Method for achieving a high quality thin oxide in integrated circuit devices
Assignee: Advanced Micro Devices Inc
•
Filing: 1992-10-29
•
Granted: 1994-11-08
•
Expires: 2012-10-29
Abstract
Abstract The quality of both a gate oxide and a tunnel oxide in a P-well active area of a CMOS EEPROM process is improved by reducing the field edge pullback arising from wet chemical etch steps prior to the growth of the gate and tunnel oxides. A first oxide is grown, and an implant is performed through the first oxide to form an implanted layer. The surface of the first oxide is then cleaned without removing all of the first oxide overlying the implanted layer. An anneal step then activates the implanted layer to form a heavily-doped region, after which the remaining first oxide is then removed. A second oxide is then grown, and a region of the second oxide is removed overlying the heavily-doped region. Lastly, a tunnel oxide is grown over the heavily-doped region while re-oxidizing the second oxide to form a gate oxide thicker than the tunnel oxide.
Inventors
- 👤 Mark I. Gardner
- 👤 Henry J. Fulford, Jr.
- 👤 Jay J. Seaton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:13
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10B; H10B41/00; H10D; H10D64/00; H10D64/01; H10D64/031; H10D64/035; H10P14/6322; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/10; H10W10/13; Y; Y10; Y10S; Y10S438/00; Y10S438/981
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
209 words
In an integrated circuit fabrication process, a method for forming two oxide layers of different thicknesses on a semiconductor body, the thinner oxide being disposed over a heavily-doped region of the semiconductor body, comprising the steps of: forming an active area in a semiconductor body having edges defined by field oxide regions; growing a first oxide upon the surface of the active area; implanting through a first region of the first oxide to form an implanted layer in the active area; annealing the implanted layer with at least some of the first oxide remaining over the implanted layer to form a heavily-doped region; removing the remaining first oxide subsequent to annealing the implanted layer, to expose the surface of the active area; growing a second oxide on the exposed surface of the active area; removing a first region of the second oxide, to expose a first region of the surface of the active area over the heavily-doped region, a second region of the second oxide remaining over a part of the active area; and oxidizing the semiconductor body to grow a third high quality oxide upon the exposed first surface region of the active area over the heavily-doped region and to thicken the second region of the second oxide.
Claim 2
Dependent Claim
209 words
In an integrated circuit fabrication process, a method for forming two oxide layers of different thicknesses on a semiconductor body, the thinner oxide being disposed over a heavily-doped region of the semiconductor body, comprising the steps of: forming an active area in a semiconductor body having edges defined by field oxide regions; growing a first oxide upon the surface of the active area; implanting through a first region of the first oxide to form an implanted layer in the active area; annealing the implanted layer with at least some of the first oxide remaining over the implanted layer to form a heavily-doped region; removing the remaining first oxide subsequent to annealing the implanted layer, to expose the surface of the active area; growing a second oxide on the exposed surface of the active area; removing a first region of the second oxide, to expose a first region of the surface of the active area over the heavily-doped region, a second region of the second oxide remaining over a part of the active area; and oxidizing the semiconductor body to grow a third high quality oxide upon the exposed first surface region of the active area over the heavily-doped region and to thicken the second region of the second oxide.
Claim 3
Dependent Claim
33 words
A method as in claim 1 wherein the heavily-doped region abutts one of the edges of the active area, and wherein the third oxide abutts one of the edges of the active area.
Claim 4
Dependent Claim
21 words
A method as in claim 2 further comprising an RCA cleaning step after the implanting step and before the annealing step.
Claim 5
Dependent Claim
14 words
A method as in claim 3 wherein the heavily-doped region comprises an N+ region.
Claim 6
Dependent Claim
42 words
The method as in claim 4 wherein the first oxide growing step comprises growing the first oxide to a thickness of approximately 300Å and wherein the first oxide removing step comprises etching the first oxide for approximately 1.3 minutes using 10:1 HF.
Claim 7
Dependent Claim
45 words
The method as in claim 5 wherein the second oxide growing step comprises growing the second oxide to a thickness of approximately 225Å and wherein the second oxide removing step comprises etching the second oxide for approximately 0.2 minutes using a 6:1 buffered oxide etchant.
Claim 8
Dependent Claim
14 words
A method as in claim 6 wherein the semiconductor body comprises a P-well region.
Claim 9
Dependent Claim
14 words
A method as in claim 3 wherein the heavily-doped region comprises a P+ region.
