US5972804A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for forming a semiconductor device
Assignee: NXP USA Inc
•
Filing: 1997-11-03
•
Granted: 1999-10-26
•
Expires: 2017-11-03
Abstract
Abstract A method for forming an oxynitride gate dielectric layer (202, 204) begins by providing a semiconductor substrate (200). This semiconductor substrate is cleaned via process steps (10-28). Optional nitridation and oxidation are performed via steps (50 and 60) to form a thin interface layer (202). Bulk oxynitride gate deposition occurs via a step (70) to form a bulk gate dielectric material (204) having custom tailored oxygen and nitrogen profile and concentration. A step (10) is then utilized to in situ cap this bulk dielectric layer (204) with a polysilicon or amorphous silicon layer (208). The layer (208) ensures that the custom tailors oxygen and nitrogen profile and concentration of the underlying gate dielectric (204) is preserved even in the presence of subsequent wafer exposure to oxygen ambients.
Inventors
- 👤 Philip J. Tobin
- 👤 Rama I. Hegde
- 👤 Hsing-Huang Tseng
- 👤 David O'Meara
- 👤 Victor Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:11
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/01344; H10D64/01354; H10D64/60; H10D64/66; H10D64/68; H10D64/693; Y; Y10; Y10S; Y10S438/00; Y10S438/906
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
105 words
A method for forming a semiconductor device, the method comprising: placing a semiconductor substrate into a first chamber; forming a dielectric overlying a semiconductor substrate, the dielectric includes a first layer formed within the first chamber, wherein: during the formation of the first layer, an oxygen-containing gas and a nitrogen-containing gas flow at a first oxygen-containing gas-to-nitrogen-containing gas ratio at a first time; during the formation of the first layer, the oxygen-containing gas and the nitrogen-containing gas flow at a second oxygen-containing gas-to-nitrogen-containing gas ratio at a second time; and the first oxygen-containing gas-to-nitrogen-containing gas ratio is higher than the second oxygen-containing gas-to-nitrogen-containing gas ratio.
Claim 2
Independent Claim
105 words
A method for forming a semiconductor device, the method comprising: placing a semiconductor substrate into a first chamber; forming a dielectric overlying a semiconductor substrate, the dielectric includes a first layer formed within the first chamber, wherein: during the formation of the first layer, an oxygen-containing gas and a nitrogen-containing gas flow at a first oxygen-containing gas-to-nitrogen-containing gas ratio at a first time; during the formation of the first layer, the oxygen-containing gas and the nitrogen-containing gas flow at a second oxygen-containing gas-to-nitrogen-containing gas ratio at a second time; and the first oxygen-containing gas-to-nitrogen-containing gas ratio is higher than the second oxygen-containing gas-to-nitrogen-containing gas ratio.
Claim 3
Dependent Claim
28 words
The method of claim 1, wherein: the first layer is deposited; and a silicon-containing gas flows during at least a portion of the deposition of the first layer.
Claim 4
Dependent Claim
22 words
The method of claim 2, wherein during the deposition of the first layer, a flow of the silicon-containing gas is substantially constant.
Claim 5
Dependent Claim
100 words
The method of claim 1, wherein: the first layer is formed along an exposed surface; the first layer has a first surface and a second surface; the first surface is closer to the exposed surface compared to the second surface; the second surface lies along an opposite side of the first layer compared to the first surface; the first layer includes a spike that is less than approximately 10 angstroms thick: the spike has an atomic oxygen concentration higher than a center of the first layer; and the spike lies closer to the first surface compared to the second surface.
Claim 6
Dependent Claim
35 words
The method of claim 4, wherein: the spike has a maximum atomic oxygen concentration; and the atomic oxygen concentration within the first layer at the first surface is lower than the maximum atomic oxygen concentration.
Claim 7
Dependent Claim
28 words
The method of claim 1, wherein, during the formation of the first layer, a flow rate of the nitrogen-containing gas is increased between the first and second times.
Claim 8
Dependent Claim
28 words
The method of claim 1, wherein, during the formation of the first layer, a flow rate of the oxygen-containing gas is reduced between the first and second times.
Claim 9
Dependent Claim
37 words
The method of claim 1, wherein the dielectric has a characteristic selected from a group consisting of: a physical thickness no greater than approximately 100 angstroms; and an effective oxide thickness no greater than approximately 50 angstroms.
Claim 10
Dependent Claim
24 words
The method of claim 1, wherein forming the dielectric further comprises exposing the semiconductor substrate to a nitrogen-containing gas before forming the first layer.
Claim 11
Dependent Claim
34 words
The method of claim 9, wherein forming the dielectric further comprises exposing the semiconductor substrate to an oxygen-containing gas after exposing the semiconductor substrate to the nitrogen-containing gas and before forming the first layer.
Claim 12
Dependent Claim
24 words
The method of claim 1, wherein forming the dielectric further comprises exposing the semiconductor substrate to a oxygen-containing gas before forming the first layer.
Claim 13
Dependent Claim
15 words
The method of claim 1, wherein the dielectric has a dielectric constant greater than 6.0.
Claim 14
Dependent Claim
14 words
The method of claim 1, further comprising: forming a capping layer over the dielectric.
Claim 15
Dependent Claim
26 words
The method of claim 13, wherein forming the capping layer is performed after forming the dielectric and before exposing the semiconductor substrate to a room ambient.
Claim 16
Dependent Claim
13 words
The method of claim 13, wherein the capping layer preserves a oxygen-to-nitrogen profile.
References Cited (Backward Citations)
US3590337A
Cited
US3765935A
Cited
US4176372A
Cited
US4114254A
Cited
US4980307A
Cited
US4675264A
Cited
US4788082A
Cited
US4717631A
Cited
US4907064A
Cited
US4961103A
Cited
US5130267A
Cited
US5168343A
Cited
US5256205A
Cited
US5268069A
Cited
US5210047A
Cited
US5464783A
Cited
US5407870A
Cited
US5529937A
Cited
US5780891A
Cited
US5691228A
Cited
US5808335A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-25 | 2003-04-26 | 2003-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-25 | 2007-04-26 | 2007-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-25 | 2011-04-26 | 2011-10-26 | $7700.00 | Window Closed / Lapsed |