Process for forming a semiconductor device
Assignee: North Star Innovations Inc
•
Filing: 1997-12-22
•
Granted: 1999-04-13
•
Expires: 2017-12-22
Abstract
Abstract A semiconductor device comprises a substrate (100), first conductive film (22 and 32) over the substrate (100), and a second conductive film (54 and 64) over the first conductive film (22 and 32). The first conductive film includes a refractory metal and nitrogen. The first conductive film has a first portion (22) that lies closer to the substrate and a second portion (32) that lies further from the substrate. The nitrogen percentage for the second portion (32) is lower than the nitrogen atomic percentage for the first portion (22). The second conductive film (54 and 64) includes mostly copper. The combination of portions (22 and 32) within the first conductive film provides a good diffusion barrier (first portion) and has good adhesion (second portion) with the second conductive film (54 and 64).
Inventors
- 👤 Jiming Zhang
- 👤 Dean J. Denning
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 14:43
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/042; H10W20/043; H10W20/033; H10W20/056; H10W20/071; H10W20/081; H10W20/084; H10W20/40; H10W20/41; H10W20/425
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
125 words
A process for forming a semiconductor device comprising the steps of: placing a substrate in a processing chamber; forming a first conductive film that includes a refractory metal and nitrogen over the substrate, wherein: the first conductive film includes a first portion and a second portion; the first portion lies closer to the substrate and has a first nitrogen atomic percentage; the second portion lies further from the substrate has a second nitrogen atomic percentage that is lower than the first nitrogen atomic percentage; and a change between the first nitrogen atomic percent and the second atomic percent within the first conductive film is essentially continuous; and forming a second conductive film over the first conductive film, wherein the second conductive film includes mostly copper.
Claim 2
Dependent Claim
125 words
A process for forming a semiconductor device comprising the steps of: placing a substrate in a processing chamber; forming a first conductive film that includes a refractory metal and nitrogen over the substrate, wherein: the first conductive film includes a first portion and a second portion; the first portion lies closer to the substrate and has a first nitrogen atomic percentage; the second portion lies further from the substrate has a second nitrogen atomic percentage that is lower than the first nitrogen atomic percentage; and a change between the first nitrogen atomic percent and the second atomic percent within the first conductive film is essentially continuous; and forming a second conductive film over the first conductive film, wherein the second conductive film includes mostly copper.
Claim 3
Dependent Claim
21 words
The process of claim 1, wherein the first nitrogen atomic percentage is in a range of approximately 33-50 atomic percent nitrogen.
Claim 4
Dependent Claim
21 words
The process of claim 1, wherein the second nitrogen atomic percentage is in a range of approximately 0-30 atomic percent nitrogen.
Claim 5
Dependent Claim
20 words
The process of claim 1, wherein the refractory metal is selected from a group consisting of tantalum, tungsten, and molybdenum.
Claim 6
Dependent Claim
13 words
The process of claim 1, wherein the second portion further comprises semiconductor atoms.
Claim 7
Dependent Claim
35 words
The process of claim 1, wherein the first conductive film includes an uppermost surface that is furthest from the substrate, and, wherein the first conductive film at the uppermost surface has essentially no nitrogen atoms.
Claim 8
Dependent Claim
63 words
The process of claim 1, wherein the step of forming the first conductive film is performed in the processing chamber and includes steps of: depositing the first portion while a nitrogen-containing gas flows into the processing chamber; and depositing the second portion on the first portion, wherein the nitrogen-containing gas has a lower flowrate compared to the step of depositing the first portion.
Claim 9
Dependent Claim
27 words
The process of claim 7, further comprising a step of depositing a third portion of the first conductive film before the step of depositing the first portion.
Claim 10
Dependent Claim
22 words
The process of claim 7, wherein the nitrogen-containing gas is reduced to zero flow during the step of depositing the second portion.
Claim 11
Dependent Claim
15 words
The process of claim 7, wherein the first portion is thicker than the second portion.
