Method of fabricating semiconductor device and method of processing substrate
Assignee: Semiconductor Energy Laboratory Co Ltd
•
Filing: 1995-11-03
•
Granted: 1998-11-17
•
Expires: 2015-11-03
Abstract
Abstract Method of fabricating a semiconductor device. A glass substrate such as Corning 7059 is used as a substrate. A bottom film is formed. Then, the substrate is annealed above the strain point of the glass substrate. The substrate is then slowly cooled below the strain point. Thereafter, a silicon film is formed, and a TFT is formed. The aforementioned anneal and slow cooling reduce shrinkage of the substrate created in later thermal treatment steps. This makes it easy to perform mask alignments. Furthermore, defects due to misalignment of masks are reduced, and the production yield is enhanced. In another method, a glass substrate made of Corning 7059 is also used as a substrate. The substrate is annealed above the strain point. Then, the substrate is rapidly cooled below the strain point. Thereafter, a bottom film is formed, and a TFT is fabricated. The aforementioned anneal and slow cooling reduce shrinkage of the substrate created in later thermal treatment steps. Thus, less cracks are created in the active layer of the TFT and in the bottom film. This improves the production yield. During heating of the substrate, it is held substantially horizontal to reduce warpage, distortions, and waviness of the substrate.
Inventors
- 👤 Hiroki Adachi
- 👤 Yuugo Goto
- 👤 Hongyong Zhang
- 👤 Toru Takayama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:56
CPC Classifications
H; H10; H10D; H10D86/00; H10D86/40; H10P; H10P10/00; H10D30/00; H10D30/01; H10D30/021; H10D30/031; H10D30/0312; H10D30/0314; H10D30/0321; H10D86/01; H10D86/021; H10D86/0212; H10D86/0221; H10D86/0223; H10D86/0225; H10D86/60; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2922; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3216; H10P14/3238; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/38; H10P14/3802; H10P14/3806; Y; Y10; Y10S; Y10S148/00; Y10S148/016; Y10S438/00; Y10S438/974
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
127 words
A method of fabricating a semiconductor device, comprising the steps of: forming a bottom film on a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate after said bottom film forming step; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a semiconductor film comprising silicon on said bottom film; and thermally annealing said substrate at a third temperature not exceeding said strain point of the glass substrate after said semiconductor film forming step, wherein all film forming steps subsequent to said semiconductor film forming step are performed at a temperature less than said strain point.
Claim 2
Independent Claim
127 words
A method of fabricating a semiconductor device, comprising the steps of: forming a bottom film on a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate after said bottom film forming step; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a semiconductor film comprising silicon on said bottom film; and thermally annealing said substrate at a third temperature not exceeding said strain point of the glass substrate after said semiconductor film forming step, wherein all film forming steps subsequent to said semiconductor film forming step are performed at a temperature less than said strain point.
Claim 3
Independent Claim
127 words
A method of fabricating a semiconductor device, comprising the steps of: forming a bottom film on a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate after said bottom film forming step; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a semiconductor film comprising silicon on said bottom film; and thermally annealing said substrate at a third temperature not exceeding said strain point of the glass substrate after said semiconductor film forming step, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
Claim 4
Independent Claim
127 words
A method of fabricating a semiconductor device, comprising the steps of: forming a bottom film on a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate after said bottom film forming step; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a semiconductor film comprising silicon on said bottom film; and thermally annealing said substrate at a third temperature not exceeding said strain point of the glass substrate after said semiconductor film forming step, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
Claim 5
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: thermally annealing a glass substrate at a first temperature higher than a strain point of said glass substrate to shrink said glass substrate; forming a bottom film on said glass substrate after said thermally annealing step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; selectively or wholly providing in contact with said semiconductor film a catalytic element which promotes crystallization of said semiconductor film; and crystallizing said semiconductor film from a location of said catalytic element by thermal annealing at a temperature less than said strain point of the glass substrate, wherein all film formation steps subsequent to said semiconductor film forming step are performed at a temperature less than said strain point.
Claim 6
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: thermally annealing a glass substrate at a first temperature higher than a strain point of said glass substrate to shrink said glass substrate; forming a bottom film on said glass substrate after said thermally annealing step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; selectively or wholly providing in contact with said semiconductor film a catalytic element which promotes crystallization of said semiconductor film; and crystallizing said semiconductor film from a location of said catalytic element by thermal annealing at a temperature less than said strain point of the glass substrate, wherein all film formation steps subsequent to said semiconductor film forming step are performed at a temperature less than said strain point.
