US5047367A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for formation of a self aligned titanium nitride/cobalt silicide bilayer
Assignee: Intel Corp
•
Filing: 1990-06-08
•
Granted: 1991-09-10
•
Expires: 2010-06-08
Abstract
Abstract A process for the formation of a titanium nitride/cobalt silicide bilayer for use in semiconductor processing. Titanium and then cobalt are deposited on a silicon substrate by sputter deposition techniques. The substrate is then annealed. During this process the titanium first cleans the silicon surface of the substrate of any native oxide. During the anneal, the titanium diffuses upward and the cobalt diffuses downward. The cobalt forms a high quality epitaxial cobalt silicide layer on the silicon substrate. The titanium layer diffuses upward to the surface of the bilayer. The anneal is carried out in a nitrogen or ammonia ambient, so that a titaniun nitride layer is formed. The resulting structure can be used in self aligned silicide technology, as a contact fill material for contact to electrical regions of the device, and as a diffusion barrier preventing the diffusion of aluminum from a subsequently deposited aluminum layer or the diffusion of dopants from a subsequently grown doped selective silicon layer into the silicon substrate.
Inventors
- 👤 Chin-Shih Wei
- 👤 David B. Fraser
- 👤 Venkatesan Murali
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:20
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; H10D64/011; H10D64/0111; H10D64/0112; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6316; H10P50/00; H10P50/60; H10P50/66; H10P50/663; H10P50/667; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10W20/057; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W20/4437; H10W20/4441; Y; Y10; Y10S; Y10S148/00; Y10S148/147
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
86 words
A process for forming a bilayer on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer.
Claim 2
Dependent Claim
86 words
A process for forming a bilayer on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer.
Claim 3
Dependent Claim
37 words
The process as described in claim 1 wherein said near-noble metal silicide layer has a thickness in the range of 300-2000 Angstroms and said refractory metal nitride layer has a thickness in the range of 50-500 Angstroms.
Claim 4
Dependent Claim
100 words
The process as described in claim 1 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, and said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal.
Claim 5
Dependent Claim
100 words
The process as described in claim 2 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, and said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal.
Claim 6
Dependent Claim
16 words
The process as described in claim 1 wherein said near-noble metal silicide is of epitaxial quality.
Claim 7
Dependent Claim
16 words
The process as described in claim 2 wherein said near-noble metal silicide is of epitaxial quality.
Claim 8
Dependent Claim
16 words
The process as described in claim 3 wherein said near-noble metal silicide is of epitaxial quality.
Claim 9
Dependent Claim
16 words
The process as described in claim 4 wherein said near-noble metal silicide is of epitaxial quality.
Claim 10
Dependent Claim
36 words
The process as described in any one of claims 1-8 wherein said refractory metal is titanium, said refractory metal nitride is titanium nitride, said near-noble metal is cobalt and said near-noble metal silicide is cobalt silicide.
Claim 11
Dependent Claim
163 words
A process for forming a bilayer on exposed silicon regions on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing a first etch to remove said near-noble metal layer from all regions except said exposed silicon regions; performing a second etch to remove said refractory metal layer from all regions except said exposed silicon regions; performing a third etch to remove said refractory metal nitride layer; selectively depositing a silicon layer on said near-noble metal silicide layer to form said bilayer comprising a near-noble metal silicide layer and a selective silicon layer.
Claim 12
Dependent Claim
163 words
A process for forming a bilayer on exposed silicon regions on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing a first etch to remove said near-noble metal layer from all regions except said exposed silicon regions; performing a second etch to remove said refractory metal layer from all regions except said exposed silicon regions; performing a third etch to remove said refractory metal nitride layer; selectively depositing a silicon layer on said near-noble metal silicide layer to form said bilayer comprising a near-noble metal silicide layer and a selective silicon layer.
Claim 13
Dependent Claim
22 words
The process as described in claim 10 wherein said near-noble metal silicide layer has a thickness in the range of 300-2000 Angstroms.
Claim 14
Dependent Claim
126 words
The process as described in claim 10 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 15
Dependent Claim
126 words
The process as described in claim 11 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 16
Dependent Claim
20 words
The process as described in claim 10 wherein said near-noble metal silicide and said selective silicon are of epitaxial quality.
Claim 17
Dependent Claim
20 words
The process as described in claim 11 wherein said near-noble metal silicide and said selective silicon are of epitaxial quality.
Claim 18
Dependent Claim
20 words
The process as described in claim 12 wherein said near-noble metal silicide and said selective silicon are of epitaxial quality.
Claim 19
Dependent Claim
20 words
The process as described in claim 13 wherein said near-noble metal silicide and said selective silicon are of epitaxial quality.
Claim 20
Dependent Claim
36 words
The process as described in any one of claims 10-17 wherein said refractory metal is titanium, said refractory metal nitride is titanium nitride, said near-noble metal is cobalt and said near-noble metal silicide is cobalt silicide.
Claim 21
Dependent Claim
165 words
A process for forming a fill for contact areas on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said contact areas on said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing a first etch of said near-noble metal layer from all regions except said contact areas; performing a second etch of said refractory metal layer from all regions except said contact areas; conformally depositing a third layer consisting essentially of aluminum; removing said aluminum from all regions except said contact areas to form said fill comprising a self aligned silicide layer, a self aligned refractory metal nitride layer and an aluminum layer.
Claim 22
Dependent Claim
165 words
A process for forming a fill for contact areas on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said contact areas on said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing a first etch of said near-noble metal layer from all regions except said contact areas; performing a second etch of said refractory metal layer from all regions except said contact areas; conformally depositing a third layer consisting essentially of aluminum; removing said aluminum from all regions except said contact areas to form said fill comprising a self aligned silicide layer, a self aligned refractory metal nitride layer and an aluminum layer.
