Preparation and sintering of refractory metal borides, carbides and nitrides of high purity
Assignee: Moltech Invent SA
•
Filing: 1985-05-29
•
Granted: 1987-09-15
•
Expires: 2005-05-29
Abstract
Abstract The invention relates to the production of desirably consolidated high purity refractory metal borides, carbides, nitrides, or mixtures, combinations of cermets thereof. In the preparation, a second stage reaction is conducted at reduced pressure and sintering temperature. Furthermore, it is carried out in the presence of sintering aid which can be initially present as a particulate material and, as such, may be incorporated with other reaction ingredients. Sintering aid, in a dual role, may serve not only as an assistant in the second stage reaction, but also as a reaction participant. Moreover, during such rection at sintering conditions, the sintering assistance is obtained by means of sintering aid vapor. High purity products of desirable microstructure can be achieved, having densities on the order of 90 percent or more.
Inventors
- 👤 Ajit Y. Sane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:44
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/563; B; B22; B22F; B22F3/00; B22F3/10; B22F3/1003; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/622; C04B35/64; C04B35/65; C22; C22C; C22C1/00; C22C1/04; C22C1/05; C22C1/051; C22C1/053; C22C1/056
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
153 words
The method of preparing a consolidated and purified Group IVb, Vb or VIb refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by means of aided, reduced pressure and elevated temperature conditions, which method comprises: (a) establishing a composition for a second stage reaction step of reaction sintering and adapted for enhanced production of desired product; (b) providing sintering aid at least in part together with said composition and resting said composition upon said sintering aid, which aid is solid at normal pressure and temperatures and aids via the vapor phase at the pressure and temperature conditions of the second stage reaction step; (c) reducing the pressure around said composition; (d) heating said composition at a temperature for sintering; while (e) establishing sintering aid atmosphere in contact with said composition; and (f) maintaining the heating for a time sufficient to consolidate said composition, and thereby prepare a consolidate and purified product.
Claim 2
Independent Claim
153 words
The method of preparing a consolidated and purified Group IVb, Vb or VIb refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by means of aided, reduced pressure and elevated temperature conditions, which method comprises: (a) establishing a composition for a second stage reaction step of reaction sintering and adapted for enhanced production of desired product; (b) providing sintering aid at least in part together with said composition and resting said composition upon said sintering aid, which aid is solid at normal pressure and temperatures and aids via the vapor phase at the pressure and temperature conditions of the second stage reaction step; (c) reducing the pressure around said composition; (d) heating said composition at a temperature for sintering; while (e) establishing sintering aid atmosphere in contact with said composition; and (f) maintaining the heating for a time sufficient to consolidate said composition, and thereby prepare a consolidate and purified product.
Claim 3
Dependent Claim
56 words
In the method of preparing a Group IVb, Vb or Vib refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by a second stage reaction step of reaction sintering, the improvement comprising conducting said second stage reaction step in the presence of boron nitride sintering aid, including resting sintering composition upon said boron nitride.
Claim 4
Dependent Claim
56 words
In the method of preparing a Group IVb, Vb or Vib refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by a second stage reaction step of reaction sintering, the improvement comprising conducting said second stage reaction step in the presence of boron nitride sintering aid, including resting sintering composition upon said boron nitride.
Claim 5
Dependent Claim
62 words
In the method of preparing a Group IVb, Vb or Vib refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by a second stage reaction step of reaction sintering, the improvement comprising conducting said second stage reaction step in the presence of boron nitride sintering aid provided as a loose particulate together with composition for the second stage reaction step.
Claim 6
Dependent Claim
62 words
In the method of preparing a Group IVb, Vb or Vib refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by a second stage reaction step of reaction sintering, the improvement comprising conducting said second stage reaction step in the presence of boron nitride sintering aid provided as a loose particulate together with composition for the second stage reaction step.
Claim 7
Independent Claim
131 words
The method of preparing a second stage reaction step sintered composite of aluminum nitride and a Group IV, Vb or VIb refractory metal boride or carbide from a precursor composition of refractory metal boride or carbide prepared from a second stage reaction step, which method comprises: (a) mixing together said precursor, particulate metallic aluminum and particulate boron nitride; (b) compacting the resulting mixture; (c) introducing the compact to a heating zone having an inert-gas-containing atmosphere; (d) heating the compact; (e) establishing during said heating a partial pressure of boron nitride vapor in said heating zone; while (f) maintaining in said heating zone a partial pressure of nitrogen for reaction with said particulate aluminum; and (g) maintaining the heating for a time sufficient to prepare the second stage reaction step sintered composite.
