Shaped refractory metal boride articles and method of making them
Assignee: Moltech Invent SA
•
Filing: 1983-12-27
•
Granted: 1985-02-19
•
Expires: 2003-12-27
Abstract
Abstract A shaped refractory article of titanium diboride or other metal has a microstructure with a weight average grain diameter of from 0.5 to 5 microns and substantially no grains larger than 10 microns diameter, from 10% to 45% by volume being made up of interconnected pores the majority having a diameter not substantially greater than 5 microns, porosity and grain size being substantially uniform throughout the microstructure, the article containing not more than about 0.2% by weight of oxygen and not more than about 0.5% by weight of carbon. The article may include inert particulate material in a matrix of the porous metal boride. The article may be formed by forming a uniformly mixed body of reactants into shaped compacts and heating the compacts to cause evolution of carbon monoxide and formation of a coherent reaction sintered product. Numerous reaction schemes are given, but the following are preferred: 2TiO.sub.2 +B.sub.4 C+3C→2TiB.sub.2 +4CO (1) TiO.sub.2 +B.sub.2 O.sub.3 +5C→TiB.sub.2 +5CO (2)
Inventors
- 👤 Adam J. Gesing
- 👤 Graham Stratford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 13:01
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C01; C01B; C01B35/00; C01B35/02; C01B35/04; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/636; C04B35/6365; C25; C25C; C25C3/00; C25C3/06; C25C3/08
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
96 words
A shaped refractory article of group IV b, V b, or VI b metal boride, which article has a microstructure with a weight average grain diameter of from 0.5 to 5 microns and substantially no grains larger than 10 microns diameter, from 10% to 45% by volume being made up of interconnected pores the majority having a diameter not substantially greater than 5 microns, porosity and grain size being substantially uniform throughout the microstructure, the article containing not more than about 0.2% by weight of oxygen and not more than about 0.5% by weight of carbon.
Claim 2
Dependent Claim
96 words
A shaped refractory article of group IV b, V b, or VI b metal boride, which article has a microstructure with a weight average grain diameter of from 0.5 to 5 microns and substantially no grains larger than 10 microns diameter, from 10% to 45% by volume being made up of interconnected pores the majority having a diameter not substantially greater than 5 microns, porosity and grain size being substantially uniform throughout the microstructure, the article containing not more than about 0.2% by weight of oxygen and not more than about 0.5% by weight of carbon.
Claim 3
Dependent Claim
16 words
A shaped refractory article as claimed in claim 1, wherein the metal boride is titanium diboride.
Claim 4
Dependent Claim
20 words
A shaped refractory article as claimed in claim 2, having a density of from 2.5 to 4.0 mg/mm 3 .
Claim 5
Dependent Claim
108 words
A shaped refractory composite of an inert particulate material in a matrix of a group IV b, V b, or VI b metal boride, which matrix has a microstructure with a weight average grain diameter of from 0.5 to 5 microns and substantially no grains larger than 10 microns diameter, from 10 to 45% by volume being made up of interconnected pores of which the majority have a diameter not substantially greater than 5 microns, porosity and a grain size being substantially uniform throughout the microstructure, the matrix containing not more than about 0.2% by weight of oxygen and not more than about 0.5% by weight of carbon.
Claim 6
Dependent Claim
108 words
A shaped refractory composite of an inert particulate material in a matrix of a group IV b, V b, or VI b metal boride, which matrix has a microstructure with a weight average grain diameter of from 0.5 to 5 microns and substantially no grains larger than 10 microns diameter, from 10 to 45% by volume being made up of interconnected pores of which the majority have a diameter not substantially greater than 5 microns, porosity and a grain size being substantially uniform throughout the microstructure, the matrix containing not more than about 0.2% by weight of oxygen and not more than about 0.5% by weight of carbon.
Claim 7
Dependent Claim
36 words
A shaped refractory composite as claimed in claim 4, wherein the inert particulate material is TiB 2 , Al 2 O 3 , AlON or AlN, and the metal boride of the matrix is titanium diboride.
