US5618575A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process and apparatus for the production of a metal oxide layer
Assignee: OC Oerlikon Balzers AG
•
Filing: 1995-04-21
•
Granted: 1997-04-08
•
Expires: 2015-04-21
Abstract
Abstract A process and apparatus for producing a metal oxide layer which is selectively permeable to ions of a given class, comprises evacuating a vacuum chamber, evaporating metal particles in the chamber and imparting to the particles kinetic energy which is at 10 eV maximum, introducing oxygen into the chamber with a quantity of oxygen being controlled to deposit a metal oxide on a substrate in the chamber, while the substrate is maintained below 900° C.
Inventors
- 👤 Gunter Peter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:00
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/54; C23C14/0021; H; H01; H01J; H01J2237/00; H01J2237/18; H01J2237/182; H01J2237/20; H01J2237/2001; H01J2237/30; H01J2237/31; H01J2237/3132
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
157 words
Process for producing a metal oxide layer on a substrate, the metal oxide layer being free of cracks, the process comprising: holding the substrate in an evacuated vacuum chamber, evacuated to 10 -1 mbar or lower; setting particles of a metal free into the chamber, the freed metal particle having a kinetic energy; introducing oxygen into the chamber; keeping a temperature of the substrate below 900° C.; reacting said particles with said oxygen to form metal oxide deposition on said substrate; steadily raising a ratio of a quantity of the oxygen introduced per unit time into said chamber to the metal particles freed into said chamber per unit time, controlled for each mono-atomic or mono-molecular layer deposited on the substrate, to result in a steadily rising degree of oxidation of metal oxide on said substrate; and limiting the kinetic energy of the metal particles freed into said chamber to a maximum of 10 eV at said substrate.
Claim 2
Dependent Claim
157 words
Process for producing a metal oxide layer on a substrate, the metal oxide layer being free of cracks, the process comprising: holding the substrate in an evacuated vacuum chamber, evacuated to 10 -1 mbar or lower; setting particles of a metal free into the chamber, the freed metal particle having a kinetic energy; introducing oxygen into the chamber; keeping a temperature of the substrate below 900° C.; reacting said particles with said oxygen to form metal oxide deposition on said substrate; steadily raising a ratio of a quantity of the oxygen introduced per unit time into said chamber to the metal particles freed into said chamber per unit time, controlled for each mono-atomic or mono-molecular layer deposited on the substrate, to result in a steadily rising degree of oxidation of metal oxide on said substrate; and limiting the kinetic energy of the metal particles freed into said chamber to a maximum of 10 eV at said substrate.
Claim 3
Dependent Claim
55 words
Process as stated in claim 1, wherein the particles of the metal are set free in the chamber at a release rate and so that the release rate averaged over time and over a release area for the metal leaving from a metal particle source is no more than 0.3 nms -1 from the source.
Claim 4
Dependent Claim
18 words
Process as stated in claim 2, wherein said release rate is no more than 0.01 nms -1 .
Claim 5
Dependent Claim
39 words
Process as stated in claim 1, wherein a precision of a release rate of the metal particles from a metal source, averaged over time and over a release area of the source is ≦10% relative to a reference value.
Claim 6
Dependent Claim
18 words
Process as stated in claim 4, wherein said release rate is no more than 0.005 nms -1 .
Claim 7
Dependent Claim
11 words
Process as stated in claim 4, wherein said precision is ≦1%.
Claim 8
Dependent Claim
37 words
Process as stated in claim 1, wherein a drift of a release rate of the metal particles from a metal source averaged over time and over a release area of the source, is ≦5% in 20 minutes.
Claim 9
Dependent Claim
26 words
Process as stated in claim 7, wherein the drift of the release rate averaged over time and over the release area, is ≦0.5% in one hour.
Claim 10
Dependent Claim
30 words
Process as stated in claim 1, wherein the substrate or a layer growing on the substrate is acted upon by oxygen and the metal oxide layer is grown in situ.
Claim 11
Dependent Claim
16 words
Process as stated in claim 1, wherein the metal is evaporated to set the particles free.
Claim 12
Dependent Claim
14 words
Process as stated in claim 10, wherein the metal is evaporated by electron beam.
Claim 13
Dependent Claim
22 words
Process as stated in claim 1, wherein a rate of metal being set free from a source of the metal is measured.
Claim 14
Dependent Claim
34 words
Process as stated in claim 12, wherein the measurement takes place in a spacial angle range in which the substrate with a region to be coated sees a source of the released metal particles.
Claim 15
Dependent Claim
19 words
Process as stated in claim 12, wherein the measurement is carried out by means of a quadruple mass spectrometer.
Claim 16
Dependent Claim
51 words
Process as stated in claim 12, wherein a result of said measurement is applied as an instantaneous value measurement in a negative feedback control circuit and setting, by means of a desired value for said rate at said circuit, the degree of oxidation at the mono-atomic or mono-molecular layer being produced.