Claim 23
Dependent Claim
49 words
The process as described in claim 19 wherein said near-noble metal silicide layer has a thickness in the range of 300-2000 Angstroms, said refractory metal nitride layer has a thickness in the range of 50-500 Angstroms and said aluminum layer has a thickness in the range of 1000-20,000 Angstroms.
Claim 24
Dependent Claim
126 words
The process as described in claim 19 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 25
Dependent Claim
126 words
The process as described in claim 20 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 26
Dependent Claim
36 words
The process as described in any one of claims 19-22 wherein said refractory metal is titanium, said refractory metal nitride is titanium nitride, said near-noble metal is cobalt and said near-noble metal silicide is cobalt silicide.
Claim 27
Dependent Claim
154 words
A process for forming a fill for contact areas on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said contact areas on said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing a first etch of said near-noble metal layer from all regions except said contact areas; etching said refractory metal layer from all regions except said contact areas; selectively depositing a third layer comprising silicon in said contact areas to form said fill comprising a self aligned silicide layer, a self aligned refractory metal nitride layer and a selective silicon layer.
Claim 28
Dependent Claim
154 words
A process for forming a fill for contact areas on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said contact areas on said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing a first etch of said near-noble metal layer from all regions except said contact areas; etching said refractory metal layer from all regions except said contact areas; selectively depositing a third layer comprising silicon in said contact areas to form said fill comprising a self aligned silicide layer, a self aligned refractory metal nitride layer and a selective silicon layer.
Claim 29
Dependent Claim
50 words
The process as described in claim 24 wherein said near-noble metal silicide layer has a thickness in the range of 300-2000 Angstroms, said refractory metal nitride layer has a thickness in the range of 50-500 Angstroms and said selective silicon layer has a thickness in the range of 1000-20,000 Angstroms.
Claim 30
Dependent Claim
126 words
The process as described in claim 24 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 31
Dependent Claim
126 words
The process as described in claim 25 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 32
Dependent Claim
16 words
The process as described in claim 24 wherein said near-noble metal silicide is of epitaxial quality.
Claim 33
Dependent Claim
16 words
The process as described in claim 25 wherein said near-noble metal silicide is of epitaxial quality.
Claim 34
Dependent Claim
16 words
The process as described in claim 26 wherein said near-noble metal silicide is of epitaxial quality.
Claim 35
Dependent Claim
16 words
The process as described in claim 27 wherein said near-noble metal silicide is of epitaxial quality.
Claim 36
Dependent Claim
36 words
The process as described in any one of claims 24-31 wherein said refractory metal is titanium, said refractory metal nitride is titanium nitride, said near-noble metal is cobalt and said near-noble metal silicide is cobalt silicide.
Claim 37
Dependent Claim
157 words
A process for forming a fill for contact areas on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said contact areas on said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing an etch of said near-noble metal layer from all regions except said contact areas; performing an etch of said refractory metal layer from all regions except said contact areas; selectively depositing a third layer comprising tungsten in said contact areas to form said fill comprising a self aligned near-noble metal silicide layer, a self aligned refractory metal nitride layer, and selective tungsten layer.
Claim 38
Dependent Claim
157 words
A process for forming a fill for contact areas on a silicon substrate comprising the steps of: conformally depositing on said silicon substrate a first layer comprising a refractory metal; conformally depositing on said first layer a second layer comprising a near-noble metal; performing an anneal on said silicon substrate in a nitrogen containing gas selected from the group consisting of nitrogen and ammonia to form a near-noble metal silicide layer disposed above said contact areas on said silicon substrate and a refractory metal nitride layer disposed above said near-noble metal silicide layer; performing an etch of said near-noble metal layer from all regions except said contact areas; performing an etch of said refractory metal layer from all regions except said contact areas; selectively depositing a third layer comprising tungsten in said contact areas to form said fill comprising a self aligned near-noble metal silicide layer, a self aligned refractory metal nitride layer, and selective tungsten layer.
Claim 39
Dependent Claim
50 words
The process as described in claim 33 wherein said near-noble metal silicide layer has a thickness in the range of 300-2000 Angstroms, said refractory metal nitride layer has a thickness in the range of 50-500 Angstroms and said selective tungsten layer has a thickness in the range of 1000-20,000 Angstroms.
Claim 40
Dependent Claim
126 words
The process as described in claim 33 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 41
Dependent Claim
126 words
The process as described in claim 34 wherein said anneal comprises a first and a second anneal, said first anneal is performed at a temperature in the range of 600-750 degrees Celsius, said first anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, said first anneal is performed before said first etch and said second etch, said second anneal is performed at a temperature in the range of 850-950 degrees Celsius, said second anneal is performed for a length of time in the range of 15-30 seconds for rapid thermal anneal and 20-40 minutes for furnace anneal, and said second anneal is performed after said first etch and said second etch.
Claim 42
Dependent Claim
36 words
The process as described in any one of claims 33-36 wherein said refractory metal is titanium, said refractory metal nitride is titanium nitride, said near-noble metal is cobalt and said near-noble metal silicide is cobalt silicide.
References Cited (Backward Citations)
US4206540A
Cited
US4378628A
Cited
US4398344A
Cited
JPS62298109A
Cited
US4864378A
Cited
US4931353A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-09 | 1995-03-11 | 1995-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-09 | 1999-03-11 | 1999-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-09 | 2003-03-11 | 2003-09-10 | $7700.00 | Window Closed / Lapsed |