Method for forming a buried subcollector in a semiconductor substrate by ion implantation
Assignee: International Business Machines Corp
•
Filing: 1983-09-16
•
Granted: 1986-02-04
•
Expires: 2003-09-16
Abstract
Abstract The method is comprised of the following steps: implanting arsenic ions through a thin screen oxide layer in the regions of a P type silicon substrate where subcollectors are to be formed, at a dose less than 2.10 16 at/cm 2 , partially etching said screen oxide layer to remove the upper portion, containing contaminating ions exposing to an oxygen ambiant to approximately reconstitute original thickness of the screen oxide layer and then annealing in an inert atmosphere, the substrate, to heal damages and distribute arsenic atoms in the substrate. It has been discovered that the step of reconstituting the original thickness of the screen oxide layer in an oxygen ambient, has the unexpected effect of permitting the subsequent growth of an absolutely defect free epitaxial layer.
Inventors
- 👤 Richard A. Cavanagh
- 👤 John L. Forneris
- 👤 Gregory B. Forney
- 👤 George Hrebin, Jr.
- 👤 Ronald A. Knapp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:50
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P30/21; H10P30/212; H10P30/28; H10W; H10W15/00; H10W15/01
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
139 words
An improvement in the method of forming a buried subcollector device wherein a thick silicon dioxide masking layer having a predetermined pattern of openings is formed on a P-type silicon substrate, followed by the growing in said openings of thin silicon dioxide screen layer, through which a beam of arsenic ions having an energy of 50 KeV and a dose less than 2.2×10 6 at/cm 2 produces the buried subcollector area, and partially etching away said screen oxide layer to remove the contaminated upper layer, characterized by; heating the thus-produced device in an oxydizing atmosphere for a time and temperature sufficient to restore the screen oxide layer to approximately its pre-etched thickness, and annealing the device in an inert atmosphere for a time and temperature sufficient to heal and damages any redistribute the arsenic ions in said subcollector region.
Claim 2
Dependent Claim
139 words
An improvement in the method of forming a buried subcollector device wherein a thick silicon dioxide masking layer having a predetermined pattern of openings is formed on a P-type silicon substrate, followed by the growing in said openings of thin silicon dioxide screen layer, through which a beam of arsenic ions having an energy of 50 KeV and a dose less than 2.2×10 6 at/cm 2 produces the buried subcollector area, and partially etching away said screen oxide layer to remove the contaminated upper layer, characterized by; heating the thus-produced device in an oxydizing atmosphere for a time and temperature sufficient to restore the screen oxide layer to approximately its pre-etched thickness, and annealing the device in an inert atmosphere for a time and temperature sufficient to heal and damages any redistribute the arsenic ions in said subcollector region.
Claim 3
Dependent Claim
15 words
The method according to claim 1 wherein said screen layer has thickness of 225 Å.
Claim 4
Dependent Claim
14 words
The method according to claim 2 wherein said partial etch removes about 100 Å.
Claim 5
Dependent Claim
13 words
The method according to claim 3 wherein said oxidizing ambient comprises dry oxygen.
Claim 6
Dependent Claim
12 words
The method according to claim 4 wherein the original thickness is preserved.
Claim 7
Dependent Claim
20 words
The method according to claim 5 wherein the substrate is heated at about 780° C. for at least 10 minutes.
Claim 8
Dependent Claim
14 words
The method according to claim 6 wherein the cycle time is about 15 minutes.
Claim 9
Dependent Claim
25 words
The method according to claim 7 wherein said inert atmosphere is Argon and the substrate is heated at about 1100° C. for about 90 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-03 | 1989-08-05 | 1990-02-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-03 | 1993-08-05 | 1994-02-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-03 | 1997-08-05 | 1998-02-04 | $7700.00 | Window Closed / Lapsed |