Claim 17
Dependent Claim
36 words
Process as stated in claim 12, wherein said measuring is performed with a material-selective rate sensor having a detection sensitivity of ≦0.1 Ås -1 relative to an amount of said metal released from said metal source.
Claim 18
Dependent Claim
14 words
Process as stated in claim 16, wherein said sensitivity is ≦0.01 Ås -1 .
Claim 19
Dependent Claim
22 words
Process as stated in claim 12, wherein said measuring is performed with a rate sensor having a response time of ≦100 ms.
Claim 20
Dependent Claim
13 words
Process as stated in claim 18, wherein said response time is ≦10 ms.
Claim 21
Dependent Claim
13 words
Process as stated in claim 19, wherein said response time is ≦1 ms.
Claim 22
Dependent Claim
36 words
Process as stated in claim 12, wherein said measuring is performed in a volume of said chamber separated from a remaining volume by a pressure stage and wherein said oxygen is inlet in said remaining volume.
Claim 23
Dependent Claim
74 words
Process as stated in claim 1, wherein at least one parameter is negative feedback controlled, where said parameter is selected from the group consisting of: (a) the temperature of the substrate, (b) a quantity of the metal set free per unit time, (c) the quantity of the oxygen introduced per unit time, and (d) the ratio of the quantity of the metal set free to the quantity of the oxygen introduced per time unit.
Claim 24
Dependent Claim
33 words
Process as stated in claim 22 wherein two of the parameters (a), (b), and (c) are kept constant at least during predetermined coating time spans, and the remaining parameter is negative feedback controlled.
Claim 25
Dependent Claim
38 words
Process as stated in claim 1, wherein a first volume of the chamber with the substrate and a second volume where the oxygen is introduced, are separated from a remaining volume of the chamber via a pressure stage.
Claim 26
Dependent Claim
43 words
Process as stated in claim 1, wherein the metal oxide layer is produced so that the metal oxide layer is sandwiched between two metal surfaces in that said ratio is reduced after the ratio is increased, to result in a metal being deposited.
Claim 27
Dependent Claim
30 words
Process as stated in claim 1, wherein the quantity of the oxygen introduced is varied at larger time intervals than a rate at which the metal particles are set free.
Claim 28
Dependent Claim
26 words
Process as stated in claim 1, wherein said oxygen comprises excited oxygen in a form of at least one of ozone, electron excited oxygen, and ions.
Claim 29
Dependent Claim
18 words
Process as stated in claim 1, wherein kinetic energy of the oxygen is not greater than 10 eV.
Claim 30
Dependent Claim
35 words
Process as stated in claim 1, wherein the oxygen is excited by at least one energy source selected from the group consisting of a glow discharge, a microwave discharge, inductively coupled plasma, and light radiation.
Claim 31
Dependent Claim
17 words
Process as stated in claim 1, wherein the substrate temperature is kept at 600° C. at most.
Claim 32
Dependent Claim
11 words
Process as stated in claim 1, wherein said metal is Ir.
Claim 33
Dependent Claim
20 words
Process as stated in claim 1, wherein an initial process pressure is set to be 10 -6 mbar or lower.
Claim 34
Dependent Claim
16 words
Process as stated in claim 32, wherein said pressure is 10 -9 gm bar or lower.
Claim 35
Dependent Claim
142 words
Process as stated in claim 1, wherein the introducing of the oxygen includes connecting an oxygen reservoir to said vacuum chamber via a first and a second valve, further connecting a pump via a third valve between the first and the second valve, providing connecting lines between said first, second and third valves, heating the connecting lines between the first, second and third valves to at least 200° C., with sequential steps of (a) the first and second valves closed and with the third valve open; (b) evacuating said lines to at least 10 -2 mbar; (c) closing said third valve; (d) opening said first valve to flood said lines with oxygen; repeating the steps (a) to (d) at least five times, then closing said first valve and opening said third valve and evacuating said lines and subsequently opening said second valve.
Claim 36
Dependent Claim
55 words
Process as stated in claim 1, including the raising of said ratio being performed by controlling a rate of setting the metal metal particles to be constant and continuously increasing the quantity of the oxygen supplied so that said degree of oxidation from one deposited monomolecular layer to a next layer changes in predeterminable manner.
References Cited (Backward Citations)
FR2341668A1
Cited
US4113599A
Cited
US4451499A
Cited
US4379040A
Cited
GB2158104A
Cited
US5016563A
Cited
US4888202A
Cited
EP0302506A2
Cited
US5362711A
Cited
US4800100A
Cited
US4936964A
Cited
US4975168A
Cited
WO1990002215A1
Cited
US4923585A
Cited
US5422338A
Cited
US5227364A
Cited
US5403433A
Cited
US5347157A
Cited
US5387459A
Cited
US5499599A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-04-07 | 2000-10-07 | 2001-04-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-04-07 | 2004-10-07 | 2005-04-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-04-07 | 2008-10-07 | 2009-04-08 | $7700.00 | Window Closed / Lapsed |