Growth of bulk single crystals of aluminum nitride
Assignee: Wolfspeed Inc
•
Filing: 1996-10-17
•
Granted: 1999-01-12
•
Expires: 2016-10-17
Abstract
Abstract Bulk, low impurity aluminum nitride (AlN) single crystals are grown by sublimation or similar deposition techniques at growth rates greater than 0.5 mm/hr.
Inventors
- 👤 Charles Eric Hunter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:01
CPC Classifications
C; C30; C30B; C30B23/00; C30B23/002; C30B23/005; C30B25/00; C30B29/00; C30B29/10; C30B29/38; Y; Y10; Y10S; Y10S117/00; Y10S117/90; Y10T; Y10T117/00; Y10T117/10; Y10T117/1016; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/266
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
55 words
A method of producing bulk single crystals of AlN at enhanced growth rates comprising: growing AlN by depositing vapor species containing Al and N on the growth surface of a seed crystal; while providing effusion of the growing crystal interface sufficient to grow AlN in single crystalline form at a rate greater than 0.5 mm/hour.
Claim 2
Independent Claim
55 words
A method of producing bulk single crystals of AlN at enhanced growth rates comprising: growing AlN by depositing vapor species containing Al and N on the growth surface of a seed crystal; while providing effusion of the growing crystal interface sufficient to grow AlN in single crystalline form at a rate greater than 0.5 mm/hour.
Claim 3
Dependent Claim
28 words
The method of claim 1 including the step of carrying out the growing step in a crucible while maintaining the height-to-diameter (H:D) aspect ratio less than about 6:1.
Claim 4
Dependent Claim
23 words
The method of claim 2 including the step of heating the crucible by a horizontally disposed heater positioned below the crystal growth interface.
Claim 5
Dependent Claim
17 words
The method of claim 3 including the step of positioning the horizontally disposed heater below the crucible.
Claim 6
Dependent Claim
79 words
The method of claim 1 wherein the vapor species are provided by a substantially constant flux of source vapor provided by a source selected from the group consisting of AlN crystal or crystals, sintered AlN, hydrostatically pressed AlN, AlN powder, AlCl 3 gas, NH 3 gas, vaporized Al, N 2 gas, atomic nitrogen, nitrogen ions, N 2 gas in combination with nitrogen ions, N 2 gas in combination with atomic nitrogen, and N 2 gas that has been excited.
Claim 7
Dependent Claim
54 words
The method of claim 1 including the steps of carrying out the growing step within a crucible and providing effusion at the growing crystal interface by removing gas at an outlet structure in the crucible located beyond the periphery of the seed crystal at approximately the same level or higher than the seed crystal.
Claim 8
Dependent Claim
24 words
The method of claim 6 including the step of providing an effusion baffle to direct gas in the crucible toward the growing crystal interface.
Claim 9
Dependent Claim
54 words
The method of claim 1 including the step of pulling the crystal during the growing and effusion steps to maintain the growing crystal interface at substantially the same position, and providing an effusion outlet located beyond the periphery of the seed crystal at approximately the same level or higher than the growing crystal interface.
Claim 10
Dependent Claim
45 words
The method of claim 1 including the step of holding the seed at a constant position during the growing and effusion steps so that the growing crystal interface moves toward the source as it grows, and providing an effusion outlet accommodating the advancing crystal interface.
Claim 11
Dependent Claim
81 words
The method of claim 1 including the steps of growing the crystal by sublimation without gas assist, holding the temperature at the source in the range from about 2025° C. to about 2492° C., while holding the temperature at the growing crystal interface in the range of about 1900° C. to about 2488° C., while providing effusion at the growing crystal interface at an effusion rate in the range of about 2% to about 80% of the total vapor flow rate.
Claim 12
Dependent Claim
79 words
The method of claim 1 including the steps of growing the crystal with gas-assisted effusion, holding the temperature at the source in the range from about 2025° C. to about 2492° C., while holding the temperature at the growing crystal interface in the range of about 1900° C. to about 2488° C., while providing effusion at the growing crystal interface at an effusion rate in the range of about 12% to about 99.9% of the total vapor flow rate.
Claim 13
Dependent Claim
40 words
The method of claim 1 including the step of exposing the seed crystal at both a primary growth surface as well as the circumferential edge thereof to define a crystal growing interface encouraging the growth of a large diameter crystal.
Claim 14
Dependent Claim
13 words
The method of claim 1 including the step of utilizing an effusion-assist gas.
Claim 15
Dependent Claim
49 words
The method of claim 13 wherein the effusion-assist gas is selected from the group consisting of argon, N 2 , nitrogen ions, atomic nitrogen, a mixture of nitrogen and nitrogen ions, a mixture of N 2 and atomic nitrogen, and a mixture containing N 2 and partially ionized nitrogen.
