Method and apparatus for the deposition of solid films of a material from a jet stream entraining the gaseous phase of said material
Assignee: Jet Process Corp
•
Filing: 1985-12-12
•
Granted: 1988-11-29
•
Expires: 2005-12-12
Abstract
Abstract Described is a method for depositing from the vapor phase a chemical species into the form of a thin solid film material which overlays a substrate material. The deposition process consists of three steps: (1) synthesis of depositing species, (2) transport of said species from site of synthesis to a prepared substrate material, and (3) condensation and subsequent film growth. The transport step is achieved by admixing small concentrations of the depositing species into the flow of a high speed jet of an inert carrier gas. This jet impinges on the substrate's surface and thereby convects the depositing species to this surface where condensation occurs. Since the gas mixture is at fairly high pressure, the deposition is achieved in a simple flow apparatus rather than in the high vacuum systems required of other methods. Also this transport technique allows the chemical and/or physical phenomena utilized in the depositing species synthesis step to be isolated from the actual condensation reaction. Consequently, the conditions governing each of these reactions can be varied independently to optimize both steps. Such flexibility permits the synthesis and deposition of a wide variety of chemical species, hence many thin film materials are susceptible to formation by this method.
Inventors
- 👤 Jerome J. Schmitt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:44
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/04; H01M4/0402; H01M4/0404; B; B22; B22F; B22F9/00; B22F9/02; B22F9/12; C; C23; C23C; C23C14/00; C23C14/0005; C23C14/0021; C23C14/22; C23C14/228; C23C14/24; C23C16/00; C23C16/01; C23C16/22; C23C16/24; C23C16/44; C23C16/455; C23C16/45502; C23C16/4551; C23C16/45563; C23C16/45593; H01M4/0421; H01M4/0423; H01M4/0428; H01M4/0438; H01M4/0471; H01M4/049; H01M4/36; H01M4/38; H01M4/383; H01M6/00; H01M6/14; H01M6/18; H01M6/185; H01M6/188
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
150 words
A method of depositing a condensible gaseous material entrained in an inert carrier gas as a solid onto a substrate surface unreactive to the condensible gaseous material comprising: (a) forming a stream of inert carrier gas; (b) generating the condensible gaseous component to be deposited on the substrate substantially contiguous to or within a means for forming a jet of the inert carrier gas; (c) transporting the condensible gaseous material and the stream of the inert carrier gas through the jet forming means toward the substrate; (d) decelerating the jet stream of inert carrier gas by impinging the jet against the substrate and thereby effecting a deposit in solid form of the condensible gaseous material; and (e) effecting relative movement having a lateral component between the substrate surface and the stream of inert carrier gas to dispose a substantially uniform thickness of solid condensible gaseous material on the substrate surface.
Claim 2
Independent Claim
150 words
A method of depositing a condensible gaseous material entrained in an inert carrier gas as a solid onto a substrate surface unreactive to the condensible gaseous material comprising: (a) forming a stream of inert carrier gas; (b) generating the condensible gaseous component to be deposited on the substrate substantially contiguous to or within a means for forming a jet of the inert carrier gas; (c) transporting the condensible gaseous material and the stream of the inert carrier gas through the jet forming means toward the substrate; (d) decelerating the jet stream of inert carrier gas by impinging the jet against the substrate and thereby effecting a deposit in solid form of the condensible gaseous material; and (e) effecting relative movement having a lateral component between the substrate surface and the stream of inert carrier gas to dispose a substantially uniform thickness of solid condensible gaseous material on the substrate surface.
Claim 3
Dependent Claim
20 words
The method of claim 1, and wherein the flow of inert carrier gas is effected through a mechanical pump means.
Claim 4
Dependent Claim
22 words
The process of claim 1 and further wherein step (e) is carried out while impinging the jet stream on the substrate surface.
Claim 5
Dependent Claim
13 words
The method of claim 1, wherein the condensible gaseous material is a metal.
Claim 6
Dependent Claim
29 words
A method according to claim 2 in which the gas atmosphere in the deposition system is controlled by the flow of inert carrier gas which purges the flow system.
Claim 7
Dependent Claim
27 words
A method according to claim 2 in which the flow of the fluid mixture is recirculated in to the deposition system gas inlet via a recirculation tube.
Claim 8
Dependent Claim
78 words
A method according to claim 2 wherein the population of condensible molecules of said deposition species is substantially maintained within a flow region which insures that the molecules are far enough downstream in a flow of inert gas which transports said species so that a saturated condensible vapor of the depositing species will be convected past nozzle surfaces, which are provided to direct said gas, before the molecules have time to diffuse to and condense on said surfaces.
Claim 9
Dependent Claim
42 words
A method according to claim 1 in which molecules of one or more reaction precursor species destined for consumption in an evolving synthesis reaction occuring in flow region are premixed with a carrier gas as an undersaturated vapor before depositing species synthesis.
Claim 10
Dependent Claim
52 words
A method according to claim 8 in which the species destined to be consumed in the evolving synthesis reactions is initially in solid or liquid phase bulk form, which is then heated until its vapor pressure rises so that the desired mass flux of reactant species is evaporated off into inert gas.
Claim 11
Dependent Claim
30 words
A method according to claim 9 in which more than one reactant species is evaporated from more than one solid or liquid bulk material sources, into the gas flow region.
Claim 12
Dependent Claim
47 words
A method according to claim 8 in which the chemical species destined for consumption in the evolving chemical symthesis reactions is a fluid which is delivered via a thin tube duct that exits into the gas flow region to be entrained in a stream flow field thereof.
Claim 13
Dependent Claim
50 words
A method according to claim 1 wherein any species so introduced into the gas flow can participate in chemical synthesis reactions (including gas phase nucleation) which are controlled by the design of a nozzle's geometry--which directly affects the flow conditions which govern the energies and trajectories of the reactant species.
Claim 14
Dependent Claim
50 words
A method according to claim 1 wherein synthesis reactions (including dissociation) are activated by energy addition to the molecules by energy means of either: (1) heating at hot solid surface, or (2) absorption of radiation, or (3) any combination of said energy means, (4) any combination of said energy means.
Claim 15
Dependent Claim
21 words
A method according to claim 1 which the production of overlay coatings on a supporting substrate is done in batch mode.
Claim 16
Dependent Claim
31 words
A method according to claim 1 in which the production of thin film overlay coatings on supporting substrate material is done in continuous mode through the use of gas gating means.
Claim 17
Dependent Claim
33 words
A method according to claim 1 in which deposited layers of coatings with differing materials is formed by the use of one or more nozzles to deposit one and then the next layer.
Claim 18
Dependent Claim
61 words
A method according to claim 1 which deposits a product film composed of the following chemical species: silicon, gold, tungsten, aluminum, magnesium, iron, carbon, chromium, cobalt, platinum, titanium and germanium; solid phases of oxides, nitrides, hydrides, fluorides, and other compounds containing an oxidizing agent; or combination thereof, including mixtures and alloys and compounds thereof in either crystal, polycrystal or amorphous phase.
Claim 19
Dependent Claim
64 words
A method according to claim 1 wherein the depositing species is introduced within an accelerating flow of the carrier gas jet continuum traveling at a speed sufficent to entrain the species, and the flow is regulated so as to define a local Stokes Number so as to achieve inertial impaction of a species to be deposited after the carrier gas jet leaves the orifice.
Claim 20
Dependent Claim
55 words
A method according to claim 1 wherein the flow of the gas jet continuum is regulated by a throttle to change the Stokes Number to define a local Stokes number so as to control the location of the said transition zone and the type of deposition which is to occur in the target area region.
Claim 21
Dependent Claim
56 words
A method according to claim 1 wherein the synthesis reaction precursor species is entrained in a flow field of the gas jet continuum where decomposition or reaction with other species so entrained form a species to be deposited in the form of saturated condensible vapor which condenses from the gas jet continuum in said second region.
Claim 22
Dependent Claim
54 words
A method according to claim 1 wherein a saturated condensible vapor of the depositing species is confined within the flow field region of the gas jet continuum and transported downstream so quickly that substantially no migration from the gas occurs until the saturated condensible vapor reaches the second region adjacent to a target surface.
Claim 23
Dependent Claim
39 words
A method according to claim 1 wherein within a flow field defining aerodynamic confinment within a field of said gas jet continuum reactions occur which complete formation of the depositing species before the gas jet reaches the target substrate.
Claim 24
Dependent Claim
30 words
A method according to claim 1 wherein the gas jet continuum efficiently entrains and accelerate vapor molecules so as to cause inertial impaction of the vapor molecules onto the substrate.
Claim 25
Dependent Claim
20 words
A method according to claim 1 wherein the gas jet continuum flows at a rate in excess of 0.1 Mach.
Claim 26
Dependent Claim
20 words
A method according to claim 1 wherein the gas jet continuum flows at a rate in excess of 0.4 Mach.
Claim 27
Dependent Claim
20 words
A method according to claim 1 wherein the gas jet continuum flows at a rate of Mach 1 or greater.
Claim 28
Dependent Claim
52 words
A method according to claim 1 wherein the synthesis and formation as a condensible vapor of the depositing species is isolated in the flow field of the gas jet continuum from the condensation through diffusion or inertial impaction of the condensible vapor which occurs in the second region at the target area.
Claim 29
Dependent Claim
44 words
A method according to claim 1 wherein the gas jet continuum fluid of inert gas is recirculated after reaching the second region and after the depositing species are disentrained on the target substrate as an inert gas substantially free of an entrained depositing species.
References Cited (Backward Citations)
US2155932A
Cited
US3382845A
Cited
US3654895A
Cited
US3840391A
Cited
US3808035A
Cited
US3850679A
Cited
US4033286A
Cited
US4351267A
Cited
US4468283A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-29 | 1992-05-30 | 1992-11-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-29 | 1996-05-30 | 1996-11-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-29 | 2000-05-30 | 2000-11-29 | $7700.00 | Window Closed / Lapsed |