Self-aligned cobalt silicide on MOS integrated circuits
Assignee: Hewlett Packard Development Co LP
•
Filing: 1995-06-07
•
Granted: 1996-10-22
•
Expires: 2015-06-07
Abstract
Abstract A method of forming cobalt silicide on source/drain regions and polysilicon gate areas of an MOS integrated circuit uses an improved technique to prevent unwanted oxidation of cobalt or growth of silicide on other areas of device. A thin titanium nitride (or titanium tungsten) film is deposited on top of a cobalt film following the steps of patterning the polysilicon gate, source/drain implant and sidewall oxide spacer deposition and etch. The titanium nitride film allows formation of defect-free cobalt silicide during an elevated-temperature anneal. Without the titanium nitride film, the cobalt is likely to oxidize and/or form cobalt silicide in unwanted regions of the device, which can cause device failure.
Inventors
- 👤 Antonio C. Berti
- 👤 Stephen P. Baranowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 09:28
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10P; H10P14/00; H10P14/40; H10P14/416; Y; Y10; Y10S; Y10S148/00; Y10S148/147
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
145 words
A method of making a semiconductor device, comprising the steps of: a) applying a gate layer at a face of a silicon body; b) forming sidewall spacers composed of oxide at edges of said gate layer the sidewall spacers having a narrow width compared to a width of said gate layer; c) applying a first layer comprising cobalt to exposed areas of said face, said first layer extending from said exposed areas across said narrow width of said sidewall spacers and access said gate layer; d) applying a second layer including titanium nitride or titanium tungsten over said first layer; e) heating said body at a temperature of 420° C. to 550° C. to cause formation of cobalt monosilicide on said gate layer; and heating said body to a temperature in excess of said first temperature range to convert the cobalt monosilicide into cobalt disilicide.
Claim 2
Independent Claim
145 words
A method of making a semiconductor device, comprising the steps of: a) applying a gate layer at a face of a silicon body; b) forming sidewall spacers composed of oxide at edges of said gate layer the sidewall spacers having a narrow width compared to a width of said gate layer; c) applying a first layer comprising cobalt to exposed areas of said face, said first layer extending from said exposed areas across said narrow width of said sidewall spacers and access said gate layer; d) applying a second layer including titanium nitride or titanium tungsten over said first layer; e) heating said body at a temperature of 420° C. to 550° C. to cause formation of cobalt monosilicide on said gate layer; and heating said body to a temperature in excess of said first temperature range to convert the cobalt monosilicide into cobalt disilicide.
Claim 3
Dependent Claim
13 words
A method according to claim 1 wherein said gate layer comprises polycrystalline silicon.
Claim 4
Dependent Claim
24 words
A method according to claim 1 including the step of forming source/drain regions in said exposed areas of said face adjacent said gate layer.
Claim 5
Dependent Claim
18 words
A method according to claim 3 wherein said cobalt silicide is formed in surfaces of said source/drain regions.
Claim 6
Dependent Claim
30 words
A method according to claim 1 wherein said first layer is less than about 300 Å in thickness, and said second layer is about 50 to 150 Å in thickness.
Claim 7
Independent Claim
206 words
A method of making an MSS transistor device, comprising the steps of: a) applying a polysilicon gate layer at a face of a silicon body and patterning said gate layer to leave a gate at a transistor area of said face; b) forming sidewall spacers at opposite edges of said gate, the sidewall spacers having a narrow width compared to a width of said gate; c) applying a first layer comprising cobalt of a first thickness to exposed areas of said transistor area of said face, said first area extending across said narrow width of said sidewall spacers and across said gate; d) applying a second layer including titanium nitride or titanium tungsten over said first layer; e) heating said body in an inert ambient at a temperature in a first range of 420° C. to 550° C. to cause formation of cobalt monosilicide by reaction of said first layer with silicon of said face in said exposed areas, said second layer acting to prevent formation of silicide over said narrow width of said sidewall spacers and to prevent oxidation of said cobalt monosilicide; and heating said body to a temperature in excess of said first temperature range to convert the cobalt monosilicide into cobalt disilicide.
Claim 8
Independent Claim
206 words
A method of making an MSS transistor device, comprising the steps of: a) applying a polysilicon gate layer at a face of a silicon body and patterning said gate layer to leave a gate at a transistor area of said face; b) forming sidewall spacers at opposite edges of said gate, the sidewall spacers having a narrow width compared to a width of said gate; c) applying a first layer comprising cobalt of a first thickness to exposed areas of said transistor area of said face, said first area extending across said narrow width of said sidewall spacers and across said gate; d) applying a second layer including titanium nitride or titanium tungsten over said first layer; e) heating said body in an inert ambient at a temperature in a first range of 420° C. to 550° C. to cause formation of cobalt monosilicide by reaction of said first layer with silicon of said face in said exposed areas, said second layer acting to prevent formation of silicide over said narrow width of said sidewall spacers and to prevent oxidation of said cobalt monosilicide; and heating said body to a temperature in excess of said first temperature range to convert the cobalt monosilicide into cobalt disilicide.
Claim 9
Dependent Claim
32 words
A method according to claim 6 including the step of forming source/drain regions in said face on said opposite sides of said gate, by introducing impurities using said gate as a mask.
Claim 10
Dependent Claim
21 words
A method according to claim 7 wherein said body is P-type in said transistor area and said source/drain regions are N-type.
Claim 11
Dependent Claim
21 words
A method according to claim 7 wherein said body is N-type in said transistor area and said source/drain regions are P-type.
Claim 12
Dependent Claim
33 words
A method according to claim 6 wherein after said first step of heating, etching said face to remove said second layer and unreacted cobalt, then subjecting said wafer to said second heat treatment.
Claim 13
Dependent Claim
19 words
A method according to claim 6 wherein said first layer is of about 165 to 300 Å in thickness.
Claim 14
Dependent Claim
18 words
A method according to claim 11 wherein said second layer is about 50 to 150 Å in thickness.
Claim 15
Dependent Claim
22 words
A method according to claim 10 wherein said second heat treatment is at a temperature of no more than about 700° C.
Claim 16
Independent Claim
88 words
A method of providing cobalt disilicide contacts over a semiconductor body comprising the steps of: applying a first layer comprising cobalt to exposed areas of a semiconductor body comprising silicon: applying a second layer including titanium nitride or titanium tungsten over said first layer; heating said body at a temperature of 420° C. to 550° C. to cause formation of cobalt monosilicide on said semiconductor body; and heating said body to a temperature in excess of said first temperature range to convert the cobalt monosilicide into cobalt disilicide.
Claim 17
Independent Claim
88 words
A method of providing cobalt disilicide contacts over a semiconductor body comprising the steps of: applying a first layer comprising cobalt to exposed areas of a semiconductor body comprising silicon: applying a second layer including titanium nitride or titanium tungsten over said first layer; heating said body at a temperature of 420° C. to 550° C. to cause formation of cobalt monosilicide on said semiconductor body; and heating said body to a temperature in excess of said first temperature range to convert the cobalt monosilicide into cobalt disilicide.
Claim 18
Dependent Claim
38 words
The method as recited in claim 14 wherein said second heating step further comprises the step of rapidly thermally annealing said cobalt monosilicide at a temperature of about 700° C. to convert said cobalt monosilicide into cobalt disilicide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-22 | 2000-04-22 | 2000-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-22 | 2004-04-22 | 2004-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-10-22 | 2008-04-22 | 2008-10-22 | $7700.00 | Window Closed / Lapsed |