Process for preventing a native oxide from forming on the surface of a semiconductor material and integrated circuit capacitors produced thereby
Assignee: Micron Technology Inc
•
Filing: 1990-10-30
•
Granted: 1991-07-16
•
Expires: 2010-10-30
Abstract
Abstract A process for forming silicon nitride layers on silicon substrates which includes initially heating the silicon substrates in a rapid thermal processor and in a substantially oxygen-free and residual moisture free environment to form a thin Si 3 N 4 layer directly on the silicon surface which is free of any measurable native SiO 2 thereon. Then, the nitridized wafers are transferred into a conventional nitride furnace where the thin Si 3 N 4 layers may be increased in thickness by a desired amount. Typically, the initial or first Si 3 N 4 layer thickness will be about 10-30 angstroms and the second Si 3 N 4 layer will be on the order of 80 angstroms or more to form a composite Si 3 N 4 layer of about 100-150 angstroms in total thickness. This novel process and the high dielectric constant integrated circuit capacitors produced thereby are highly useful in the manufacture of certain very large scale integrated circuit (VLSI) components such as dynamic random access memories and the like.
Inventors
- 👤 Trung T. Doan
- 👤 Tyler A. Lowrey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 02:15
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6322; H10D; H10D1/00; H10D1/01; H10D1/045; H10D1/047; H10P14/6316; H10P70/00; H10P70/10; H10P70/12; H10P14/69; H10P14/694; H10P14/6943; H10P14/69433; Y; Y10; Y10S; Y10S438/00; Y10S438/906; Y10S438/974
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
139 words
A process for forming a silicon nitride, Si 3 N 4 , dielectric layer on the surface of a silicon substrate while substantially eliminating the formation of a native silicon oxide or silicon dioxide on the silicon substrate surface, which includes the steps of: a. cleaning said surface of said silicon substrate to remove any native oxide thereon, b. inserting the cleaned silicon substrate into a rapid thermal processing chamber which is cooled down to a predetermined low initial temperature and flushed to remove substantially all oxygen molecules and residual moisture therefrom, and c. heating said rapid thermal processing chamber to a predetermined elevated temperature within a predetermined time in the presence of a nitrogen-containing reactant gas to thereby thermally decompose said nitrogen-containing reactant gas and form a thin layer of silicon nitride on the surface of said substrate.
Claim 2
Dependent Claim
139 words
A process for forming a silicon nitride, Si 3 N 4 , dielectric layer on the surface of a silicon substrate while substantially eliminating the formation of a native silicon oxide or silicon dioxide on the silicon substrate surface, which includes the steps of: a. cleaning said surface of said silicon substrate to remove any native oxide thereon, b. inserting the cleaned silicon substrate into a rapid thermal processing chamber which is cooled down to a predetermined low initial temperature and flushed to remove substantially all oxygen molecules and residual moisture therefrom, and c. heating said rapid thermal processing chamber to a predetermined elevated temperature within a predetermined time in the presence of a nitrogen-containing reactant gas to thereby thermally decompose said nitrogen-containing reactant gas and form a thin layer of silicon nitride on the surface of said substrate.
Claim 3
Dependent Claim
23 words
The process defined in claim 1 wherein said nitrogen containing reactant gas is either ammonia, NH 3 , or nitrogen, N 2 .
Claim 4
Dependent Claim
82 words
The process defined in claim 1 wherein said rapid thermal processing chamber is initially flushed with an inert gas such as nitrogen to remove substantially all oxygen molecules and residual moisture therefrom, and said silicon substrate is heated in said rapid thermal processing chamber to an elevated temperature on the order of about 1000° C. within about 10 to 20 seconds to form a thin layer of silicon nitride of approximately 10-30 angstroms in thickness on the surface of said silicon substrate.
Claim 5
Dependent Claim
23 words
The process defined in claim 3 wherein said nitrogen containing reactant gas is either ammonia, NH 3 , or nitrogen, N 2 .
Claim 6
Dependent Claim
65 words
The process defined in claim 4 which further includes transferring said silicon substrate processed in said rapid thermal processing chamber to a conventional nitride furnace and forming thereon an additional silicon nitride layer on the order of about 80 angstroms or more in thickness so that the total silicon nitride dielectric layer thickness is formed to a value on the order of about 50-150 angstroms.
Claim 7
Dependent Claim
140 words
A process for forming a thin layer of silicon nitride, Si 3 N 4 , wherein said layer is formed by: a. introducing a silicon wafer into a small heating chamber, b. flushing said heating chamber to remove substantially all residual oxygen and moisture therefrom, and c. passing a nitrogen-containing reactant gas comprising nitrogen, N 2 , or ammonia, NH 3 , through said small heating chamber at a controlled flow rate until a gas stabilized condition and ambient oxygen-free nitrogen concentration is attained within said heating chamber, and d. rapidly heating said silicon wafer in said heating chamber in the presence of said nitrogen-containing reactant gas to a predetermined elevated temperature within a predetermined period of time to form said Si 3 N 4 layer thereon by the thermal reaction of nitrogen with the surface of said silicon wafer.
