Method for fabrication of semiconductor device
Assignee: Denso Corp
•
Filing: 1992-10-12
•
Granted: 1996-01-02
•
Expires: 2012-10-12
Abstract
Abstract An object of the invention is to prevent the occurrence of breaking or short-circuiting of a wiring caused by a difference in level in an isolation trench area formed in an SOI substrate. An oxide film is formed for a pad on the main surface of an SOI layer formed on an insulating substrate, a silicon nitride film are formed and an SiO 2 film in order, then an isolation trench reaching to the insulating substrate is by means of an R.I.E process using the SiO 2 film as a mask. Thereafter an insulating film is formed on an inside wall of the isolation trench by means of thermal oxidation, the isolation trench is filled with polysilicon, the polysilicon is etched back while controlling the etching so that the top of the polysilicon in the isolation trench remains higher than the top of the silicon nitride film, an extra part of the polysilicon deposited on the surface of the substrate, is removed and then the SiO 2 film used as a mask when forming the isolation trench is etched off using the polysilicon in the isolation trench and the silicon nitride film as an etching stopper. In this manner, since the SiO 2 film used as a mask is etched off after filling the isolation trench with polysilicon, the oxide film for isolating between the substrates is not etched when removing the mask film. Moreover since the polysilicon is the isolation trench and the silicon nitride film act as an etching stopper when etching off the SiO 2 film used as a mask, the oxide film for a pad existing thereunder and the insulating film formed on an inside wall of the trench can also be prevented from being etched and a flatness at an isolation trench area is not deteriorated.
Inventors
- 👤 Shoji Miura
- 👤 Takayuki Sugisaka
- 👤 Atsushi Komura
- 👤 Toshio Sakakibara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:28
CPC Classifications
H; H10; H10P; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10W; H10W10/00; H10W10/01; H10W10/041; H10W10/061; H10W10/10; H10W10/181; H10W10/40; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10P90/1914; H10W10/011; H10W10/012; H10W10/13; Y; Y10; Y10S; Y10S148/00; Y10S148/05; Y10S148/135; Y10S438/00; Y10S438/977
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
128 words
A method for manufacturing a semiconductor device comprising steps of: depositing a mask layer on a main surface of a semiconductor substrate; forming an opening in the mask layer exposing a portion of the main surface of the semiconductor substrate; forming a groove by etching the semiconductor substrate through the opening in the mask layer; processing an inside wall of the groove by means of a chemical dry etching process; annealing the inside wall of the groove processed by the chemical dry etching process; forming an insulating film on an inside wall of the groove; filling the groove with a filler through the opening; exposing the mask layer by removing a portion of the filler deposited on the surface of the mask layer; and removing the mask layer.
Claim 2
Independent Claim
128 words
A method for manufacturing a semiconductor device comprising steps of: depositing a mask layer on a main surface of a semiconductor substrate; forming an opening in the mask layer exposing a portion of the main surface of the semiconductor substrate; forming a groove by etching the semiconductor substrate through the opening in the mask layer; processing an inside wall of the groove by means of a chemical dry etching process; annealing the inside wall of the groove processed by the chemical dry etching process; forming an insulating film on an inside wall of the groove; filling the groove with a filler through the opening; exposing the mask layer by removing a portion of the filler deposited on the surface of the mask layer; and removing the mask layer.
Claim 3
Dependent Claim
36 words
A method for manufacturing a semiconductor device as defined in claim 1, wherein the annealing process is a process of heating the semiconductor substrate at about 1000° to 1100° C. in an atmosphere of inactive gas.
Claim 4
Independent Claim
148 words
A method for manufacturing a semiconductor device comprising steps of: depositing a mask layer on a main surface of an SOI layer set on an insulating substrate; forming an opening in the mask layer exposing a portion of the main surface of the SOI layer; forming an isolation trench reaching through to the insulating substrate by etching the SOI layer through the opening in the mask layer; processing an inside wall of the isolation trench by means of a chemical dry etching process; annealing the inside wall of the isolation trench processed by the chemical dry etching process; forming an insulating film on an inside wall of the isolation trench; filling in the isolation trench with a filler through the opening; exposing the layer for a mask by removing an extra part of the filler deposited on the surface of the mask layer; and removing the mask layer.
