating comprising: providing a porous network coating produced from a resin molecule containing at least 2 Si—H groups; and plasma curing the porous network coating to reduce an amount of Si—H bonds and to produce an SiO 2 —containlng plasma cured coating having a first dielectric constant and having a first elastic modulus.
Claim 2
Independent Claim
60 words
A method of making a plasma cured coating comprising: providing a porous network coating produced from a resin molecule containing at least 2 Si—H groups; and plasma curing the porous network coating to reduce an amount of Si—H bonds and to produce an SiO 2 —containlng plasma cured coating having a first dielectric constant and having a first elastic modulus.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein the porous network coating is plasma cured for a time in the range of about 15 to about 120 seconds.
Claim 4
Dependent Claim
22 words
The method of claim 1 wherein the porous network coating is plasma cured at a temperature less than or about 350° C.
Claim 5
Dependent Claim
27 words
The method of claim 1 wherein the porous network coating is plasma cured at a temperature in the range of about 80° C. to about 280° C.
Claim 6
Dependent Claim
27 words
The method of claim 1 wherein the porous network coating is plasma cured at a temperature in the range of about 195° C. to about 230° C.
Claim 7
Dependent Claim
46 words
The method of claim 1 further comprising annealing the plasma cured coating to provide an annealed, plasma cured coating having a second dielectric constant which is less than the first dielectric constant and having a second elastic modulus which is comparable to the first elastic modulus.
Claim 8
Dependent Claim
21 words
The method of claim 6 wherein the plasma cured coating is annealed at a temperature less than or about 475° C.
Claim 9
Dependent Claim
26 words
The method of claim 6 wherein the plasma cured coating is annealed at a temperature in the range of about 350° C. to about 450° C.
Claim 10
Dependent Claim
20 words
The method of claim 6 wherein the plasma cured coating is annealed for no more than or about 180 seconds.
Claim 11
Dependent Claim
23 words
The method of claim 6 wherein the second elastic modulus of the annealed, plasma cured coatIng is greater than or about 4 GPa.
Claim 12
Dependent Claim
25 words
The method of claim 6 wherein the second elastic modulus of the annealed, plasma cured coating is between about 4 GPa and about 10 GPa.
Claim 13
Dependent Claim
27 words
The method of claim 6 wherein the second dielectric constant of the annealed, plasma cured coating is in the range of from about 1.1 to about 3.5.
Claim 14
Dependent Claim
27 words
The method of claim 6 wherein the second dielectric constant of the annealed, plasma cured coating is in the range of from about 2 to about 2.5.
References Cited (Backward Citations)
US3615272A
Cited
US4636440A
Cited
US4756977A
Cited
US4822697A
Cited
US4749631A
Cited
US4808653A
Cited
US4749631B1
Cited
US5008320A
Cited
US4847162A
Cited
US4842888A
Cited
US4905117A
Cited
US5210160A
Cited
US4885186A
Cited
US4999397A
Cited
US5010159A
Cited
US6171703B1
Cited
US5262201A
Cited
US5116637A
Cited
US5063267A
Cited
US5145723A
Cited
US5290394A
Cited
US5416190A
Cited
US5770260A
Cited
US5523163A
Cited
US5547703A
Cited
US5456952A
Cited
US5567658A
Cited
US5618878A
Cited
JPH0950993A
Cited
US5961851A
Cited
WO1999021706A1
Cited
US6287990B1
Cited
US6054206A
Cited
US6303192B1
Cited
EP1003210A2
Cited
US6231989B1
Cited
US6143360A
Cited
US6184260B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2006-05-05 | 2006-11-04 | 2007-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2010-05-05 | 2010-11-04 | 2011-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2014-05-05 | 2014-11-04 | 2015-05-06 | $7700.00 | Window Closed / Lapsed |