Claim 8
Dependent Claim
140 words
A process for forming a thin layer of silicon nitride, Si 3 N 4 , wherein said layer is formed by: a. introducing a silicon wafer into a small heating chamber, b. flushing said heating chamber to remove substantially all residual oxygen and moisture therefrom, and c. passing a nitrogen-containing reactant gas comprising nitrogen, N 2 , or ammonia, NH 3 , through said small heating chamber at a controlled flow rate until a gas stabilized condition and ambient oxygen-free nitrogen concentration is attained within said heating chamber, and d. rapidly heating said silicon wafer in said heating chamber in the presence of said nitrogen-containing reactant gas to a predetermined elevated temperature within a predetermined period of time to form said Si 3 N 4 layer thereon by the thermal reaction of nitrogen with the surface of said silicon wafer.
Claim 9
Dependent Claim
62 words
The process defined in claim 6 wherein said silicon wafer is inserted into a relatively small heating chamber having a volume on the order of about three (3) liters, whereby said relatively small heating chamber is adapted to be purged and flushed substantially free of all residual oxygen and moisture before it is rapidly heated up to a predetermined elevated reaction temperature.
Claim 10
Dependent Claim
19 words
The process defined in claim 7 wherein said small heating chamber is contained within a rapid thermal processing unit.
Claim 11
Dependent Claim
25 words
The process defined in claim 6 wherein said Si 3 N 4 layer is formed in accordance with the following expression: 4NH.sub.3 +3Si→Si.sub.3 N.sub.4 +6H.sub.2
Claim 12
Dependent Claim
64 words
The process defined in claim 10 which further includes forming a second layer of Si 3 N 4 on top of said surface Si 3 N 4 layer by reacting dichlorosilane and ammonia at a predetermined elevated temperature in the presence of said silicon wafer, whereby the ε·A/d capacitance defining ratio for the combination of said first and second silicon nitride layers is maximized.
Claim 13
Dependent Claim
124 words
A process for forming thin film layers of silicon nitride, Si 3 N 4 , on the surfaces of silicon substrates without forming thereon a native silicon oxide or silicon dioxide layer to any significant degree, which comprises the steps of: a. inserting said wafers in a small rapid thermal processing (RTP) unit which is flushed with an inert purge gas and thereafter filled with a nitrogen-containing reactant gas, b. rapidly heating said reactant gas in the presence of said wafers to a predetermined elevated temperature within a predetermined time, and thereby c. thermally decomposing said reactant gas to thereby react elemental nitrogen with silicon at the surfaces of said wafers to form thin layers of silicon nitride, Si 3 N 4 , thereon.
Claim 14
Dependent Claim
124 words
A process for forming thin film layers of silicon nitride, Si 3 N 4 , on the surfaces of silicon substrates without forming thereon a native silicon oxide or silicon dioxide layer to any significant degree, which comprises the steps of: a. inserting said wafers in a small rapid thermal processing (RTP) unit which is flushed with an inert purge gas and thereafter filled with a nitrogen-containing reactant gas, b. rapidly heating said reactant gas in the presence of said wafers to a predetermined elevated temperature within a predetermined time, and thereby c. thermally decomposing said reactant gas to thereby react elemental nitrogen with silicon at the surfaces of said wafers to form thin layers of silicon nitride, Si 3 N 4 , thereon.
Claim 15
Dependent Claim
35 words
The process defined in claim 11 wherein said silicon wafers are heated in said rapid thermal processing unit to an elevated temperature on the order of about 1000° C. within about 10 to 20 seconds.
Claim 16
Dependent Claim
30 words
The process defined in claim 12 wherein said thin layers of silicon nitride, Si 3 N 4 , are formed in accordance with the following expression: 4NH.sub.3 +3Si→Si.sub.3 N.sub.4 +6H.sub.2
Claim 17
Dependent Claim
67 words
The process defined in claim 13 which further includes forming a second layer of silicon nitride, Si 3 N 4 , on top of the first formed layers of silicon nitride by reacting dichlorosilane and ammonia at a predetermined elevated temperature in the presence of said silicon wafers, whereby the ε·A/d capacitance defining quotient for the combination of said first and second silicon nitride layers is maximized.
Claim 18
Dependent Claim
38 words
The process defined in claim 9 wherein said silicon wafers are heated in a rapid thermal processing unit to an elevated temperature on the order of about a 1000° C. or greater within about ten to twenty seconds.
Claim 19
Dependent Claim
37 words
The process defined in claim 10 wherein said silicon wafers are heated in a rapid thermal processing unit to an elevated temperature on the order of about 1000° C. or greater within about ten to twenty seconds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-15 | 1995-01-14 | 1995-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-15 | 1999-01-14 | 1999-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-15 | 2003-01-14 | 2003-07-16 | $7700.00 | Window Closed / Lapsed |