Claim 5
Independent Claim
148 words
A method for manufacturing a semiconductor device comprising steps of: depositing a mask layer on a main surface of an SOI layer set on an insulating substrate; forming an opening in the mask layer exposing a portion of the main surface of the SOI layer; forming an isolation trench reaching through to the insulating substrate by etching the SOI layer through the opening in the mask layer; processing an inside wall of the isolation trench by means of a chemical dry etching process; annealing the inside wall of the isolation trench processed by the chemical dry etching process; forming an insulating film on an inside wall of the isolation trench; filling in the isolation trench with a filler through the opening; exposing the layer for a mask by removing an extra part of the filler deposited on the surface of the mask layer; and removing the mask layer.
Claim 6
Dependent Claim
36 words
A method for manufacturing a semiconductor device as defined in claim 3, wherein the annealing process is a process of heating the semiconductor substrate at about 1000° to 1100° C. in an atmosphere of inactive gas.
Claim 7
Independent Claim
187 words
A method for manufacturing a semiconductor device comprising steps of: depositing in order a first layer and a second layer on a main surface of a semiconductor substrate; forming an opening in the first layer and the second layer exposing a portion of the main surface of the semiconductor substrate; forming a groove by etching the semiconductor substrate through the opening using the second layer as a mask; forming an insulating film on an inside wall of the groove, the insulating film being a material different from a material of the first layer; filling the groove with a filler through the opening until a top surface of the filler becomes equal to or higher than the first layer in height and so that the filler contacts the first layer at the opening; and removing the second layer using the filler filled to the height equal to or higher than the first layer and the first layer as an etching stopper to prevent the insulating film located below a contact portion between the first layer and the filler from being etched during the removal of the second layer.
Claim 8
Independent Claim
187 words
A method for manufacturing a semiconductor device comprising steps of: depositing in order a first layer and a second layer on a main surface of a semiconductor substrate; forming an opening in the first layer and the second layer exposing a portion of the main surface of the semiconductor substrate; forming a groove by etching the semiconductor substrate through the opening using the second layer as a mask; forming an insulating film on an inside wall of the groove, the insulating film being a material different from a material of the first layer; filling the groove with a filler through the opening until a top surface of the filler becomes equal to or higher than the first layer in height and so that the filler contacts the first layer at the opening; and removing the second layer using the filler filled to the height equal to or higher than the first layer and the first layer as an etching stopper to prevent the insulating film located below a contact portion between the first layer and the filler from being etched during the removal of the second layer.
Claim 9
Dependent Claim
30 words
A method for manufacturing a semiconductor device as defined in claim 5, comprising a further step, after the step of removing the second layer, of selectively removing the first layer.
Claim 10
Dependent Claim
58 words
A method for manufacturing a semiconductor device as defined in claim 5, comprising further steps, after the step of forming a groove by etching the semiconductor substrate, of: processing an inside wall of the groove by means of a chemical dry etching process; and annealing the inside wall of the groove processed by the chemical dry etching process.
Claim 11
Dependent Claim
47 words
A method for manufacturing a semiconductor device as defined in claim 5, comprising a step, before the step of forming an insulating film on an inside wall of the groove, of covering an end face of the first layer exposed inside the opening with an oxidation-resisting film.
Claim 12
Independent Claim
189 words
A method for manufacturing a semiconductor device comprising steps of: depositing in order a first layer and a second layer on a main surface of an SOI layer set on an insulating substrate; forming an opening in the first layer and the second layer exposing a portion of the main surface of the SOI layer; forming an isolation trench reaching through to the insulating substrate by etching the SOI layer through the opening using the second layer as a mask; forming an insulating film on an inside wall of the isolation trench, the insulating film being a material different from a material of the first layer; filling the isolation trench with a filler through the opening until a top surface of the filler becomes equal to or higher than the first layer in height and so that the filler contacts the first layer at the opening; and removing the second layer using the filler and the first layer as an etching stopper to prevent the insulating film located below a contact portion between the first layer and the filler from being etched during the removal of the second layer.
Claim 13
Independent Claim
189 words
A method for manufacturing a semiconductor device comprising steps of: depositing in order a first layer and a second layer on a main surface of an SOI layer set on an insulating substrate; forming an opening in the first layer and the second layer exposing a portion of the main surface of the SOI layer; forming an isolation trench reaching through to the insulating substrate by etching the SOI layer through the opening using the second layer as a mask; forming an insulating film on an inside wall of the isolation trench, the insulating film being a material different from a material of the first layer; filling the isolation trench with a filler through the opening until a top surface of the filler becomes equal to or higher than the first layer in height and so that the filler contacts the first layer at the opening; and removing the second layer using the filler and the first layer as an etching stopper to prevent the insulating film located below a contact portion between the first layer and the filler from being etched during the removal of the second layer.