Claim 8
Independent Claim
115 words
A method of making a shaped refractory article of a group IV b, V b, or VI b metal boride, or a refractory shaped composite of an inert particulate material in a matrix of the metal boride, which method comprises forming a uniformly mixed body of reactants containing the said metal as an oxide sub-oxide, borate or carbide, boron as an element, oxide or carbide, and if necessary carbon in the stoichiometric proportions desired to form the desired metal boride, boron suboxides and carbon monoxide, forming the reaction mixture optionally together with an inert particulate material into a shaped compact, and heating the shaped compact in an inert atmosphere to form a reaction sintered product.
Claim 9
Independent Claim
115 words
A method of making a shaped refractory article of a group IV b, V b, or VI b metal boride, or a refractory shaped composite of an inert particulate material in a matrix of the metal boride, which method comprises forming a uniformly mixed body of reactants containing the said metal as an oxide sub-oxide, borate or carbide, boron as an element, oxide or carbide, and if necessary carbon in the stoichiometric proportions desired to form the desired metal boride, boron suboxides and carbon monoxide, forming the reaction mixture optionally together with an inert particulate material into a shaped compact, and heating the shaped compact in an inert atmosphere to form a reaction sintered product.
Claim 10
Dependent Claim
31 words
A method as claimed in claim 6, wherein the uniformly mixed body of reactants is formed by precipitating one reactant on to a dispersion of another reactant and drying the mixture.
Claim 11
Dependent Claim
28 words
A method as claimed in claim 6, wherein the uniformly mixed body of reactants is formed by co-precipitating two or more of the reactants and drying the mixture.
Claim 12
Dependent Claim
15 words
A method as claimed in claim 6, wherein the metal boride is TiB 2 .
Claim 13
Dependent Claim
60 words
A method as claimed in claim 9, wherein the reaction mixture is formed by providing one or more of the reactants as a dispersion in an aqueous solution of a titanium halide and precipitating the titanium values on to the one or more dispersed reactants and drying the mixture and heating to convert the titanium values to TiO 2 .
Claim 14
Dependent Claim
14 words
A method as claimed in claim 10, wherein the titanium halide is titanium tetrachloride.
Claim 15
Dependent Claim
73 words
A method as claimed in claim 9, wherein the uniformly mixed body of reactants is formed by pre-heating a comminuted mixture of 2 molar parts of TiO 2 , substantially one molar part of B 4 C and substantially 3 atomic parts of C in vacuum or inert atmosphere to a temperature at which CO is evolved but below that at which TiB 2 is formed, and then cooling and grinding the mixture.
Claim 16
Dependent Claim
62 words
A method as claimed in claim 9, wherein the uniformly mixed body of reactants is formed by pre-heating a comminuted mixture of TiO 2 and C to produce an intermediate product consisting essentially of one or more titanium sub-oxides, and grinding and mixing the intermediate product with B 4 C and C in the proportions required to produce TiB 2 and CO.
Claim 17
Dependent Claim
21 words
A method as claimed in claim 12, wherein the comminuted mixture is pre-heated at a temperature not greater than 650° C.
Claim 18
Dependent Claim
40 words
A method as claimed in claim 9, wherein the uniformly mixed body of reactants is heated at a temperature of at least 1300° C. for a time to effect essentially complete formation of the TiB 2 and evolution of CO.
Claim 19
Dependent Claim
94 words
A method as claimed in claim 6, wherein the metal boride matrix has a microstructure with a weight average grain diameter of from 0.5 to 5 microns and substantially no grains larger than 10 microns diameter, from 10 to 45% by volume being made up of interconnected pores of which the majority have a diameter not substantially greater than 5 microns, porosity and a grain size being substantially uniform throughout the microstructure, the matrix containing not more than about 0.2% by weight of oxygen and not more than about 0.5 by weight of carbon.
Claim 20
Dependent Claim
15 words
A method as claimed in claim 7, wherein the metal boride is TiB 2 .
Claim 21
Dependent Claim
15 words
A method as claimed in claim 8, wherein the metal boride is TiB 2 .
References Cited (Backward Citations)
US4108670A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-19 | 1988-08-20 | 1989-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-19 | 1992-08-20 | 1993-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-19 | 1996-08-20 | 1997-02-19 | $7700.00 | Window Closed / Lapsed |