Claim 12
Dependent Claim
22 words
The process of claim 1, wherein the first conductive film has a thickness in a range of approximately 10 to 500 angstroms.
Claim 13
Dependent Claim
33 words
The process of claim 1, wherein the step of forming the second conductive film includes a step of depositing at least a portion of the second conductive film by metal-organic chemical vapor deposition.
Claim 14
Dependent Claim
66 words
The process of claim 1, wherein the step of forming the second conductive film includes a step of depositing at least a portion of the second conductive film using physical vapor deposition, wherein: the substrate is placed on a susceptor; and at least one of the substrate and the susceptor is at a temperature in a range of approximately 350-450° C. during the step of depositing.
Claim 15
Dependent Claim
21 words
The process of claim 1, further comprising a step of forming a passivation layer over the first and second conductive films.
Claim 16
Dependent Claim
20 words
The process of claim 5, wherein the second portion comprises semiconductor atoms selected from a group consisting silicon and germanium.
Claim 17
Dependent Claim
26 words
The process of claim 1, further comprising forming an insulating layer prior to forming the first conductive film, wherein the first portion contacts the insulating layer.
Claim 18
Dependent Claim
31 words
The process of claim 16, wherein the first portion consists essentially of tantalum and nitrogen, and wherein the first nitrogen atomic percent is in a range of approximately 33-50 atomic percent.
Claim 19
Dependent Claim
150 words
A process for forming a semiconductor device comprising the steps of: forming a patterned insulating layer over a substrate, wherein the patterned insulating layer includes an opening; forming a first conductive film that includes tantalum and nitrogen, wherein: the first conductive film includes a first portion and a second portion; the first portion lies closer to the substrate and has a first nitrogen atomic percentage; and the second portion lies further from the substrate and has a second nitrogen atomic percentage that is lower than the first nitrogen atomic percentage; and forming a second conductive film on the first conductive film, wherein the second conductive film includes mostly copper; polishing the second conductive film to remove the second conductive film overlying the patterned insulating layer outside of the opening; and polishing the first conductive film to remove the first conductive film overlying the patterned insulating layer outside of the opening.
Claim 20
Dependent Claim
150 words
A process for forming a semiconductor device comprising the steps of: forming a patterned insulating layer over a substrate, wherein the patterned insulating layer includes an opening; forming a first conductive film that includes tantalum and nitrogen, wherein: the first conductive film includes a first portion and a second portion; the first portion lies closer to the substrate and has a first nitrogen atomic percentage; and the second portion lies further from the substrate and has a second nitrogen atomic percentage that is lower than the first nitrogen atomic percentage; and forming a second conductive film on the first conductive film, wherein the second conductive film includes mostly copper; polishing the second conductive film to remove the second conductive film overlying the patterned insulating layer outside of the opening; and polishing the first conductive film to remove the first conductive film overlying the patterned insulating layer outside of the opening.
Claim 21
Dependent Claim
42 words
The process of claim 18, wherein the step of forming the second conductive film includes a step of depositing at least a portion of the second conductive film by metal-organic chemical vapor deposition onto the second portion of the first conductive film.
Claim 22
Dependent Claim
21 words
The process of claim 18, wherein the second portion further comprises semiconductor atoms selected from a group consisting silicon and germanium.
Claim 23
Dependent Claim
14 words
The process of claim 18, wherein the first portion contacts the patterned insulating layer.
Claim 24
Dependent Claim
20 words
The process of claim 21, wherein the first nitrogen atomic percent is in a range of approximately 33-50 atomic percent.
References Cited (Backward Citations)
EP0163830A2
Cited
US5231053A
Cited
US5289035A
Cited
US5206187A
Cited
US5323047A
Cited
US5468339A
Cited
US5391517A
Cited
US5747360A
Cited
US5420072A
Cited
EP0673063A2
Cited
US5614437A
Cited
US5677238A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-04-12 | 2002-10-12 | 2003-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-04-12 | 2006-10-12 | 2007-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-04-12 | 2010-10-12 | 2011-04-13 | $7700.00 | Window Closed / Lapsed |