Use of selectively deposited tungsten for contact formation and shunting metallization
Assignee: NCR OH A CORP OF
•
Filing: 1985-06-12
•
Granted: 1987-03-10
•
Expires: 2005-06-12
Abstract
Abstract A process for using selectively deposited tungsten in the making of ohmic contacts and contact/interconnect metallization patterns. In one form the process is employed to interconnect fully formed field effect devices using contacts through the dielectric layer. A thin layer of intrinsic polysilicon or amorphous silicon is conformally deposited, patterned and covered by selectively deposited tungsten, An anneal operation then forms self-aligned contacts or shunts, between the tungsten layer and the source/drain type diffusions exposed during the contact cut, by updiffusion through the thin intrinsic silicon, or by conversion of the thin intrinsic silicon to tungsten. Alternatively, contacts and shunts can be formed using polysilicon layers without regard to impurity type by making contact cuts through the dielectric to expose substrate regions, patterning a deposited polysilicon layer to cover only parts of such exposed regions, forming the field effect device source/drain regions, and then selectively depositing tungsten on all exposed surfaces of silicon. The tungsten thereby bridges the polysilicon layer to the adjacent, exposed substrate region and shunts all surface adjacent p-n junctions, including the polysilicon-to-substrate contact junction.
Inventors
- 👤 Werner A. Metz, Jr.
- 👤 Nicholas J. Szluk
- 👤 Gayle W. Miller
- 👤 Michael J. Drury
- 👤 Paul A. Sullivan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 05:18
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0113; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0186; H10D84/02; H10D84/03; H10D84/038; H10W; H10W20/00; H10W20/01; H10W20/031; H10D84/80; H10D84/82; H10D84/83; H10D84/85; H10D84/859
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
131 words
A process for forming a self-aligned, low resistance, ohmic, metal shunted contact and interconnect structure, comprising the steps of: providing a silicon substrate having doped surface regions; forming a layer of undoped silicon having a nominal thickness of 50 nanometers or less on the substrate over at least said selected doped surface regions; patterning the silicon to retain regions of the undoped silicon over the selected doped surface regions; sintering the structure at a lower temperature to updiffuse dopant from the silicon substrate regions into and through the silicon layer overlying the selected doped surface regions of the silicon substrate; and selectively depositing a layer of refractory metal on the silicon to form ohmic contacts between the doped surface regions and the immediately overlying metal layer through the selectively doped silicon.
Claim 2
Dependent Claim
131 words
A process for forming a self-aligned, low resistance, ohmic, metal shunted contact and interconnect structure, comprising the steps of: providing a silicon substrate having doped surface regions; forming a layer of undoped silicon having a nominal thickness of 50 nanometers or less on the substrate over at least said selected doped surface regions; patterning the silicon to retain regions of the undoped silicon over the selected doped surface regions; sintering the structure at a lower temperature to updiffuse dopant from the silicon substrate regions into and through the silicon layer overlying the selected doped surface regions of the silicon substrate; and selectively depositing a layer of refractory metal on the silicon to form ohmic contacts between the doped surface regions and the immediately overlying metal layer through the selectively doped silicon.
Claim 3
Dependent Claim
28 words
The process recited in claim 1, wherein the step of forming a layer of undoped silicon is an LPCVD process in which the undoped silicon is conformally deposited.
Claim 4
Dependent Claim
20 words
The process recited in claim 2, wherein the undoped silicon is deposited in polycrystalline form and the metal is tungsten.
Claim 5
Dependent Claim
20 words
The process recited in claim 2, wherein the undoped silicon is deposited in amorphous form and the metal is tungsten.
Claim 6
Dependent Claim
31 words
The process recited in claim 3, wherein the sinter operation is performed at a temperature in the range of 800°-1000° C. and an inert atmosphere of N 2 at atmospheric pressure.
Claim 7
Dependent Claim
31 words
The process recited in claim 4, wherein the sinter operation is performed at a temperature in the range of 800°-1000° C. and an inert atmosphere of N 2 at atmospheric pressure.
Claim 8
Dependent Claim
99 words
A process for forming an aligned, low resistance, ohmic, tungsten shunted contact and interconnect structure, comprising the steps of: providing a silicon substrate with exposed regions for making buried contacts and exposed regions for making contacts between the silicon substrate and a silicon interconnect layer; forming a silicon interconnect layer on the silicon substrate to cover part of the exposed regions for making contacts between the silicon substrate and a silicon interconnect layer; and selectively depositing a layer of tungsten on exposed surfaces of the silicon substrate and the silicon interconnect layer to shunt any surface adjacent p-n junctions.
Claim 9
Dependent Claim
99 words
A process for forming an aligned, low resistance, ohmic, tungsten shunted contact and interconnect structure, comprising the steps of: providing a silicon substrate with exposed regions for making buried contacts and exposed regions for making contacts between the silicon substrate and a silicon interconnect layer; forming a silicon interconnect layer on the silicon substrate to cover part of the exposed regions for making contacts between the silicon substrate and a silicon interconnect layer; and selectively depositing a layer of tungsten on exposed surfaces of the silicon substrate and the silicon interconnect layer to shunt any surface adjacent p-n junctions.
Claim 10
Dependent Claim
31 words
The process recited in claim 7, further including after the step of forming a silicon interconnect layer the step of: doping the source/drain and diffused interconnect regions of the silicon substrate.
Claim 11
Dependent Claim
52 words
The process recited in claim 8, wherein the step of forming a silicon interconnect layer is comprised of: forming a conformally deposited interconnect layer on the substrate; and patterning the conformally deposited interconnect layer in the presence of a mask to expose silicon substrate regions immediately adjacent the regions for making contacts.
Claim 12
Dependent Claim
31 words
The process recited in claim 9, wherein the silicon interconnect layer is of polycrystalline form and is conductively doped in conjunction with the doping of the source/drain and diffused interconnect regions.
References Cited (Backward Citations)
US3632436A
Cited
US3699646A
Cited
US4152823A
Cited
US4101349A
Cited
US4265935A
Cited
US4128439A
Cited
US4333099A
Cited
US4239559A
Cited
US4322736A
Cited
US4249968A
Cited
US4356622A
Cited
US4276688A
Cited
US4330931A
Cited
US4374700A
Cited
US4441247A
Cited
US4445266A
Cited
US4450620A
Cited
US4503601A
Cited
US4562640A
Cited
US4517225A
Cited
US4540607A
Cited
US4519126A
Cited
US4563805A
Cited
US4549914A
Cited
US4584207A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-09 | 1990-09-08 | 1991-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-09 | 1994-09-08 | 1995-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-09 | 1998-09-08 | 1999-03-10 | $7700.00 | Window Closed / Lapsed |