Moisture stable polyurethane biasable transfer members
Assignee: Eastman Kodak Co
•
Filing: 1991-11-26
•
Granted: 1993-05-18
•
Expires: 2011-11-26
Abstract
Abstract The invention provides rolls, belts and other biasable members having at least one layer or coating of an elastomeric resilient polyurethane formed by reacting (a) a polyisocyanate prepolymer comprising the reaction product of a saturated aliphatic polyisocyanate, a saturated cycloaliphatic polyisocyanate, or an aromatic polyisocyanate and a polyol free of aliphatic unsaturation, preferably a polyalkylene glycol in which the alkylene group contains 2 to 8 carbon atoms, and (b) a hardening mixture comprising a polyol of (a) or a diamine free of aliphatic unsaturation, or a mixture thereof and, as a conductivity control agent, from 0.001 to 5.0 weight percent, based on the total weight of (b), of a complex of ethylene glycil or an oligoethylene glycol selected from the group consisting of di-, tri- and tetraethylene glycol with an ionizable ferric halide salt selected from the group consisting of ferric flouride, ferric chloride and ferric bromide.
Inventors
- 👤 John C. Wilson
- 👤 William B. Vreeland
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:56
CPC Classifications
G; G03; G03G; G03G15/00; G03G15/14; G03G15/16; G03G15/1665; G03G15/167; G03G15/1685; C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
200 words
A member for electrically cooperating with a conductive support surface to attract charged toner particles from the surface towards the member comprising a conductive substrate capable of supporting a uniform bias potential thereon and at least one coating comprising a resilient elastomeric polyurethane formed by reacting: (a) a polyisocyanate prepolymer comprising the reaction product of: (i) a saturated aliphatic polyisocyanate, a saturated cycloaliphatic polyisocyanate or an aromatic polyisocyanate; and (ii) a polyol free of aliphatic unsaturation; and (b) a hardening mixture comprising: (i) a polyol of (a) (ii) or a diamine free of aliphatic unsaturation thereof; and, (ii) as a conductivity control agent for controlling the resistivity of the elastomeric polyurethane, from 0.001 to 5.0 weight percent, based on the total weight of (b), of a complex of ethylene glycol or an oligoethylene glycol selected from the group consisting of di-, tri- and tetraethylene glycol with an ionizable ferric halide salt selected from the group consisting of ferric fluoride, ferric chloride and ferric bromide, the coating being in electrical contact with the conductive substrate and having an electrical resistivity such that the coating is capable of transmitting a bias potential from the substrate to the outer periphery of the coating.
Claim 2
Dependent Claim
200 words
A member for electrically cooperating with a conductive support surface to attract charged toner particles from the surface towards the member comprising a conductive substrate capable of supporting a uniform bias potential thereon and at least one coating comprising a resilient elastomeric polyurethane formed by reacting: (a) a polyisocyanate prepolymer comprising the reaction product of: (i) a saturated aliphatic polyisocyanate, a saturated cycloaliphatic polyisocyanate or an aromatic polyisocyanate; and (ii) a polyol free of aliphatic unsaturation; and (b) a hardening mixture comprising: (i) a polyol of (a) (ii) or a diamine free of aliphatic unsaturation thereof; and, (ii) as a conductivity control agent for controlling the resistivity of the elastomeric polyurethane, from 0.001 to 5.0 weight percent, based on the total weight of (b), of a complex of ethylene glycol or an oligoethylene glycol selected from the group consisting of di-, tri- and tetraethylene glycol with an ionizable ferric halide salt selected from the group consisting of ferric fluoride, ferric chloride and ferric bromide, the coating being in electrical contact with the conductive substrate and having an electrical resistivity such that the coating is capable of transmitting a bias potential from the substrate to the outer periphery of the coating.
Claim 3
Dependent Claim
24 words
The member of claim 1 wherein the elastomeric polyurethane coating has a resistivity of from about 1.0×10 7 to about 5.0×10 10 ohm cm.
Claim 4
Dependent Claim
24 words
The member of claim 1 wherein the elastomeric polyurethane coating has a resistivity of from about 2.0×10 8 to about 2.0×10 10 ohm cm.
