Method for fabricating stacked layer silicon nitride for low leakage and high capacitance
Assignee: Micron Technology Inc
•
Filing: 1994-09-14
•
Granted: 1999-06-15
•
Expires: 2014-09-14
Abstract
Abstract A method is provided for forming silicon nitride stacks. A semiconductor substrate is cleaned to remove any native oxide, and an insulative material is disposed thereon. A plurality of films are deposited superjacent the insulative material, and each of the plurality of films converted into a dielectric to form a multi-layered stack. A fill layer is formed superjacent the multi-layered stack to seal any pinholes. The fill layer is formed by at least one of low temperature chemical vapor deposition (CVD) of oxide, low temperature deposition of nitride, low temperature re-oxidation of ozone, the low temperature is at least 20° C.
Inventors
- 👤 Randhir P. S. Thakur
- 👤 Gurtej Singh Sandhu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:17
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/694; H10P14/6943; H10P14/69433; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6326; H10P14/6328; H10P14/6332; H10P14/6334; H10P14/65; H10P14/6502; H10P14/6504; H10P14/6516; H10P14/6518; H10P14/6519; H10P14/6522; H10P14/6529; H10P14/66; H10P14/662; H10P14/692; H10P14/6921; H10P14/69215; H10P70/00; H10P70/10; H10P70/12; H10P70/125; H10W; H10W20/00; H10W20/01; H10W20/071; H10P14/6316; H10P14/6322
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
119 words
A method for fabricating muiti-layer dielectrics, the method comprising the steps of: cleaning of a silicon substrate with a reactive gas at a temperature which is within a range of 850° C. to 1250° C. to remove native oxide from the silicon substrate, the reactive gas comprising at least one of NF 3 , GeH 4 , HF, and H 2 ; after the step of cleaning, rapid thermal nitridizing followed by depositing nitride to form a first dielectric layer on the silicon substrate; depositing a semiconductor layer on the first dielectric layer; rapid thermal nitridizing to convert at least a portion of the semiconductor layer to a second dielectric layer; and rapid thermal oxidizing the second dielectric layer.
Claim 2
Independent Claim
119 words
A method for fabricating muiti-layer dielectrics, the method comprising the steps of: cleaning of a silicon substrate with a reactive gas at a temperature which is within a range of 850° C. to 1250° C. to remove native oxide from the silicon substrate, the reactive gas comprising at least one of NF 3 , GeH 4 , HF, and H 2 ; after the step of cleaning, rapid thermal nitridizing followed by depositing nitride to form a first dielectric layer on the silicon substrate; depositing a semiconductor layer on the first dielectric layer; rapid thermal nitridizing to convert at least a portion of the semiconductor layer to a second dielectric layer; and rapid thermal oxidizing the second dielectric layer.
Claim 3
Dependent Claim
49 words
A method, as in claim 1, wherein the step of depositing the semiconductor layer and the step of depositing the nitride are done with a process comprising at least one of molecular beam epitaxial, chemical vapor deposition, low pressure chemical vapor deposition, and rapid thermal process chemical vapor deposition.
Claim 4
Independent Claim
97 words
A method for fabricating multi-layer dielectrics, the method comprising the steps of: cleaning of a silicon substrate with vapor phase hydrogen halide at a temperature which is as low as 20° C. to remove native oxide from the silicon substrate; after the step of cleaning, rapid thermal nitridizing followed by depositing nitride to form a first dielectric layer on the silicon substrate; depositing a semiconductor layer on the first dielectric layer; rapid thermal nitridizing to convert at least a portion of the semiconductor layer to a second dielectric layer; and rapid thermal oxidizing the second dielectric layer.
Claim 5
Independent Claim
97 words
A method for fabricating multi-layer dielectrics, the method comprising the steps of: cleaning of a silicon substrate with vapor phase hydrogen halide at a temperature which is as low as 20° C. to remove native oxide from the silicon substrate; after the step of cleaning, rapid thermal nitridizing followed by depositing nitride to form a first dielectric layer on the silicon substrate; depositing a semiconductor layer on the first dielectric layer; rapid thermal nitridizing to convert at least a portion of the semiconductor layer to a second dielectric layer; and rapid thermal oxidizing the second dielectric layer.
Claim 6
Dependent Claim
49 words
A method, as in claim 3, wherein the step of depositing the semiconductor layer and the step of depositing the nitride are done with a process comprising at least one of molecular beam epitaxial, chemical vapor deposition, low pressure chemical vapor deposition, and rapid thermal process chemical vapor deposition.
References Cited (Backward Citations)
US4435447A
Cited
US4277320A
Cited
JPS5817677A
Cited
US4996081A
Cited
CA1252372A
Cited
JPS62149139A
Cited
US4715937A
Cited
US4855258A
Cited
US5178682A
Cited
US5100495A
Cited
US5332697A
Cited
US5173152A
Cited
US5250452A
Cited
US5238500A
Cited
US5067218A
Cited
US5294568A
Cited
US5330935A
Cited
US5032545A
Cited
US5248380A
Cited
US5208189A
Cited
US5422291A
Cited
US5423944A
Cited
US5380399A
Cited
US5445999A
Cited
US5503708A
Cited
US5376593A
Cited
US5264396A
Cited
US5443863A
Cited
US5547642A
Cited
US5451425A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-06-14 | 2002-12-14 | 2003-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-06-14 | 2006-12-14 | 2007-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-06-14 | 2010-12-14 | 2011-06-15 | $7700.00 | Window Closed / Lapsed |