Manufacturing capping layer for the fabrication of cobalt salicide structures
Assignee: GlobalFoundries Inc
•
Filing: 1998-12-08
•
Granted: 1999-10-19
•
Expires: 2018-12-08
Abstract
Abstract An improved process for manufacturing cobalt silicide layers uses two capping layers. A first capping layer of titanium nitride prevents the formation of a cobalt/titanium intermetallic. A subsequently formed titanium metallic layer getters impurities from outgassing and the ambient preventing corruption of the cobalt layer. Two rapid thermal annealing steps convert the cobalt at the cobalt/silicon intermetallic into highly conductive cobalt disilicide. The cobalt silicide does not suffer from linewidth dependent increases in resistivity. Therefore, the cobalt disilicide formed by the present method is useful for semiconductor devices with linewidths and feature sizes less than 0.20 μm. The process has wide applicability and may be used to fabricate local circuit interconnects, floating gates, double polysilicon stacked floating gates as well as other uses.
Inventors
- 👤 Paul R. Besser
- 👤 Robin W. Cheung
- 👤 Robert Chen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:26
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0212; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698; Y; Y10; Y10S; Y10S438/00; Y10S438/902
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
69 words
A process for forming a cobalt disilicide layer on a silicon substrate comprising the steps of: forming on said silicon substrate, a first layer comprising a metallic cobalt material; forming on said cobalt layer, a second layer comprising a titanium nitride material; forming on said titanium nitride layer, a third layer comprising a metallic titanium material; and performing a plurality of annealing steps to form a cobalt disilicide layer.
Claim 2
Dependent Claim
69 words
A process for forming a cobalt disilicide layer on a silicon substrate comprising the steps of: forming on said silicon substrate, a first layer comprising a metallic cobalt material; forming on said cobalt layer, a second layer comprising a titanium nitride material; forming on said titanium nitride layer, a third layer comprising a metallic titanium material; and performing a plurality of annealing steps to form a cobalt disilicide layer.
Claim 3
Dependent Claim
76 words
A process as in claim 1, wherein said plurality of annealling steps comprise the steps of: performing a first anneal of said substrate to form a cobalt monosilicide layer disposed above said silicon substrate; stripping said layers of metallic cobalt material, titanium nitride material, and metallic titanium material, leaving said layer of cobalt monosilicide; and performing a second anneal of said substrate whereby said cobalt monosilicide layer undergoes further reaction to form a cobalt disilicide layer.
Claim 4
Dependent Claim
35 words
A process as in claim 2, wherein said first anneal is a rapid thermal anneal or a furnace anneal process and said second anneal is a rapid thermal anneal process or a furnace anneal process.
Claim 5
Dependent Claim
70 words
A process as in claim 2, wherein said first anneal is a rapid thermal anneal performed at a temperature in the range of 400-600 degrees Celsius and for a length of time in the range of 10-90 seconds and said second anneal is a rapid thermal anneal performed at a temperature in the range of 700-850 degrees Celsius and for a length of time in the range of 10-90 seconds.
Claim 6
Dependent Claim
46 words
A process as in claim 2, wherein said cobalt layer has a thickness in the range of 50-250 Ångstroms and said titanium nitride layer has a thickness in the range of 100-500 Ångstroms and said titanium layer has a thickness in the range of 50-500 Ångstroms.
Claim 7
Dependent Claim
70 words
A process as in claim 5, wherein said first anneal is a rapid thermal anneal performed at a temperature in the range of 400-600 degrees Celsius and for a length of time in the range of 10-90 seconds and said second anneal is a rapid thermal anneal performed at a temperature in the range of 700-850 degrees Celsius and for a length of time in the range of 10-90 seconds.
Claim 8
Dependent Claim
17 words
A process as in claim 1, wherein said first, second, and third layers are formed using deposition.
Claim 9
Dependent Claim
30 words
A process as in claim 7, wherein said steps of depositing said first, second, and third layers comprise depositing said first, second, and third layers in three separate sputtering chambers.
Claim 10
Dependent Claim
28 words
A process as in claim 8, wherein said steps of depositing said second and third layers comprise depositing said second and third layers in a single sputtering chamber.
Claim 11
Dependent Claim
88 words
A process for forming a cobalt disilicide layer on exposed silicon regions of a silicon substrate comprising the steps of: providing a silicon substrate having exposed and unexposed silicon regions; depositing on said silicon substrate a first layer comprising a metallic cobalt material; depositing on said cobalt layer a second layer comprising a titanium nitride material; depositing on said titanium nitride layer a third layer comprising a metallic titanium material; performing a plurality of annealling steps to form a cobalt disilicide layer disposed above said exposed silicon regions.
Claim 12
Dependent Claim
88 words
A process for forming a cobalt disilicide layer on exposed silicon regions of a silicon substrate comprising the steps of: providing a silicon substrate having exposed and unexposed silicon regions; depositing on said silicon substrate a first layer comprising a metallic cobalt material; depositing on said cobalt layer a second layer comprising a titanium nitride material; depositing on said titanium nitride layer a third layer comprising a metallic titanium material; performing a plurality of annealling steps to form a cobalt disilicide layer disposed above said exposed silicon regions.
