Abstract An electrically conductive cement having substantially stable conductivity and resistance characteristics under high humidity conditions comprises a mixture of two epoxy resins with the proportion of each epoxy resin adjusted to provide a volumetric shrinkage in the mixture in the 4 to 16% and a conductive silver particular filler including agglomerates having size and surface characteristics that maintain stable electrical contact with an electrical component lead. The epoxy mixture is preferably a combination of a high-shrinkage epoxy resin and a lower-shrinkage epoxy resin in the appropriate amounts of each so as to produce the desired volumetric shrinkage characteristic. The conductive particle filler is preferably an admixture of silver flakes, silver powder, and an effective amount of silver agglomerates. The agglomerates are irregularly shaped particles having multiple surface indentations and recesses to produce many rough-edged salients or ridges and having a particle length, width, and thickness aspect ratio of about 1:1:1. An effective amount of such agglomerates appears to effect penetration of surface oxides when establishing the cemented connection as a result of the volumetric shringage of the polymeric carrier upon curing.
An assembly comprising a substrate having a circuit printed thereon and at least one electrical component electrically connected to said circuit with an electrically conductive cement, the electrically conductive cement comprising a polymeric carrier having a volumetric shrinkage characteristic of about 4 to about 16%; and a filler comprising about 60 to about 90% by weight of the cement including conductive particles consisting of: i) agglomerate particles having a mean particle size of about 4.5 microns, an aspect ratio of about 1:1:1 and a rough external appearance characterized by sufficient recesses and ridge-like boundaries so as to effect enhanced electrical contact between surfaces adhered with the cement, ii) a mixture of flake particles having a FSSS of about 0.90 to about 1.30 microns and a surface area of about 0.3 to 0.6 m 2 /g and a particle size distribution of about 90%<14 microns, 50%<7 microns, and 10%<2 microns, and iii) powder particles having a mean particle size of about 1.6 microns.
Claim 2
Dependent Claim
162 words
An assembly comprising a substrate having a circuit printed thereon and at least one electrical component electrically connected to said circuit with an electrically conductive cement, the electrically conductive cement comprising a polymeric carrier having a volumetric shrinkage characteristic of about 4 to about 16%; and a filler comprising about 60 to about 90% by weight of the cement including conductive particles consisting of: i) agglomerate particles having a mean particle size of about 4.5 microns, an aspect ratio of about 1:1:1 and a rough external appearance characterized by sufficient recesses and ridge-like boundaries so as to effect enhanced electrical contact between surfaces adhered with the cement, ii) a mixture of flake particles having a FSSS of about 0.90 to about 1.30 microns and a surface area of about 0.3 to 0.6 m 2 /g and a particle size distribution of about 90%<14 microns, 50%<7 microns, and 10%<2 microns, and iii) powder particles having a mean particle size of about 1.6 microns.
Claim 3
Dependent Claim
10 words
The assembly of claim 1 wherein the substrate is flexible.