Claim 16
Dependent Claim
39 words
The method of claim 1 wherein the bulk single crystals of AlN are grown in a form selected from the group consisting of intrinsic AlN, doped AlN, and AlN alloys and compounds containing greater than 50% Al and N.
Claim 17
Dependent Claim
38 words
The method of claim 1 wherein said growing step is carried out utilizing a seed crystal having a diameter of greater than about one inch and the AlN is grown with a diameter greater than about one inch.
Claim 18
Dependent Claim
13 words
A bulk single crystal of AlN produced by the method of claim 16.
Claim 19
Independent Claim
54 words
A method for commercial production of bulk single crystals of AlN, said method comprising; growing AlN by depositing vapor species containing Al and N on the growth surface of a seed crystal; while providing effusion of the growing crystal interface at an effusion rate greater than about 2% of the total vapor flow rate.
Claim 20
Independent Claim
54 words
A method for commercial production of bulk single crystals of AlN, said method comprising; growing AlN by depositing vapor species containing Al and N on the growth surface of a seed crystal; while providing effusion of the growing crystal interface at an effusion rate greater than about 2% of the total vapor flow rate.
Claim 21
Dependent Claim
34 words
The method of claim 18 including the step of growing the crystal without gas assist with an effusion rate in the range from about 2% to about 80% of the total vapor flow rate.
Claim 22
Dependent Claim
34 words
The method of claim 18 including the step of growing the crystal with gas-assisted effusion with an effusion rate in the range of about 12% to about 99.9% of the total vapor flow rate.
Claim 23
Dependent Claim
29 words
A bulk single crystal of AlN produced by the method of claim 18 at a growth rate greater than 0.5 mm/hour and having a diameter greater than one inch.
Claim 24
Dependent Claim
39 words
the method of claim 18 wherein the bulk single crystals of AlN are grown in a form selected from the group consisting of intrinsic AlN, doped AlN, and AlN alloys and compounds containing greater than 50% Al and N.
Claim 25
Dependent Claim
38 words
The method of claim 18 wherein said growing step is carried out utilizing a seed crystal having a diameter of greater than about one inch and the AlN is grown with a diameter greater than about one inch.
Claim 26
Dependent Claim
13 words
A bulk single crystal of AlN produced by the method of claim 23.
Claim 27
Dependent Claim
28 words
The method of claim 18 including the step of carrying out the growing step in a crucible while maintaining the height-to-diameter (H:D) aspect ratio less than about 6:1.
Claim 28
Independent Claim
87 words
A method of producing a prepared substrate comprising the steps of: growing a bulk single crystal of AlN by depositing vapor species containing Al and N on the growth surface of a seed crystal; while providing effusion of the growing crystal interface sufficient to grow AlN in single crystalline form at a rate greater than 0.5 mm/hour; and thereafter cutting a wafer from the bulk single crystal; and preparing a surface on the wafer receptive to an epitaxial layer; and depositing an epitaxial layer on the surface.
Claim 29
Independent Claim
87 words
A method of producing a prepared substrate comprising the steps of: growing a bulk single crystal of AlN by depositing vapor species containing Al and N on the growth surface of a seed crystal; while providing effusion of the growing crystal interface sufficient to grow AlN in single crystalline form at a rate greater than 0.5 mm/hour; and thereafter cutting a wafer from the bulk single crystal; and preparing a surface on the wafer receptive to an epitaxial layer; and depositing an epitaxial layer on the surface.
Claim 30
Dependent Claim
16 words
The method of claim 26 including the step of forming a component on the prepared substrate.
Claim 31
Dependent Claim
59 words
The method of claim 27 wherein the component material is selected from the group consisting of AlN, Al 0 .8 In 0 .2 N, Al x In y N where X is 0→1, InN, Al 0 .8 In 0 .2 N/InN, BN, BN/diamond, diamond, BP, AlP and InP with the component material being doped n-type, p-type, intrinsic or compensated.
Claim 32
Dependent Claim
48 words
The method of claim 27 wherein the component is formed in multiple layers with the component material for at least some of said layers being selected from the group consisting of AlN, Al x IN y N where X is 0→1, InN, AlP, BN, diamond, InP and BP.
References Cited (Backward Citations)
US3121062A
Cited
US3275415A
Cited
US3634149A
Cited
US4147572A
Cited
US4152182A
Cited
US4382837A
Cited
US4489128A
Cited
US4597949A
Cited
US4897149A
Cited
USRE34861E
Cited
US5387804A
Cited
US5034604A
Cited
US5350699A
Cited
US5270263A
Cited
US5433167A
Cited
US5679965A
Cited
US5637146A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-01-11 | 2002-07-13 | 2003-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-01-11 | 2006-07-13 | 2007-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-01-11 | 2010-07-13 | 2011-01-12 | $7700.00 | Window Closed / Lapsed |