Process for fabricating a semiconductor device having a high reliability dielectric material
Assignee: Apple Inc
•
Filing: 1993-06-07
•
Granted: 1995-04-18
•
Expires: 2013-06-07
Abstract
Abstract A process for fabricating a high-reliability composite dielectric layer (19) includes the formation of a first oxynitride layer (14) on the surface (12) of a silicon substrate (10). The formation of the first oxynitride layer (14) is followed by an oxidation step to form a silicon dioxide layer (16) at the surface (12) of the substrate (10) and underlying the first oxynitride layer (14). The composite dielectric layer (19) is completed by exposing the substrate (10) to nitrous oxide, and diffusing a nitrogen bearing species through both the silicon dioxide layer (16) and the first oxynitride layer (14) to form a second oxynitride layer (18) underlying the silicon dioxide layer (16). The composite dielectric layer (19) exhibits a nitrogen-rich region at the interface between second oxynitride layer (18) and the silicon substrate (10). A second nitrogen rich region is also formed near the surface of the first oxynitride layer (14).
Inventors
- 👤 Yoshio Okada
- 👤 Philip J. Tobin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 14:06
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0411; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/01338; H10D64/031; H10D64/035; H10D64/60; H10D64/66; H10D64/68; H10D64/681
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
72 words
A process for fabricating a semiconductor device comprising the steps of: providing a silicon substrate having a surface; forming a first oxynitride layer on the substrate; oxidizing the substrate surface to form an oxide layer underlying the first oxynitride layer; and exposing the substrate to nitrous oxide and diffusing a nitrogen bearing species through the first oxynitride layer and the oxide layer to form a second oxynitride layer underlying the oxide layer.
Claim 2
Dependent Claim
72 words
A process for fabricating a semiconductor device comprising the steps of: providing a silicon substrate having a surface; forming a first oxynitride layer on the substrate; oxidizing the substrate surface to form an oxide layer underlying the first oxynitride layer; and exposing the substrate to nitrous oxide and diffusing a nitrogen bearing species through the first oxynitride layer and the oxide layer to form a second oxynitride layer underlying the oxide layer.
Claim 3
Dependent Claim
27 words
The process of claim 1, wherein the step of exposing the substrate to nitrous oxide comprises thermal diffusion at a temperature of 900° C. to 1150° C.
Claim 4
Dependent Claim
22 words
The process of claim 1 further comprising precleaning the silicon substrate to remove native oxide prior to forming the first oxynitride layer.
Claim 5
Dependent Claim
33 words
The process of claim 1, wherein the step of forming a first oxynitride layer comprises forming oxynitride in a thermally-controlled reactor using nitrous oxide at a temperature of 900° C. to 1150° C.
Claim 6
Dependent Claim
18 words
The process of claim 1 further comprising depositing a layer of polycrystalline silicon on the first oxynitride layer.
Claim 7
Dependent Claim
29 words
The process of claim 1, wherein diffusing a nitrogen bearing species comprises diffusing a nitrogen species selected from the group consisting of nitrous oxide, nitric oxide, and nitrogen dioxide.
Claim 8
Dependent Claim
94 words
A process for fabricating a semiconductor device comprising the steps of: placing a silicon substrate having a surface in a thermally-controlled reactor; flowing hydrogen fluoride gas to remove native oxides from the substrate surface; flowing nitrous oxide gas to form a first oxynitride layer on the substrate; flowing oxygen gas and oxidizing the substrate surface to form a silicon oxide layer on the substrate; and flowing nitrous oxide gas and diffusing a nitrogen bearing species through the first oxynitride layer and the oxide layer form a second oxynitride layer underlying the silicon oxide layer.
Claim 9
Dependent Claim
94 words
A process for fabricating a semiconductor device comprising the steps of: placing a silicon substrate having a surface in a thermally-controlled reactor; flowing hydrogen fluoride gas to remove native oxides from the substrate surface; flowing nitrous oxide gas to form a first oxynitride layer on the substrate; flowing oxygen gas and oxidizing the substrate surface to form a silicon oxide layer on the substrate; and flowing nitrous oxide gas and diffusing a nitrogen bearing species through the first oxynitride layer and the oxide layer form a second oxynitride layer underlying the silicon oxide layer.
Claim 10
Dependent Claim
19 words
The process of claim 7, wherein the process steps are sequentially performed without exposing the substrate to room ambient.
Claim 11
Dependent Claim
26 words
The process of claim 7, wherein the substrate is heated to a temperature of 900° C. to 1150° C. prior to forming the first oxynitride layer.
Claim 12
Dependent Claim
19 words
The process of claim 7, wherein the nitrous oxide flow rate is 4 to 14 standard liters per minute.
Claim 13
Dependent Claim
29 words
The process of claim 7, wherein diffusing a nitrogen bearing species comprises diffusing a nitrogen species selected from the group consisting of nitrous oxide, nitric oxide, and nitrogen dioxide.
Claim 14
Dependent Claim
121 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having an active region defined by a field oxide region; forming a gate oxide layer overlying the active region; etching away a portion of the gate oxide layer to expose a portion of the substrate; forming a first oxynitride layer on the exposed portion of the substrate; oxidizing the exposed portion of the substrate to form an oxide layer underlying the first oxynitride layer; diffusing a nitrogen bearing species through the first oxynitride layer and the oxide layer to form a second oxynitride layer underlying the oxide layer; and forming a gate electrode overlying the first oxynitride layer and a portion of the gate oxide layer.
Claim 15
Dependent Claim
121 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having an active region defined by a field oxide region; forming a gate oxide layer overlying the active region; etching away a portion of the gate oxide layer to expose a portion of the substrate; forming a first oxynitride layer on the exposed portion of the substrate; oxidizing the exposed portion of the substrate to form an oxide layer underlying the first oxynitride layer; diffusing a nitrogen bearing species through the first oxynitride layer and the oxide layer to form a second oxynitride layer underlying the oxide layer; and forming a gate electrode overlying the first oxynitride layer and a portion of the gate oxide layer.
Claim 16
Dependent Claim
24 words
The process of claim 12, wherein the step of diffusing nitrous oxide comprises thermal diffusion at a temperature of 900° C. to 1150° C.
Claim 17
Dependent Claim
25 words
The process of claim 12 further comprising precleaning exposed portion of the silicon substrate to remove native oxide prior to forming the first oxynitride layer.
Claim 18
Dependent Claim
32 words
The process of claim 12, wherein the step of forming a first oxynitride layer comprises chemical vapor deposition using nitrous oxide source gas at a temperature of 900° C. to 1150° C.
Claim 19
Dependent Claim
29 words
The process of claim 12, wherein diffusing a nitrogen bearing species comprises diffusing a nitrogen species selected from the group consisting of nitrous oxide, nitric oxide, and nitrogen dioxide.
References Cited (Backward Citations)
JPS60189972A
Cited
JPS62122222A
Cited
US5254506A
Cited
US5198392A
Cited
US5278087A
Cited
US5225361A
Cited
US5258333A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-04-17 | 1998-10-17 | 1999-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-04-17 | 2002-10-17 | 2003-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-04-17 | 2006-10-17 | 2007-04-18 | $7700.00 | Window Closed / Lapsed |