Claim 14
Dependent Claim
30 words
A method for manufacturing a semiconductor device as defined in claim 9, comprising a further step, after the step of removing the second layer, of selectively removing the first layer.
Claim 15
Dependent Claim
56 words
A method for manufacturing a semiconductor device as defined in claim 9, comprising further steps, after the step of forming an isolation trench, of: processing an inside wall of the isolation trench by means of a chemical dry etching process; and annealing the inside wall of the isolation trench processed by the chemical dry etching process.
Claim 16
Independent Claim
152 words
A method for manufacturing a semiconductor device comprising steps of: depositing in order a first layer and a second layer on a main surface of an SOI layer set on an insulating substrate; forming an opening in the first layer and the second layer exposing a portion of the main surface of the SOI layer; forming an isolation trench reaching through to the insulating substrate by etching the SOI layer through the opening using the second layer as a mask; covering an end face of the first layer exposed inside the opening with an oxidation-resisting film; forming an insulating film on an inside wall of the isolation trench; filling the isolation trench with a filler through the opening until a top surface of the filler becomes equal to or higher than the first layer in height; and removing the second layer using the filler and the first layer as an etching stopper.
Claim 17
Independent Claim
152 words
A method for manufacturing a semiconductor device comprising steps of: depositing in order a first layer and a second layer on a main surface of an SOI layer set on an insulating substrate; forming an opening in the first layer and the second layer exposing a portion of the main surface of the SOI layer; forming an isolation trench reaching through to the insulating substrate by etching the SOI layer through the opening using the second layer as a mask; covering an end face of the first layer exposed inside the opening with an oxidation-resisting film; forming an insulating film on an inside wall of the isolation trench; filling the isolation trench with a filler through the opening until a top surface of the filler becomes equal to or higher than the first layer in height; and removing the second layer using the filler and the first layer as an etching stopper.
Claim 18
Independent Claim
182 words
A method for manufacturing a semiconductor device comprising steps of: forming a field oxide film having a thick portion and a thin portion, a silicon nitride film, and a silicon oxide film to be used as a mask, in order, on a main surface of a silicon substrate; forming an opening in the thick portion of the field oxide film by selectively etching the thick portion of the field oxide film, the silicon nitride film, and the silicon oxide film; forming a groove by etching the silicon substrate through the opening using the silicon oxide film as a mask; forming an insulating film on an inside wall of the groove; filling the groove with polysilicon; etching back the polysilicon deposited on the silicon oxide film by controlling the etching so that a top surface of the polysilicon in the groove becomes higher than a top surface of the silicon nitride film; and etching off the silicon oxide film using the polysilicon in the groove and the silicon nitride film as an etching stopper for the field oxide film and the insulating film.
Claim 19
Independent Claim
182 words
A method for manufacturing a semiconductor device comprising steps of: forming a field oxide film having a thick portion and a thin portion, a silicon nitride film, and a silicon oxide film to be used as a mask, in order, on a main surface of a silicon substrate; forming an opening in the thick portion of the field oxide film by selectively etching the thick portion of the field oxide film, the silicon nitride film, and the silicon oxide film; forming a groove by etching the silicon substrate through the opening using the silicon oxide film as a mask; forming an insulating film on an inside wall of the groove; filling the groove with polysilicon; etching back the polysilicon deposited on the silicon oxide film by controlling the etching so that a top surface of the polysilicon in the groove becomes higher than a top surface of the silicon nitride film; and etching off the silicon oxide film using the polysilicon in the groove and the silicon nitride film as an etching stopper for the field oxide film and the insulating film.
Claim 20
Independent Claim
202 words
A method for manufacturing a semiconductor device comprising: forming a field oxide film having a thick portion and a thin portion, a polysilicon film, and a silicon oxide film to be used as a mask, in order, on a main surface of a silicon substrate; forming an opening in the thick portion of the field oxide film by selectively etching the thick portion of the field oxide film, the polysilicon film, and the silicon oxide film; covering the polysilicon film exposed on a surface of a wall of the opening with an oxidation-resisting film; forming a groove by etching the silicon substrate from the opening using the silicon oxide film as a mask; forming an insulating film on an inside wall of the groove; filling the groove with polysilicon for filling; etching back the polysilicon for filling deposited on the silicon oxide film while controlling the etching so that a top surface of the polysilicon for filling in the groove becomes higher than a top surface of the polysilicon film; and etching off the silicon oxide film using the polysilicon for filling in the groove and the polysilicon film as an etching stopper for the field oxide film and the insulating film.
