Compositions and method for enhancing electrical life of copolymers
Assignee: Xerox Corp
•
Filing: 1976-07-01
•
Granted: 1978-09-26
•
Expires: 1996-07-01
Abstract
Abstract Butadiene copolymers having controlled electrical life and controlled resistivity are described. A method is disclosed for enhancing the electrical life of butadiene copolymers having solubilized conductivity control agents incorporated therein by varying specified quantities of terminally unsaturated hydrocarbon nitriles in copolymers of the butadiene and the specified nitriles by using mixtures of such copolymers having conductivity control agents therein. The method and polymers are useful for enhancing the electrical life and polymer stability in xerographic devices where control of conductivity and/or relaxation behavior is important, e.g., in bias transfer rolls.
Inventors
- 👤 James A. Lentz
- 👤 George J. Safford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 03:40
CPC Classifications
G; G03; G03B; G03B15/00; G03B15/14; H; H01; H01B; H01B3/00; H01B3/002; H01B3/004; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31855; Y10T428/31931
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
128 words
A composition containing a copolymer of butadiene and a terminally unsaturated hydrocarbon nitrile having improved electrical life comprising about 1.0 percent to about 12.0 percent terminally unsaturated hydrocarbon nitrile having the formula R--C.tbd.N where R is an unsaturated, straight or branched chain hydrocarbon, the balance of the copolymer being butadiene and a sufficient amount of conductivity control agent to produce a composition having a resistivity from about 10 7 ohm-cm to about 5.0 × 10 11 ohm-cm, the conductivity control agent being selected from the group consisting of organic dyes, organic pigments, organic salts, polyelectrolytes, inorganic salts, inorganic pigments and charge transfer complexes or materials which produce charge transfer complexes with the copolymer, the conductivity control agent being solubilized in the copolymer and in the composition formed therewith.
Claim 2
Dependent Claim
128 words
A composition containing a copolymer of butadiene and a terminally unsaturated hydrocarbon nitrile having improved electrical life comprising about 1.0 percent to about 12.0 percent terminally unsaturated hydrocarbon nitrile having the formula R--C.tbd.N where R is an unsaturated, straight or branched chain hydrocarbon, the balance of the copolymer being butadiene and a sufficient amount of conductivity control agent to produce a composition having a resistivity from about 10 7 ohm-cm to about 5.0 × 10 11 ohm-cm, the conductivity control agent being selected from the group consisting of organic dyes, organic pigments, organic salts, polyelectrolytes, inorganic salts, inorganic pigments and charge transfer complexes or materials which produce charge transfer complexes with the copolymer, the conductivity control agent being solubilized in the copolymer and in the composition formed therewith.
Claim 3
Dependent Claim
26 words
The composition of claim 1 wherein the terminally unsaturated hydrocarbon nitrile portion of the copolymer comprises about 2.0 percent to about 8.0 percent of the copolymer.
Claim 4
Dependent Claim
24 words
The composition of claim 1 wherein the conductivity control agent is from about 0.05 percent to about 1.75 percent (by weight) of the copolymer.
Claim 5
Dependent Claim
13 words
The composition of claim 1 wherein the terminally unsaturated hydrocarbon nitrile is acrylonitrile.
Claim 6
Dependent Claim
90 words
The composition of claim 1 further comprising the reaction product of the copolymer with an agent to convert the copolymer to an elastomer, a polymeric foam material, a polymer film or a cross-linked copolymer having improved electrical life wherein the terminally unsaturated hydrocarbon nitrile content of the copolymer is from about 1.0 percent to about 12.0 percent and the conductivity control agent is sufficient to produce in the reaction product a resistivity at the desired level within the range of about 10 7 to about 5.0 × 10 11 ohm-cm.
Claim 7
Dependent Claim
49 words
The composition of claim 5 wherein the agent to convert the copolymer to an elastomer, a polymeric foam material, a polymer film or a crosslinked copolymer is a dibasic acid which forms an ester with the said copolymer as the reaction product, the reaction product having improved electrical life.
Claim 8
Dependent Claim
20 words
The composition of claim 1 further comprising the cross-linked product of the copolymer said cross-linked product having improved electrical life.
Claim 9
Dependent Claim
13 words
The composition of claim 5 wherein the terminally unsaturated hydrocarbon nitrile is acrylonitrile.
Claim 10
Independent Claim
120 words
A method for controlling the electrical life of copolymers of butadiene and terminally unsaturated hydrocarbon nitrile having solubilized conductivity control agents therein comprising incorporating in the copolymer from about 1.0 percent to about 12.0 percent (by weight) terminally unsaturated hydrocarbon nitrile having the formula R--C .tbd.N where R is an unsaturated, straight or branched chain hydrocarbon, and a sufficient amount of the conductivity control agent to produce a copolymer having a resistivity from about 10 7 ohm-cm to about 5.0 × 10 11 ohm-cm, the conductivity control agent being selected from the group consisting of organic dyes, organic pigments, organic salts, polyelectrolytes, inorganic salts, inorganic pigments, and charge transfer complexes or materials which produce charge transfer complexes with the copolymer.
Claim 11
Independent Claim
120 words
A method for controlling the electrical life of copolymers of butadiene and terminally unsaturated hydrocarbon nitrile having solubilized conductivity control agents therein comprising incorporating in the copolymer from about 1.0 percent to about 12.0 percent (by weight) terminally unsaturated hydrocarbon nitrile having the formula R--C .tbd.N where R is an unsaturated, straight or branched chain hydrocarbon, and a sufficient amount of the conductivity control agent to produce a copolymer having a resistivity from about 10 7 ohm-cm to about 5.0 × 10 11 ohm-cm, the conductivity control agent being selected from the group consisting of organic dyes, organic pigments, organic salts, polyelectrolytes, inorganic salts, inorganic pigments, and charge transfer complexes or materials which produce charge transfer complexes with the copolymer.
Claim 12
Dependent Claim
29 words
The method of claim 9 wherein from about 2.0 percent to about 8.0 percent terminally unsaturated hydrocarbon nitrile is incorporated in the copolymer to control the electrical life thereof.
Claim 13
Dependent Claim
13 words
The method of claim 9 wherein the terminally unsaturated hydrocarbon nitrile is acrylonitrile.
Claim 14
Dependent Claim
15 words
The method of claim 9 wherein the conductivity control agent is asymmetrical quaternary ammonium compound.
Claim 15
Dependent Claim
25 words
The method of claim 9 wherein the solubilized conductivity control agent is from about 0.05 percent to about 1.75 percent (by weight) of the copolymer.
Claim 16
Dependent Claim
33 words
The method of claim 9 further comprising reacting the copolymer having improved electrical life with a suitable functional agent capable of forming a reaction product therewith, the reaction product having improved electrical life.
Claim 17
Dependent Claim
22 words
The method of claim 14 wherein the functional agent capable of forming a reaction product with the copolymer is a dibasic acid.
References Cited (Backward Citations)
US2385258A
Cited
US2435790A
Cited
US2444870A
Cited
US2582160A
Cited
US2821514A
Cited
US2846559A
Cited
US3346444A
Cited
US4070324A
Cited
US3959573A
Cited
US4058879A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-25 | 1982-03-27 | 1982-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-25 | 1986-03-27 | 1986-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-25 | 1990-03-27 | 1990-09-26 | $7700.00 | Window Closed / Lapsed |