Claim 13
Dependent Claim
93 words
A process as in claim 10, wherein said plurality of annealling steps comprise the steps of: performing a first anneal of said substrate in a nitrogen gas to form a cobalt monosilicide layer disposed above said exposed silicon regions; etching to remove said layers of unreacted metallic cobalt material, titanium nitride material, and metallic titanium material from all regions, leaving said layer of cobalt monosilicide; and performing a second anneal of said substrate whereby said cobalt monosilicide layer undergoes further reaction to form a cobalt disilicide layer disposed above said exposed silicon regions.
Claim 14
Dependent Claim
35 words
A process as in claim 11, wherein said first anneal is a rapid thermal anneal or a furnace anneal process and said second anneal is a rapid thermal anneal process or a furnace anneal process.
Claim 15
Dependent Claim
70 words
A process as in claim 12, wherein said first anneal is a rapid thermal anneal performed at a temperature in the range of 400-600 degrees Celsius and for a length of time in the range of 10-90 seconds and said second anneal is a rapid thermal anneal performed at a temperature in the range of 700-850 degrees Celsius and for a length of time in the range of 10-90 seconds.
Claim 16
Dependent Claim
29 words
A process as in claim 10, wherein said steps of depositing said first, second, and third layers comprise depositing said first, second, and third layers in three separate chambers.
Claim 17
Dependent Claim
27 words
A process as in claim 10, wherein said steps of depositing said second and third layers comprise depositing said second and third layers in a single chamber.
Claim 18
Dependent Claim
46 words
A process as in claim 10, wherein said cobalt layer has a thickness in the range of 50-250 Ångstroms and said titanium nitride layer has a thickness in the range of 100-500 Ångstroms and said titanium layer has a thickness in the range of 50-500 Ångstroms.
Claim 19
Dependent Claim
70 words
A process as in claim 16, wherein said first anneal is a rapid thermal anneal performed at a temperature in the range of 400-600 degrees Celsius and for a length of time in the range of 10-90 seconds and said second anneal is a rapid thermal anneal performed at a temperature in the range of 700-850 degrees Celsius and for a length of time in the range of 10-90 seconds.
Claim 20
Independent Claim
163 words
A method for forming a polycrystalline cobalt disilicide structure on a metal oxide transistor in a silicon substrate, comprising the steps of: providing a silicon substrate having a transistor formed thereon, said transistor having gate, source, and drain regions, said gate having a length dimension of about 0.20 μm or less; depositing a layer of cobalt on said substrate; thereafter depositing a layer of titanium nitride on said cobalt layer; thereafter depositing a layer of titanium on said titanium nitride layer; thereafter heating said substrate to form a polycrystalline cobalt disilicide layer on said source, gate, and drain regions of said transistor, said heating step comprising a first heating step and a second heating step, said second heating step being performed at a higher temperature than said first heating step; and selectively etching, in between said first and second heating steps, to strip the remaining nonsilicide cobalt, titanium, and titanium nitride material from said substrate except in said gate, source, and drain regions.
Claim 21
Independent Claim
163 words
A method for forming a polycrystalline cobalt disilicide structure on a metal oxide transistor in a silicon substrate, comprising the steps of: providing a silicon substrate having a transistor formed thereon, said transistor having gate, source, and drain regions, said gate having a length dimension of about 0.20 μm or less; depositing a layer of cobalt on said substrate; thereafter depositing a layer of titanium nitride on said cobalt layer; thereafter depositing a layer of titanium on said titanium nitride layer; thereafter heating said substrate to form a polycrystalline cobalt disilicide layer on said source, gate, and drain regions of said transistor, said heating step comprising a first heating step and a second heating step, said second heating step being performed at a higher temperature than said first heating step; and selectively etching, in between said first and second heating steps, to strip the remaining nonsilicide cobalt, titanium, and titanium nitride material from said substrate except in said gate, source, and drain regions.
Claim 22
Dependent Claim
137 words
A process for forming cobalt disilicide contacts on a semiconductor device comprising the steps of: providing a semiconductor substrate, said substrate having a microcircuit structure with silicon contact areas formed thereon; depositing a metallic cobalt layer onto said silicon substrate; depositing a titanium nitride layer onto said cobalt layer; depositing a metallic titanium layer onto said titanium nitride layer; performing a first anneal of said substrate whereby the contact areas and some of said cobalt layer react to form a cobalt monosilicide layer disposed above said contact areas; stripping said layers of metallic cobalt material, titanium nitride material, and metallic titanium material, leaving said cobalt monosilicide disposed above said contact areas; and performing a second anneal of said substrate whereby said cobalt monosilicide layer undergoes further reaction to form cobalt disilicide contacts disposed above said contact areas.