Claim 7
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: thermally annealing a glass substrate at a first temperature higher than a strain point of said glass substrate to shrink said glass substrate; forming a bottom film on said glass substrate after said thermally annealing step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; selectively or wholly providing in contact with said semiconductor film a catalytic element which promotes crystallization of said semiconductor film; and crystallizing said semiconductor film from a location of said catalytic element by thermal annealing at a temperature less than said strain point of the glass substrate, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
Claim 8
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: thermally annealing a glass substrate at a first temperature higher than a strain point of said glass substrate to shrink said glass substrate; forming a bottom film on said glass substrate after said thermally annealing step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; selectively or wholly providing in contact with said semiconductor film a catalytic element which promotes crystallization of said semiconductor film; and crystallizing said semiconductor film from a location of said catalytic element by thermal annealing at a temperature less than said strain point of the glass substrate, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
Claim 9
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: preparing a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a bottom film on said substrate after said cooling step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; and heat-treating said substrate and said semiconductor film at a third temperature not higher than said strain point of the glass substrate, wherein all film formation steps subsequent to said semiconductor film forming step are performed at a temperature less than said strain point.
Claim 10
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: preparing a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a bottom film on said substrate after said cooling step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; and heat-treating said substrate and said semiconductor film at a third temperature not higher than said strain point of the glass substrate, wherein all film formation steps subsequent to said semiconductor film forming step are performed at a temperature less than said strain point.
Claim 11
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: preparing a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a bottom film on said substrate after said cooling step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; and heat-treating said substrate and said semiconductor film at a third temperature not higher than said strain point of the glass substrate, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
Claim 12
Independent Claim
128 words
A method of fabricating a semiconductor device comprising the steps of: preparing a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate; cooling said substrate from said first temperature to a second temperature lower than said strain point at a rate of less than 2° C./min; forming a bottom film on said substrate after said cooling step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; and heat-treating said substrate and said semiconductor film at a third temperature not higher than said strain point of the glass substrate, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
Claim 13
Independent Claim
72 words
A method of fabricating a semiconductor device comprising the steps of: thermally annealing a glass substrate at a first temperature higher than a strain point of said glass substrate to shrink said glass substrate; forming a bottom film on said glass substrate after said thermally annealing step; forming a semiconductor device on said bottom film with a temperature of said glass substrate being less than said strain point of said glass substrate.
Claim 14
Independent Claim
72 words
A method of fabricating a semiconductor device comprising the steps of: thermally annealing a glass substrate at a first temperature higher than a strain point of said glass substrate to shrink said glass substrate; forming a bottom film on said glass substrate after said thermally annealing step; forming a semiconductor device on said bottom film with a temperature of said glass substrate being less than said strain point of said glass substrate.
Claim 15
Independent Claim
120 words
A method of fabricating a semiconductor device comprising the steps of: preparing a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate; cooling said substrate from said first temperature to a second temperature lower than said strain point; forming a bottom film on said substrate after said cooling step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; and heat-treating said substrate and said semiconductor film at a third temperature not higher than said strain point of the glass substrate, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
Claim 16
Independent Claim
120 words
A method of fabricating a semiconductor device comprising the steps of: preparing a glass substrate having a strain point; thermally annealing said glass substrate at a first temperature higher than said strain point of said glass substrate; cooling said substrate from said first temperature to a second temperature lower than said strain point; forming a bottom film on said substrate after said cooling step; forming a non-single crystal semiconductor film comprising silicon on said bottom film; and heat-treating said substrate and said semiconductor film at a third temperature not higher than said strain point of the glass substrate, wherein temperature of said glass substrate in all steps subsequent to said semiconductor film forming step is less than said strain point.
References Cited (Backward Citations)
US3250605A
Cited
JPS58114037A
Cited
US4547256A
Cited
US4525355A
Cited
US4709466A
Cited
US4851363A
Cited
US5252140A
Cited
US4894080A
Cited
JPH02102150A
Cited
US4977748A
Cited
US5306651A
Cited
US5254208A
Cited
US5147826A
Cited
US5112764A
Cited
US5064775A
Cited
US5262654A
Cited
US5297956A
Cited
US5294238A
Cited
US5308998A
Cited
JPH05186235A
Cited
US5403772A
Cited
US5275851A
Cited
US5426064A
Cited
US5580792A
Cited
US5501989A
Cited
US5481121A
Cited
US5529937A
Cited
US5569935A
Cited
US5534716A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-16 | 2002-05-18 | 2002-11-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-16 | 2006-05-18 | 2006-11-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-16 | 2010-05-18 | 2010-11-17 | $7700.00 | Window Closed / Lapsed |