Method of forming transparent conductive film and apparatus for forming the same
Assignee: Casio Computer Co Ltd
•
Filing: 1989-04-17
•
Granted: 1990-12-04
•
Expires: 2009-04-17
Abstract
Abstract A method of forming a transparent conductive thin film by sputtering includes the step of placing a target consisting of a conductive oxide material and a substrate on which the thin film is to be formed in a pressure vessel, the step of supplying argon gas and oxygen gas after the pressure vessel is substantially evacuated, the step of supplying a sputtering current to the target to maintain a discharge state, the step of detecting the partial pressure of oxygen in the gas mixture in the pressure chamber, and the step of controlling the flow rate of oxygen gas. The flow rate of the oxygen gas is controlled by a control unit such that the value of the partial pressure of oxygen which is detected in the partial pressure detection step is always kept constant.
Inventors
- 👤 Ichiro Ohno
- 👤 Junji Shiota
- 👤 Hidetaka Uchiumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:17
CPC Classifications
H; H01; H01J; H01J37/00; H01J37/32; H01J37/32431; H01J37/3244; C; C23; C23C; C23C14/00; C23C14/0021; C23C14/0036; C23C14/0042; C23C14/22; C23C14/54; C23C14/542; C23C14/545; C23C14/547
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
191 words
A method of forming a transparent conductive thin film by sputtering, comprising: a first step of placing a target including a conductive oxide material and a substrate on which a thin film is to be formed, in a pressure vessel; a second step of substantially evacuating the pressure vessel and supplying a sputtering gas mixture comprising a gas of a Group VIII element of the periodic table and oxygen gas; a third step of supplying a sputtering current to the target to maintain a discharge state; a fourth step of detecting the partial pressure of oxygen in the sputtering gas mixture filled in the pressure vessel; a fifth step of controlling the flow rate of oxygen gas in the second step so that the partial pressure of oxygen which is detected in the fourth step is kept substantially constant; a sixth step of detecting a thickness of the transparent conductive thin film deposited on the substrate; and a seventh step of controlling the sputtering current supplied to the target such that the final thickness of said film detected in the sixth step is controlled to be a substantially constant predetermined value.
Claim 2
Independent Claim
191 words
A method of forming a transparent conductive thin film by sputtering, comprising: a first step of placing a target including a conductive oxide material and a substrate on which a thin film is to be formed, in a pressure vessel; a second step of substantially evacuating the pressure vessel and supplying a sputtering gas mixture comprising a gas of a Group VIII element of the periodic table and oxygen gas; a third step of supplying a sputtering current to the target to maintain a discharge state; a fourth step of detecting the partial pressure of oxygen in the sputtering gas mixture filled in the pressure vessel; a fifth step of controlling the flow rate of oxygen gas in the second step so that the partial pressure of oxygen which is detected in the fourth step is kept substantially constant; a sixth step of detecting a thickness of the transparent conductive thin film deposited on the substrate; and a seventh step of controlling the sputtering current supplied to the target such that the final thickness of said film detected in the sixth step is controlled to be a substantially constant predetermined value.
Claim 3
Dependent Claim
65 words
A method according to claim 1, wherein the fourth step comprises: the substep of detecting an ionic current corresponding to the partial pressure of oxygen by a quadrupole electrode mass analyzing tube for receiving the sputtering gas mixture in the pressure vessel; and the substep of calculating the partial pressure of oxygen by an arithmetic control unit on the basis of the detected ionic current.
Claim 4
Dependent Claim
60 words
A method according to claim 2, wherein the fifth step comprises: the substep of comparing the partial pressure of oxygen detected in the fourth step and a reference partial pressure of oxygen prestored in the arithmetic control unit and calculating a difference therebetween; and the substep of controlling the flow rate of oxygen gas on the basis of the difference.
Claim 5
Dependent Claim
18 words
A method according to claim 1, wherein the sixth step comprises the step of optically measuring the thickness.
Claim 6
Dependent Claim
69 words
A method according to claim 1, wherein the sixth step comprises: the substep of measuring a spectral distribution of a beam transmitted through the thin film formed on the substrate; the substep of detecting a wavelength representing a minimum or maximum value of the spectral distribution; and the substep of calculating the thickness of the thin film on the basis of the wavelength representing the minimum or maximum value.
Claim 7
Dependent Claim
21 words
A method according to claim 1, including forming films on a number of substrates fed in line through the pressure vessel.
Claim 8
Independent Claim
263 words
A method of forming a transparent conductive thin film by sputtering, comprising: a step of placing a target including a conductive oxide material in a pressure vessel; a step of substantially evacuating the pressure vessel; a step of feeding a substrate on which the thin film is to be formed into the pressure vessel; a step of supplying a sputtering gas mixture comprising a gas of a Group VIII element of the periodic table and oxygen gas in the pressure vessel; a step of supplying a sputtering current to the target to maintain a discharge state; a step of detecting the a partial pressure of oxygen of the sputtering gas mixture filled in the pressure vessel; a step of controlling a flow rate of oxygen gas in the gas supply step so that the partial pressure of oxygen detected in the step of detecting the partial pressure of oxygen is kept constant; a step of detecting the thickness of the transparent conductive thin film deposited on the substrate; a step of controlling the sputtering current supplied to the target such that the final thickness of said film detected by the film thickness detection step is controlled to a substantially constant predetermined value; and a step of unloading the substrate having the thin film thereon from the pressure vessel, wherein the thin film forming step including at least the substrate feed step, the gas supply step, the discharge maintaining step, and the substrate unloading step is repeated a plurality of times to continuously form transparent conductive thin films on a large number of substrates.
Claim 9
Independent Claim
263 words
A method of forming a transparent conductive thin film by sputtering, comprising: a step of placing a target including a conductive oxide material in a pressure vessel; a step of substantially evacuating the pressure vessel; a step of feeding a substrate on which the thin film is to be formed into the pressure vessel; a step of supplying a sputtering gas mixture comprising a gas of a Group VIII element of the periodic table and oxygen gas in the pressure vessel; a step of supplying a sputtering current to the target to maintain a discharge state; a step of detecting the a partial pressure of oxygen of the sputtering gas mixture filled in the pressure vessel; a step of controlling a flow rate of oxygen gas in the gas supply step so that the partial pressure of oxygen detected in the step of detecting the partial pressure of oxygen is kept constant; a step of detecting the thickness of the transparent conductive thin film deposited on the substrate; a step of controlling the sputtering current supplied to the target such that the final thickness of said film detected by the film thickness detection step is controlled to a substantially constant predetermined value; and a step of unloading the substrate having the thin film thereon from the pressure vessel, wherein the thin film forming step including at least the substrate feed step, the gas supply step, the discharge maintaining step, and the substrate unloading step is repeated a plurality of times to continuously form transparent conductive thin films on a large number of substrates.
Claim 10
Dependent Claim
71 words
A method according to claim 7, wherein the film thickness detection step comprises: the substep of measuring a spectral distribution of a beam transmitted through the thin film deposited on the substrate; the substep of detecting a wavelength representing a minimum or maximum value of the spectral distribution; and the substep of calculating the thickness of the thin film on the basis of the wavelength representing the minimum or maximum value.
Claim 11
Dependent Claim
71 words
A method according to claim 7, wherein the film thickness detection step comprises: the substep of measuring a spectral distribution of a beam reflected by the thin film deposited on the substrate; the substep of detecting a wavelength representing a minimum or maximum value of the spectral distribution; and the substep of calculating the thickness of the thin film on the basis of the wavelength representing the minimum or maximum value.
Claim 12
Dependent Claim
57 words
A method according to claim 7, wherein the sputtering current control step comprises: the substep of calculating a sputtering current to be updated on the basis of the thickness detected in the film thickness detection step; and the substep of setting the output current of a sputtering power source to the calculated value of the sputtering current.
Claim 13
Dependent Claim
26 words
A method according to claim 7, wherein the film thickness detection step and the sputtering current control step are executed every formation cycle of one substrate.
Claim 14
Dependent Claim
25 words
A method according to claim 7, wherein the film thickness detection step and the sputtering current control step are performed every plurality of formation cycles.
Claim 15
Dependent Claim
31 words
A method according to claim 12, wherein the film thickness detection step and the sputtering current control step have a low frequency when the number of film formation steps is increased.
Claim 16
Independent Claim
233 words
An apparatus for forming a transparent conductive thin film, comprising: a vacuum pump; a pressure vessel, connected to said vacuum pump and arranged for evacuation by said vacuum pump to exhaust internal gas therefrom; a target placed in said pressure vessel and including a conductive oxide material; means for feeding a substrate into said pressure vessel and on which substrate the transparent conductive thin film is to be formed; a sputtering power source, connected to said target, for supplying a sputtering current thereto; sputtering gas supply means for supplying a gas of a Group VIII element of the periodic table to said pressure vessel; oxygen gas supply means for supplying oxygen gas to said pressure vessel; oxygen gas detecting means for detecting the partial pressure of oxygen in the sputtering gas mixture filled in said pressure vessel; control means for controlling the flow rate of oxygen gas supplied from said oxygen gas supply means such that the partial pressure of oxygen detected by said oxygen gas detecting means is controlled to be substantially constant; film thickness detecting means for optically detecting the thickness of the thin film deposited on said substrate; and current control means for controlling the sputtering current supplied from said sputtering power source to said target such that the final thickness of said film detected by said film thickness detecting means is controlled to be a substantially constant predetermined value.
Claim 17
Independent Claim
233 words
An apparatus for forming a transparent conductive thin film, comprising: a vacuum pump; a pressure vessel, connected to said vacuum pump and arranged for evacuation by said vacuum pump to exhaust internal gas therefrom; a target placed in said pressure vessel and including a conductive oxide material; means for feeding a substrate into said pressure vessel and on which substrate the transparent conductive thin film is to be formed; a sputtering power source, connected to said target, for supplying a sputtering current thereto; sputtering gas supply means for supplying a gas of a Group VIII element of the periodic table to said pressure vessel; oxygen gas supply means for supplying oxygen gas to said pressure vessel; oxygen gas detecting means for detecting the partial pressure of oxygen in the sputtering gas mixture filled in said pressure vessel; control means for controlling the flow rate of oxygen gas supplied from said oxygen gas supply means such that the partial pressure of oxygen detected by said oxygen gas detecting means is controlled to be substantially constant; film thickness detecting means for optically detecting the thickness of the thin film deposited on said substrate; and current control means for controlling the sputtering current supplied from said sputtering power source to said target such that the final thickness of said film detected by said film thickness detecting means is controlled to be a substantially constant predetermined value.
Claim 18
Dependent Claim
64 words
An apparatus according to claim 14, wherein said film thickness detecting means comprises: means for measuring a spectral distribution of a beam transmitted through the thin film; means for detecting a wavelength representing a minimum or maximum value of the spectral distribution; and means for calculating the thickness of the thin film on the basis of the wavelength representing the minimum or maximum value.
Claim 19
Dependent Claim
54 words
An apparatus according to claim 14, wherein said current control means comprises: means for calculating a sputtering current to be updated on the basis of the thickness detected by said film thickness detecting means; and means for setting an output current of said sputtering power source to a value of the calculated sputtering current.
Claim 20
Dependent Claim
101 words
An apparatus according to claim 14, further comprising: a loading pressure vessel, connected to said pressure vessel through a sealing door, for loading said substrate into said pressure vessel; an unloading pressure vessel, connected to said pressure vessel through a sealing door, for unloading said substrate having the thin film thereon from said pressure vessel; and transfer means for sequentially transferring said substrate inside said loading pressure vessel, said pressure vessel, and said unloading pressure vessel, wherein a plurality of substrates are sequentially fed by said transfer means to continuously form transparent conductive thin films on a large number of substrates.
Claim 21
Dependent Claim
26 words
An apparatus according to claim 14, wherein said target consists of indium-tin oxide, and a low-resistive indium-tin oxide transparent conductive film is formed on said substrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-03 | 1994-06-04 | 1994-12-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-03 | 1998-06-04 | 1998-12-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-03 | 2002-06-04 | 2002-12-04 | $7700.00 | Window Closed / Lapsed |