Electrical conductor
Assignee: Von Roll Isola USA Inc
•
Filing: 1983-01-28
•
Granted: 1984-12-11
•
Expires: 2003-01-28
Abstract
Abstract A low-cost conductor, e.g. a printed circuit, is prepared by applying a mixture of a metallic powder and polymer on a substrate and curing the polymer, followed by an augmentation replacement reaction being effected to replace some of the metallic powder with a more noble metal in such a way that the total volume of deposited metal on the surface exceeds that of the original metal powder at that surface. This procedure produces a contiguous layer of conducting metal on the substrate. The conductors thus formed can easily be soldered without leaching using conventional tin-lead solders.
Inventors
- 👤 Charles W. Eichelberger
- 👤 Robert J. Wojnarowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:49
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/245; H05K3/246; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K1/095; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/0125; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
85 words
An electrical conductor adhered to desired areas upon a surface of an underlying substrate, in which said conductor comprises: a cured polymer containing therein a finely divided first metallic composition having a particle size greater than about 3 microns and a second metal, the amount of the metals in said cured polymer being about 60%-80% by volume; and a contiguous layer of said second metal on said cured polymer, wherein said second metal is below the first metal in the activity series of the metals.
Claim 2
Dependent Claim
85 words
An electrical conductor adhered to desired areas upon a surface of an underlying substrate, in which said conductor comprises: a cured polymer containing therein a finely divided first metallic composition having a particle size greater than about 3 microns and a second metal, the amount of the metals in said cured polymer being about 60%-80% by volume; and a contiguous layer of said second metal on said cured polymer, wherein said second metal is below the first metal in the activity series of the metals.
Claim 3
Dependent Claim
22 words
The electrical conductor of claim 1, wherein said finely divided metallic composition has a praticle size of less than about 50 microns.
Claim 4
Dependent Claim
22 words
The electrical conductor of claim 2, wherein said finely divided metallic composition has a particle size of less than about 25 microns.
Claim 5
Dependent Claim
21 words
The electrical conductor of claim 3, wherein said finely divided metallic composition has a particle size of less than 10 microns.
Claim 6
Dependent Claim
20 words
The electrical conductor of claim 1, wherein the amount of metals in said cured polymer is about 70% by volume.
Claim 7
Dependent Claim
22 words
The electrical conductor of claim 1, in which said polymer is a thermally curable polymeric material which exhibits volumetric shrinkage upon curing.
Claim 8
Dependent Claim
12 words
The electrical conductor of claim 6, wherein said polymer is a polyester.
Claim 9
Dependent Claim
14 words
The electrical conductor of claim 1, wherein said finely divided metallic composition comprises iron.
Claim 10
Dependent Claim
15 words
The electrical conductor of claim 8, wherein said finely divided metallic composition further comprises tin.
Claim 11
Dependent Claim
53 words
The electrical conductor of claim 9, wherein said finely divided metallic composition comprises about 25-40% by weight of iron, about 10-25% by weight of aluminum, about 15-30% by weight of tin and about 20-35% by weight of copper, prior to formation of said contiguous layer of said second metal on said cured polymer.
Claim 12
Dependent Claim
44 words
The electrical conductor of claim 10, wherein the amount of iron is about 30-35% by weight, the amount of aluminum is about 15-20% by weight, the amount of tin is about 20-25% by weight and the amount of copper is about 25-30% by weight.
Claim 13
Dependent Claim
19 words
The electrical conductor of claim 1, wherein said finely divided metallic composition comprises a mixture of nickel and zinc.
Claim 14
Dependent Claim
43 words
The electrical conductor of claim 12, wherein the amount of said zinc is about 15-45% by weight and the amount of said nickel is about 55-85% by weight, prior to formation of said contiguous layer of said second metal on said cured polymer.
Claim 15
Dependent Claim
28 words
The electrical conductor of claim 13, wherein the amount of said zinc is about 25% by weight and the amount of said nickel is about 75% by weight.
Claim 16
Dependent Claim
20 words
The electrical conductor of claim 1, wherein said substrate is a structural member of a device which contains a conductor.
Claim 17
Dependent Claim
12 words
The electrical conductor of claim 1, wherein saio second metal is copper.
Claim 18
Dependent Claim
21 words
The electrical conductor of claim 1, having a layer of a third metal on said contiguous layer of said second metal.
Claim 19
Dependent Claim
18 words
The electrical conductor of claim 17, wnerein said second metal is copper and said third metal is tin.
Claim 20
Dependent Claim
21 words
The electrical conductor of claim l, wherein said cured polymer is in contact with a resistive material carried by said substrate.
Claim 21
Dependent Claim
14 words
The electrical conductor of claim 19, wherein said resistive material is a thick-film resistor.
Claim 22
Dependent Claim
18 words
The electrical conductor of claim 20 wherein said contiguous layer of said second metal also contacts said resistor.
Claim 23
Dependent Claim
29 words
The conductor of claims 20 or 21, wherein a portion of said resistor is disposed between a portion of said cured polymer and said contiguous layer of second metal.
Claim 24
Dependent Claim
26 words
The electrical conductor of claims 20 or 21, wherein a portion of said resistor is disposed between a portion of said cured polymer and said substrate.
Claim 25
Dependent Claim
25 words
The electrical conductor of claim 1, further comprising an electrically conductive member extending through said contiguous layer of said second metal into said cured polymer.
Claim 26
Dependent Claim
18 words
The electrical conductor of claim 24, wherein said electrically conductive member is a lead of an electrical device.
Claim 27
Dependent Claim
24 words
The electrical conductor of claim 1, wherein said finely divided metallic composition includes at least one of the group consisting of aluminum and magnesium.
Claim 28
Dependent Claim
12 words
The electrical conductor of claim 1, wherein said polymer is an epoxy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-11 | 1988-06-11 | 1988-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-11 | 1992-06-11 | 1992-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-11 | 1996-06-11 | 1996-12-11 | $7700.00 | Window Closed / Lapsed |