Claim 10
Dependent Claim
326 words
In an integrated circuit fabrication process, a method for forming a heavily-doped region in a semiconductor body and for growing a first high quality oxide upon a surface of the semiconductor body over the heavily-doped region and for growing a second high quality oxide, of thickness greater than the first high quality oxide, upon the surface of the semiconductor body, comprising the steps of: growing a first oxide upon the surface; depositing a first photoresist layer on the first oxide; removing a region of the first photoresist layer to expose a region of the first oxide, and leaving a remaining region of the first photoresist layer; implanting through the exposed region of the first oxide to form an implanted layer in the semiconductor body; removing the remaining region of the first photoresist layer; cleaning the surface of the first oxide such that some thickness portion of the first oxide remains over the implanted layer subsequent to the cleaning; annealing the implanted layer to form a heavily-doped region; etching the first oxide subsequent to annealing the implanted layer, to expose the surface of the semiconductor body over the heavily-doped region; growing a second oxide upon the exposed surface; depositing a second photoresist layer upon the second oxide; removing a region of the second photoresist layer to expose a region of the second oxide over the heavily-doped region, and leaving a remaining region of the second photoresist layer; removing the exposed region of the second oxide, to expose the surface of the semiconductor body over the heavily-doped region, and leaving a remaining region of the second oxide; removing the remaining region of the second photoresist layer, to expose the remaining region of the second oxide; etching the remaining region of the second oxide to reduce its thickness; and growing a first high quality oxide upon the exposed surface of the semiconductor body while re-oxidizing the remaining region of the second oxide to form a second high quality oxide.
Claim 11
Dependent Claim
326 words
In an integrated circuit fabrication process, a method for forming a heavily-doped region in a semiconductor body and for growing a first high quality oxide upon a surface of the semiconductor body over the heavily-doped region and for growing a second high quality oxide, of thickness greater than the first high quality oxide, upon the surface of the semiconductor body, comprising the steps of: growing a first oxide upon the surface; depositing a first photoresist layer on the first oxide; removing a region of the first photoresist layer to expose a region of the first oxide, and leaving a remaining region of the first photoresist layer; implanting through the exposed region of the first oxide to form an implanted layer in the semiconductor body; removing the remaining region of the first photoresist layer; cleaning the surface of the first oxide such that some thickness portion of the first oxide remains over the implanted layer subsequent to the cleaning; annealing the implanted layer to form a heavily-doped region; etching the first oxide subsequent to annealing the implanted layer, to expose the surface of the semiconductor body over the heavily-doped region; growing a second oxide upon the exposed surface; depositing a second photoresist layer upon the second oxide; removing a region of the second photoresist layer to expose a region of the second oxide over the heavily-doped region, and leaving a remaining region of the second photoresist layer; removing the exposed region of the second oxide, to expose the surface of the semiconductor body over the heavily-doped region, and leaving a remaining region of the second oxide; removing the remaining region of the second photoresist layer, to expose the remaining region of the second oxide; etching the remaining region of the second oxide to reduce its thickness; and growing a first high quality oxide upon the exposed surface of the semiconductor body while re-oxidizing the remaining region of the second oxide to form a second high quality oxide.
Claim 12
Dependent Claim
15 words
A method as in claim 9 wherein the cleaning step comprises an RCA clean step.
Claim 13
Dependent Claim
14 words
A method as in claim 10 wherein the heavily-doped region comprises an N+ region.
Claim 14
Dependent Claim
42 words
The method as in claim 11 wherein the first oxide growing step comprises growing the first oxide to a thickness of approximately 300Å and wherein the first oxide etching step comprises etching the first oxide for approximately 1.3 minutes using 10:1 HF.
Claim 15
Dependent Claim
45 words
The method as in claim 12 wherein the second oxide growing step comprises growing the second oxide to a thickness of approximately 225Å and wherein the second oxide removing step comprises etching the second oxide for approximately 0.2 minutes using a 6:1 buffered oxide etchant.
Claim 16
Dependent Claim
28 words
The method as in claim 13 wherein the second oxide etching step comprises etching the remaining region of the second oxide for approximately 50 seconds using 50:1 HF.
Claim 17
Dependent Claim
14 words
A method as in claim 14 wherein the semiconductor body comprises a P-well region.
Claim 18
Independent Claim
89 words
A method for minimizing surface roughness of the surface of a semiconductor body over a previously formed and annealed heavily-doped region, for enhancing the quality of a subsequently grown oxide, comprising the steps of: growing a first oxide upon the surface of the semiconductor body; annealing the first oxide prior to any ion implantation therethrough; removing the first oxide, to expose the surface of the semiconductor body over the heavily-doped region, so as to leave the surface of the semiconductor body having an RMS surface roughness of approximately 1.08Å.
Claim 19
Independent Claim
89 words
A method for minimizing surface roughness of the surface of a semiconductor body over a previously formed and annealed heavily-doped region, for enhancing the quality of a subsequently grown oxide, comprising the steps of: growing a first oxide upon the surface of the semiconductor body; annealing the first oxide prior to any ion implantation therethrough; removing the first oxide, to expose the surface of the semiconductor body over the heavily-doped region, so as to leave the surface of the semiconductor body having an RMS surface roughness of approximately 1.08Å.
References Cited (Backward Citations)
US3945856A
Cited
US4329773A
Cited
US4517732A
Cited
US4567645A
Cited
US5215934A
Cited
US5057463A
Cited
US5225361A
Cited
US5208173A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-11-07 | 1998-05-09 | 1998-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-11-07 | 2002-05-09 | 2002-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-11-07 | 2006-05-09 | 2006-11-08 | $7700.00 | Window Closed / Lapsed |