Claim 21
Independent Claim
202 words
A method for manufacturing a semiconductor device comprising: forming a field oxide film having a thick portion and a thin portion, a polysilicon film, and a silicon oxide film to be used as a mask, in order, on a main surface of a silicon substrate; forming an opening in the thick portion of the field oxide film by selectively etching the thick portion of the field oxide film, the polysilicon film, and the silicon oxide film; covering the polysilicon film exposed on a surface of a wall of the opening with an oxidation-resisting film; forming a groove by etching the silicon substrate from the opening using the silicon oxide film as a mask; forming an insulating film on an inside wall of the groove; filling the groove with polysilicon for filling; etching back the polysilicon for filling deposited on the silicon oxide film while controlling the etching so that a top surface of the polysilicon for filling in the groove becomes higher than a top surface of the polysilicon film; and etching off the silicon oxide film using the polysilicon for filling in the groove and the polysilicon film as an etching stopper for the field oxide film and the insulating film.
Claim 22
Dependent Claim
37 words
A method for manufacturing a semiconductor device according to claim 5, wherein the first layer is a silicon nitride film, the second layer is a silicon oxide film, and the insulating film is a silicon oxide film.
Claim 23
Dependent Claim
17 words
A method for manufacturing a semiconductor device according to claim 15, wherein the filler is polycrystalline silicon.
Claim 24
Dependent Claim
37 words
A method for manufacturing a semiconductor device according to claim 6, wherein the first layer is a silicon nitride film, the second layer is a silicon oxide film, and the insulating film is a silicon oxide film.
Claim 25
Dependent Claim
17 words
A method for manufacturing a semiconductor device according to claim 17, wherein the filler is polycrystalline silicon.
Claim 26
Dependent Claim
37 words
A method for manufacturing a semiconductor device according to claim 7, wherein the first layer is a silicon nitride film, the second layer is a silicon oxide film, and the insulating film is a silicon oxide film.
Claim 27
Dependent Claim
17 words
A method for manufacturing a semiconductor device according to claim 19, wherein the filler is polycrystalline silicon.
Claim 28
Dependent Claim
37 words
A method for manufacturing a semiconductor device according to claim 9, wherein the first layer is a silicon nitride film, the second layer is a silicon oxide film, and the insulating film is a silicon oxide film.
Claim 29
Dependent Claim
17 words
A method for manufacturing a semiconductor device according to claim 21, wherein the filler is polycrystalline silicon.
Claim 30
Dependent Claim
37 words
A method for manufacturing a semiconductor device according to claim 10, wherein the first layer is a silicon nitride film, the second layer is a silicon oxide film, and the insulating film is a silicon oxide film.
Claim 31
Dependent Claim
17 words
A method for manufacturing a semiconductor device according to claim 23, wherein the filler is polycrystalline silicon.
Claim 32
Dependent Claim
37 words
A method for manufacturing a semiconductor device according to claim 11, wherein the first layer is a silicon nitride film, the second layer is a silicon oxide film, and the insulating film is a silicon oxide film.
Claim 33
Dependent Claim
17 words
A method for manufacturing a semiconductor device according to claim 25, wherein the filler is polycrystalline silicon.
References Cited (Backward Citations)
US3966577A
Cited
US4307180A
Cited
US4389294A
Cited
JPS59208744A
Cited
JPS615544A
Cited
US4740480A
Cited
JPS6159852A
Cited
US4571819A
Cited
JPS61214446A
Cited
JPS62101034A
Cited
EP0224646A2
Cited
US4671851A
Cited
JPS62214638A
Cited
JPS6333829A
Cited
US4897154A
Cited
JPS6333839A
Cited
JPS6386560A
Cited
US5072287A
Cited
JPH01265536A
Cited
JPH0267963A
Cited
JPH02148855A
Cited
EP0388597A2
Cited
US4952524A
Cited
EP0398468A2
Cited
JPH03155650A
Cited
JPH03127850A
Cited
JPH03129854A
Cited
JPH03149836A
Cited
JPH03149849A
Cited
EP0437950A2
Cited
JPH04209551A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-01-01 | 1999-07-03 | 2000-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-01-01 | 2003-07-03 | 2004-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-01-01 | 2007-07-03 | 2008-01-02 | $7700.00 | Window Closed / Lapsed |