Assignee: SINTEF AS
•
Filing: 1986-07-29
•
Granted: 1988-09-27
•
Expires: 2006-07-29
Abstract
Abstract Magnetic polymer particles prepared by treating compact or porous polymer particles with a solution of iron salts and, if desired, salts of other metals which are capable of forming magnetic ferrites, in which the solution swells or penetrates into the particles. Iron hydroxide and possible other metal hydroxides are precipitated, for instance by raising the pH value, and the particles are optionally heated. In the iron salts used the ratio between di- and trivalent iron is suitably such that magnetic iron oxide is formed directly. It is also possible to use oxidizing or reducing groups or additives to obtain such a ratio. When other metal salts are used in addition to iron salts, the operation is carried out in the same manner. For instance, when Mn ++ , Co ++ or Ni ++ salts are used in addition to Fe ++ salts, the divalent iron is oxidized to trivalent so that magnetic ferrite is obtained. The polymer particles which are treated with metal salts preferably contain metal-binding groups. Such groups are incorporated for instance by using monomers which contain said groups for the preparation of the polymer particles, or the groups are incorporated in the polymer particles prepared. The magnetic polymer particles are spherical and have a uniform concentration of magnetic material. They may be used for medical, diagnostic or other purposes.
Inventors
- 👤 John Ugelstad
- 👤 Turid Ellingsen
- 👤 Arvid Berge
- 👤 Oskar B. Helgee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:36
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/42; B; B03; B03C; B03C1/00; B03C1/005; B03C1/01; G; G01; G01N; G01N33/00; G01N33/48; G01N33/50; G01N33/53; G01N33/543; G01N33/54313; G01N33/54326; G01N33/5434; H01F1/01; H01F1/03; H01F1/032; H01F1/10; H01F1/11; H01F1/111; G01N2446/00; G01N2446/10; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2998
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
129 words
A process for the preparation of magnetic polymer particles which comprises: mixing: (i) a solution of iron salts alone or in combination with salts of other metals which are capable of forming magnetic oxides, (ii) an aqueous dispersion of filterable polymer particles having a particle size above about 0.2μ containing groups which are capable of binding with the iron and metal salts so that a substantial portion of the iron or metal salts are retained on and in the particles which are porous and/or capable of being swollen by water, and then adding (iii) a base to increase the pH, to precipitate hydroxides of iron and said other metals, if present, thereby forming magnetic particles having said magnetic oxides on the surface as well as within the body thereof.
Claim 2
Dependent Claim
129 words
A process for the preparation of magnetic polymer particles which comprises: mixing: (i) a solution of iron salts alone or in combination with salts of other metals which are capable of forming magnetic oxides, (ii) an aqueous dispersion of filterable polymer particles having a particle size above about 0.2μ containing groups which are capable of binding with the iron and metal salts so that a substantial portion of the iron or metal salts are retained on and in the particles which are porous and/or capable of being swollen by water, and then adding (iii) a base to increase the pH, to precipitate hydroxides of iron and said other metals, if present, thereby forming magnetic particles having said magnetic oxides on the surface as well as within the body thereof.
Claim 3
Dependent Claim
51 words
The process according to claim 1 wherein when said base is added to a mixture of (i) and (ii), there is produced a mixture of Me(OH) 2 , and Fe(OH) 3 , wherein Me represents Fe II , Ni, Co or Mn, thus providing magnetic ferrite on and in the particles.
Claim 4
Dependent Claim
12 words
The process according to claim 1 wherein the polymer particles are cross-linked.
Claim 5
Dependent Claim
59 words
The process according to claim 1 wherein porous macroreticular particles are employed, said particles being prepared by copolymerization of a monomer mixture of vinyl monomers selected from the group consisting of styrene, styrene derivatives and monoacrylates and polyvinyl monomers selected from the group consisting of divinyl benzene, di- and tri-acrylates in the presence of inert solvents for the monomers.
Claim 6
Dependent Claim
46 words
The process according to claim 1 wherein there are employed solid, porous polymer particles to which there is added a material which will attach to the surface of the pores of said polymer particles and which contains groups which bind the metal salt which is added.
Claim 7
Dependent Claim
72 words
The process according to claim 1 wherein the polymer particles are prepared by copolymerization of vinyl monomer with epoxy groups and other vinyl monomers and/or polyvinyl monomers, and are then treated with substances containing one or more primary and/or secondary amino groups which react with the epoxy group so that these substances are bound on and in the particles and provide groups which are capable of binder metal salts with coordinate bonding.
Claim 8
Dependent Claim
101 words
The process according to claim 1 wherein the polymer particles are formed by copolymerization of a mixture of vinyl monomers with or without polyvinyl monomers and wherein one or more of said monomers contain amino groups which directly form polymer particles containing amino groups which, upon the addition of a mixture of iron metal salts, bind these on and in the particles or wherein one or more of the monomers contain acid groups or groups which may be converted to acid groups, whereby the polymer particles formed contain acid groups which in the ionic form, bind metal salts by ionic bonds.
Claim 9
Dependent Claim
87 words
The process according to claim 1 wherein in order to obtain metal-binding primary and/or secondary and/or tertiary amino groups or acid groups on the interior surface of the polymer particles, there are added substances which bind to the surface of said particles by physical adsorption and which contain amino groups which bind metal ions by coordinative bonding or contain acid groups which bind metal ions by ionic bonding, so that the metal ions are bound in and on the particles, upon the subsequent addition of metal salt.
Claim 10
Dependent Claim
34 words
The process according to claim 1 wherein amino groups, imino groups and/or ethylene oxide groups are incorporated in the already polymerized particles before contacting the particles with the salts of iron and other metals.
Claim 11
Dependent Claim
28 words
The process according to claim 1 wherein acid groups are incorporated in the already polymerized particles before contacting the particles with the salts of iron and other metals.
Claim 12
Dependent Claim
16 words
The process according to claim 10 wherein said acid groups are sulphonic or carboxylic acid groups.
Claim 13
Dependent Claim
19 words
The process according to claim 1 wherein magnetic particles are heated to a temperature below 100° C. after formation.
References Cited (Backward Citations)
US3520860A
Cited
US4169804A
Cited
US4381244A
Cited
US4447475A
Cited
US4421660A
Cited
US4609608A
Cited
US4452773A
Cited
US4554088A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |