Method for fabricating thin oxides for a semiconductor technology
Assignee: GlobalFoundries Inc
•
Filing: 1994-07-26
•
Granted: 1996-03-12
•
Expires: 2014-07-26
Abstract
Abstract In one embodiment a high-quality tunnel oxide suitable for programmable devices, such as EEPAL devices, is formed upon a surface region of a semiconductor body over a heavily-doped N+layer, and a gate oxide is formed over a gate region, by first oxidizing the semiconductor body to form an initial oxide layer upon the surface region of the semiconductor body over the heavily-doped N+layer and upon the surface of the gate region. Next, at least a portion of the initial oxide layer overlying the heavily-doped N+layer is removed. The semiconductor body is then exposed to an environment suitable for oxidation, to thicken the remaining portions of the initial oxide, thereby forming the gate oxide, and to form the tunnel oxide over the heavily doped N+layer. A concentration of nitrogen is introduced into both gate and tunnel oxides by introducing the semiconductor body to a source of nitrogen.
Inventors
- 👤 H. Jim Fulford, Jr.
- 👤 Mark I. Gardner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:47
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/0134; H10B; H10B41/00; H10B41/30; H10B41/35; H10D64/60; H10D64/66; H10D64/68; H10D64/693; H10D64/01342; H10D64/01344; H10D64/01346; Y; Y10; Y10S; Y10S438/00; Y10S438/981
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
174 words
In an integrated circuit fabrication process, a method for forming a first oxide layer upon a first surface region of a semiconductor body, and further for forming a second oxide layer, of greater thickness than the first oxide layer, upon a second surface region of the semiconductor body, comprising the steps of: forming an initial oxide layer upon the first and second surface regions of the semiconductor body; removing at least a portion of the initial oxide layer in a region disposed above the first surface region of the semiconductor body; exposing, subsequent to the removing step, the semiconductor body to an environment suitable for oxide formation, to form a first oxide layer disposed above the first surface region of the semiconductor body and to thicken the initial oxide layer disposed above the second surface region, thus forming the second oxide layer; and introducing, subsequent to the commencement of the exposing step, the semiconductor body to a source of nitrogen, to form a concentration of nitrogen in both the first and second oxide layers.
Claim 2
Dependent Claim
174 words
In an integrated circuit fabrication process, a method for forming a first oxide layer upon a first surface region of a semiconductor body, and further for forming a second oxide layer, of greater thickness than the first oxide layer, upon a second surface region of the semiconductor body, comprising the steps of: forming an initial oxide layer upon the first and second surface regions of the semiconductor body; removing at least a portion of the initial oxide layer in a region disposed above the first surface region of the semiconductor body; exposing, subsequent to the removing step, the semiconductor body to an environment suitable for oxide formation, to form a first oxide layer disposed above the first surface region of the semiconductor body and to thicken the initial oxide layer disposed above the second surface region, thus forming the second oxide layer; and introducing, subsequent to the commencement of the exposing step, the semiconductor body to a source of nitrogen, to form a concentration of nitrogen in both the first and second oxide layers.
Claim 3
Dependent Claim
37 words
A method as in claim 1 wherein the removing step comprises the complete removal of the initial oxide within the region disposed above the first surface region, thus exposing the first surface region of the semiconductor body.
Claim 4
Dependent Claim
59 words
A method as in claim 1 wherein the removing step comprises the partial removal of the initial oxide within the region disposed above the first surface region, thus leaving a remaining portion of the initial oxide, of lesser thicknes than its thickness at the completion of the forming step, disposed above the first surface region of the semiconductor body.
Claim 5
Dependent Claim
38 words
A method as in claim 1 further comprising, subsequent to the removing step and prior to the exposing step, the additional step of thinning the initial oxide layer disposed above the second surface region of the semiconductor body.
Claim 6
Dependent Claim
45 words
A method as in claim 1 wherein the initial oxide layer disposed above the second surface region of the semiconductor body is of a thickness, just prior to the exposing step, substantially unchanged as compared to its thickness at the completion of the forming step.
Claim 7
Dependent Claim
25 words
A method as in claim 1 wherein the first surface region of the semiconductor body is disposed overlying a heavily-doped layer of the semiconductor body.
Claim 8
Dependent Claim
45 words
A method as in claim 1 wherein the introducing step comprises the step of annealing the semiconductor body, subsequent to the exposing step, under an ambient containing nitrogen, to form a surface layer in both the first and second oxides containing a concentration of nitrogen.
Claim 9
Dependent Claim
25 words
A method as in claim 7 wherein the annealing step comprises an RTP annealing step and wherein the exposing step comprises a furnace growth step.
Claim 10
Dependent Claim
25 words
A method as in claim 7 wherein the annealing step comprises an LPCVD annealing step and wherein the exposing step comprises a furnace growth step.
Claim 11
Dependent Claim
25 words
A method as in claim 9 wherein the LPCVD annealing step is performed at a temperature in the range from 900° C. to 1050° C.
Claim 12
Dependent Claim
25 words
A method as in claim 9 wherein the LPCVD annealing step is performed at a pressure in the range from 5 torr to 30 torr.
Claim 13
Dependent Claim
22 words
A method as in claim 1 further comprising, subsequent to the exposing and introducing steps, the step of annealing the semiconductor body.
Claim 14
Dependent Claim
25 words
A method as in claim 12 wherein the annealing step comprises an RTP annealing step and wherein the exposing step comprises a furnace growth step.
Claim 15
Dependent Claim
25 words
A method as in claim 13 wherein the RTP annealing step is performed at a temperature in the range from 900° C. to 1050° C.
Claim 16
Dependent Claim
25 words
A method as in claim 13 wherein the furnace growth step is performed at a temperature in the range from 700° C. to 950° C.
Claim 17
Dependent Claim
25 words
A method as in claim 13 wherein the furnace growth step is performed at a temperature in the range from 800° C. to 850° C.
Claim 18
Dependent Claim
25 words
A method as in claim 12 wherein the annealing step comprises an LPCVD annealing step and wherein the exposing step comprises a furnace growth step.
Claim 19
Dependent Claim
56 words
A method as in claim 1 wherein the introducing step is performed simultaneously with the exposing step, wherein the environment suitable for oxide formation includes a source of nitrogen during at least a portion of the exposing step, to form a concentration of nitrogen in at least a portion of both the first and second oxides.
Claim 20
Dependent Claim
15 words
A method as in claim 18 wherein the exposing step comprises an LPCVD exposing step.
Claim 21
Dependent Claim
32 words
A method as in claim 19 wherein the environment suitable for oxidation comprises a mixture of N 2 O and SiH 4 having a ratio in the range from 2:1 to 10:1.
Claim 22
Dependent Claim
25 words
A method as in claim 19 wherein the LPCVD exposing step is performed at a pressure in the range from 100 mTorr to 500 mTorr.
Claim 23
Dependent Claim
25 words
A method as in claim 19 wherein the LPCVD exposing step is performed at a temperature in the range from 700° C. to 850° C.
Claim 24
Dependent Claim
15 words
A method as in claim 18 wherein the exposing step comprises a PECVD exposing step.
Claim 25
Dependent Claim
32 words
A method as in claim 23 wherein the environment suitable for oxidation comprises a mixture of N 2 O and SiH 4 having a ratio in the range from 2:1 to 10:1.
Claim 26
Dependent Claim
25 words
A method as in claim 23 wherein the PECVD exposing step is performed at a pressure in the range from 2 Torr to 30 Torr.
Claim 27
Dependent Claim
26 words
A method as in claim 23 wherein the PECVD exposing step is performed at a temperature in the range from approximately 25° C. to 400° C.
Claim 28
Dependent Claim
26 words
A method as in claim 23 wherein the PECVD exposing step is performed at a power level in the range from 50 W to 500 W.
Claim 29
Dependent Claim
45 words
A method as in claim 1 wherein the environment suitable for oxide formation includes a source of HCL during at least a portion of the exposing step, to form a concentration of chlorine in at least a portion of both the first and second oxides.
Claim 30
Dependent Claim
32 words
A method as in claim 1 wherein the environment suitable for oxide formation comprises an HCl-free environment during the exposing step, to form both the first and second oxides free from chlorine.
Claim 31
Dependent Claim
26 words
A method as in claim 1 wherein the forming step comprises a process chosen from the group consisting of LPCVD, PECVD, RTP, and furnace oxidation processes.
Claim 32
Dependent Claim
26 words
A method as in claim 1 wherein the exposing step comprises a process chosen from the group consisting of LPCVD, PECVD, RTP, and furnace oxidation processes.
Claim 33
Dependent Claim
24 words
A method as in claim 1 wherein the introducing step comprises a process chosen from the group consisting of PECVD, RTP, and furnace processes.
Claim 34
Dependent Claim
120 words
An integrated circuit comprising: a first oxide layer formed upon a first surface region of a semiconductor body by first forming an initial oxide layer thereupon, removing at least a portion thereof, and then exposing the semiconductor body to an environment suitable for oxide formation; a second oxide layer formed upon a second surface region of said semiconductor body by first forming an initial oxide layer thereupon, then exposing the semiconductor body to said environment suitable for oxide formation so as to thicken said initial oxide layer, thus creating the second oxide; wherein both the first and second oxides further comprise at least a respective portion thereof containing nitrogen formed by introducing the semiconductor body to an ambient containing nitrogen.
Claim 35
Dependent Claim
120 words
An integrated circuit comprising: a first oxide layer formed upon a first surface region of a semiconductor body by first forming an initial oxide layer thereupon, removing at least a portion thereof, and then exposing the semiconductor body to an environment suitable for oxide formation; a second oxide layer formed upon a second surface region of said semiconductor body by first forming an initial oxide layer thereupon, then exposing the semiconductor body to said environment suitable for oxide formation so as to thicken said initial oxide layer, thus creating the second oxide; wherein both the first and second oxides further comprise at least a respective portion thereof containing nitrogen formed by introducing the semiconductor body to an ambient containing nitrogen.
References Cited (Backward Citations)
US3945856A
Cited
US4329773A
Cited
US4517732A
Cited
US4567645A
Cited
US4774197A
Cited
US4784975A
Cited
US5225355A
Cited
US4894353A
Cited
US5219774A
Cited
US5215934A
Cited
US5057463A
Cited
US5225361A
Cited
US5208173A
Cited
US5077230A
Cited
JPH04148088A
Cited
US5210056A
Cited
US5316981A
Cited
US5362685A
Cited
US5296411A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-12 | 1999-09-11 | 2000-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-12 | 2003-09-11 | 2004-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-12 | 2007-09-11 | 2008-03-12 | $7700.00 | Window Closed / Lapsed |