Process for producing titanium diboride and boron nitride powders
Assignee: Praxair ST Technology Inc
•
Filing: 1991-03-13
•
Granted: 1992-03-31
•
Expires: 2011-03-13
Abstract
Abstract A process for the simultaneous production of titanium diboride and boron nitride powders using a single reaction procedure in which the raw materials of the TiB 2 reaction and the BN reaction are blended together and subjected to a synthesis process which yields synthesized TiB 2 and BN powders.
Inventors
- 👤 Lionel C. Montgomery
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:19
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C01; C01B; C01B21/00; C01B21/06; C01B21/064; C01B35/00; C01B35/02; C01B35/04; C04B35/583; C04B35/622; C04B35/626; C04B35/64; C04B35/645; C01P; C01P2006/00; C01P2006/10
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
135 words
A process for the simultaneous production of a mixture of titanium diboride powders and boron nitride powders comprising the steps: a) mixing together at least one titanium-containing compound, at least one boron-containing compound, particulate carbon and at least one nitrogen-containing compound in an amount sufficient to produce titanium diboride and boron nitride powders; b) heating the mixture of step a) to an elevated temperature of at least 1400° C. for a time period sufficient to produce a synthesized titanium diboride and boron nitride mixture; c) washing the synthesized titanium diboride and boron nitride mixture of step b) in a solution followed by filtering to remove any excess B 2 O 3 and then drying the residue; and d) pulverizing the residue of step c) to produce a powdered mixture of titanium diboride and boron nitride.
Claim 2
Dependent Claim
135 words
A process for the simultaneous production of a mixture of titanium diboride powders and boron nitride powders comprising the steps: a) mixing together at least one titanium-containing compound, at least one boron-containing compound, particulate carbon and at least one nitrogen-containing compound in an amount sufficient to produce titanium diboride and boron nitride powders; b) heating the mixture of step a) to an elevated temperature of at least 1400° C. for a time period sufficient to produce a synthesized titanium diboride and boron nitride mixture; c) washing the synthesized titanium diboride and boron nitride mixture of step b) in a solution followed by filtering to remove any excess B 2 O 3 and then drying the residue; and d) pulverizing the residue of step c) to produce a powdered mixture of titanium diboride and boron nitride.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein step e) is added as follows: e) hot-pressing the synthesized titanium diboride and boron nitride powders from step d) to form titanium diboride-boron nitride compacted billets.
Claim 4
Dependent Claim
80 words
The process of claim 1 wherein in step a) the at least one titanium-containing compound is selected from the group consisting of titanium carbide, titanium oxide, and titanium; the at least one boron-containing compound is selected from the group consisting of B 4 C, B 2 O 3 , and boron; and the at least one nitrogen-containing compound is selected from the group consisting of melamine, urea, dicyandiamide, guanidine, organic salts of melamine, NH 3 gas, cyanamide, and cyanamide compounds.
Claim 5
Dependent Claim
31 words
The process of claim 1 wherein in step a) the titanium-containing compound is TiO 2 ; the boron-containing compound is B 2 O 3 ; and the nitrogen-containing compound is melamine.
Claim 6
Dependent Claim
40 words
The process of claim 4 wherein in step b) the mixture is heated to about 1600° C. and held at this temperature for a period of time sufficient to substantially complete the reactions to form BN and TiB 2 powders.
Claim 7
Dependent Claim
28 words
The process of claim 4 wherein in step b) the temperature in increased at a rate from 100° C. to 500° C. per hour to about 1600° C.
Claim 8
Dependent Claim
23 words
The process of claim 6 wherein in step c) the synthesized titanium diboride and boron nitride powders are washed in an acid solution.
Claim 9
Dependent Claim
51 words
The process of claim 7 wherein step e) is added as follows: e) hot-pressing the synthesized titanium diboride and boron nitride powders from step d) at an elevated temperature up to about 1900° C. and under a pressure of up to about 2300 psi to form titanium diboride-boron nitride compacted billets.
Claim 10
Dependent Claim
19 words
The process of claim 8 wherein the percent of theoretical density of the compacted billet is at least 93%.
Claim 11
Dependent Claim
19 words
The process of claim 9 wherein the percent of theoretical density of the compacted billet is at least 97%.
Claim 12
Dependent Claim
25 words
The process of claim 4 wherein in step c) the synthesized titanium diboride and boron nitride powders are washed in an acid or alcohol solution.
Claim 13
Dependent Claim
13 words
The process of claim 11 wherein in step c) the solution is methanol.
Claim 14
Dependent Claim
32 words
The process of claim 11 wherein in step b) the mixture is heated to about 1600° C. and held at this temperature for a period of time from 1/2 to 2 hours.
Claim 15
Dependent Claim
32 words
The process of claim 4 wherein the amount of TiO 2 , B 2 O 3 , C and melamine is a stoichiometric amount to produce titanium diboride and boron nitride powders.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-31 | 1995-09-30 | 1996-03-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-31 | 1999-09-30 | 2000-03-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-31 | 2003-09-30 | 2004-03-31 | $7700.00 | Window Closed / Lapsed |