US5427987A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Group IVB boride based cutting tools for machining group IVB based materials
Assignee: Kennametal Inc
•
Filing: 1993-05-10
•
Granted: 1995-06-27
•
Expires: 2013-05-10
Abstract
Abstract A densified titanium diboride based ceramic composition is provided having W and Co therein and a fine grain size. The composition has particular usefulness as a cutting tool for the machining of titanium based alloys at high speeds.
Inventors
- 👤 Pankai K. Mehrotra
- 👤 Deepak P. Ahuja
- 👤 Holly S. Brooks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:03
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; B; B24; B24D; B24D3/00; B24D3/02; B24D3/04; B24D3/06; B24D3/34; B24D3/342; C04B35/58078; C04B35/622; C04B35/64; C04B35/645; Y; Y10; Y10S; Y10S264/00; Y10S264/36
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
79 words
A metalcutting tool for the chip forming machining of a group IVB metallic material comprising: a rake face over which said chips will flow during said machining of said group IVB metallic material; a flank face and a cutting edge, for cutting into said group IVB metallic material at high speeds, formed at a juncture of said rake and said flank face; wherein said metal cutting tool has a ceramic composition consisting essentially of a Group IVB boride phase.
Claim 2
Dependent Claim
79 words
A metalcutting tool for the chip forming machining of a group IVB metallic material comprising: a rake face over which said chips will flow during said machining of said group IVB metallic material; a flank face and a cutting edge, for cutting into said group IVB metallic material at high speeds, formed at a juncture of said rake and said flank face; wherein said metal cutting tool has a ceramic composition consisting essentially of a Group IVB boride phase.
Claim 3
Dependent Claim
20 words
The metalcutting tool according to claim 1 wherein the composition has an average grain size of 8 μm or less.
Claim 4
Dependent Claim
18 words
The metalcutting tool according to claim 1 wherein the Group IVB boride phase is a titanium boride phase.
Claim 5
Dependent Claim
18 words
The metalcutting tool according to claim 2 wherein the Group IVB boride phase is a titanium boride phase.
Claim 6
Dependent Claim
91 words
A cutting tool comprising: a rake face; a flank face; and a cutting edge formed at a juncture of said rake face and said flank face; wherein said cutting tool is characterized by: a microstructure consisting essentially of phases having a TiB 2 crystal structure; and wherein said phases include phases containing tungsten at differing concentration levels; a density of at least 97% of theoretical density; a hardness of 94.3 to 96.5 Rockwell A at room temperature; and wherein said microstructure has an average grain size of 8 μm or less.
Claim 7
Dependent Claim
91 words
A cutting tool comprising: a rake face; a flank face; and a cutting edge formed at a juncture of said rake face and said flank face; wherein said cutting tool is characterized by: a microstructure consisting essentially of phases having a TiB 2 crystal structure; and wherein said phases include phases containing tungsten at differing concentration levels; a density of at least 97% of theoretical density; a hardness of 94.3 to 96.5 Rockwell A at room temperature; and wherein said microstructure has an average grain size of 8 μm or less.
Claim 8
Dependent Claim
21 words
The metalcutting tool according to claim 1 wherein said ceramic composition is made from at least 75 weight percent titanium diboride.
Claim 9
Dependent Claim
21 words
The metalcutting tool according to claim 2 wherein said ceramic composition is made from at least 75 weight percent titanium diboride.
Claim 10
Dependent Claim
21 words
The metalcutting tool according to claim 1 wherein said ceramic composition is made from at least 85 weight percent titanium diboride.
Claim 11
Dependent Claim
21 words
The metalcutting tool according to claim 2 wherein said ceramic composition is made from at least 85 weight percent titanium diboride.
Claim 12
Dependent Claim
21 words
The metalcutting tool according to claim 1 wherein said ceramic composition is made from at least 90 weight percent titanium diboride.
Claim 13
Dependent Claim
21 words
The metalcutting tool according to claim 2 wherein said ceramic composition is made from at least 90 weight percent titanium diboride.
Claim 14
Dependent Claim
20 words
The metalcutting tool according to claim 1 wherein said composition has an average grain size of 6 μm or less.
Claim 15
Dependent Claim
20 words
The metalcutting tool according to claim 1 wherein said composition has an average grain size of 4 μm or less.
Claim 16
Dependent Claim
20 words
The metalcutting tool according to claim 6 wherein said composition has an average grain size of 6 μm or less.
Claim 17
Dependent Claim
20 words
The metalcutting tool according to claim 8 wherein said composition has an average grain size of 6 μm or less.
Claim 18
Dependent Claim
20 words
The metalcutting tool according to claim 10 wherein said composition has an average grain size of 6 μm or less.
Claim 19
Dependent Claim
23 words
The metalcutting tool according to claim 6 wherein said composition has a density of at least 98 percent of the theoretical calculated density.
Claim 20
Dependent Claim
23 words
The metalcutting tool according to claim 8 wherein said composition has a density of at least 98 percent of the theoretical calculated density.
Claim 21
Dependent Claim
23 words
The metalcutting tool according to claim 10 wherein said composition has a density of at least 98 percent of the theoretical calculated density.
Claim 22
Dependent Claim
23 words
The metalcutting tool according to claim 12 wherein said composition has a density of at least 98 percent of the theoretical calculated density.
Claim 23
Dependent Claim
23 words
The metalcutting tool according to claim 14 wherein said composition has a density of at least 98 percent of the theoretical calculated density.
Claim 24
Dependent Claim
23 words
The metalcutting tool according to claim 15 wherein said composition has a density of at least 98 percent of the theoretical calculated density.
Claim 25
Dependent Claim
23 words
The metalcutting tool according to claim 16 wherein said composition has a density of at least 98 percent of the theoretical calculated density.
Claim 26
Dependent Claim
15 words
The cutting tool according to claim 5 wherein said density is at least 98 percent.
Claim 27
Dependent Claim
20 words
The cutting tool according to claim 24 wherein said microstructure is made from at least 75 weight percent titanium diboride.
Claim 28
Dependent Claim
20 words
The cutting tool according to claim 24 wherein said microstructure is made from at least 85 weight percent titanium diboride.
Claim 29
Dependent Claim
20 words
The cutting tool according to claim 24 wherein said microstructure is made from at least 90 weight percent titanium diboride.
References Cited (Backward Citations)
US3215545A
Cited
US3305373A
Cited
US3649312A
Cited
US4266977A
Cited
US4259119A
Cited
US4292081A
Cited
US4379852A
Cited
US4492764A
Cited
US4528121A
Cited
US4621547A
Cited
US4647405A
Cited
US5017217A
Cited
US4876227A
Cited
US4931413A
Cited
US5102835A
Cited
US4873053A
Cited
US4867761A
Cited
US4910171A
Cited
US5032242A
Cited
US4957884A
Cited
US4925346A
Cited
US5185112A
Cited
US4876941A
Cited
US5078031A
Cited
US4889836A
Cited
US4863490A
Cited
US4933308A
Cited
US5021368A
Cited
US5047372A
Cited
US5019540A
Cited
US5045512A
Cited
US5013694A
Cited
US5163975A
Cited
US5180533A
Cited
US5137665A
Cited
US5141367A
Cited
US5100845A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-06-26 | 1998-12-26 | 1999-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-06-26 | 2002-12-26 | 2003-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-06-26 | 2006-12-26 | 2007-06-27 | $7700.00 | Window Closed / Lapsed |