Claim 5
Dependent Claim
23 words
The member of claim 1 wherein the elastomeric polyurethane has a hardness of between about 10 Shore A and about 80 Shore D.
Claim 6
Dependent Claim
28 words
The member of claim 1 wherein the conductive substrate having a coating of elastomeric polyurethane is formed of a conductive metal in the shape of an endless belt.
Claim 7
Dependent Claim
27 words
The member of claim 1 wherein the conductive substrate having a coating of elastomeric polyurethane is formed of a conductive metal in the shape of a roll.
Claim 8
Dependent Claim
34 words
The member of claim 1 wherein (a) the polyisocyanate in the prepolymer is methylenebis(4-isocyanatocyclohexane), hexamethylene diisocyanate or toluene diisocyanate and (b) the polyol is poly(oxyethylene glycol), poly(oxypropylene glycol), poly(tetramethylene ether glycol) or mixtures thereof.
Claim 9
Dependent Claim
22 words
The member of claim 1 wherein (a) the polyisocyanate in the prepolymer is methylenebis(4-isocyanatocyclohexane) and (b) the polyol is poly(tetramethylene ether glycol).
Claim 10
Dependent Claim
28 words
The member of claim 1 wherein the conductivity control agent is present in an amount of 0.001 to 5.0 weight percent based on the total weight of (b).
Claim 11
Dependent Claim
19 words
The member of claim 1 wherein the conductivity control agent is a complex of ferric chloride and diethylene glycol.
Claim 12
Dependent Claim
19 words
The member of claim 1 wherein the conductivity control agent is a complex of ferric chloride and tetraethylene glycol.
Claim 13
Dependent Claim
27 words
The member of claim 1 wherein the conductivity control agent for controlling the resistivity further substantially reduces the sensitivity of the resistivity to changes in relative humidity.
Claim 14
Dependent Claim
13 words
The member of claim 1 wherein the conductive support surface comprises a photoconductor.
Claim 15
Independent Claim
209 words
A method of controlling the resistivity of a member for electrically cooperating with a conductive support surface to attract charged toner particles from the surface towards the member comprising coating a conductive substrate capable of supporting a uniform bias potential thereon with at least one layer of a resilient elastomeric polyurethane, said coating being in electrical contact with the conductive substrate and formed by reacting: (a) a polyisocyanate prepolymer comprising the reaction product of: (i) a saturated aliphatic polyisocyanate, a saturated cycloaliphatic polyisocyanate or an aromatic polyisocyanate; and (ii) a polyol free of aliphatic unsaturation; and (b) a hardening mixture comprising: (i) a polyol of (a) (ii) or a diamine free of aliphatic unsaturation, or a mixture thereof; and, (ii) as a conductivity control agent for controlling the resistivity of the elastomeric polyurethane, from 0.001 to 5.0 weight percent, based on the total weight of (b), of a complex of ethylene glycol or an oligoethylene glycol selected from the group consisting of di-, tri- and tetraethylene glycol with an ionizable ferric halide salt selected from the group consisting of ferric fluoride, ferric chloride and ferric bromide, whereby the elastomeric polyurethane having an altered resistivity is capable of transmitting a bias potential from the substrate to the outer periphery thereof.
Claim 16
Independent Claim
209 words
A method of controlling the resistivity of a member for electrically cooperating with a conductive support surface to attract charged toner particles from the surface towards the member comprising coating a conductive substrate capable of supporting a uniform bias potential thereon with at least one layer of a resilient elastomeric polyurethane, said coating being in electrical contact with the conductive substrate and formed by reacting: (a) a polyisocyanate prepolymer comprising the reaction product of: (i) a saturated aliphatic polyisocyanate, a saturated cycloaliphatic polyisocyanate or an aromatic polyisocyanate; and (ii) a polyol free of aliphatic unsaturation; and (b) a hardening mixture comprising: (i) a polyol of (a) (ii) or a diamine free of aliphatic unsaturation, or a mixture thereof; and, (ii) as a conductivity control agent for controlling the resistivity of the elastomeric polyurethane, from 0.001 to 5.0 weight percent, based on the total weight of (b), of a complex of ethylene glycol or an oligoethylene glycol selected from the group consisting of di-, tri- and tetraethylene glycol with an ionizable ferric halide salt selected from the group consisting of ferric fluoride, ferric chloride and ferric bromide, whereby the elastomeric polyurethane having an altered resistivity is capable of transmitting a bias potential from the substrate to the outer periphery thereof.
