US4292081A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Boride-based refractory bodies
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1980-03-05
•
Granted: 1981-09-29
•
Expires: 2000-03-05
Abstract
Abstract The invention provides a novel class of sintered refractory and abrasive bodies composed mainly of one or a combination of metal diborides such as titanium diboride TiB2, chromium diboride CrB2, tantalum diboride TaB2 and the like admixed with a minor amount of one or more kinds of metal borides exemplified by MnB, Mn3B4, Mn2B, Mn4B, TiB, Ti2B5, Ti2B, W2B5 and Mo2B5. The sintered body can be prepared by conventional powder metallurgical processes such as hot pressing or sintering of a green body shaped in advance by molding in cold with the powder blend of the above described components. Further advantages are obtained by admixing the powder blend with small amounts of one or more of binder ingredients of relatively low melting points such as cobalt borides, iron borides, nickel borides and an alloy of nickel and phosphorus. So-called infusion process is also applicable for the preparation of the inventive sintered body.
Inventors
- 👤 Tadahiko Watanabe
- 👤 Shinichi Kono
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:04
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/645; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/58078; C04B35/626; C04B35/63; C04B35/6303
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
163 words
A sintered refractory body which comprises (a) from 99.99 to 60% by weight of at least one metal diboride selected from the group consisting of titanium diboride, chromium diboride, tantalum diboride, manganese diboride, molybdenum diboride, yttrium diboride, vanadium diboride, hafnium diboride, niobium diboride, aluminum diboride and zirconium diboride, (b) from 0.01 to 40% by weight of at least one metal boride selected from the group consisting of MnB, Mn 3 B 4 , Mn 2 B, Mn 4 B, TiB, Ti 2 B 5 , Ti 2 B, W 2 B 5 and Mo 2 B 5 , and (c) from 0.001 to 30% by weight of a binder ingredient selected from the group consisting of NiB, Ni 4 B 3 , Ni 2 B, Ni 3 B, FeB, Fe 2 B, CoB, Co 2 B, Co 3 B and an alloy of nickel and phosphorus composed of 3 to 25% by weight of phosphorus and 97 to 75% by weight of nickel.
Claim 2
Dependent Claim
163 words
A sintered refractory body which comprises (a) from 99.99 to 60% by weight of at least one metal diboride selected from the group consisting of titanium diboride, chromium diboride, tantalum diboride, manganese diboride, molybdenum diboride, yttrium diboride, vanadium diboride, hafnium diboride, niobium diboride, aluminum diboride and zirconium diboride, (b) from 0.01 to 40% by weight of at least one metal boride selected from the group consisting of MnB, Mn 3 B 4 , Mn 2 B, Mn 4 B, TiB, Ti 2 B 5 , Ti 2 B, W 2 B 5 and Mo 2 B 5 , and (c) from 0.001 to 30% by weight of a binder ingredient selected from the group consisting of NiB, Ni 4 B 3 , Ni 2 B, Ni 3 B, FeB, Fe 2 B, CoB, Co 2 B, Co 3 B and an alloy of nickel and phosphorus composed of 3 to 25% by weight of phosphorus and 97 to 75% by weight of nickel.
Claim 3
Dependent Claim
63 words
The sintered refractory body as claimed in claim 1 wherein the component (a) is a combination of at least two metal diborides selected from the group consisting of the diborides of titanium, chromium, tantalum, manganese, molybdenum, yttrium, vanadium, hafnium, niobium, aluminum and zirconium, the amount of each of the metal diborides in the sintered refractory body being not smaller than 1% by weight.
Claim 4
Independent Claim
182 words
A method for the preparation of a sintered ceramic body which comprises (a) mixing from 99.99 to 60% by weight of at least one metal diboride selected from the group consisting of titanium diboride, chromium diboride, tantalum diboride, manganese diboride, molybdenum diboride, yttrium diboride, vanadium diboride, hafnium diboride, niobium diboride, aluminum diboride and zirconium diboride and from 0.01 to 40% by weight of at least one metal boride selected from the group consisting of MnB, Mn 2 B, Mn 4 B, TiB, Ti 2 B 5 , Ti 2 B, W 2 B 5 and Mo 2 B 5 with from 0.001 to 30% by weight of a binder ingredient selected from the group consisting of NiB, Ni 4 B 3 , Ni 2 B, Ni 3 B, FeB, Fe 2 B, CoB, Co 2 B, Co 3 B and an alloy of nickel and phosphorus composed of 3 to 25% by weight of phosphorus and 97 to 75% by weight of nickel to form a powder blend, and (b) subjecting the powder blend to sintering by heating into a sintered body.
Claim 5
Independent Claim
182 words
A method for the preparation of a sintered ceramic body which comprises (a) mixing from 99.99 to 60% by weight of at least one metal diboride selected from the group consisting of titanium diboride, chromium diboride, tantalum diboride, manganese diboride, molybdenum diboride, yttrium diboride, vanadium diboride, hafnium diboride, niobium diboride, aluminum diboride and zirconium diboride and from 0.01 to 40% by weight of at least one metal boride selected from the group consisting of MnB, Mn 2 B, Mn 4 B, TiB, Ti 2 B 5 , Ti 2 B, W 2 B 5 and Mo 2 B 5 with from 0.001 to 30% by weight of a binder ingredient selected from the group consisting of NiB, Ni 4 B 3 , Ni 2 B, Ni 3 B, FeB, Fe 2 B, CoB, Co 2 B, Co 3 B and an alloy of nickel and phosphorus composed of 3 to 25% by weight of phosphorus and 97 to 75% by weight of nickel to form a powder blend, and (b) subjecting the powder blend to sintering by heating into a sintered body.
Claim 6
Dependent Claim
26 words
The method as claimed in claim 3 wherein the step of sintering by heating is carried out with the powder blend simultaneously under pressure for compression.
Claim 7
Dependent Claim
28 words
The method as claimed in claim 3 wherein the step of sintering by heating is carried out with the powder blend shaped in advance by molding in cold.
Claim 8
Dependent Claim
35 words
The method as claimed in claim 3 wherein the metal boride is replaced with the metal corresponding to the metal boride or a combination of the metal corresponding to the metal boride and elementary boron.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-28 | 1985-03-30 | 1985-09-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-28 | 1989-03-30 | 1989-09-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-28 | 1993-03-30 | 1993-09-29 | $7700.00 | Window Closed / Lapsed |