Claim 8
Independent Claim
131 words
The method of preparing a second stage reaction step sintered composite of aluminum nitride and a Group IV, Vb or VIb refractory metal boride or carbide from a precursor composition of refractory metal boride or carbide prepared from a second stage reaction step, which method comprises: (a) mixing together said precursor, particulate metallic aluminum and particulate boron nitride; (b) compacting the resulting mixture; (c) introducing the compact to a heating zone having an inert-gas-containing atmosphere; (d) heating the compact; (e) establishing during said heating a partial pressure of boron nitride vapor in said heating zone; while (f) maintaining in said heating zone a partial pressure of nitrogen for reaction with said particulate aluminum; and (g) maintaining the heating for a time sufficient to prepare the second stage reaction step sintered composite.
Claim 9
Independent Claim
152 words
The method of preparing a consolidated and purified Group IVb, Vb or VIb refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by means of aided, reduced pressure and elevated temperature conditions, which method comprises: (a) establishing a composition for a second stage reaction step of reaction sintering and adapted for enhanced production of desired product; (b) providing sintering aid at least in part together with said composition and as loose particulate around said composition, which aid is solid at normal pressure and temperature and aids via the vapor phase at the pressure and temperature conditions of the second stage reaction step; (c) reducing the pressure around said composition; (d) heating said composition at a temperature for sintering; while (e) establishing sintering aid atmosphere in contact with said composition; and (f) maintaining the heating for a time sufficient to consolidate said composition, and thereby prepare a consolidate and purified product.
Claim 10
Independent Claim
152 words
The method of preparing a consolidated and purified Group IVb, Vb or VIb refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by means of aided, reduced pressure and elevated temperature conditions, which method comprises: (a) establishing a composition for a second stage reaction step of reaction sintering and adapted for enhanced production of desired product; (b) providing sintering aid at least in part together with said composition and as loose particulate around said composition, which aid is solid at normal pressure and temperature and aids via the vapor phase at the pressure and temperature conditions of the second stage reaction step; (c) reducing the pressure around said composition; (d) heating said composition at a temperature for sintering; while (e) establishing sintering aid atmosphere in contact with said composition; and (f) maintaining the heating for a time sufficient to consolidate said composition, and thereby prepare a consolidate and purified product.
Claim 11
Independent Claim
155 words
The method of preparing a consolidated and purified Group IVb, Vb or VIb refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by means of aided, reduced pressure and elevated temperature conditions, which method comprises: (a) establishing a composition for a second stage reaction step of reaction sintering and adapted for enhanced production of desired product; (b) providing sintering aid for aiding via the vapor phase in the seconnd stage reaction step of reaction sintering at reduced pressure; (c) reducing the pressure around said composition; (d) heating said composition at a temperature for sintering; while (e) establishing sintering aid atmosphere in contact with said composition by at least in part providing said aid in the vapor phase in a zone external to said second stage reaction step and feeding said vapor thereto; and (f) maintaining the heating for a time sufficient to consolidate said composition, and thereby prepare a consolidate and purified product.
Claim 12
Independent Claim
155 words
The method of preparing a consolidated and purified Group IVb, Vb or VIb refractory metal boride, carbide, nitride, or mixture, combination or cermet thereof by means of aided, reduced pressure and elevated temperature conditions, which method comprises: (a) establishing a composition for a second stage reaction step of reaction sintering and adapted for enhanced production of desired product; (b) providing sintering aid for aiding via the vapor phase in the seconnd stage reaction step of reaction sintering at reduced pressure; (c) reducing the pressure around said composition; (d) heating said composition at a temperature for sintering; while (e) establishing sintering aid atmosphere in contact with said composition by at least in part providing said aid in the vapor phase in a zone external to said second stage reaction step and feeding said vapor thereto; and (f) maintaining the heating for a time sufficient to consolidate said composition, and thereby prepare a consolidate and purified product.
References Cited (Backward Citations)
US2973247A
Cited
US3003885A
Cited
GB1004585A
Cited
US3316062A
Cited
US3379647A
Cited
US3749571A
Cited
US4008183A
Cited
US4108670A
Cited
US4275026A
Cited
JPS5738658A
Cited
US4486544A
Cited
US4492764A
Cited
US4500643A
Cited
US4514268A
Cited
US4592882A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-14 | 1991-03-16 | 1991-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-14 | 1995-03-16 | 1995-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-14 | 1999-03-16 | 1999-09-15 | $7700.00 | Window Closed / Lapsed |