Growth enhancement of hemispherical grain silicon on a doped polysilicon storage node capacitor structure, for dynamic random access memory applications
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-06-26
•
Granted: 2000-04-04
•
Expires: 2018-06-26
Abstract
Abstract A process for creating a storage node electrode for a DRAM capacitor structure, featuring increased surface area accomplished using an HSG silicon layer as the top layer for the storage node electrode, has been developed. The process features the use of a composite buffer layer of undoped and lightly doped amorphous silicon layers, located overlying a heavily doped amorphous silicon layer, and then followed by the deposition of HSG silicon seeds. A first anneal cycle then allows formation of an undoped HSG silicon layer to be realized on the underlying heavily doped amorphous silicon layer, via consumption of the HSG seeds, and of the composite buffer layer of undoped and lightly doped amorphous silicon layers. A second anneal cycle then allows dopant from the underlying heavily doped amorphous silicon layer to reach the undoped HSG silicon layer, resulting in a doped HSG silicon layer. Patterning, or CMP, of the doped HSG silicon layer, and of the heavily doped amorphous silicon layer, results in the creation of a storage node electrode. The use of the composite buffer layer allows the growth of an undoped HSG silicon layer to be achieved, thus maximizing uniformity and HSG silicon roughness, while the anneal cycle, applied to the undoped HSG silicon layer, results in the attainment of the doped HSG silicon layer, offering reduced capacitance depletion compared to undoped HSG silicon counterparts.
Inventors
- 👤 Dahcheng Lin
- 👤 Jung-Ho Chang
- 👤 Hsi-Chuan Chen
- 👤 Kuo-Shu Tseng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:57
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/712; H10D1/01; H10D1/041; H10D1/042; H10D1/716
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
410 words
A method for fabricating a storage node electrode, for a DRAM capacitor structure, featuring a doped hemispherical grain silicon (HSG) layer, used as the top layer of a storage node shape, and with said doped HSG silicon layer formed during an anneal cycle, from consumption of HSG silicon seeds, and from consumption of undoped, and lightly doped, amorphous silicon layers, comprising the steps of: providing a transfer gate transistor on a semiconductor substrate, comprised of a polysilicon gate structure, on an underlying gate insulator layer, and a source/drain region in said semiconductor substrate; depositing a first insulator layer on said transfer gate transistor; planarizing said first insulator layer; opening a storage node contact hole in said first insulator layer, exposing the top surface of a source region in said transfer gate transistor; depositing a doped amorphous silicon layer on said first insulator layer, and completely filling said storage node contact hole; forming a silicon plug, in said storage node contact hole, via removal of said doped amorphous silicon layer from the top surface of said first insulator layer; depositing a second insulator layer; forming an opening in said second insulator layer, exposing the top surface of said silicon plug; depositing a heavily doped amorphous silicon layer; depositing a first undoped amorphous silicon layer, on said heavily doped amorphous silicon layer; depositing a lightly doped amorphous silicon layer, on said first undoped amorphous silicon layer; depositing a second undoped amorphous silicon layer, on said lightly doped amorphous silicon layer; forming hemispherical grain (HSG) silicon seeds, on the top surface of said second undoped amorphous silicon layer; performing a first anneal cycle to create an HSG silicon layer, on said heavily doped amorphous silicon layer, with said undoped HSG silicon layer being formed from consumption of said HSG silicon seeds, from consumption of said second undoped amorphous silicon layer, from consumption of said lightly doped amorphous silicon layer, and from consumption of said first undoped amorphous silicon layer; performing a second anneal cycle to convert said undoped HSG silicon layer, to said doped HSG silicon layer; removing said doped HSG silicon layer from the top surface of said second insulator layer, via a chemical mechanical polishing procedure, creating a bottom electrode structure; forming a capacitor dielectric layer on said doped HSG silicon layer; depositing a doped polysilicon layer; patterning of said doped polysilicon layer, and of said capacitor dielectric layer to form a polysilicon upper electrode shape, for said DRAM capacitor structure.