Claim 17
Dependent Claim
30 words
The method of claim 14 wherein the resistivity of the elastomeric polyurethane having the conductivity control agent included therein is from about 1.0×10 7 to about 5.0×10 10 ohm cm.
Claim 18
Dependent Claim
30 words
The method of claim 14 wherein the resistivity of the elastomeric polyurethane having the conductivity control agent included therein is from about 2.0×10 8 to about 2.0×10 10 ohm cm.
Claim 19
Dependent Claim
10 words
The method of claim 14 wherein the resistivity is increased.
Claim 20
Dependent Claim
10 words
The method of claim 14 wherein the resistivity is decreased.
Claim 21
Dependent Claim
28 words
The method of claim 14 wherein the conductivity control agent is present in an amount of 0.001 to 5.0 weight percent based on the total weight of (b).
Claim 22
Dependent Claim
30 words
The method of claim 14 wherein the conductivity control agent for altering the resistivity further substantially reduces the sensitivity of the resistivity of the member to changes in relative humidity.
Claim 23
Dependent Claim
34 words
The method of claim 14 wherein (a) the polyisocyanate in the prepolymer is methylenebis(4-isocyanatocyclohexane), hexamethylene diisocyanate or toluene diisocyanate and (b) the polyol is poly(oxyethylene glycol), poly(oxypropylene glycol), poly(tetramethylene ether glycol) or mixtures thereof.
Claim 24
Dependent Claim
22 words
The method of claim 14 wherein (a) the polyisocyanate in the prepolymer is methylenebis(4-isocyanatocyclohexane) and (b) the polyol is poly(tetramethylene ether glycol).
Claim 25
Dependent Claim
19 words
The method of claim 14 wherein the conductivity control agent is a complex of ferric chloride and diethylene glycol.
Claim 26
Dependent Claim
19 words
The method of claim 14 wherein the conductivity control agent is a complex of ferric chloride and tetraethylene glycol.
Claim 27
Dependent Claim
13 words
The method of claim 14 wherein the conductive support surface comprises a photoconductor.
Claim 28
Independent Claim
228 words
A method of preventing changes in the resistivity of members for electrically cooperating with a conductive support surface to attract charged toner particles from the surface towards the members caused by changes in relative humidity comprising applying at least one coating of a resilient elastomeric polyurethane formed by reacting: (a) a polyisocyanate prepolymer comprising the reaction product of: (i) a saturated aliphatic polyisocyanate, a saturated cycloaliphatic, polyisocyanate or an aromatic polyisocyanate; and (ii) a polyol free of aliphatic unsaturation; and (b) a hardening mixture comprising: (i) a polyol of (a) (ii) or a diamine free of aliphatic unsaturation, or a mixture thereof; and, (ii) as a conductivity control agent for controlling the resistivity of the elastomeric polyurethane, from 0.001 to 5.0 weight percent, based on the total weight of (b), of a complex of ethylene glycol or an oligoethylene glycol selected from the group consisting of di-, tri- and tetraethylene glycol with an ionizable ferric halide salt selected from the group consisting of ferric fluoride, ferric chloride and ferric bromide, to a cylindrical core of electrically conductive material for electrically cooperating with the conductive support surface when brought into contact therewith whereby the elastomer is capable of transmitting a bias potential from the core of electrically conductive material to the outer periphery thereof and significant reductions in the sensitivity of the resistivity to changes in relative humidity occur.
Claim 29
Independent Claim
228 words
A method of preventing changes in the resistivity of members for electrically cooperating with a conductive support surface to attract charged toner particles from the surface towards the members caused by changes in relative humidity comprising applying at least one coating of a resilient elastomeric polyurethane formed by reacting: (a) a polyisocyanate prepolymer comprising the reaction product of: (i) a saturated aliphatic polyisocyanate, a saturated cycloaliphatic, polyisocyanate or an aromatic polyisocyanate; and (ii) a polyol free of aliphatic unsaturation; and (b) a hardening mixture comprising: (i) a polyol of (a) (ii) or a diamine free of aliphatic unsaturation, or a mixture thereof; and, (ii) as a conductivity control agent for controlling the resistivity of the elastomeric polyurethane, from 0.001 to 5.0 weight percent, based on the total weight of (b), of a complex of ethylene glycol or an oligoethylene glycol selected from the group consisting of di-, tri- and tetraethylene glycol with an ionizable ferric halide salt selected from the group consisting of ferric fluoride, ferric chloride and ferric bromide, to a cylindrical core of electrically conductive material for electrically cooperating with the conductive support surface when brought into contact therewith whereby the elastomer is capable of transmitting a bias potential from the core of electrically conductive material to the outer periphery thereof and significant reductions in the sensitivity of the resistivity to changes in relative humidity occur.
Claim 30
Dependent Claim
28 words
The method of claim 26 wherein the conductivity control agent is present in an amount of 0.001 to 5.0 weight percent based on the total weight of (b).
Claim 31
Dependent Claim
34 words
The method of claim 26 wherein (a) the polyisocyanate in the prepolymer is methylenebis(4-isocyanatocyclohexane), hexamethylene diisocyanate or toluene diisocyanate, and (b) the polyol is poly(oxyethylene glycol), poly(oxypropylene glycol), poly(tetramethylene ether glycol) or mixtures thereof.
Claim 32
Dependent Claim
22 words
The method of claim 26 wherein (a) the polyisocyanate in the prepolymer is methylenebis(4-isocyanatocyclohexane) and (b) the polyol is poly(tetramethylene ether glycol).
Claim 33
Dependent Claim
19 words
The method of claim 26 wherein the conductivity control agent is a complex of ferric chloride and diethylene glycol.
Claim 34
Dependent Claim
19 words
The method of claim 26 wherein the conductivity control agent is a complex of ferric chloride and tetraethylene glycol.
Claim 35
Dependent Claim
13 words
The method of claim 26 wherein the conductive support surface comprises a photoconductor.
References Cited (Backward Citations)
US2807233A
Cited
US2836725A
Cited
US2951443A
Cited
US2969386A
Cited
US3455855A
Cited
US3379687A
Cited
US3552972A
Cited
US3520604A
Cited
US3694413A
Cited
US3608792A
Cited
US3708482A
Cited
US3620616A
Cited
US3633543A
Cited
US3769022A
Cited
US3702482A
Cited
US3740379A
Cited
US3743684A
Cited
US3860611A
Cited
JPS4927675A
Cited
US3969306A
Cited
US3781105A
Cited
US4066352A
Cited
US4182909A
Cited
US3959573A
Cited
US3959574A
Cited
US3920325A
Cited
US3954332A
Cited
US4113649A
Cited
US4062812A
Cited
US4116894A
Cited
US4058879A
Cited
US4200701A
Cited
US4404408A
Cited
US4177335A
Cited
DE2820609A1
Cited
US4272616A
Cited
US4303748A
Cited
US4357401A
Cited
US4309803A
Cited
US4407739A
Cited
US4476297A
Cited
US4456548A
Cited
US4556614A
Cited
US4365036A
Cited
US4390679A
Cited
US4471037A
Cited
US4654267A
Cited
US4774265A
Cited
US4436841A
Cited
DE3223119A1
Cited
US4871854A
Cited
SU1071627A1
Cited
US4405741A
Cited
US4548737A
Cited
US4618454A
Cited
US4547440A
Cited
US4438251A
Cited
GB2143539A
Cited
US4476292A
Cited
US4542095A
Cited
FR2568574A1
Cited
US4654279A
Cited
US4698391A
Cited
US4729925A
Cited
US4762941A
Cited
GB2205437A
Cited
JPH02218471A
Cited
US4963616A
Cited
WO1991000314A1
Cited
US5011739A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-17 | 1996-11-16 | 1997-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-17 | 2000-11-16 | 2001-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-17 | 2004-11-16 | 2005-05-18 | $7700.00 | Window Closed / Lapsed |