Claim 23
Dependent Claim
137 words
A process for forming cobalt disilicide contacts on a semiconductor device comprising the steps of: providing a semiconductor substrate, said substrate having a microcircuit structure with silicon contact areas formed thereon; depositing a metallic cobalt layer onto said silicon substrate; depositing a titanium nitride layer onto said cobalt layer; depositing a metallic titanium layer onto said titanium nitride layer; performing a first anneal of said substrate whereby the contact areas and some of said cobalt layer react to form a cobalt monosilicide layer disposed above said contact areas; stripping said layers of metallic cobalt material, titanium nitride material, and metallic titanium material, leaving said cobalt monosilicide disposed above said contact areas; and performing a second anneal of said substrate whereby said cobalt monosilicide layer undergoes further reaction to form cobalt disilicide contacts disposed above said contact areas.
Claim 24
Dependent Claim
154 words
A process for forming fill structures leading to cobalt disilicide contacts, comprising the steps of: providing a semiconductor substrate having contact regions; depositing on said silicon substrate a first layer comprising a metallic cobalt material; depositing on said cobalt layer a second layer comprising a titanium nitride material; depositing on said titanium nitride layer a third layer comprising a metallic titanium material; performing a first anneal of said substrate, said first annealling forming cobalt monosilicide regions disposed above said contact regions; stripping said layers of unreacted metallic cobalt material, titanium nitride material, and metallic titanium material, leaving the cobalt monosilicide regions in place; performing a second anneal of said substrate whereby said cobalt monosilicide undergoes further reaction to form cobalt disilicide contacts disposed above said contact regions; forming a passivation layer over said substrate, said passivation layer having vias disposed above said cobalt disilicide contacts; and filling said vias with a conducting fill material.
Claim 25
Dependent Claim
154 words
A process for forming fill structures leading to cobalt disilicide contacts, comprising the steps of: providing a semiconductor substrate having contact regions; depositing on said silicon substrate a first layer comprising a metallic cobalt material; depositing on said cobalt layer a second layer comprising a titanium nitride material; depositing on said titanium nitride layer a third layer comprising a metallic titanium material; performing a first anneal of said substrate, said first annealling forming cobalt monosilicide regions disposed above said contact regions; stripping said layers of unreacted metallic cobalt material, titanium nitride material, and metallic titanium material, leaving the cobalt monosilicide regions in place; performing a second anneal of said substrate whereby said cobalt monosilicide undergoes further reaction to form cobalt disilicide contacts disposed above said contact regions; forming a passivation layer over said substrate, said passivation layer having vias disposed above said cobalt disilicide contacts; and filling said vias with a conducting fill material.
Claim 26
Dependent Claim
28 words
A process as in claim 20, wherein said second annealling step to form a cobalt disilicide layer is performed at a higher temperature than said first annealling step.
Claim 27
Dependent Claim
35 words
A process as in claim 21, wherein said first anneal is a rapid thermal anneal or a furnace anneal process and said second anneal is a rapid thermal anneal process or a furnace anneal process.
Claim 28
Dependent Claim
70 words
A process as in claim 21, wherein said first anneal is a rapid thermal anneal performed at a temperature in the range of 400-600 degrees Celsius and for a length of time in the range of 10-90 seconds and said second anneal is a rapid thermal anneal performed at a temperature in the range of 700-850 degrees Celsius and for a length of time in the range of 10-90 seconds.
Claim 29
Dependent Claim
35 words
A process as in claim 21, wherein said first anneal is a rapid thermal anneal or a furnace anneal process and said second anneal is a rapid thermal anneal process or a furnace anneal process.
Claim 30
Dependent Claim
29 words
A process as in claim 20, wherein said steps of depositing said first, second, and third layers comprise depositing said first, second, and third layers in three separate chambers.
Claim 31
Dependent Claim
27 words
A process as in claim 20, wherein said steps of depositing said second and third layers comprise depositing said second and third layers in a single chamber.
Claim 32
Dependent Claim
52 words
A process as in claim 20, wherein said cobalt layer is deposited to a thickness in the range of 50-250 Ångstroms and said titanium nitride layer is deposited to a thickness in the range of 100-500 Ångstroms and said titanium layer is deposited to a thickness in the range of 50-500 Ångstroms.
Claim 33
Dependent Claim
70 words
A process as in claim 27, wherein said first anneal is a rapid thermal anneal performed at a temperature in the range of 400-600 degrees Celsius and for a length of time in the range of 10-90 seconds and said second anneal is a rapid thermal anneal performed at a temperature in the range of 700-850 degrees Celsius and for a length of time in the range of 10-90 seconds.
Claim 34
Dependent Claim
27 words
A process as in claim 20 wherein said conducting fill material is selected from the group consisting of polysilicon, doped polysilicon, tungsten, aluminum, copper, and copper alloys.
References Cited (Backward Citations)
US5047367A
Cited
US5231053A
Cited
EP0525637A1
Cited
US5567651A
Cited
US5317187A
Cited
US5266156A
Cited
EP0598422A1
Cited
EP0651076A1
Cited
US5593924A
Cited
US5582881A
Cited
US5780362A
Cited
US5902129A
Cited
US5874342A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-18 | 2003-04-19 | 2003-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-18 | 2007-04-19 | 2007-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-18 | 2011-04-19 | 2011-10-19 | $7700.00 | Window Closed / Lapsed |