Claim 2
Independent Claim
410 words
A method for fabricating a storage node electrode, for a DRAM capacitor structure, featuring a doped hemispherical grain silicon (HSG) layer, used as the top layer of a storage node shape, and with said doped HSG silicon layer formed during an anneal cycle, from consumption of HSG silicon seeds, and from consumption of undoped, and lightly doped, amorphous silicon layers, comprising the steps of: providing a transfer gate transistor on a semiconductor substrate, comprised of a polysilicon gate structure, on an underlying gate insulator layer, and a source/drain region in said semiconductor substrate; depositing a first insulator layer on said transfer gate transistor; planarizing said first insulator layer; opening a storage node contact hole in said first insulator layer, exposing the top surface of a source region in said transfer gate transistor; depositing a doped amorphous silicon layer on said first insulator layer, and completely filling said storage node contact hole; forming a silicon plug, in said storage node contact hole, via removal of said doped amorphous silicon layer from the top surface of said first insulator layer; depositing a second insulator layer; forming an opening in said second insulator layer, exposing the top surface of said silicon plug; depositing a heavily doped amorphous silicon layer; depositing a first undoped amorphous silicon layer, on said heavily doped amorphous silicon layer; depositing a lightly doped amorphous silicon layer, on said first undoped amorphous silicon layer; depositing a second undoped amorphous silicon layer, on said lightly doped amorphous silicon layer; forming hemispherical grain (HSG) silicon seeds, on the top surface of said second undoped amorphous silicon layer; performing a first anneal cycle to create an HSG silicon layer, on said heavily doped amorphous silicon layer, with said undoped HSG silicon layer being formed from consumption of said HSG silicon seeds, from consumption of said second undoped amorphous silicon layer, from consumption of said lightly doped amorphous silicon layer, and from consumption of said first undoped amorphous silicon layer; performing a second anneal cycle to convert said undoped HSG silicon layer, to said doped HSG silicon layer; removing said doped HSG silicon layer from the top surface of said second insulator layer, via a chemical mechanical polishing procedure, creating a bottom electrode structure; forming a capacitor dielectric layer on said doped HSG silicon layer; depositing a doped polysilicon layer; patterning of said doped polysilicon layer, and of said capacitor dielectric layer to form a polysilicon upper electrode shape, for said DRAM capacitor structure.
Claim 3
Dependent Claim
62 words
The method of claim 1, wherein said heavily doped amorphous silicon layer is obtained via LPCVD procedures, at a temperature below 550° C., and is in situ doped, during deposition, via the addition of phosphine, to a silane ambient, resulting in a bulk concentration, for said heavily doped amorphous silicon layer, of 4E20 atoms/cm 3 , or greater to its saturation level.
Claim 4
Dependent Claim
37 words
The method of claim 1, wherein said first undoped amorphous silicon layer is obtained via LPCVD procedures, at a temperature below 550° C., to a thickness less than 200 Angstroms, using silane, or disilane, as a source.
Claim 5
Dependent Claim
70 words
The method of claim 1, wherein said lightly doped amorphous silicon layer is obtained via LPCVD procedures, at a temperature below 550° C., to a thickness less than 400 Angstroms, and is in situ doped, during deposition, via the addition of phosphine to a silane, or to a disilane flow, resulting in a bulk concentration, for said lightly doped amorphous silicon layer, between about 1E19 to 4E20 atom/cm 3 .
Claim 6
Dependent Claim
37 words
The method of claim 1, wherein said second undoped amorphous silicon layer is deposited via LPCVD procedures, at a temperature below 550° C., to a thickness less than 200 Angstroms, using silane, or disilane, as a source.
Claim 7
Dependent Claim
62 words
The method of claim 1, wherein said HSG silicon seeds are formed using LPCVD procedures, at a temperature between about 550 to 580° C., at a pressure less than 1.0 torr, for a time between about 5 to 120 min., and using silane, or disilane, as a source, at a flow concentration less than 1.0E-3 moles/m 3 , in a nitrogen ambient.
Claim 8
Dependent Claim
44 words
The method of claim 1, wherein said first anneal cycle, used to form said undoped HSG silicon layer, is performed at a temperature between about 550 to 580° C., at a pressure below 1.0 torr, for a time between about 0 to 120 min.
Claim 9
Dependent Claim
48 words
The method of claim 1, wherein said second anneal cycle, used to convert said undoped HSG silicon layer to said doped HSG silicon layer, is performed at a temperature between about 800 to 850° C., for a time between about 20 to 60 min, in a nitrogen ambient.
Claim 10
Dependent Claim
77 words
The method of claim 1, wherein said capacitor dielectric layer is ONO, with an equivalent silicon dioxide thickness between about 40 to 80 Angstroms, created by growing a thin silicon oxide layer on said doped HSG silicon layer, at a thickness between about 10 to 50 Angstroms, depositing between about 10 to 60 Angstroms of a silicon nitride layer, and oxidizing said silicon nitride layer to from a silicon oxynitride layer on said thin silicon oxide layer.
Claim 11
Dependent Claim
33 words
The method of claim 1, wherein said doped polysilicon layer is deposited using LPCVD procedures, at a temperature between about 500 to 700° C., to a thickness between about 1000 to 2000 Angstroms.
Claim 12
Dependent Claim
28 words
The method of claim 1, wherein said polysilicon upper electrode is created using an anisotropic RIE procedure, applied to said polysilicon layer, using Cl 2 as an etchant.
References Cited (Backward Citations)
US5266514A
Cited
US5656531A
Cited
US5837580A
Cited
US5639689A
Cited
US5597754A
Cited
US5639685A
Cited
US5831282A
Cited
US5634974A
Cited
US5691228A
Cited
US5760434A
Cited
US5858852A
Cited
US5963805A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-04-04 | 2003-10-04 | 2004-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-04-04 | 2007-10-04 | 2008-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-04-04 | 2011-10-04 | 2012-04-04 | $7700.00 | Window Closed / Lapsed |