Method for forming via contact hole in a semiconductor device
Assignee: United Microelectronics Corp
•
Filing: 1997-10-03
•
Granted: 1999-07-20
•
Expires: 2017-10-03
Abstract
Abstract A method of plasma etching photoresist and sidewall polymer with an etch gas mixture comprising a fluorine containing gas (CF4 or NF3) and H2O demonstrating very aggressive ashrate of photoresist but maintains an exceptionally low etch rate for titanium nitride and other metals is provided. The very low TiN etch rate permits the inventive method to effectively breakdown sidewall polymer without removing any significant amount of these metals. The invention is particularly suited for stripping sidewall polymer from etched via holes and from etched metal lines. Vias fabricated with this technique exhibit exceptionally low resistance.
Inventors
- 👤 Ramiro Solis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:05
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/26; G03F7/36; G03F7/42; G03F7/427; H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287; H10P70/00; H10P70/20; H10P70/23; H10P70/234; H10P70/27; H10P70/273; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; Y; Y10; Y10S; Y10S438/00; Y10S438/963
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
144 words
A method of forming a via contact hole in a semiconductor device that comprises the steps of: forming a metal layer on a wafer; forming a dielectric layer on said metal layer; forming a photoresist pattern after a photoresist layer is coated on said dielectric layer; forming a via contact hole by an etching process employing said photoresist pattern as a mask; and removing a layer of sidewall polymer on said via contact hole and a part of said photoresist layer by a process comprising the steps of: (i) positioning said semiconductor device into a chamber; (ii) introducing effective amounts of a fluorine containing etchant gas and H 2 O gas into the chamber; (iii) decomposing said etchant gas and H 2 O gas and plasma phase reacting the decomposed gases with the sidewall polymer; and (iv) dissolving the sidewall polymer with a solvent.
Claim 2
Independent Claim
144 words
A method of forming a via contact hole in a semiconductor device that comprises the steps of: forming a metal layer on a wafer; forming a dielectric layer on said metal layer; forming a photoresist pattern after a photoresist layer is coated on said dielectric layer; forming a via contact hole by an etching process employing said photoresist pattern as a mask; and removing a layer of sidewall polymer on said via contact hole and a part of said photoresist layer by a process comprising the steps of: (i) positioning said semiconductor device into a chamber; (ii) introducing effective amounts of a fluorine containing etchant gas and H 2 O gas into the chamber; (iii) decomposing said etchant gas and H 2 O gas and plasma phase reacting the decomposed gases with the sidewall polymer; and (iv) dissolving the sidewall polymer with a solvent.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein the fluorine containing etchant gas is CF 4 .
Claim 4
Dependent Claim
31 words
The method of claim 2 wherein the ratio of the H 2 O flow rate to the CF 4 flow rate into the chamber is at least about 2.5 to 1.
Claim 5
Dependent Claim
27 words
The method of claim 2 wherein the ratio of the etch rate for sidewall polymer to the etch rate for metal is at least 5 to 1.
Claim 6
Dependent Claim
22 words
The method of claim 2 wherein the sidewall polymer is etched at a rate of at least about 5000 Å per minute.
Claim 7
Dependent Claim
25 words
The method of claim 1 wherein the metal is material that is selected from the group consisting of TiN, TiW, aluminum, AlCu, and mixtures thereof.
Claim 8
Dependent Claim
25 words
The method of claim 2 wherein the metal is material that is selected from the group consisting of TiN, TiW, aluminum, AlCu, and mixtures thereof.
Claim 9
Dependent Claim
11 words
The method of claim 1 wherein the metal layer is TiN.
Claim 10
Dependent Claim
11 words
The method of claim 2 wherein the metal layer is TiN.
Claim 11
Dependent Claim
13 words
The method of claim 1 wherein the dielectric material comprises SiO 2 .
Claim 12
Dependent Claim
13 words
The method of claim 2 wherein the dielectric material comprises SiO 2 .
References Cited (Backward Citations)
US4123841A
Cited
US4514254A
Cited
US4670091A
Cited
US4983254A
Cited
US5077598A
Cited
US5122225A
Cited
US5451291A
Cited
US5348619A
Cited
US5358602A
Cited
US5485304A
Cited
US5497262A
Cited
US5512507A
Cited
US5526951A
Cited
US5521104A
Cited
US5573971A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-07-19 | 2003-01-18 | 2003-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-07-19 | 2007-01-18 | 2007-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-07-19 | 2011-01-18 | 2011-07-20 | $7700.00 | Window Closed / Lapsed |